REWITEC NanocoatingDurable Wear Protection and Reconditioning

for high loaded Gearboxes and Bearings

in Windturbines

All Energy 2011

That is our world…

REWITEC presents the unique possibility

to coat, to protect and to recondition new and worn outmetal surfaces!

REWITEC-Technology

What happens to the lubricant?

Replacement of the friction pair „metal-metal“ by „meta l ceramic-metal ceramic“

Advantages:

Reduction of abrasion and wear of rubbing metal surfaces

Coating process during system is running, without down time

Obvious increase and smoothening of load carrying areas

Prolongation of gearbox and bearing life time

Targets of REWITEC Technology

Reduction of friction, vibration and noise

Cost saving by:

Extension of lifetime Reduction of repairs Prolongation of maintenance intervals Bridging of delivery times/ Planned exchange possible

Improvement of efficiency:

Savings of energy and fuel up to 11 %

Reduction of emissions (Diesel soot, CO2, HC und NOx)

Emergency running properties in case of oil loss

Advantages of REWITEC Technology

Damages of gear wheels before Rewitec

Repair, freeze, better prevent demages!

Damages of gear wheels after Rewitec

Repair, freeze, better prevent demages!

Gear teeth before and after REWITEC Treatment

The microsection shows the running surface of a ball bear ing of a planet gear box after 250 hours of operation in an area of fatigue. The Rewitec Coating up to 30µm could be obviously recognized.

Microsection of a ball bearing surface

Rewitec Coating

Origin metal

Test on 2 gears of company Tandler

HL HWS A1 3.1 IIITests with Rewitec

0

20

40

60

80

100

120

140

10:3

0:44

12:3

5:32

14:4

0:12

16:4

5:32

18:5

0:28

20:5

5:53

23:0

0:39

01:0

5:49

03:1

0:57

05:1

5:33

07:2

0:55

09:2

5:50

11:3

0:54

13:3

5:58

15:4

1:03

17:4

6:07

19:5

1:11

21:5

6:15

23:5

9:45

02:0

6:02

04:1

1:21

06:1

5:56

08:2

1:03

10:2

6:11

12:3

1:19

14:3

6:26

16:4

1:34

18:4

6:42

20:5

0:41

22:5

5:22

01:0

0:54

03:0

5:48

05:1

0:58

07:1

5:56

09:2

0:58

11:2

5:57

13:3

1:01

Time in hms

Tem

pera

ture

in °C

[°C] 23/1

[°C] 23/2

[°C] 23/3

[°C] 23/4

[°C] 28/5

[°C] 27/6

[°C] 27/7

[°C] 27/8

[°C] 27/9

Temperature trend of the 2 Tandler gears with 2 differen t oils with and without Rewitec- Temperature reduction of 6 – 10 ºCelsius

Temperature Oil 1 107,7 ºCTemperature Oil 2 103,5º C

Fill in of the oil with the Rewitec concentrate at the start temperature of 113,5º Celsius

Bearing load test comparisenOEM grease versus REWITEC treated OEM grease in a 2 0.000 N bearing load test

Temperature measurement at axial bearings type 81105: Results: Bearings with untreated grease failed after about 7 hours load test. Bearings withRewitec treated grease did not fail for over 19 hours. The bearings running with Rewitec lasted for around 2.7 times longer.

Bearing Load Test

0

20

40

60

80

100

120

1 423 845 1267 1689 2111 2533 2955 3377 3799 4221 4643 5065 5487 5909 6331 6753 7175 7597 8019

Time/ sec.

Tem

pera

ture

/ deg

ree

Cel

sius

Fett rot

Fett rot

Fett rot mit Rewitec

Fett rot mit Rewitec

Complete Failure

--- Grease without

--- Rewitec

--- Grease treated with

--- Rewitec

Bearing load test comparisenOEM grease versus REWITEC treated OEM grease in a 2 0.000 N bearing load test

Friction measurement at axial bearings type 81105: Results: Bearings with untreated grease failed after about 7 hours load test. Bearings with Rewitec treated grease did not fail for over 19 hours. The bearings running withRewitec lasted for around 2.7 times longer.

Zerstörung der Lager

Bearing Load Test

-5

0

5

10

15

20

25

30

35

40

1 352 703 1054 1405 1756 2107 2458 2809 3160 3511 3862 4213 4564 4915 5266 5617 5968 6319 6670 7021 7372 7723 8074

Time/sec.

Load

/Nm

Fett rot

Fett rot

Fett rot mit Rewitec

Fett rot mit Rewitec

Complete Failure

--- Grease without

--- Rewitec

--- Grease treated with

--- Rewitec

Photos of the raceways of two ball bearings after 5 0 hours of operation in a range of fatigue

Bearing type: No. 6205 (d=25mm D=52mm)Lubricant: Special bearing greaseOperating time: 50 hoursRotational speed: 500 min -1

Nominal load: 5000 N radial (range of fatigu e)

This ball bearing does not show any wear. The runni ng surface of the balls clearly shows a wear resistant coating.

Load Test of Ball Bearings

This ball bearing shows damage due to wear and tear. The running surface of the balls clearly shows pitting

Bearing type: No. 6205 (d=25mm D=52mm)Lubricant: Special bearing grease treated with REWITECOperating time: 50 hoursRotational speed: 500 min -1

Nominal load: 5000 N radial (range of fatigu e)

running surfacesof the balls

Range of Applications

Industry

Automotive

Shipping

Industry:

Gears

Combustion engines Compressors

Bearings

Hydraulic pumps/ -motors

Vacuum pumps Chain drives

Gear racks, pinions

Range of REWITEC applications

Utility vehicles:

Gasoline- and diesel engines Gears Rear axles, differentials Universal shafts Compressors Roller-, slide bearings

Range of REWITEC applications

Railways:

Diesel engines Gears Compressors Bearings

REWITEC applications in shipping business

Treatment of 2 drill head gears at Volkswagen engines produktion line in Salzgitter

Problem:Short lifetime, extreme high costs in case of idleness and breakdown (>25.000,-€), higher oiltemperature (51°C). Emergency run problems due to oil le akage.

Result: Oil and oil filter are clean with nearly no metal particles. After REWITEC coating oiltemperature was reduced by about 6°C to max. 45°C. Due to a system leakage drillingemulsion went into the gearbox. The REWITEC Nanocoating prevented the system againstdamages.

Savings of about 100,000 Euro p.a.Treatment costs are 149 Euro per gearbox

Coating of a wind turbine gearbox of a Tacke TW250

Goal of application: - Rebuilding of worn out teeth surfaces- Reduction of grey stoking- Protection against further wear and prolongation of life time

Results after about 700 hours operating time:- The teeth surfaces are much smoother and more shiny (replicas before and after) - The damages are without sharp edges- The coated teeth surfaces had a higher electrical resistance of about 50 Ω

Savings of about 80,000 EuroTreatment costs are 1,200 Euro

Coating and analyses of a 600KW wind turbine gearbox

Goal of application: - Reduction of grey staining- Protection against further wear and prolongation of life time

Condition after 64 days operating time:- The teeth surfaces are much smoother and more shiny (replicas before and after) - The damages are without sharp edges- The coated teeth surfaces had a higher electrical resistance of about 100 Ω

Savings of about 150,000 EuroTreatment costs are 2,560 Euro

Coating and analyses of 1MW Windturbine gearbox

Before Rewitec treatment at 17.03.2009 After Rewitec treatment at 23.09.2009

Results after 150 days: - The teeth surfaces are much smoother and more shiny (replicas before and after) -3D-Topografie-Analyses of NanoFocus AG with µsurf-Technology proves that the surface smoothening/

refinement and results in a 18-times bigger load carrying tooth area!

Topography

Coating of a AN Bonus 1MW wind turbine gearbox

Goal of application: - Rebuilding of worn out teeth surfaces and Reduction of grey stoking- Anaylsis via µ-Sen CMS- Protection against further wear and prolongation of life time

Results after about 700 hours operating time:- The teeth surfaces are much smoother and more shiny (replicas before and after) - The coated teeth surfaces had a higher electrical resistance of about 50 Ω- µ-Sen CMS shows a 20% reduced damage frequency and noise in the system

Coating of a AN Bonus 1MW wind turbine generator beari ng

Goal of application: - Wear protection of generator bearing, due to use of Rewitec coating grease in December 2008- Anaylsis via µ-Sen CMS (Condition Monitoring System)- Protection against further wear and prolongation of life time

Results after 6 months: -µ-Sen CMS shows clearly the stop of the progressive increase of the damage frequency in generator bearing

We have treated already about 600-700 wind turbines:

AN Bonus 1,0MW, 1,3MWDeWind D4, D6GE 1,5MWGamesa G47HSW1000 1,0MWNEG Micon NM48, NM60, NM82Nordex S70, S77, N90, N54Repower 5MSuzlon different typesTacke TW250, TW600, 1.5sVestas V20, V25, V39, V47, V66, V80

Already treated wind turbines

26

Wind Energy Update on Wind Mill O & M

Press ReleaseNew report defines true cost of wind turbine operatio ns & maintenance

March 1, 2010

“Gearboxes are still the Achilles’ heel for the wind industry, and can cost up to $500,000 to fix due to the high cost of replacement parts, cranes (which can cost $75,000-$100,000), post installation testing, re-commissioning and lost power production,” says one long-term veteran O&M technician.

Economy of the Nano Coating in case of breakdown

6,2 daysAmortization time due to down time

4,3 months**Amortization time dueto longer life time

6.400,- EuroCosts of treatment

1.028,- EuroCommission per day

9,5 Ct/ kWhCommission

10.822 kWh Output per day

3.950.000 kWh *Output per year

1.500 kWTurbine Power

*Output related to referenz location with a medium yearly wind speed of 5,5m/s** Prolongation of life time with a bank rate of 6% and costs of a new gearbox 300.000,- Euro

Economy of the Treatment „WPD“

5,9 Mio. EuroExpected cost reductions per year

3.511 GWh** Energy Production per year (GWh)

50%Expected reduction of gearbox replacements

15 – 20%Increase of net profit

2,52 Mio. EURTreatment costs Rewitec per year

16,78 Mio. EURTotal downtime costs per year

2,63 Mio. EUR**** Downtime costs per year

14,15 Mio. EUR*** Gearbox replacement costs per year

316 Mio. Euro *** Revenues per year (Euro)

1.179 MW* Total Power

* Without Enercon, Status 2009** Production related to average wind speed of 6,5m/s, 9 Ct/kWh feed in tarif*** Expected is 1 gearbox replacement in 10 years with 120 TEUR per MW**** Expected is 30 days downtime für gearbos replacementl

• Surfaces pictures, endoscopies

• Oil analyses

• Measurements of the electrical resistance of the coated s urfaces

• Imprints of tooth- and bearing surfaces

• Condition Monitoring

Proof of REWITEC Technology

28. Innovation Award of German Economy Wirtschaft

0n 19th of January 2008 REWITEC was announced as finalist of 28. German Innovation Award 2007. The Award for one of the best innovations in 2007 was presented to REWITEC from the Ministry of Economics and Technology in the „Old Opera“ in Frankfurt.

1st Husum WindEnergy Award 2009

REWITEC was Finalist of the 1st HUSUM WindEnergy Award 2009. REWITEC‘s„Nanocoating for Tribosystems“ is belonging now to one of the best innovations forwind industry.

Present cooperations and customers

HatlapaMarine EquipmentPeterson & Söhne

ThyssenKruppZollern

Leonhardt & Blumberg

Thank you for your attention !

Stefan Bill, Managing Director

bill@rewitec.com

Mobil: +49(0)173/6790063

Tel: +49(0)6441/44599-0