Residual Stresses:
• Caused because of localized heating and cooling during welding, expansion and contraction of the weld area causes residual stresses in the work piece.
• Distortion,Warping and buckling of welded parts
• Stress corrosion cracking
• Further distortion if a portion of the welded structure is subsequently removed
• Reduced fatigue life
![Page 2: Residual stresses &distorsi](https://reader038.fdocuments.net/reader038/viewer/2022100507/55841688d8b42aa4398b47f3/html5/thumbnails/2.jpg)
Distortion after Welding
Fig : Distortion of parts after welding : (a) butt joints; (b) fillet welds. Distortion is caused by differential thermal expansion and contraction of different parts of the welded assembly.
![Page 3: Residual stresses &distorsi](https://reader038.fdocuments.net/reader038/viewer/2022100507/55841688d8b42aa4398b47f3/html5/thumbnails/3.jpg)
Residual Stresses developed during welding
Fig : Residual stresses developed during welding of a butt joint.
![Page 4: Residual stresses &distorsi](https://reader038.fdocuments.net/reader038/viewer/2022100507/55841688d8b42aa4398b47f3/html5/thumbnails/4.jpg)
Stress relieving of welds :
• Preheating reduces reduces problems caused by preheating the base metal or the parts to be welded
• Heating can be done electrically,in furnace,for thin surfaces radiant lamp or hot air blast
• Some other methods of stress relieving : Peening, hammering or surface rolling
![Page 5: Residual stresses &distorsi](https://reader038.fdocuments.net/reader038/viewer/2022100507/55841688d8b42aa4398b47f3/html5/thumbnails/5.jpg)
Weldability:• Capacity to be welded into a specific structure that has certain
properties and characteristics and will satisfactorily meet service requirements
• Thorough knowledge of the phase diagram is essential
• Factors such as strength, toughness, ductility, notch sensitivity, elastic modulus, specific heat, melting point, thermal expansion, surface tension characteristics of the molten metal, corrosion resistance.
Testing Welded Joints
• Quality of the welding joint is established by welded joint
• Each technique has capabilities ,limitations and sensitivity reliability and requirement for special equipment and operator skill.