TEST REPORT No. : GZIN161202337CCM Date : Dec. 30, 2016 Page: 1 of 9 CUSTOMER NAME: UQESH ADVANCED MATERIALS TECHNOLOGY(SHANGHAI) CO., LTD. ADDRESS: ROOM 6008, 588 YINDU ROAD, MINHANG DISTRICT, SHANGHAI, CHINA. Sample Name : Waterborne polyurethane mortar Manufacturer : UQESH ADVANCED MATERIALS TECHNOLOGY(SHANGHAI) CO., LTD. Above information and sample(s) was/were submitted and confirmed by the client. SGS, however, assumes no responsibility to verify the accuracy, adequacy and completeness of the sample information provided by client. *********** SGS Ref. No. : GZIN161202337CCM Date of Receipt : Dec. 19, 2016 Testing Start Date : Dec. 19, 2016 Testing End Date : Dec. 27, 2016 Test result(s) : For further details, please refer to the following page(s) (Unless otherwise stated the results shown in this test report refer only to the sample(s) tested) Signed for and on behalf of SGS-CSTC Standards Technical Services Co.,Ltd Guangzhou Branch Authorized signatory
Transcript of TEST REPORT - 15093461.s21d-15.faiusrd.com
TEST REPORT
No. : GZIN161202337CCM
Date : Dec. 30, 2016
Page: 1 of 9
CUSTOMER NAME: UQESH ADVANCED MATERIALS TECHNOLOGY(SHANGHAI) CO.,
LTD.
ADDRESS: ROOM 6008, 588 YINDU ROAD, MINHANG DISTRICT, SHANGHAI,
CHINA.
Sample Name : Waterborne polyurethane mortar
Manufacturer : UQESH ADVANCED MATERIALS TECHNOLOGY(SHANGHAI) CO.,
LTD.
Above information and sample(s) was/were submitted and confirmed by the client. SGS, however, assumes no responsibility to verify the accuracy, adequacy and completeness of the sample information provided by client.
*********** SGS Ref. No. : GZIN161202337CCM
Date of Receipt : Dec. 19, 2016
Testing Start Date : Dec. 19, 2016
Testing End Date : Dec. 27, 2016
Test result(s) : For further details, please refer to the following page(s) (Unless otherwise stated the results shown in this test report refer only to the sample(s) tested)
Signed for and on behalf of SGS-CSTC Standards Technical Services Co.,Ltd Guangzhou Branch
Authorized signatory
TEST REPORT
No. : GZIN161202337CCM
Date : Dec. 30, 2016
Page: 2 of 9
Summary of Results:
No. Test Item Test Method Result Conclusion
1 Shore Hardness
With reference to GB/T
2411-2008 and client’s
requirement
See results /
Note: Pass : Meet the requirements;
Fail : Does not meet the requirements;
/ : Not Apply to the judgment.
Original Sample Photo:
Sample 1 Sample 2
Sample 3 Sample 4
TEST REPORT
No. : GZIN161202337CCM
Date : Dec. 30, 2016
Page: 3 of 9
Sample 5 Sample 6
Sample 7 Sample 8
Sample 9 Sample 10
TEST REPORT
No. : GZIN161202337CCM
Date : Dec. 30, 2016
Page: 4 of 9
Sample 11 Sample 12
Sample 13 Sample 14
Sample 15 Sample 16
TEST REPORT
No. : GZIN161202337CCM
Date : Dec. 30, 2016
Page: 5 of 9
Sample 17 Sample 18
Sample 19 Sample 20
Sample 21 Sample 22
TEST REPORT
No. : GZIN161202337CCM
Date : Dec. 30, 2016
Page: 6 of 9
Sample 23 Sample 24
Sample 25 Sample26
Sample 27
TEST REPORT
No. : GZIN161202337CCM
Date : Dec. 30, 2016
Page: 7 of 9
Test Item: Shore Hardness
Sample Description: See photo
Test Method: With reference to GB/T 2411-2008 and client’s requirement
Lab Environmental Condition: (23±2℃), (50±5)%RH
Test Result:
Sample
Test Condition
Test Result Reagent
Test
method
Specimen
thickness
1 10%(m/m) Bottle Additives YI XI
YANG C
Immersion
for 168h
Specimen
thickness: 7.91mm D/1:76
2 10%(m/m) XY-12 Specimen
thickness: 8.90mm D/1:87
3 10%(m/m) AC-3 CIP Acid Cleaner Specimen
thickness: 8.57mm D/1:87
4 10%(m/m) Bottle Additives YI XI
YANG A
Specimen
thickness: 7.74mm D/1:85
5 10%(m/m) OXONET Oxidizing Agent Specimen
thickness: 8.75mm D/1:82
6 10%(m/m) Quaternary Ammonium
Salt Disinfectant
Specimen
thickness: 8.83mm D/1:86
7 Run Bao EC Chain Lubricants Specimen
thickness: 8.86mm D/1:90
8 10%(m/m) OXODES Acid Generator Specimen
thickness: 8.78mm D/1:80
9 10%(m/m) OXOMIA ACTIVE
Peracetic Acid Fungicides
Specimen
thickness: 8.99mm D/1:83
10 10%(m/m) TOPAX 19 Alkaline Foam
Cleaner
Specimen
thickness: 8.12mm D/1:85
TEST REPORT
No. : GZIN161202337CCM
Date : Dec. 30, 2016
Page: 8 of 9
Sample
Test Condition
Test Result Reagent
Test
method
Specimen
thickness
11 10%(m/m) Bottle Additives YI XI
YANG C
Immersion
for 168h
Specimen
thickness: 8.99mm D/1:86
12 10%(m/m) XY-12 Specimen
thickness: 9.57mm D/1:82
13 10%(m/m) AC-3 CIP Acid Cleaner Specimen
thickness: 7.99mm D/1:87
14 10%(m/m) Bottle Additives YI XI
YANG A
Specimen
thickness: 8.01mm D/1:87
15 10%(m/m) OXONET Oxidizing Agent Specimen
thickness: 7.97mm D/1:86
16 10%(m/m) Quaternary Ammonium
Salt Disinfectant
Specimen
thickness: 8.12mm D/1:83
17 Run Bao EC Chain Lubricants Specimen
thickness: 8.25mm D/1:85
18 Tai Hua Shi®Lubricant
Specimen
thickness: 8.09mm D/1:81
19
10%(m/m) Tai Hua Shi ®
SPARTEC
Quaternary Ammonium Salt
Disinfectant
Specimen
thickness: 8.52mm D/1:82
20 30%（m/m）NaOH, 85℃ Specimen
thickness: 8.88mm D/1:86
TEST REPORT
No. : GZIN161202337CCM
Date : Dec. 30, 2016
Page: 9 of 9
Sample
Test Condition
Test Result Reagent
Test
method
Specimen
thickness
21 30%（m/m）NaOH
Immersion
for 168h
Specimen
thickness: 7.92mm D/1:86
22 Market Beer Specimen
thickness: 7.99mm D/1:88
23 12%（m/m）H3PO4+12%（m/m）
Citric Acid
Specimen
thickness: 8.87mm D/1:87
24 12%（m/m）Arawana®Peanut Oil
Specimen
thickness: 9.13mm D/1:86
25 12%（m/m）Sodium Hypochlorite Specimen
thickness: 9.64mm D/1:87
26 12%（m/m）H2O2 Specimen
thickness: 9.09mm D/1:82
27 - - Specimen
thickness: 9.31mm D/1:84
Note:
1. The smooth surface was tested.
2. The result was for reference only due to the uneven specimen surface.
3. D/1:X Indicated that D is the type of durometer; 1 s is the reading time; X is the hardness value.
4. The specimens were derive from the specimens of GZIN161202194CCM.
******* End of report********