Nickel Characterization for Signal Integrity Analysis Nickel characterization at microwave...
Transcript of Nickel Characterization for Signal Integrity Analysis Nickel characterization at microwave...
![Page 1: Nickel Characterization for Signal Integrity Analysis Nickel characterization at microwave frequencies Anomalies in ENIG plated interconnects Identification of nickel parameters GMS-parameters](https://reader036.fdocuments.net/reader036/viewer/2022062907/5aaa645b7f8b9a7c188e0560/html5/thumbnails/1.jpg)
Nickel Characterization for Interconnect Analysis
Y. Shlepnev, Simberian Inc. S. McMorrow, Teraspeed Consulting Group LLC
8/16/2011 © 2011 Teraspeed Consulting Group LLC © 2011 Simberian Inc.
1
![Page 2: Nickel Characterization for Signal Integrity Analysis Nickel characterization at microwave frequencies Anomalies in ENIG plated interconnects Identification of nickel parameters GMS-parameters](https://reader036.fdocuments.net/reader036/viewer/2022062907/5aaa645b7f8b9a7c188e0560/html5/thumbnails/2.jpg)
Property rights disclosure
8/16/2011 © 2011 Teraspeed Consulting Group LLC © 2011 Simberian Inc.
2
“PROPERTY OF TERASPEED CONSULTING GROUP LLC” Information contained in this document is not to be reproduced in any form without permission of Teraspeed Consulting Group LLC. Any information in this document is proprietary and may not be used or disclosed without the express permission of Teraspeed Consulting Group LLC.
“CONFIDENTIAL PROPERTY OF TERASPEED CONSULTING GROUP LLC”
This document includes valuable trade secrets. Unauthorized disclosure of use of this document may violate the Uniform Trade Secrets Act.
![Page 3: Nickel Characterization for Signal Integrity Analysis Nickel characterization at microwave frequencies Anomalies in ENIG plated interconnects Identification of nickel parameters GMS-parameters](https://reader036.fdocuments.net/reader036/viewer/2022062907/5aaa645b7f8b9a7c188e0560/html5/thumbnails/3.jpg)
Property rights disclosure
8/16/2011 © 2011 Teraspeed Consulting Group LLC © 2011 Simberian Inc.
3
Copyright © 2011 by Simberian Inc., All rights reserved. THIS DOCUMENT IS CONFIDENTIAL AND
PROPRIETARY TO SIMBERIAN INC. AND MAY NOT BE REPRODUCED, PUBLISHED OR DISCLOSED TO OTHERS WITHOUT PERMISSION OF SIMBERIAN INC.
Simberian® and Simbeor® are registered trademarks of Simberian Inc. Other product and company names mentioned in this
presentation may be the trademarks of their respective owners.
![Page 4: Nickel Characterization for Signal Integrity Analysis Nickel characterization at microwave frequencies Anomalies in ENIG plated interconnects Identification of nickel parameters GMS-parameters](https://reader036.fdocuments.net/reader036/viewer/2022062907/5aaa645b7f8b9a7c188e0560/html5/thumbnails/4.jpg)
Outline Nickel characterization at microwave frequencies Anomalies in ENIG plated interconnects Identification of nickel parameters
GMS-parameters extraction from measured data Electromagnetic model for plated traces Landau-Lifshits model for ferromagnetic metal Nickel parameters identification
Effect of Nickel on multi-gigabit digital signals Conclusion
8/16/2011 © 2011 Teraspeed Consulting Group LLC © 2011 Simberian Inc.
4
![Page 5: Nickel Characterization for Signal Integrity Analysis Nickel characterization at microwave frequencies Anomalies in ENIG plated interconnects Identification of nickel parameters GMS-parameters](https://reader036.fdocuments.net/reader036/viewer/2022062907/5aaa645b7f8b9a7c188e0560/html5/thumbnails/5.jpg)
Nickel characterization at microwave frequencies From S. Lucyszyn, Microwave Characterization of Nickel, PIERS online, vol.
4, N 6, 2008, p. 686-690.
8/16/2011 © 2011 Teraspeed Consulting Group LLC © 2011 Simberian Inc.
5
Results from different authors show drop in permeability of nickel at microwave frequency range – though the data are inconsistent due to differences in the identification techniques and differences in the investigated material
10. R. M. Bozorth, Ferromagnetism, D. Van Nostrand Co. Inc., 1951. 11. W. Arkadiew, “Absorption of electromagnetic waves in two parallel wires," Ann. Physik, Vol. 58, 1919. 12. I. Simon, “Magnetic permeability of Ni in region of cm waves," Nature, Vol. 157, 735, June 1946. 13. G. F. Hodsman, G. Eichholz, and R. Millership, “Magnetic dispersion at microwave frequencies," Proceedings of the Physical Society Section B, 377{390, 1949.
![Page 6: Nickel Characterization for Signal Integrity Analysis Nickel characterization at microwave frequencies Anomalies in ENIG plated interconnects Identification of nickel parameters GMS-parameters](https://reader036.fdocuments.net/reader036/viewer/2022062907/5aaa645b7f8b9a7c188e0560/html5/thumbnails/6.jpg)
Plated Nickel effect: Case 1 J. Moreira, M. Tsai, J. Kenton, H. Barnes, D. Faller, PCB Loadboard Design
Challenges for Multi-Gigabit Devices in Automated Test Applications, DesignCon 2006
8/16/2011 © 2011 Teraspeed Consulting Group LLC © 2011 Simberian Inc.
6
Figure 13: Measured loss per inch for Ag plating, OSP, electroplated 30 μinches Au and 15 μinches Au, soldermask and immersion 5 μinches Au [6].
Anomaly in attenuation for case of thin Au layer over Ni is clearly visible between 2 and 4 GHz (black curve)
Nickel modeled as non-dispersive metal with permeability varying from 1 to 100 – no anomaly observed in such model Effect of nickel plating on 10 Gbps signal degradation is shown experimentally
![Page 7: Nickel Characterization for Signal Integrity Analysis Nickel characterization at microwave frequencies Anomalies in ENIG plated interconnects Identification of nickel parameters GMS-parameters](https://reader036.fdocuments.net/reader036/viewer/2022062907/5aaa645b7f8b9a7c188e0560/html5/thumbnails/7.jpg)
Plated Nickel effect: Case 2 X. Wu, D. Cullen, G. Brist, and O. M. Ramahi, Surface Finish Effects on
High-Speed Signal Degradation, IEEE Trans. On Adv. Packaging, Vol. 31, No 1, Feb. 2008, p. 182-189.
8/16/2011 © 2011 Teraspeed Consulting Group LLC © 2011 Simberian Inc.
7
Anomaly in attenuation for case of Au layer over Ni is clearly visible between 1 and 3 GHz (red curve) Simulation shows substantial differences in the insertion loss (black curve)
![Page 8: Nickel Characterization for Signal Integrity Analysis Nickel characterization at microwave frequencies Anomalies in ENIG plated interconnects Identification of nickel parameters GMS-parameters](https://reader036.fdocuments.net/reader036/viewer/2022062907/5aaa645b7f8b9a7c188e0560/html5/thumbnails/8.jpg)
Plated Nickel effect: Case 3 A. Aguayo, Advances in high frequency printed circuit board materials,
Microwave Engineering Europe, Dec. 2009, p.11-14.
8/16/2011 © 2011 Teraspeed Consulting Group LLC © 2011 Simberian Inc.
8
Anomaly in attenuation for case of Au layer over Ni is clearly visible between 1 and 5 GHz (magenta curve) Simulation did not reproduce the anomaly
From Internal Rogers Corporation study, “Increased Circuit Loss due to Ni/Au”, Dr. Al Horn, January 2006.
![Page 9: Nickel Characterization for Signal Integrity Analysis Nickel characterization at microwave frequencies Anomalies in ENIG plated interconnects Identification of nickel parameters GMS-parameters](https://reader036.fdocuments.net/reader036/viewer/2022062907/5aaa645b7f8b9a7c188e0560/html5/thumbnails/9.jpg)
Plated Nickel effect: Case 3.1 X. Chen, “EM modeling of microstrip conductor losses including surface roughness
effect,” IEEE Microwave and Wireless Components Letters, v. 17, n.2, p. 94, February 2007
8/16/2011 © 2011 Isola © 2011 Simberian Inc.
9
![Page 10: Nickel Characterization for Signal Integrity Analysis Nickel characterization at microwave frequencies Anomalies in ENIG plated interconnects Identification of nickel parameters GMS-parameters](https://reader036.fdocuments.net/reader036/viewer/2022062907/5aaa645b7f8b9a7c188e0560/html5/thumbnails/10.jpg)
Plated Nickel effect: Case 4 S-parameters of single-ended microstrip lines with ENIG finish with about
0.05 um of Au and about 6 um of Ni over the copper
8/16/2011 © 2011 Teraspeed Consulting Group LLC © 2011 Simberian Inc.
10
Reflection Loss
Insertion Loss
100 mm lines
150 mm lines
S-parameters for three structures with 100 mm microstrip line segments and for four structures with 150 mm segments are plotted
Anomaly in attenuation around 2.7 GHz – cannot be reproduced with regular metal models
![Page 11: Nickel Characterization for Signal Integrity Analysis Nickel characterization at microwave frequencies Anomalies in ENIG plated interconnects Identification of nickel parameters GMS-parameters](https://reader036.fdocuments.net/reader036/viewer/2022062907/5aaa645b7f8b9a7c188e0560/html5/thumbnails/11.jpg)
Plated Nickel effect: Case 4 S-parameters of single-ended microstrip lines with ENIG finish with about
0.05 um of Au and about 6 um of Ni over the copper
8/16/2011 © 2011 Teraspeed Consulting Group LLC © 2011 Simberian Inc.
11
Anomaly in group delay around 2.7 GHz - not previously reported! Cannot be reproduced with regular metal model
Group delays for three structures with 100 mm microstrip line segments and for four structures with 150 mm segments are plotted
100 mm lines
150 mm lines
![Page 12: Nickel Characterization for Signal Integrity Analysis Nickel characterization at microwave frequencies Anomalies in ENIG plated interconnects Identification of nickel parameters GMS-parameters](https://reader036.fdocuments.net/reader036/viewer/2022062907/5aaa645b7f8b9a7c188e0560/html5/thumbnails/12.jpg)
Plated Nickel effect: Case 4 S-parameters of single-ended microstrip lines with ENIG finish with about
0.05 um of Au and about 6 um of Ni over the copper
8/16/2011 © 2011 Teraspeed Consulting Group LLC © 2011 Simberian Inc.
12
Structures with strip lines did not show any anomaly in IL and GD – it is clearly the effect of plating Strip line structures can be used to identify dielectric properties
Dielectric parameters were identified with GMS-parameters of the strip line structures as wideband Debye model with DK=3.x and LT=0.01x at 1 GHz
Structure with 150 mm microstrip line
Structure with 150 mm strip line
![Page 13: Nickel Characterization for Signal Integrity Analysis Nickel characterization at microwave frequencies Anomalies in ENIG plated interconnects Identification of nickel parameters GMS-parameters](https://reader036.fdocuments.net/reader036/viewer/2022062907/5aaa645b7f8b9a7c188e0560/html5/thumbnails/13.jpg)
Plated Nickel effect: Case 5 S-parameters of differential microstrip lines with ENIG finish with about 0.05
um of Au and about 6 um of Ni over the copper
8/16/2011 © 2011 Teraspeed Consulting Group LLC © 2011 Simberian Inc.
13
Anomaly in attenuation around 2.7 GHz – cannot be reproduced with regular metal models
Reflection Loss
Insertion Loss
100 mm lines
150 mm line
Differential S-parameters for three structures with 100 mm microstrip line segments and for one structure with 150 mm segments are plotted
![Page 14: Nickel Characterization for Signal Integrity Analysis Nickel characterization at microwave frequencies Anomalies in ENIG plated interconnects Identification of nickel parameters GMS-parameters](https://reader036.fdocuments.net/reader036/viewer/2022062907/5aaa645b7f8b9a7c188e0560/html5/thumbnails/14.jpg)
Plated Nickel effect: Case 5 S-parameters of differential microstrip lines with ENIG finish with about 0.05
um of Au and about 6 um of Ni over the copper
8/16/2011 © 2011 Teraspeed Consulting Group LLC © 2011 Simberian Inc.
14
Anomaly in group delay around 2.7 GHz - not previously reported! Cannot be reproduced with regular metal model
Differential group delays for three structures with 100 mm microstrip line segments and one structure with 150 mm segments are plotted
100 mm lines
150 mm lines
![Page 15: Nickel Characterization for Signal Integrity Analysis Nickel characterization at microwave frequencies Anomalies in ENIG plated interconnects Identification of nickel parameters GMS-parameters](https://reader036.fdocuments.net/reader036/viewer/2022062907/5aaa645b7f8b9a7c188e0560/html5/thumbnails/15.jpg)
Structures for Nickel Model Identification Two structures suitable for the identification – contain 100 mm and 150 mm
segments of microstrip line – both structures show anomalies around 2.7 GHz
8/16/2011 © 2011 Teraspeed Consulting Group LLC © 2011 Simberian Inc.
15
ENIG finish with about 0.05 um of Au and about 6 um of Ni over the copper Microstrip width 74 um, thickness 15 um, substrate 30 um, wideband Debye model DK=3.x and LT=0.01x at 1 GHz
Reflection Loss
Insertion Loss
100 mm line
150 mm line
100 mm line
150 mm line
![Page 16: Nickel Characterization for Signal Integrity Analysis Nickel characterization at microwave frequencies Anomalies in ENIG plated interconnects Identification of nickel parameters GMS-parameters](https://reader036.fdocuments.net/reader036/viewer/2022062907/5aaa645b7f8b9a7c188e0560/html5/thumbnails/16.jpg)
Anomaly in IL and GD is clearly due to Nickel plating Deviation 2-3 dB from Insertion Loss expected with regular conductor Deviation 40-60 ps from Group Delay expected with regular conductor
8/16/2011 © 2011 Teraspeed Consulting Group LLC © 2011 Simberian Inc.
16
100 mm line
150 mm line 100 mm line
150 mm line
ENIG finish with about 0.05 um of Au and about 6 um of Ni over the copper Microstrip width 69 um, thickness 12 um, substrate 30 um, wideband Debye dielectric model: DK=3.x and LT=0.01x at 1 GHz GMS-parameters (reflection-less) can be extracted from these two models for identification
![Page 17: Nickel Characterization for Signal Integrity Analysis Nickel characterization at microwave frequencies Anomalies in ENIG plated interconnects Identification of nickel parameters GMS-parameters](https://reader036.fdocuments.net/reader036/viewer/2022062907/5aaa645b7f8b9a7c188e0560/html5/thumbnails/17.jpg)
Generalized Modal Scattering (GMS) Parameters S-parameters of reflective structures with 100 mm and 150 mm segments of
microstrip line can be converted into GMS-parameters of 50 mm segment
8/16/2011 © 2011 Teraspeed Consulting Group LLC © 2011 Simberian Inc.
17
100 mm line
150 mm line
Y. Shlepnev, A. Neves, T. Dagostino, S. McMorrow, Practical identification of dispersive dielectric models with generalized modal S-parameters for analysis of interconnects in 6-100 Gb/s applications, DesignCon 2010.
No Reflection and anomalies are still here!
GMS-parameters are noisy at high frequencies due to non-identities of probes/launches and cross-sections of two test structures (see more on sensitivity in app note #2010_03, www.simberian.com)
![Page 18: Nickel Characterization for Signal Integrity Analysis Nickel characterization at microwave frequencies Anomalies in ENIG plated interconnects Identification of nickel parameters GMS-parameters](https://reader036.fdocuments.net/reader036/viewer/2022062907/5aaa645b7f8b9a7c188e0560/html5/thumbnails/18.jpg)
Landau-Lifshits Model of Ferromagnetic Metal
Magnetic permeability dispersion equations are derived from description moving boundaries of oppositely magnetized layers in ferromagnetic metal
Usable at microwave frequency band Lorentz model may be also acceptable for resonance description (2-nd order Debye) Can be combined with Debye model at lower frequencies and Lorentz model at the
millimeter frequencies
8/16/2011 © 2011 Teraspeed Consulting Group LLC © 2011 Simberian Inc.
18
( ) ( )2
02 2
0 2h l hf i ff
f i f fγµ µ µ µ
γ+ ⋅ ⋅
= + − ⋅+ ⋅ ⋅ −
0
; ;[ ]; [ ]
l hpermeability at low frequencies permeability at high frequenciesf resonance frequency Hz damping coefficient Hzµ µ
γ− −− −
L. Landau, E. Lifshits, On the theory of the dispersion of magnetic permeability in ferromagnetic bodies, Phys. Zeitsch. der Sow., v. 8, p. 153-169, 1935
![Page 19: Nickel Characterization for Signal Integrity Analysis Nickel characterization at microwave frequencies Anomalies in ENIG plated interconnects Identification of nickel parameters GMS-parameters](https://reader036.fdocuments.net/reader036/viewer/2022062907/5aaa645b7f8b9a7c188e0560/html5/thumbnails/19.jpg)
Electromagnetic model of microstrip line Hybrid model has been constructed to simulate segment of transmission line Method of Lines (MoL) is used for multi-layered dielectric and plane layer – produced
grid Green’s function (GGF) (*) Multi-layered conductor interior meshed with Trefftz-Nikol’skiy finite elements and
matched with the GGF (*) Method of simultaneous diagonalization is used to extract modal and per unit length
parameters of microstrip line (*)
8/16/2011 © 2011 Teraspeed Consulting Group LLC © 2011 Simberian Inc.
19
(*) References are in the paper Model is implemented in electromagnetic signal integrity software Simbeor 2011 – available at www.simberian.com
Dielectric layer
yJ
yJ
,y zE H
,y xE H
y
x
z
,y xE H
,y zE H
Au Ni
Cu Conductor interior model
![Page 20: Nickel Characterization for Signal Integrity Analysis Nickel characterization at microwave frequencies Anomalies in ENIG plated interconnects Identification of nickel parameters GMS-parameters](https://reader036.fdocuments.net/reader036/viewer/2022062907/5aaa645b7f8b9a7c188e0560/html5/thumbnails/20.jpg)
Plated Nickel Model Identification Adjust Ni model parameters to match measured and computed GMS-parameters for
50 mm segment of microstrip line, strip width 69 um, thickness 12 um
8/16/2011 © 2011 Teraspeed Consulting Group LLC © 2011 Simberian Inc.
20
ENIG finish with about 0.05 um of Au and about 6 um of Ni over the copper Substrate dielectric DK=3.x and LT=0.01x at 1 GHz, wideband Debye model Landau-Lifshits model for Nickel: Mul=6, Muh=2, f0=2.6, dc/f0=0.18, relative resistivity 6
Computed (red)
Measured (blue)
Computed (red)
Measured (blue)
![Page 21: Nickel Characterization for Signal Integrity Analysis Nickel characterization at microwave frequencies Anomalies in ENIG plated interconnects Identification of nickel parameters GMS-parameters](https://reader036.fdocuments.net/reader036/viewer/2022062907/5aaa645b7f8b9a7c188e0560/html5/thumbnails/21.jpg)
Identified Model for Plated Nickel Resistivity 1.0e-7 Ohm*meter Landau-Lifshits Permeability Model: Mul=6, Muh=2, f0=2.6, dc/f0=0.18
8/16/2011 © 2011 Teraspeed Consulting Group LLC © 2011 Simberian Inc.
21
May be further refined with a dedicated experiment with more defined geometry
Real Part
Imaginary Part
Relative Permeability
![Page 22: Nickel Characterization for Signal Integrity Analysis Nickel characterization at microwave frequencies Anomalies in ENIG plated interconnects Identification of nickel parameters GMS-parameters](https://reader036.fdocuments.net/reader036/viewer/2022062907/5aaa645b7f8b9a7c188e0560/html5/thumbnails/22.jpg)
Effect of nickel on t-line parameters We can observe decrease of group delay and increase in
attenuation per unit length
8/16/2011 © 2011 Teraspeed Consulting Group LLC © 2011 Simberian Inc.
22
Group Delay in ps/mm Attenuation in dB/mm
![Page 23: Nickel Characterization for Signal Integrity Analysis Nickel characterization at microwave frequencies Anomalies in ENIG plated interconnects Identification of nickel parameters GMS-parameters](https://reader036.fdocuments.net/reader036/viewer/2022062907/5aaa645b7f8b9a7c188e0560/html5/thumbnails/23.jpg)
Effect of nickel on t-line parameters The effect is less visible on the characteristic impedance and
effective dielectric constant
8/16/2011 © 2011 Teraspeed Consulting Group LLC © 2011 Simberian Inc.
23
Characteristic Impedance Effective Dielectric Constant
![Page 24: Nickel Characterization for Signal Integrity Analysis Nickel characterization at microwave frequencies Anomalies in ENIG plated interconnects Identification of nickel parameters GMS-parameters](https://reader036.fdocuments.net/reader036/viewer/2022062907/5aaa645b7f8b9a7c188e0560/html5/thumbnails/24.jpg)
S-parameters of test fixtures
8/16/2011 © 2011 Teraspeed Consulting Group LLC © 2011 Simberian Inc.
24
Nickel: resistivity 1.0e-7 Ohm*meter, Landau-Lifshits Permeability Model: Mul=6, Muh=2, f0=2.6, dc/f0=0.18
100 mm line
150 mm line 100 mm line
150 mm line
Insertion Loss
![Page 25: Nickel Characterization for Signal Integrity Analysis Nickel characterization at microwave frequencies Anomalies in ENIG plated interconnects Identification of nickel parameters GMS-parameters](https://reader036.fdocuments.net/reader036/viewer/2022062907/5aaa645b7f8b9a7c188e0560/html5/thumbnails/25.jpg)
Possible sources of discrepancies Simulated – rectangular shape with 0.05 um of Au/6 um of Ni/9 um of Cu Actual structure has irregular shape – not even trapezoidal
8/16/2011 © 2011 Teraspeed Consulting Group LLC © 2011 Simberian Inc.
25
Strip bottom: RMS roughness 0.6-1.2, Roughness factor 2.5 – should be defined formally with profilometer measurements
Au Ni
Cu
Actual shape Modeled Au/Ni Cu
![Page 26: Nickel Characterization for Signal Integrity Analysis Nickel characterization at microwave frequencies Anomalies in ENIG plated interconnects Identification of nickel parameters GMS-parameters](https://reader036.fdocuments.net/reader036/viewer/2022062907/5aaa645b7f8b9a7c188e0560/html5/thumbnails/26.jpg)
Plated Nickel Model Identification (2) Adjust Ni model parameters to match measured and computed GMS-parameters for
50 mm segment of microstrip line, strip width 69 um, thickness 12 um
8/16/2011 © 2011 Teraspeed Consulting Group LLC © 2011 Simberian Inc.
26
ENIG finish with about 1 um of Ni over the copper Substrate dielectric DK=3.x and LT=0.01x at 1 GHz, wideband Debye model Landau-Lifshits model for Nickel: Mul=5.7, Muh=1.4, f0=2.5, dc/f0=0.22, relative resistivity 3.75
Computed (red)
Measured (blue)
Computed (red)
Measured (blue)
![Page 27: Nickel Characterization for Signal Integrity Analysis Nickel characterization at microwave frequencies Anomalies in ENIG plated interconnects Identification of nickel parameters GMS-parameters](https://reader036.fdocuments.net/reader036/viewer/2022062907/5aaa645b7f8b9a7c188e0560/html5/thumbnails/27.jpg)
Identified Model for Plated Nickel (2) Resistivity 6.46e-8 Ohm*meter (conductivity 1.55e7 S/m) Landau-Lifshits Permeability Model: Mul=5.7, Muh=1.4, f0=2.5, dc/f0=0.22
8/16/2011 © 2011 Teraspeed Consulting Group LLC © 2011 Simberian Inc.
27
May be further refined with a dedicated experiment with more defined geometry
Real Part
Imaginary Part
Relative Permeability
![Page 28: Nickel Characterization for Signal Integrity Analysis Nickel characterization at microwave frequencies Anomalies in ENIG plated interconnects Identification of nickel parameters GMS-parameters](https://reader036.fdocuments.net/reader036/viewer/2022062907/5aaa645b7f8b9a7c188e0560/html5/thumbnails/28.jpg)
S-parameters of test fixtures
8/16/2011 © 2011 Teraspeed Consulting Group LLC © 2011 Simberian Inc.
28
Nickel: resistivity 6.46e-8 Ohm*meter, Landau-Lifshits Permeability Model: : Mul=5.7, Muh=1.4, f0=2.5, dc/f0=0.22
100 mm line
150 mm line 100 mm line
150 mm line
Insertion Loss
![Page 29: Nickel Characterization for Signal Integrity Analysis Nickel characterization at microwave frequencies Anomalies in ENIG plated interconnects Identification of nickel parameters GMS-parameters](https://reader036.fdocuments.net/reader036/viewer/2022062907/5aaa645b7f8b9a7c188e0560/html5/thumbnails/29.jpg)
3.125 Gbps signal in structure with 150 mm line
8/16/2011 © 2011 Teraspeed Consulting Group LLC © 2011 Simberian Inc.
29
Measured Modeled
![Page 30: Nickel Characterization for Signal Integrity Analysis Nickel characterization at microwave frequencies Anomalies in ENIG plated interconnects Identification of nickel parameters GMS-parameters](https://reader036.fdocuments.net/reader036/viewer/2022062907/5aaa645b7f8b9a7c188e0560/html5/thumbnails/30.jpg)
5 Gbps signal in structure with 150 mm line
8/16/2011 © 2011 Teraspeed Consulting Group LLC © 2011 Simberian Inc.
30
Measured Modeled
![Page 31: Nickel Characterization for Signal Integrity Analysis Nickel characterization at microwave frequencies Anomalies in ENIG plated interconnects Identification of nickel parameters GMS-parameters](https://reader036.fdocuments.net/reader036/viewer/2022062907/5aaa645b7f8b9a7c188e0560/html5/thumbnails/31.jpg)
8 Gbps signal in structure with 150 mm line
8/16/2011 © 2011 Teraspeed Consulting Group LLC © 2011 Simberian Inc.
31
Measured Modeled
![Page 32: Nickel Characterization for Signal Integrity Analysis Nickel characterization at microwave frequencies Anomalies in ENIG plated interconnects Identification of nickel parameters GMS-parameters](https://reader036.fdocuments.net/reader036/viewer/2022062907/5aaa645b7f8b9a7c188e0560/html5/thumbnails/32.jpg)
10 Gbps signal in structure with 150 mm line
8/16/2011 © 2011 Teraspeed Consulting Group LLC © 2011 Simberian Inc.
32
Measured Modeled
![Page 33: Nickel Characterization for Signal Integrity Analysis Nickel characterization at microwave frequencies Anomalies in ENIG plated interconnects Identification of nickel parameters GMS-parameters](https://reader036.fdocuments.net/reader036/viewer/2022062907/5aaa645b7f8b9a7c188e0560/html5/thumbnails/33.jpg)
12 Gbps signal in structure with 150 mm line
8/16/2011 © 2011 Teraspeed Consulting Group LLC © 2011 Simberian Inc.
33
Measured Modeled
![Page 34: Nickel Characterization for Signal Integrity Analysis Nickel characterization at microwave frequencies Anomalies in ENIG plated interconnects Identification of nickel parameters GMS-parameters](https://reader036.fdocuments.net/reader036/viewer/2022062907/5aaa645b7f8b9a7c188e0560/html5/thumbnails/34.jpg)
Conclusion Resonant behavior of interconnects made of copper plated with nickel
and gold (ENIG finish) has been reported Resonance at about 2.7 GHz shows up on insertion loss as well as on
group delay graphs and cannot be simply explained The resonance is attributed to ferromagnetic properties of nickel layer
Electromagnetic model of copper microstrip line segment plated with Ni and Au has been constructed
Landau-Lifshits (L-L) ferromagnetic metal model is used to simulate nickel in the multi-layered conductor
Parameters of the L-L model are identified by matching measured and computed GMS-parameters of line segment
Use of accurate Nickel models increases confidence in modeling of ENIG-finished interconnects
8/16/2011 © 2011 Teraspeed Consulting Group LLC © 2011 Simberian Inc.
34
![Page 35: Nickel Characterization for Signal Integrity Analysis Nickel characterization at microwave frequencies Anomalies in ENIG plated interconnects Identification of nickel parameters GMS-parameters](https://reader036.fdocuments.net/reader036/viewer/2022062907/5aaa645b7f8b9a7c188e0560/html5/thumbnails/35.jpg)
Be sure to visit us:
8/16/2011 © 2011 Teraspeed Consulting Group LLC © 2011 Simberian Inc.