Textile architecture 13 31 00/FERBuyLine 8605

Composite membranes for textile architecture, manufactured according to the exclusive Précontraint® technology.• Optimum and controlled translucency• Exceptional dimensional stability and consistency of production from

batch to batch• Long term durability thanks to a superior top coat thickness• Fluotop® T2 surface treatment• 20 year experience in high concentration PVDF formulation for better

weathering and better aesthetics.• Formula S surface treatment• Calibrated PVDF treatment designed for permanent or temporary structures• Production possible in a wide range of colors• 100 % recyclable through the Texyloop process• Life Cycle Assessment (LCA) data available

2

Textile architecture

Thermal performance: membrane optionsNEW Low Emissivity treatment:

• By applying a calibrated Low Emissivity (LowE) aluminiumtreatment, the fabric becomes a reinforced thermal shield.

• Its capacity to reflect and produce heat is considerably reduced, thus contributing to the decreasing of energycosts.

• In the winter months the low emissivity treatment on the interior of the membrane reduces heat loss, and instead reflects it back into the building.

• For more accurate information regarding heat gain or loss;ask for examples using our TexTherm modeling software.

Single membrane option• 1002 T2 Opaque LowE

Double membrane option• 1002 T2 LowE outer skin• 402 translucent inner skin

Worldwide patented Ferrari® Précontraint® technology consistsof pre-stressing the textile base cloth both before and duringthe coating process.

This technology results in unrivalled dimensional stability• limited creep over time • longer life • performance homogeneity from batch to batch.

The exclusive Précontraint® Ferrari® technology

Weave of high-tenacitypolyester yarns

Two-way tensioningkeeps yarns completely straight

Surfacetreatment

Conventional coatedtextiles present a high levelof crimp in the weft direction.

Conventional coatedtextiles exhibit seriousdeformation of the weftyarn which in additionvary greatly from onebatch to the other.

Ferrari® Précontraint®

textiles respect the weftyarn direction which stays identical from one batchto the other.

Précontraint® 702

Type I classic coated textile

Précontraint® textileshave very low crimp,that is similar in bothwarp and weft direction.

3

Textile architecture 13 31 00/FERBuyLine 8605

Technical properties Précontraint® 1002 T2 Opaque LowE Précontraint® 402 Translucent Standards

Yarn 1100 Dtex PES HT 1100 Dtex PES HT

Weight 1050 g/m² / 31 oz/sq.yd 490 g/m² / 14.45 oz/sq.yd EN ISO 2286-2

Width 178 cm / 70.1 in 267 cm / 105.1 in (-1mm/+1mm)

Tensile strength 420/400 daN/5 cm 250/250 daN/5 cm ASTM D 751-00 P.16(warp/weft) 944/899 lbs/2 in 562/562 lbs/2 in Cut Strip Method

Tear strength 55/50 daN 20/20 daN ASTM D 751-00 P.37(warp/weft) 124/112 lbs 45/45 lbs Trapezoid Tear Method

Flame retardancy Test 2/NFPA 701 • CSFM T19 • CSFM T19 • CLASS C/ASTM E108 • G1/GIST30244-94G1/GIST30244-94

Euroclass B-s2,do B-s2,do EN 13501-1

Surface treatment Fluotop® T2 (High concentration PVDF) Both sides varnishThe technical data here above are average values with a+/- 5% tolerance.

Customgraphics

100%recyclable textile (upon request)

U.V.resistant (upon request)

Dimensionalstability

Technical features

Shade structures with open mesh: Précontraint® 392S

Long lifeEasymaintenance

Technical properties Précontraint® 392S Standards

Yarn 1100 Dtex PES HT

Weight 820 g/m² / 24 oz/sq.yd EN ISO 2286-2

Width 180 cm / 70.8 in (-1mm/+1mm)

Tensile strength 300/300 daN/5 cm ASTM D 751-00 P.16(warp/weft) 674/674 lbs/2 in Cut Strip Method

Flame retardancy Test 2/NFPA 701 • CSFM T19

Surface treatment Formula S / Weldable calibrated PVDF alloyThe technical data here above are average values with a+/- 5% tolerance.

Specification service The Ferrari® specification service is available toinform you, advise you and suggest innovativesolutions for your specific requirements.

For more information, please go to: www.ferrari-architecture.com

CSI Specifications available upon request at info@ferraritextiles.com

100% recyclable Ferrari® developed the Texyloop® technologyspecifically for the recycling of compositePVC membranes and textiles. Through themanagement of its end-of-life products Ferrari®

is committed to sustainable development.www.texyloop.com

Sustainable developmentFerrari® development is based on strict adherance to good safety and environmentalpractices, that include an understanding ofLife Cycle Analysis (LCA), selection of thebest materials, and eco-design.The Company obtained its first ISO 14001 certification in 2003.

4

FERRARI SALa Tour du Pin - FRANCETel: +33 (0)4 74 97 41 33Fax: +33 (0)4 74 97 67 20

STAMOID AGEglisau - SWITZERLANDTel: +41 (0)44 868 26 26Fax: +41 (0)44 868 27 27

EUROPEFERRARI TEXTILES CORP.Florida - USATel: +1 954 942 3600Fax: +1 954 942 5555

NORTH AMERICAFERRARI DUBAIDubai - U.A.ETel: +971 4 886 5506Fax: +971 4 886 5507

MIDDLE EASTFERRARI CHINAShanghaiTel: +86 21 6211 6936 Fax: +86 21 6211 6389

CHINAFERRARI HONG-KONG LTDHONG-KONGTel: +852 3622 1340Fax: +852 3622 1354

ASIA - PACIFICFERRARI LATINOAMERICA S.A.Santiago - CHILETel: +56 2 737 0909Tel: +56 2 737 2818

São Paulo - BRAZILTel: +55 11 3262 3405Mexico - MEXICOTel: +52 55 5018 5742

LATIN AMERICA

Textile architecture

Technical properties Précontraint® 1002 Précontraint® 1202 Précontraint® 1302 Précontraint® 1502 Standards

Weight 1050 g/m² 1050 g/m² 1350 g/m² 1500 g/m² EN ISO 2286-231 oz/sq.yd 31 oz/sq.yd 39.8 oz/sq.yd 44.2 oz/sq.yd

Width (-1mm/+1mm)Fluotop® T2 178 cm / 70.1 in 178 cm / 70.1 in 178 cm / 70.1 in 178 cm / 70.1 inFormula S 180 cm / 70.8 in 180 cm / 70.8 in 180 cm / 70.8 in 180 cm / 70.8 in

Tensile strength 420/400 daN/5 cm 560/560 daN/5 cm 800/700 daN/5 cm 1000/800 daN/5 cm ASTM D 751-00 P.16(warp/weft) 944/899 lbs/2 in 1259/1259 lbs/2 in 1798/1574 lbs/2 in 2248/1798 lbs/2 in Cut Strip Method

Tear strength 55/50 daN 80/65 daN 120/110 daN 160/140 daN ASTM D 751-00 P.37(warp/weft) 124/112 lbs 180/146 lbs 270/247 lbs 360/315 lbs Trapezoid Tear Method

Flame retardancy Test 2/NFPA 701 • CSFM T19 • CLASS C/ASTM E108 • UBC 31-1

Back side treatment Weldable PVDF (for a better resistance to pollution of the reverse side of the fabric)

Surface treatmentFluotop® T2 Fluotop® T2 (High concentration PVDF) / no weldableFormula S Formula S PVDF alloy / weldable

Product applicationFluotop® T2 Permanent structures onlyFormula S Static and permanent structures

The technical data here above are average values with a+/- 5% tolerance.

Flame retardant

100%recyclable textile (upon request)

U.V.resistant (upon request)

Dimensionalstability

Technical features

Long life Easymaintenance