SiO2 etching with ZEP520A resist mask · 2009. 2. 4. · some small extra buffer for Si etching....
Transcript of SiO2 etching with ZEP520A resist mask · 2009. 2. 4. · some small extra buffer for Si etching....
![Page 1: SiO2 etching with ZEP520A resist mask · 2009. 2. 4. · some small extra buffer for Si etching. The etch rate of resist with the DEVIN1.SET recipe is known to be ~4.6nm/sec. Prior](https://reader035.fdocuments.net/reader035/viewer/2022070218/61238cf31f561362fb14b20e/html5/thumbnails/1.jpg)
Si etching with ZEP520A resist and oxide hard mask
Devin Brown2/04/09
![Page 2: SiO2 etching with ZEP520A resist mask · 2009. 2. 4. · some small extra buffer for Si etching. The etch rate of resist with the DEVIN1.SET recipe is known to be ~4.6nm/sec. Prior](https://reader035.fdocuments.net/reader035/viewer/2022070218/61238cf31f561362fb14b20e/html5/thumbnails/2.jpg)
Summary• ZEP520A typically has a 1:1 dry plasma etch
selectivity relative to Si and SiO2• required lateral pattern dimensions usually
restrict ZEP520A thickness to less than 600nm• if more than 600nm of Si or SiO2 is desired to be
etched, then 600nm of ZEP20A will be insufficient
• this summary shows how an SiO2 "hard mask" can be used to etch Silicon to depths beyond what would be possible with ZEP520A alone
![Page 3: SiO2 etching with ZEP520A resist mask · 2009. 2. 4. · some small extra buffer for Si etching. The etch rate of resist with the DEVIN1.SET recipe is known to be ~4.6nm/sec. Prior](https://reader035.fdocuments.net/reader035/viewer/2022070218/61238cf31f561362fb14b20e/html5/thumbnails/3.jpg)
Process Flow
ZEP520A resist
PECVD oxide
silicon substrate
ZEP520A resist
PECVD oxide
silicon substrate
ZEP520A resistPECVD oxide
silicon substrate
PECVD oxide
silicon substrate
1. resist coat
2. EBL expose/develop
3. SiO2 hard mask etch
4. Si etch
![Page 4: SiO2 etching with ZEP520A resist mask · 2009. 2. 4. · some small extra buffer for Si etching. The etch rate of resist with the DEVIN1.SET recipe is known to be ~4.6nm/sec. Prior](https://reader035.fdocuments.net/reader035/viewer/2022070218/61238cf31f561362fb14b20e/html5/thumbnails/4.jpg)
Process Flow• PECVD oxide dep• Resist Coat
– ZEP520A• EBL exposure
– 100kV, 2nA• Resist Develop
– 2min immersion n-Amyl Acetate, 30sec immersion IPA rinse• SiO2 etch
– Plasma Therm ICP– 5mTorr, 25sccm C4F6, 15sccm CF4, 4sccm Ar, 4sccm O2, RF1 =
400W, RF2 = 400W• Si etch
– STS SOE ICP– 5mTorr, 20sccm Cl2, 5sccm Ar, coil = 600W, plate = 50W
![Page 5: SiO2 etching with ZEP520A resist mask · 2009. 2. 4. · some small extra buffer for Si etching. The etch rate of resist with the DEVIN1.SET recipe is known to be ~4.6nm/sec. Prior](https://reader035.fdocuments.net/reader035/viewer/2022070218/61238cf31f561362fb14b20e/html5/thumbnails/5.jpg)
Post expose/develop
![Page 6: SiO2 etching with ZEP520A resist mask · 2009. 2. 4. · some small extra buffer for Si etching. The etch rate of resist with the DEVIN1.SET recipe is known to be ~4.6nm/sec. Prior](https://reader035.fdocuments.net/reader035/viewer/2022070218/61238cf31f561362fb14b20e/html5/thumbnails/6.jpg)
ZEP520A
PECVD SiO2
Si substrate
2um line post expose/develop
![Page 7: SiO2 etching with ZEP520A resist mask · 2009. 2. 4. · some small extra buffer for Si etching. The etch rate of resist with the DEVIN1.SET recipe is known to be ~4.6nm/sec. Prior](https://reader035.fdocuments.net/reader035/viewer/2022070218/61238cf31f561362fb14b20e/html5/thumbnails/7.jpg)
ZEP520A
PECVD SiO2
Si substrate
0.5um line post expose/develop
![Page 8: SiO2 etching with ZEP520A resist mask · 2009. 2. 4. · some small extra buffer for Si etching. The etch rate of resist with the DEVIN1.SET recipe is known to be ~4.6nm/sec. Prior](https://reader035.fdocuments.net/reader035/viewer/2022070218/61238cf31f561362fb14b20e/html5/thumbnails/8.jpg)
100nm line post expose/develop
ZEP520A
PECVD SiO2
Si substrate
![Page 9: SiO2 etching with ZEP520A resist mask · 2009. 2. 4. · some small extra buffer for Si etching. The etch rate of resist with the DEVIN1.SET recipe is known to be ~4.6nm/sec. Prior](https://reader035.fdocuments.net/reader035/viewer/2022070218/61238cf31f561362fb14b20e/html5/thumbnails/9.jpg)
Post partial SiO2 etch
![Page 10: SiO2 etching with ZEP520A resist mask · 2009. 2. 4. · some small extra buffer for Si etching. The etch rate of resist with the DEVIN1.SET recipe is known to be ~4.6nm/sec. Prior](https://reader035.fdocuments.net/reader035/viewer/2022070218/61238cf31f561362fb14b20e/html5/thumbnails/10.jpg)
2um line post 30sec SiO2 etch
ZEP520A
PECVD SiO2
Si substrate
![Page 11: SiO2 etching with ZEP520A resist mask · 2009. 2. 4. · some small extra buffer for Si etching. The etch rate of resist with the DEVIN1.SET recipe is known to be ~4.6nm/sec. Prior](https://reader035.fdocuments.net/reader035/viewer/2022070218/61238cf31f561362fb14b20e/html5/thumbnails/11.jpg)
0.5um line post 30sec SiO2 etch
ZEP520A
PECVD SiO2
Si substrate
![Page 12: SiO2 etching with ZEP520A resist mask · 2009. 2. 4. · some small extra buffer for Si etching. The etch rate of resist with the DEVIN1.SET recipe is known to be ~4.6nm/sec. Prior](https://reader035.fdocuments.net/reader035/viewer/2022070218/61238cf31f561362fb14b20e/html5/thumbnails/12.jpg)
100nm line post 30sec SiO2 etch
ZEP520A
PECVD SiO2
Si substrate
![Page 13: SiO2 etching with ZEP520A resist mask · 2009. 2. 4. · some small extra buffer for Si etching. The etch rate of resist with the DEVIN1.SET recipe is known to be ~4.6nm/sec. Prior](https://reader035.fdocuments.net/reader035/viewer/2022070218/61238cf31f561362fb14b20e/html5/thumbnails/13.jpg)
parameter data
PECVD oxide thickness mean = 293nm, st dev = 14nm, N = 8
ZEP520A resist thickness mean = 389nm, st dev = 4nm, N = 3
Post expose/develop and before etch
parameter data
PECVD oxide thickness etched
mean = 116nm, st dev = 16nm, N = 5
PECVD oxide etch rate 3.9nm/s
ZEP520A resist thickness remaining
mean = 286nm, st dev = 21nm, N = 5
ZEP520 resist etch rate 3.4nm/s
selectivityPECVD oxide : ZEP520
1.1 : 1
After 30sec of SiO2 etch
time required to fully etch 293nm of PECVD oxide + 10% overetch = 83sec(slides that follow show SiO2 fully etched at 83sec)
![Page 14: SiO2 etching with ZEP520A resist mask · 2009. 2. 4. · some small extra buffer for Si etching. The etch rate of resist with the DEVIN1.SET recipe is known to be ~4.6nm/sec. Prior](https://reader035.fdocuments.net/reader035/viewer/2022070218/61238cf31f561362fb14b20e/html5/thumbnails/14.jpg)
Post full SiO2 etch
![Page 15: SiO2 etching with ZEP520A resist mask · 2009. 2. 4. · some small extra buffer for Si etching. The etch rate of resist with the DEVIN1.SET recipe is known to be ~4.6nm/sec. Prior](https://reader035.fdocuments.net/reader035/viewer/2022070218/61238cf31f561362fb14b20e/html5/thumbnails/15.jpg)
2um line post 83sec SiO2 etch
ZEP520A
PECVD SiO2
Si substrate
![Page 16: SiO2 etching with ZEP520A resist mask · 2009. 2. 4. · some small extra buffer for Si etching. The etch rate of resist with the DEVIN1.SET recipe is known to be ~4.6nm/sec. Prior](https://reader035.fdocuments.net/reader035/viewer/2022070218/61238cf31f561362fb14b20e/html5/thumbnails/16.jpg)
0.5um line post 83sec SiO2 etch
ZEP520A
PECVD SiO2
Si substrate
![Page 17: SiO2 etching with ZEP520A resist mask · 2009. 2. 4. · some small extra buffer for Si etching. The etch rate of resist with the DEVIN1.SET recipe is known to be ~4.6nm/sec. Prior](https://reader035.fdocuments.net/reader035/viewer/2022070218/61238cf31f561362fb14b20e/html5/thumbnails/17.jpg)
100nm line post 83sec SiO2 etch
ZEP520A
PECVD SiO2
Si substrate
![Page 18: SiO2 etching with ZEP520A resist mask · 2009. 2. 4. · some small extra buffer for Si etching. The etch rate of resist with the DEVIN1.SET recipe is known to be ~4.6nm/sec. Prior](https://reader035.fdocuments.net/reader035/viewer/2022070218/61238cf31f561362fb14b20e/html5/thumbnails/18.jpg)
Post partial Si etch(resist was not removed)
![Page 19: SiO2 etching with ZEP520A resist mask · 2009. 2. 4. · some small extra buffer for Si etching. The etch rate of resist with the DEVIN1.SET recipe is known to be ~4.6nm/sec. Prior](https://reader035.fdocuments.net/reader035/viewer/2022070218/61238cf31f561362fb14b20e/html5/thumbnails/19.jpg)
2um line post 120sec Si etch
![Page 20: SiO2 etching with ZEP520A resist mask · 2009. 2. 4. · some small extra buffer for Si etching. The etch rate of resist with the DEVIN1.SET recipe is known to be ~4.6nm/sec. Prior](https://reader035.fdocuments.net/reader035/viewer/2022070218/61238cf31f561362fb14b20e/html5/thumbnails/20.jpg)
0.5um line post 120sec Si etch
![Page 21: SiO2 etching with ZEP520A resist mask · 2009. 2. 4. · some small extra buffer for Si etching. The etch rate of resist with the DEVIN1.SET recipe is known to be ~4.6nm/sec. Prior](https://reader035.fdocuments.net/reader035/viewer/2022070218/61238cf31f561362fb14b20e/html5/thumbnails/21.jpg)
100nm line post 120sec Si etch
![Page 22: SiO2 etching with ZEP520A resist mask · 2009. 2. 4. · some small extra buffer for Si etching. The etch rate of resist with the DEVIN1.SET recipe is known to be ~4.6nm/sec. Prior](https://reader035.fdocuments.net/reader035/viewer/2022070218/61238cf31f561362fb14b20e/html5/thumbnails/22.jpg)
parameter data
PECVD oxide thickness etched mean = 41nm, st dev = 6nm, N = 8
PECVD oxide etch rate 0.45nm/s
After 120sec of Si etch
Resist was not removed after SiO2 etch and prior to Si etch, because it can help provide some small extra buffer for Si etching. The etch rate of resist with the DEVIN1.SET recipe is known to be ~4.6nm/sec. Prior to this etch, there was 139nm of resist still remaining. So, after 30sec, the 139nm of resist will be gone, and then the oxide mask layer will be exposed. The data in the table summarizes the etch parameters.
2um line 500nm line 100nm line
silicon etched mean = 599nmsigma = 7nmN = 2
mean = 625nmsigma = 5nmN = 2
mean = 493nmsigma = 19nmN = 3
silicon etch rate 5.0nm/s 5.2nm/s 4.1nm/s
selectivity to oxide 11.1 11.6 9.1
note: sample size is small, don’t expect 2um line to etch more slowly than 500nm line