Available online at www.worldscientificnews.com
WSN 35 (2016) 44-61 EISSN 2392-2192
Plasma Electrolytic Oxidation as a modern method to form porous coatings enriched in phosphorus
and copper on biomaterials
Krzysztof Rokosza, Tadeusz Hryniewiczb
Division of Surface Electrochemistry and Engineering, Koszalin University of Technology, Racławicka 15-17, PL 75-620 Koszalin, Poland
a,bE-mail address: [email protected] , [email protected]
ABSTRACT
In the paper, the porous coatings obtained on niobium and two titanium alloys (Ti6Al4V, and
TNZ) after Plasma Electrolytic Oxidation (PEO), known also as Micro Arc Oxidation, were studied.
The samples were treated at the voltage of 450 V for 3 minutes in the electrolyte consisting of 300 g
and 600 g of copper nitrate Cu(NO3)2 in 1 litre of concentrated phosphoric acid H3PO4, consecutively.
SEM and EDS studies were performed on the samples. Based on the obtained results it may be
concluded that enriched in copper porous coatings on all studied materials were created in the
electrolyte within copper nitrate amounting for 600 g. The proposed by the Authors factor to evaluate
the obtained coatings, i.e. copper-to-phosphorus ratio, which for the studied materials amounted to
0.21, clearly indicates that the performed electrochemical PEO treatment for surface modification
especially of bioimplants may be advised.
Keywords: Plasma Electrolytic Oxidation (PEO); Niobium; Ti6Al4V; TNZ; Porous coatings
World Scientific News 35 (2016) 44-61
-45-
1. INTRODUCTION
The modification in nanoscale is possible by using electropolishing [1-6],
magnetoelectropolishing [7-14] as well as high-current density electropolishing [15-17]
processes, while in microscale – by Plasma Electrolytic Oxidation (PEO), known also as
Micro Arc Oxidation [18-21] of surface layer. Nowadays the surface modification by Plasma
Electrolytic Oxidation of biomaterials, such as titanium, niobium, zirconium, tantalum as well
as on their alloys, is widely used in medical techniques. By this method of electrolytic
treatment it is possible to obtain the porous coatings having a thickness of about 10
micrometers and consisting mainly of phosphorus within some desirable chemical elements,
resulting in their biocompatibility [22]. Most important feature of the present studies is the
possibility to obtain the coating with antibacterial copper [23-28] inside and with small
amount of toxic elements such as aluminum [29-34], vanadium [25-41] and tin [42].
2. METHOD
2. 1. Material
The Niobium and two titanium alloys (Ti6Al4V, TNZ) samples cut off from the cold-
rolled plate served for the study (Table 1). The samples were prepared in the form of
rectangular specimens of dimensions 5301.3 mm and cleaned with acetone before the PEO
treatment.
Table 1. Nominal composition of Ti alloys/materials used in the study, wt %.
Ti Nb Zr V Al
Ti6Al4V 90 0 0 4 6
TNZ 74 20 60 0 0
2. 2. PEO set up and parameters
Fig. 1. Set up for Plasma Electrolytic Oxidation.
World Scientific News 35 (2016) 44-61
-46-
The plasma electrolytic oxidation (PEO) was performed at the average voltage of 450 V,
according to the machining set up, which is presented in Figure 1. The shapes of voltage
pulsations and current are visible in Figure 2. The main elements of the set-up were:
a processing cell, a dc three-phase power supply, the electrodes and connecting wiring. The
studies were carried out in the electrolyte of initial temperature of 20 2 C. For the studies,
the electrolyte composed of orthophosphoric (85%) acid with an addition of copper II nitrate
was used. For each run, the electrolytic cell made of glass was used, containing up to 500 ml
of the electrolyte.
Fig. 2. Shapes of voltage and current during Plasma Electrolytic Oxidation process.
2. 3. Set up of SEM/EDS
The scanning electron microscope Quanta 250 FEI with Low Vacuum and ESEM mode
and a field emission cathode as well as the energy dispersive EDX system in a Noran System
Six with nitrogen-free silicon drift detector were used. The magnification of 6000 times for
SEM photos and EDS analyses were used.
3. RESULTS
3. 1. Niobium – electrolyte of lower Cu(NO3)2 concentration
In Figures 3 through 8 and in Tables 2-3 there are presented results of Niobium sample
after PEO treatment at 450 V for 3 minutes in the electrolyte consisting of 300 g of Cu(NO3)2
in 1 L H3PO4. Based on the SEM picture, presented in Figure 3, it is possible to conclude that
the PEO coating is porous, but the pores are small and mostly closed. Additionally, the
studied surface consisted mainly of niobium and phosphorus (Fig. 4) in the amounts of 48.23
±0.8 wt% and 9.03 ±0.26 wt%, respectively. In that place of analysis it was not possible to
detect copper, what is noticeable in Table 2. In the other place of the study on the same
sample, presented in Figure 5, a bigger pore is included and in this case it was possible to
record the small amount of copper, see Table 3 (1.32 ±0.29 wt%). The other elements, which
World Scientific News 35 (2016) 44-61
-47-
are dominant, i.e. niobium and phosphorus were detected in the amounts of 47.73±0.65 wt%
and 8.11 ±0.26 wt%, respectively (Table 3). In Figures 7-8, the higher magnifications of
50000 times and 75000 times are presented, to demostrate the pore diameter, which amounts
to about one micrometer.
Fig. 3. SEM image of Niobium after PEO treatment at 450 V for 3 minutes in the electrolyte
consisting of 300 g Cu(NO3)2 in 1 L H3PO4, magnification: 6000 times.
Fig. 4. EDS spectrum of Niobium after PEO treatment at 450 V for 3 minutes in the electrolyte
consisting of 300 g Cu(NO3)2 in 1 L H3PO4
World Scientific News 35 (2016) 44-61
-48-
Table 2. Results of EDS analysis of Niobium after PEO treatment at 450 V for 3 minutes in the
electrolyte consisting of 300 g Cu(NO3)2 in 1 L H3PO4
Element
lines wt%
Error
wt% at%
Error
at%
C K 2.75 ± 0.15 6.48 ± 0.69
O K 39.88 --- 70.49 ± 2.39
Si K 0.11 ± 0.05 0.11 ± 0.11
P K 9.03 ± 0.26 8.24 ± 0.47
Nb L 48.23 ± 0.80 14.68 ± 0.48
Fig. 5. SEM image and EDS spectrum of Niobium after PEO treatment at 450 V for 3 minutes in the
electrolyte consisting of 300 g Cu(NO3)2 in 1 L H3PO4, magnification: 6000 times.
World Scientific News 35 (2016) 44-61
-49-
Fig. 6. SEM image and EDS spectrum of Niobium after PEO treatment at 450 V for 3 minutes in the
electrolyte consisting of 300 g Cu(NO3)2 in 1 L H3PO4
Fig. 7. SEM image of Niobium after PEO treatment at 450 V for 3 minutes in the electrolyte
consisting of 300 g Cu(NO3)2 in 1 L H3PO4, magnification: 50000 times.
World Scientific News 35 (2016) 44-61
-50-
Fig. 8. SEM image of Niobium after PEO treatment at 450 V for 3 minutes in the electrolyte
consisting of 300 g Cu(NO3)2 in 1 L H3PO4, magnification: 75000 times.
Table 3. Results of EDS analysis of Niobium after PEO treatment at 450 V for 3 minutes in the
electrolyte consisting of 300 g Cu(NO3)2 in 1 L H3PO4
Element
lines wt%
Error
wt% at%
Error
at%
C K 3.18 ± 0.16 7.49 ± 0.76
O K 39.66 --- 70.02 ± 2.45
P K 8.11 ± 0.26 7.39 ± 0.47
Cu K 1.32 ± 0.29 0.59 ± 0.26
Nb L 47.73 ± 0.65 14.51 ± 0.40
World Scientific News 35 (2016) 44-61
-51-
3. 2. Niobium – electrolyte of higher Cu(NO3)2 concentration
Fig. 9. SEM image of Niobium after PEO treatment at 450 V for 3 minutes in the electrolyte
consisting of 600 g Cu(NO3)2 in 1 L H3PO4; magnification: 6000 times.
Fig. 10. EDS spectrum of Niobium after PEO treatment at 450 V for 3 minutes in the electrolyte
consisting of 600 g Cu(NO3)2 in 1 L H3PO4
In Figures 9-10 and in Table 4, there are presented results of Niobium sample after
PEO treatment at 450 V for 3 minutes in the electrolyte consisting of 600 g of Cu(NO3)2 in
1 L H3PO4.
World Scientific News 35 (2016) 44-61
-52-
Fig. 11. SEM image of Niobium after PEO treatment at 450 V for 3 minutes in the electrolyte
consisting of 600 g Cu(NO3)2 in 1 L H3PO4; magnification: 20000 times.
Table 4. Results of EDS analysis of Niobium after PEO treatment at 450 V for 3 minutes in the
electrolyte consisting of 600 g Cu(NO3)2 in 1 L H3PO4
Element
lines wt%
Error
wt% at%
Error
at%
C K 2.89 ± 0.20 6.08 ± 0.83
O K 44.04S --- 69.51 ± 2.09
P K 16.93 ± 0.31 13.81 ± 0.50
Fe K 1.83 ± 0.20 0.83 ± 0.18
Cu K 3.58 ± 0.35 1.42 ± 0.28
Nb L 30.72 ± 0.82 8.35 ± 0.44
World Scientific News 35 (2016) 44-61
-53-
Based on the SEM pictures, presented in Figure 9, it is possible to conclude that the
PEO coating is very porous, but the pores are sharp and mostly opened. The studied results of
surface layer (Figure 10), containing mainly the niobium and phosphorus in the amounts of
30.72 ±0.82 wt% and 16.93 ±0.31 wt%, respectively, within the copper (3.58 ±0.35 wt%) and
iron (1.83 ±0.2 wt%) inside, are reported in Table 4. In Figure 11, the shape of the pore is
presented. Most important information is that the pores are layered, i.e. in the larger ones
there are located the smaller pores
3. 3. Titanium alloy – electrolyte of lower Cu(NO3)2 concentration
In Figures 12-13 and in Table 5, there are presented results of Ti6Al4V alloy sample
after PEO treatment at 450 V for 3 minutes in the electrolyte consisting of 300 g of Cu(NO3)2
in 1 L H3PO4. Based on the SEM picture, presented in Figure 12, it is possible to conclude
that the PEO coating is very porous, but the pores are sharp and mostly opened. The studied
results of the surface layer (Figure 13), containing mainly the titanium and phosphorus in the
amounts of 26.71 ±0.34 wt% and 18.55 ±0.21 wt%, respectively, within the copper (1.72
±0.26 wt%), iron (1.05±0.14 wt%), aluminum (1.33 ±0.09 wt%), as well as calcium (0.26
±0.05 wt%) inside, are presented in Table 5.
Fig. 12. SEM image of Ti6Al4V alloy after PEO treatment at 450 V for 3 minutes in the electrolyte
consisting of 300 g Cu(NO3)2 in 1 L H3PO4; magnification: 6000 times
World Scientific News 35 (2016) 44-61
-54-
Fig. 13. EDS spectrum of Ti6Al4V alloy after PEO treatment at 450 V for 3 minutes in the electrolyte
consisting of 300 g Cu(NO3)2 in 1 L H3PO4
Table 5. Results of of Ti6Al4V alloy after PEO treatment at 450 V for 3 minutes in the electrolyte
consisting of 300 g Cu(NO3)2 in 1 L H3PO4
Element
lines wt%
Error
wt% at%
Error
at%
C K 1.81 ± 0.16 3.39 ± 0.59
O K 48.57 --- 68.30 ± 2.18
Al K 1.33 ± 0.09 1.11 ± 0.14
P K 18.55 ± 0.21 13.47 ± 0.31
Ca K 0.26 ± 0.05 0.15 ± 0.05
Ti K 26.71 ± 0.34 12.55 ± 0.32
Fe K 1.05 ± 0.14 0.42 ± 0.11
Cu K 1.72 ± 0.26 0.61 ± 0.18
3. 4. Titanium alloys – electrolyte of higher Cu(NO3)2 concentration
In Figures 14-15 and in Table 6, there are presented results of Ti6Al4V alloy sample
after PEO treatment at 450 V for 3 minutes in the electrolyte consisting of 600 g of Cu(NO3)2
in 1 L H3PO4. Based on the SEM picture, presented in Figure 14, it is possible to conclude
that the PEO coating is very porous, but the pores are also sharp and mostly opened. The
studied results of the surface layer (Figure 15), containing mainly the titanium and
phosphorus in the amounts of 22.36 ±0.31 wt% and 18.75 ±0.21 wt%, respectively, within the
copper (3.85 ±0.51 wt%), iron (0.58 ±0.13 wt %), aluminum (1.08 ±0.08 wt%) inside, have
been presented in Table 6.
World Scientific News 35 (2016) 44-61
-55-
Fig. 14. SEM image of Ti6Al4V alloy after PEO treatment at 450 V for 3 minutes in the electrolyte
consisting of 600 g Cu(NO3)2 in 1 L H3PO4,
Table 6. Results of Ti6Al4V alloy after PEO treatment at 450 V for 3 minutes in the electrolyte
consisting of 600 g Cu(NO3)2 in 1 L H3PO4
Element
lines wt%
Error
wt% at%
Error
at%
C K 3.42 ± 0.19 6.20 ± 0.68
O K 49.96 --- 68.02 ± 2.07
Al K 1.08 ± 0.08 0.87 ± 0.13
P K 18.75 ± 0.21 13.19 ± 0.30
Ti K 22.36 ± 0.31 10.17 ± 0.28
Fe K 0.58 ± 0.13 0.22 ± 0.10
Cu K 3.85 ± 0.51 1.32 ± 0.35
World Scientific News 35 (2016) 44-61
-56-
Fig. 15. EDS spectrum of Ti6Al4V alloy after PEO treatment at 450 V for 3 minutes in the electrolyte
consisting of 600 g Cu(NO3)2 in 1 L H3PO4
In Figures 16-17 and in Table 7, there are presented results of TNZ alloy sample after
PEO treatment at 450 V for 3 minutes in the electrolyte consisting of 600 g of Cu(NO3)2 in
1 L H3PO4. Based on the SEM picture, presented in Figure 16, it is possible to conclude that
the PEO coating is very porous, but the pores are sharp and mostly opened. The studied
results of the surface layer (Figure 17), containing mainly the titanium, niobium, zirconium
and phosphorus in the amounts of 17.19 ±0.22 wt%, 5.39 ±0.92 wt%, 5.89 ±2.13 wt% and
17.97 ±0.85 wt%, respectively, within the copper (3.81 ±0.32 wt %), iron (1.03 ±0.16 wt %)
and calcium (0.23 ±0.06 wt %) inside, are given in Table 7.
Table 7. Results of TNZ alloy after PEO treatment at 450 V for 3 minutes in the electrolyte consisting
of 600 g Cu(NO3)2 in 1 L H3PO4
Element
lines wt%
Error
wt% at%
Error
at%
C K 2.29 ± 0.17 4.52 ± 0.66
O K 46.20 --- 68.36 ± 2.24
P K 17.97 ± 0.85 13.74 ± 1.30
Ca K 0.23 ± 0.06 0.14 ± 0.07
Ti K 17.19 ± 0.22 8.50 ± 0.22
Fe K 1.03 ± 0.16 0.44 ± 0.14
Cu K 3.81 ± 0.32 1.42 ± 0.24
Zr L 5.89 ± 2.13 1.53 ± 1.11
Nb L 5.39 ± 0.92 1.37 ± 0.47
World Scientific News 35 (2016) 44-61
-57-
Fig. 16. SEM image of TNZ alloy after PEO treatment at 450 V for 3 minutes in the electrolyte
consisting of 600 g Cu(NO3)2 in 1 L H3PO4; magnification: 6000 times.
Fig. 17. EDS spectrum of TNZ alloy after PEO treatment at 450 V for 3 minutes in the electrolyte
consisting of 600 g Cu(NO3)2 in 1 L H3PO4
4. CONCLUSION
Due to the fact that all studied samples (matrices) have different chemical compositions
(wt%), the ratio of copper-to-phosphorus in the PEO coating was selected to carry out their
World Scientific News 35 (2016) 44-61
-58-
comparison. For the electrolytes containing of 600 g Cu(NO3)2 in 1 L H3PO4 to all studied
materials the calculated copper-to-phosphorus ratio was equal and amounted to 0.21.
In case of less concentrated solutions, consisting of 1 L H3PO4 within 300 g Cu(NO3)2,
the copper content in PEO coating was much smaller: in case of niobium it was between 0 and
0.16, while for Ti6Al4V amounted to 0.09.
It must be concluded that to obtain a porous PEO coatings enriched in copper, it is
advisable to use the electrolyte consisting of 600 g Cu(NO3)2 in 1 L H3PO4.
ACKNOWLEDGMENTS
Dra G. Vara, and Dra M.B. García-Blanco from Fundación Cidetec. Parque Tecnológico de San Sebastián Pº
Miramón, 196 20009 Donostia-San Sebastián (Gipuzkoa), Spain, are highly acknowledged for delivering
Ti6Al4V for the PEO experiments.
Prof. F. Prima from Ecole Nationale Supérieure de Chimie de Paris, France, as well as Prof. Zschommler
Sandim, H. R. from DEMAR-EEL-USP, Universidade de São Paulo, Brazil are thankful for delivering TNZ and
Niobium materials for the PEO experiments, respectively.
Prof. Dr.-Ing. Winfried Malorny and Dr Torsten Barfels from Hochschule Wismar, Germany, are highly
acknowledged for providing access to the SEM/EDS apparatus allowing to perform the studies.
References
[1] Hryniewicz T, Physico-chemical and technological fundamentals of electropolishing
steels (Fizykochemiczne i technologiczne podstawy procesu elektropolerowania stali).
Monograph no. 26, ed. by Koszalin University of Technology Publishing: 1989, 161
pages.
[2] Hryniewicz T, On the surface treatment of metallic biomaterials (Wstęp do obróbki
powierzchniowej biomateriałów metalowych). Ed. by Koszalin University of
Technology Publishing: 2007, 155 pages.
[3] Rokosz K, Electrochemical polishing in the magnetic field (Polerowanie
elektrochemiczne w polu magnetycznym). Ed. by Koszalin University of Technology
Publishing: 2012, 211 pages.
[4] Hryniewicz T, Rokicki R, Rokosz K, Co-Cr alloy corrosion behaviour after
electropolishing and "magnetoelectropolishing" treatments. Surface and Coatings
Technology, 62(17-18) (2008) 3073-3076; DOI: 10.1016/j.matlet.2008.01.130
[5] Hryniewicz T, Rokosz K, Analysis of XPS results of AISI 316L SS electropolished and
magnetoelectropolished at varying conditions. Surface and Coatings Technology,
204(16-17) (2010) 2583-2592; DOI: 10.1016/j.surfcoat.2010.02.005
[6] Hryniewicz T, Rokosz K, Zschommler Sandim H R, SEM/EDX and XPS studies of
niobium after electropolishing. Applied Surface Science, 263 (2012) 357-361;
DOI:10.1016/j.apsusc.2012.09.060
[7] Hryniewicz T, Rokicki R, Rokosz K, Magnetoelectropolishing for metal surface
modification. Transactions of The Institute of Metal Finishing, 85(6) (2007) 325-332;
DOI: 10.1179/174591907X246537
World Scientific News 35 (2016) 44-61
-59-
[8] Hryniewicz T, Rokicki R, Rokosz K, Corrosion and surface characterization of
titanium biomaterial after magnetoelectropolishing. Surface and Coatings Technology,
203(9) (2008) 1508-1515; DOI:10.1016/j.surfcoat.2008.11.028
[9] Hryniewicz T, Rokosz K, Polarization characteristics of magnetoelectropolishing
stainless steels. Materials Chemistry and Physics, 122(1) (2010) 169-174.
[10] Rokosz K, Hryniewicz T, Raaen S, Characterization of passive film formed on AISI
316L stainless steel after magnetoelectropolishing in a broad range of polarization
parameters. Journal of Iron and Steel Research, 83(9) (2012) 910-918.
[11] Hryniewicz T, Rokosz K, Investigation of selected surface properties of AISI 316L SS
after magnetoelectropolishing. Materials Chemistry and Physics, 123(1) (2010) 47-55.
[12] Hryniewicz T, Rokosz K, Corrosion resistance of magnetoelectropolished AISI 316L
SS biomaterial. Anti-Corrosion Methods and Materials, 61(2) (2014) 57-64.
[13] Hryniewicz T, Rokosz K, Valiček J, Rokicki R, Effect of magnetoelectropolishing on
nanohardness and Young’s modulus of titanium biomaterial. Materials Letters, 83
(2012) 69-72; DOI:10.1016/j.matlet.2012.06.010
[14] Hryniewicz T, Rokosz K, Rokicki R, Prima F, Nanoindentation and XPS Studies of
Titanium TNZ Alloy after Electrochemical Polishing in a Magnetic Field. Materials, 8
(2015) 205-215; DOI:10.3390/ma8010205
[15] Rokosz K, Hryniewicz T, Simon F, Rzadkiewicz S, Comparative XPS analysis of
passive layers composition formed on AISI 304L SS after standard and high-current
density electropolishing. Surface and Interface Analysis, 47(1) (2015) 87-92.
[16] Rokosz K, Lahtinen J, Hryniewicz T, Rzadkiewicz S, XPS depth profiling analysis of
passive surface layers formed on austenitic AISI 304L and AISI 316L SS after high-
current-density electropolishing. Surface and Coatings Technology, 276 (2015) 516-
520; DOI:10.1016/j.surfcoat.2015.06.022
[17] Rokosz K, Hryniewicz T, Rzadkiewicz S, Raaen S, High-Current-Density
Electropolishing (HDEP) of AISI 316L (EN 1.4404) Stainless Steel. Tehnicki Vjesnik-
Technical Gazette, 22(2) (2015) 415-424.
[18] Yerokhin A L, Nie X, Leyland A, Matthews A, Dowey S J, Plasma electrolysis for
surface engineering. Surface and Coatings Technology, 122(2-3) (1999) 73-93.
[19] Yerokhin A L, Nie X, Leyland A, Matthews A, Characterisation of oxide films
produced by plasma electrolytic oxidation of a Ti–6Al–4V alloy. Surface and Coatings
Technology, 130(2-3) (2000) 195-206.
[20] Wheeler J M, Collier C A, Paillard J M, Curran J A, Evaluation of micromechanical
behaviour of plasma electrolytic oxidation (PEO) coatings on Ti–6Al–4V. Surface and
Coatings Technology, 204(21-22) (2010) 339-3409.
[21] Krzakala A, Mlynski J, Dercz G, Michalska J, Maciej A, Nieuzyla L, Simka W,
Modification of Ti-6Al-4V alloy surface by EPD-PEO process in ZrSiO4 suspension.
Archives of Metallurgy and Materials, 59(1) (2014) 199-204.
World Scientific News 35 (2016) 44-61
-60-
[22] Rokicki R, Hryniewicz T, Pulletikurthi C, Rokosz K, Munroe N, Towards a better
corrosion resistance and biocompatibility improvement of Nitinol medical devices.
Journal of Materials Engineering and Performance, 24 (2015) 163401640; DOI:
10.1007/s11665-015-1429-x
[23] Zhang Xiangyu, Huang Xiaobo, Ma Yong, Lin Naiming, Fan Ailan, Tang Bin,
Bactericidal behavior of Cu-containing stainless steel surfaces. Applied Surface Science,
258 (2012) 10058-10063.
[24] Xiaohong Y, Xiangyug Z, Haibo W, Linhai T, Yong M, Bin T, Microstructure and
antibacterial properties of Cu-doped TiO2 coating on titanium by micro-arc oxidation.
Applied Surface Science, 292 (2014) 944-947; DOI: 10.1016/j.apsusc.2013.12.083
[25] Hempel F, Finke B, Zietz C, Bader R, Weltmann K D, Polak M, Antimicrobial surface
modification of titanium substrates by means of plasma immersion ion implantation and
deposition of copper. Surface and Coatings Technology, 256 (2014) 52058;
DOI:10.1016/j.surfcoat.2014.01.027
[26] Zhua W, Zhang Z, Gu B, Sun J, Zhu L, Biological Activity and Antibacterial Property
of Nano-structured TiO2 Coating Incorporated with Cu Prepared by Micro-arc
Oxidation. Journal of Materials Science and Technology, 29(3) (2013) 237-244;
DOI:10.1016/j.jmst.2012.12
[27] Parajulee S, Hayakawa M, Ikezawa S, Adhesion Strength of TiN Stacked TiO2 Film
Correlated with Contact Angle, Critical Load, and XPS Spectra. Plasma and Fusion
Research: Letters, 4(055) (2009) 055-1-055-4; DOI:10.1585/pfr.4.055
[28] Fernandez A M, Guzman A M, Vera E, Rodriguez Paez J E, Efectos de
fotodegradación propiciados por recubrimientos de TiO2 y TiO2 -SiO2 obtenidos por
Sol-Gel. Boletín de la Sociedad Española de Cerámica y Vidrio V, 47(5) (2008) 259-
266.
[29] Seiler H, Sigel H, Dekker M, Handbook of toxicity of inorganic compounds, New York,
1998.
[30] Kobayashi E, Wang T, Doi H, Mechanical properties and corrosion resistance of Ti-
6Al-7Nb alloy dental castings. Journal of Materials Science: Materials in Medicine, 9
(1998) 567-574.
[31] Łaskawiec J, Michalik R, Theoretical and application issues in implants, Publishing
House of Silesian University of Technology, Gliwice, 2002 (in Polish).
[32] Simka W, Autoreferat habilitacyjny, Wydział Chemiczny Politechniki Śląskiej, 2013, 1-
18.
[33] Browne R C, Vanadium Poisoning from Gas Turbines. British Journal of Industrial
Medicine, 2(12) (1955) 57-59.
[34] Hulcher F H, Spectrophotometric Determination of Vanadium in Biological Material.
Analytical Chemistry, 32 (1960) 1183-1185.
[35] Krewski D, Yokel R A, Nieboer E, Borchelt D, Cohen J, Harry J, Kacew S, Lindsay J,
Mahfouz A M, Rondeau V, Human health risk assessment for aluminium, aluminium
World Scientific News 35 (2016) 44-61
-61-
oxide, and aluminium hydroxide. J. Toxicol. Environ. Health B Crit. Rev., 10(1) (2007)
1-269.
[36] Jacobs J J, Skipor A K, Black J, Urban R, Galante J O, Release and excretion of metal
in patients who have a total hip-replacement component made of titanium-base alloy.
The Journal of Bone and Joint Surgery, 73 (1991) 1475-1486.
[37] Ku C.H., Pioletti D.P., Browne M., Gregson P.J., Effect of different Ti–6Al–4V surface
treatments on osteoblasts behaviour, Biomaterials 23 (2002) 1447-1454.
[38] Bellows C G, Heersche J N, Aubin J E, Aluminium accelerates osteoblastic
differentiation but is cytotoxic in long-term rat calvaria cell cultures. Calcified Tissue
International, 65 (1999) 59-65.
[39] Aluminum CAS # 7429-90-5, PUBLIC HEALTH STATEMENT, Agency for Toxic
Substances and Disease Registry, Division of Toxicology and Environmental
Medicine, http://www.atsdr.cdc.gov Atlanta (2008)
[40] Davidson J A, Mishra A K, Kovasc P, Poggie R A, New Surface-Hardened, Low-
Modulus, Corrosion-Resistant Ti-13Nb-13Zr Alloy for Total HIP Arthroplasty. Bio-
Medical Materials and Engineering, 4 (1994) 231-243.
[41] Landsberg J P, McDonald B, Watt F, Absence of aluminium in neuritic plaque cores in
Alzheimer's disease. Nature, 360 (1992) 65-68.
[42] Winship K A, Toxicity of tin and its compounds. Adverse Drug React Acute Poisoning
Rev., 7(1) (1988) 19-38.