Thermal Behavior of Materials ME 2105 Dr. R. Lindeke.
-
Upload
gretchen-mapp -
Category
Documents
-
view
253 -
download
3
Transcript of Thermal Behavior of Materials ME 2105 Dr. R. Lindeke.
![Page 1: Thermal Behavior of Materials ME 2105 Dr. R. Lindeke.](https://reader033.fdocuments.net/reader033/viewer/2022061601/551aa0d5550346e0158b58d4/html5/thumbnails/1.jpg)
Thermal Behavior of Materials
ME 2105Dr. R. Lindeke
![Page 2: Thermal Behavior of Materials ME 2105 Dr. R. Lindeke.](https://reader033.fdocuments.net/reader033/viewer/2022061601/551aa0d5550346e0158b58d4/html5/thumbnails/2.jpg)
Some Definitions
• Heat Capacity: the amount of heat (energy) required to raise a fundamental quantity of a material 1 K˚
• The quantity is usually set at 1 gm-atom (elements) or 1 gm-mole (compounds)• Given by the foumula: C=q/(mT) in units of J/gm-
atom* K˚ or J/gm-mole* K˚
• Specific Heat: a measure of the amount of heat energy to raise a specific mass of a material 1 K˚
![Page 3: Thermal Behavior of Materials ME 2105 Dr. R. Lindeke.](https://reader033.fdocuments.net/reader033/viewer/2022061601/551aa0d5550346e0158b58d4/html5/thumbnails/3.jpg)
Heat Capacity
• Heat capacity is reported in 1 of two ways: • Cv – the heat capacity when a constant volume of
material is considered• Cp – the heat capacity when a constant pressure is
maintained while higher than Cv these values are nearly equal for most materials• Cp is most common in engineering applications (heat
stored or needed at 1 atm of pressure)• At temperature above the Debye Temperature Cv 3R
Cp
![Page 4: Thermal Behavior of Materials ME 2105 Dr. R. Lindeke.](https://reader033.fdocuments.net/reader033/viewer/2022061601/551aa0d5550346e0158b58d4/html5/thumbnails/4.jpg)
![Page 5: Thermal Behavior of Materials ME 2105 Dr. R. Lindeke.](https://reader033.fdocuments.net/reader033/viewer/2022061601/551aa0d5550346e0158b58d4/html5/thumbnails/5.jpg)
Definitions• Thermal Expansion is the “growth” of materials due to
increasing vibration leading to larger inter-atomic distances and increasing vacancy counts for materials as temperature increases
![Page 6: Thermal Behavior of Materials ME 2105 Dr. R. Lindeke.](https://reader033.fdocuments.net/reader033/viewer/2022061601/551aa0d5550346e0158b58d4/html5/thumbnails/6.jpg)
Thermal Expansion
• Linear thermal expansion is given by this model:
• As an Example:• A gold ring (diameter = 12.5 mm) is worn by a person,
they are asked to wash the dishes at their apartment – water temperature is 50˚C – how big is the ring while it is submerged?
dL
LdT
![Page 7: Thermal Behavior of Materials ME 2105 Dr. R. Lindeke.](https://reader033.fdocuments.net/reader033/viewer/2022061601/551aa0d5550346e0158b58d4/html5/thumbnails/7.jpg)
Thermal Expansion is “Temperature Dependent”
![Page 8: Thermal Behavior of Materials ME 2105 Dr. R. Lindeke.](https://reader033.fdocuments.net/reader033/viewer/2022061601/551aa0d5550346e0158b58d4/html5/thumbnails/8.jpg)
Solving:
0
0 0
37.5 27 37.537.5
37.5 27
37.5
50
6
60
data from table 7.2
* 12.5*3.14159 39.2699
14.1
16.5 14.1
14.15
similarly for 50 : 14.21
14.21 14.1514.18*102
14.18*10 *39.2
avg
avg
L L T
L d
mmmm C
L L T
7*12.5 0.007
39.27 .00712.502f
mm
D mm
![Page 9: Thermal Behavior of Materials ME 2105 Dr. R. Lindeke.](https://reader033.fdocuments.net/reader033/viewer/2022061601/551aa0d5550346e0158b58d4/html5/thumbnails/9.jpg)
Definition:
• Thermal Conductivity: the transfer of heat energy through a material (analogous to diffusion of mass)
• Modeled by:• Note, k is a function of
temperature (like was)
at steady state conditions:
dQdtk
dTA dx
Qtk
TA x
![Page 10: Thermal Behavior of Materials ME 2105 Dr. R. Lindeke.](https://reader033.fdocuments.net/reader033/viewer/2022061601/551aa0d5550346e0158b58d4/html5/thumbnails/10.jpg)
• Modeling Fourier’s Law of Thermal Conduction (heat flow thru a bounded area)
![Page 11: Thermal Behavior of Materials ME 2105 Dr. R. Lindeke.](https://reader033.fdocuments.net/reader033/viewer/2022061601/551aa0d5550346e0158b58d4/html5/thumbnails/11.jpg)
Thermal Conductivity
• Involves two primary (atomic level) mechanisms:• Atomic vibrations – in ceramics and polymers this dominates• Conduction by free electrons – in metals this dominates
• Focusing on Metals: • thermal conductivity decreases as temperature increases
since atomic vibration disrupt the primary free electron conduction mechanism
• Adding alloying “impurities” also disrupts free electron conduction so alloys are less conductive than pure metals
![Page 12: Thermal Behavior of Materials ME 2105 Dr. R. Lindeke.](https://reader033.fdocuments.net/reader033/viewer/2022061601/551aa0d5550346e0158b58d4/html5/thumbnails/12.jpg)
Thermal Conductivity
• Focusing on Ceramics and Polymers: • Atomic/lattice vibrations are “wave-like” in nature and
impeded by structural disorder• Thermal conductivity will, thus, drop with increasing
temperature• In some ceramics, which are “transparent” to IR radiation,
TC will eventually rise at elevated temperatures since radiant heat transfer will begin to dominate “mechanical” conduction
• Porosity level has a dramatic effect of TC (pores are filled with low TC gases which limits overall TC for a structure (think fiberglass insulation and ‘stryo-foam’ cups)
![Page 13: Thermal Behavior of Materials ME 2105 Dr. R. Lindeke.](https://reader033.fdocuments.net/reader033/viewer/2022061601/551aa0d5550346e0158b58d4/html5/thumbnails/13.jpg)
![Page 14: Thermal Behavior of Materials ME 2105 Dr. R. Lindeke.](https://reader033.fdocuments.net/reader033/viewer/2022061601/551aa0d5550346e0158b58d4/html5/thumbnails/14.jpg)
Continuing Table 7.4:
![Page 15: Thermal Behavior of Materials ME 2105 Dr. R. Lindeke.](https://reader033.fdocuments.net/reader033/viewer/2022061601/551aa0d5550346e0158b58d4/html5/thumbnails/15.jpg)
Figure 7.5 Thermal conductivity of several ceramics over a range of temperatures.
(From W. D. Kingery, H. K. Bowen, and D. R. Uhlmann, Introduction to Ceramics, 2nd ed., John Wiley & Sons, Inc., New York, 1976.)
![Page 16: Thermal Behavior of Materials ME 2105 Dr. R. Lindeke.](https://reader033.fdocuments.net/reader033/viewer/2022061601/551aa0d5550346e0158b58d4/html5/thumbnails/16.jpg)
Definition:
• Thermal Shock: it is simply defined as the fracture of a material (usually a brittle ceramic) as the result of a (sudden) temperature change and is dependent of the interplay of the two material behaviors: thermal expansion and thermal conductivity
• Thermal Shock can be explained in one of two ways:• Failure stress can be built up by constrained thermal
expansion• Rapid temperature changes lead to internal temperature
gradients and internal residual stresses – finite thermal conductivity reasoning – see figure 7.7
![Page 17: Thermal Behavior of Materials ME 2105 Dr. R. Lindeke.](https://reader033.fdocuments.net/reader033/viewer/2022061601/551aa0d5550346e0158b58d4/html5/thumbnails/17.jpg)
By Constrained Thermal Expansion:
Figure 7.6 Thermal shock resulting from constraint of uniform thermal expansion. This process is equivalent to: a. free expansion followed by; b. mechanical compression back to the original length.
![Page 18: Thermal Behavior of Materials ME 2105 Dr. R. Lindeke.](https://reader033.fdocuments.net/reader033/viewer/2022061601/551aa0d5550346e0158b58d4/html5/thumbnails/18.jpg)
Let’s Consider an Example:
• A 400 mm long ‘rod’ of Stabilized ZrO2 ( = 4.7x10-6 mm/mm˚C) is subject to a thermal cycle in a ‘ceramic’ engine – it’s the crank shaft! – from RT (25˚C) to 800˚C. Determine the induced stress and determine if it is likely to fail?
• E for Stabilized ZrO2 is 150 GPa – table 6.4
• MOR for Stabilized ZrO2 is 83 MPa -- table 6.4
![Page 19: Thermal Behavior of Materials ME 2105 Dr. R. Lindeke.](https://reader033.fdocuments.net/reader033/viewer/2022061601/551aa0d5550346e0158b58d4/html5/thumbnails/19.jpg)
exp
0
6
where:
4.7*10 * 800 25 0.00364
150 *0.00364 0.546 546
TI TI
TTI
TI
TI
E
ll
mmT mmmmMPa GPa MPamm
Since the Inducted Compressive Stress exceeds the MOR (from Table 6.4) one might expect the ‘rod’ to fail or rupture – unless it is allowed to expand into a designed in ‘pocket’ built into the engine block to accept the shaft’s expansion
![Page 20: Thermal Behavior of Materials ME 2105 Dr. R. Lindeke.](https://reader033.fdocuments.net/reader033/viewer/2022061601/551aa0d5550346e0158b58d4/html5/thumbnails/20.jpg)
By Thermal Conductivity (induced)Temperature Gradients:
Figure 7.7 Thermal shock resulting from temperature gradients created by a finite thermal conductivity. Rapid cooling produces surface tensile stresses and Griffith Crack Generation.
![Page 21: Thermal Behavior of Materials ME 2105 Dr. R. Lindeke.](https://reader033.fdocuments.net/reader033/viewer/2022061601/551aa0d5550346e0158b58d4/html5/thumbnails/21.jpg)
Figure 7.8 Thermal quenches that produce failure by thermal shock are illustrated. The temperature drop necessary to produce fracture (T0 − T) is plotted against a heat-transfer parameter (rmh). More important than the values of rmh are the regions corresponding to given types of quench (e.g., water quench corresponds to an rmh around 0.2 to 0.3).
(From W. D. Kingery, H. K. Bowen, and D. R. Uhlmann, Introduction to Ceramics, 2nd ed., John Wiley & Sons, Inc., New York, 1976.)