Structure-phase investigation Structure-phase investigation and mechanical properties of and mechanical properties of Zr-1%Nb alloy claddings after Zr-1%Nb alloy claddings after LOCA tests on PARAMETR LOCA tests on PARAMETR
facility under 1400 facility under 1400 °C°C
FSUE SRI SIA «LUCH»
Gukov M.Yu., Deniskin V.P., Ignatjev D.N., Konstantinov V.S., Nalivaev V.I., Fedik I.I.FSUE “SRI SIA LUCH”
Nechaeva O.A., Novikov V.V., Salatov A.V., Fedotov P.V.FSUE VNIINM
Semishkin V.P.FSUE EDB “Gidropress”
![Page 2: FSUE SRI SIA « LUCH »](https://reader035.fdocuments.net/reader035/viewer/2022062309/568141d3550346895dadad32/html5/thumbnails/2.jpg)
2
ContentContent
1. Experimental Facility:Design and basis Technical Parameters
2. Experimetal Results of Tests under the Quench Conditions at different Temperatures:
- 1-st Test (FA1) – 900 °C - 2-nd Test (FA2) – 1200 °C- 3-d Test (FA3) – 1400 °C
3. Material researches CONCLUSIONSCONCLUSIONS
![Page 3: FSUE SRI SIA « LUCH »](https://reader035.fdocuments.net/reader035/viewer/2022062309/568141d3550346895dadad32/html5/thumbnails/3.jpg)
3
Heated rod Unheated rod Test Bundle
Test InstrumentationTest InstrumentationTest Bundle SpecificationTest Bundle Specification
![Page 4: FSUE SRI SIA « LUCH »](https://reader035.fdocuments.net/reader035/viewer/2022062309/568141d3550346895dadad32/html5/thumbnails/4.jpg)
4
Experimental FacilityExperimental Facility
Functional DiagramFunctional Diagram
![Page 5: FSUE SRI SIA « LUCH »](https://reader035.fdocuments.net/reader035/viewer/2022062309/568141d3550346895dadad32/html5/thumbnails/5.jpg)
5
Basis parametersBasis parameters of testsof tests
Quench temperature, °C
![Page 6: FSUE SRI SIA « LUCH »](https://reader035.fdocuments.net/reader035/viewer/2022062309/568141d3550346895dadad32/html5/thumbnails/6.jpg)
6
Appearance of claddings after tests of Appearance of claddings after tests of FA1FA1 and FA2and FA2
Fuel Assembly #1Fuel Assembly #1
Fuel Assembly #2Fuel Assembly #2
![Page 7: FSUE SRI SIA « LUCH »](https://reader035.fdocuments.net/reader035/viewer/2022062309/568141d3550346895dadad32/html5/thumbnails/7.jpg)
7
Вход пара
Залив снизу
Appearance of FA3 after testsAppearance of FA3 after tests
4
1
2
3
1 2
3 4
TTcladdingscladdings=1=100000 °0 °СС TTcladdingscladdings=1=120200 °0 °СС
TTcladdingscladdings=1=140400 °0 °СС TTcladdings claddings >>22000000 °°СС
Input of steamInput of steam
Embayment from Embayment from belowbelow
![Page 8: FSUE SRI SIA « LUCH »](https://reader035.fdocuments.net/reader035/viewer/2022062309/568141d3550346895dadad32/html5/thumbnails/8.jpg)
8
Appearance of external surface of FA1 Appearance of external surface of FA1
and FA2 deformed claddingsand FA2 deformed claddings
Multilayer oxide film on external cladding surface (FA2)
Profile of oxide film rupture in a zone of maximal deformation of claddings (FA1)
State of an external surface of State of an external surface of strainedstrained claddings claddings (FA1, FA2) (FA1, FA2)
![Page 9: FSUE SRI SIA « LUCH »](https://reader035.fdocuments.net/reader035/viewer/2022062309/568141d3550346895dadad32/html5/thumbnails/9.jpg)
9
Maximum valuations of structural Maximum valuations of structural
parameters of claddings FA1-3parameters of claddings FA1-3
![Page 10: FSUE SRI SIA « LUCH »](https://reader035.fdocuments.net/reader035/viewer/2022062309/568141d3550346895dadad32/html5/thumbnails/10.jpg)
10
Change of Change of - Zr (O) layer thickness - Zr (O) layer thickness depending depending
onon ECR value ECR value (FA1–3)FA1–3)
![Page 11: FSUE SRI SIA « LUCH »](https://reader035.fdocuments.net/reader035/viewer/2022062309/568141d3550346895dadad32/html5/thumbnails/11.jpg)
11
Change of structural-phase parameters and Change of structural-phase parameters and – Zr failure type depending on ECR value – Zr failure type depending on ECR value
(FA 1 – 3)(FA 1 – 3)
![Page 12: FSUE SRI SIA « LUCH »](https://reader035.fdocuments.net/reader035/viewer/2022062309/568141d3550346895dadad32/html5/thumbnails/12.jpg)
12
Change of ECR on azimuth of claddings Change of ECR on azimuth of claddings depressurization zonedepressurization zone
![Page 13: FSUE SRI SIA « LUCH »](https://reader035.fdocuments.net/reader035/viewer/2022062309/568141d3550346895dadad32/html5/thumbnails/13.jpg)
13
Character of ZrOCharacter of ZrO22 and and αα-Zr(O)-Zr(O)
layers failurelayers failure
ZrOZrO2 2 ((x1600)x1600) αα-Zr(O) (x3000)-Zr(O) (x3000)
![Page 14: FSUE SRI SIA « LUCH »](https://reader035.fdocuments.net/reader035/viewer/2022062309/568141d3550346895dadad32/html5/thumbnails/14.jpg)
14
Change of Change of – Zr layer failure character under – Zr layer failure character under
mechanical tests of samplesmechanical tests of samples
FA1 (x2000) FA2 (x2000) FA3 (x2000)
Ductile Quasi-brittle Brittle
![Page 15: FSUE SRI SIA « LUCH »](https://reader035.fdocuments.net/reader035/viewer/2022062309/568141d3550346895dadad32/html5/thumbnails/15.jpg)
15
Strength Strength propertiesproperties of claddings in a of claddings in a transverse direction depending on ECR valuetransverse direction depending on ECR value
(FA 1 – 3) FA 1 – 3)
![Page 16: FSUE SRI SIA « LUCH »](https://reader035.fdocuments.net/reader035/viewer/2022062309/568141d3550346895dadad32/html5/thumbnails/16.jpg)
16
Microhardness Microhardness level at which level at which spreading of the spreading of the crack, arisen in crack, arisen in brittle brittle αα-Zr (O) -Zr (O) layer, was layer, was complicated due to complicated due to enough enough high fracture high fracture toughness of toughness of αα '-Zr '-Zr layerlayer
![Page 17: FSUE SRI SIA « LUCH »](https://reader035.fdocuments.net/reader035/viewer/2022062309/568141d3550346895dadad32/html5/thumbnails/17.jpg)
17
““Constructive strength” of unstrained and Constructive strength” of unstrained and depressurized claddings of FA1 and FA2 depressurized claddings of FA1 and FA2
under tensionunder tension
![Page 18: FSUE SRI SIA « LUCH »](https://reader035.fdocuments.net/reader035/viewer/2022062309/568141d3550346895dadad32/html5/thumbnails/18.jpg)
18
Change of microhardness on azimuth of Change of microhardness on azimuth of claddings rupture zone (FA1, FA2)claddings rupture zone (FA1, FA2)
![Page 19: FSUE SRI SIA « LUCH »](https://reader035.fdocuments.net/reader035/viewer/2022062309/568141d3550346895dadad32/html5/thumbnails/19.jpg)
19
• It was experimentally shown, that quenching of It was experimentally shown, that quenching of bundles at temperatures 900 C (FA1) and 1200 C bundles at temperatures 900 C (FA1) and 1200 C (FA2) did not result in the claddings fragmentation, (FA2) did not result in the claddings fragmentation, and the residual resource of mechanical properties and the residual resource of mechanical properties was sufficient for its subsequent dismantling and was sufficient for its subsequent dismantling and transportation. transportation.
• The increase of bundle temperature up to 1400°The increase of bundle temperature up to 1400°СС (FA3) before quenching resulted in the claddings (FA3) before quenching resulted in the claddings fragmentation.fragmentation.
• The faultiest zone ofThe faultiest zone of the claddings of FA1 and FA2 the claddings of FA1 and FA2 was the rupture zone due to the thinning of the was the rupture zone due to the thinning of the cladding under the peripheral deformation and its cladding under the peripheral deformation and its double-side oxidation.double-side oxidation.
CONCLUSIONSCONCLUSIONS
![Page 20: FSUE SRI SIA « LUCH »](https://reader035.fdocuments.net/reader035/viewer/2022062309/568141d3550346895dadad32/html5/thumbnails/20.jpg)
20
• Non-monotonic character of changing strength Non-monotonic character of changing strength characteristics of the claddings was established characteristics of the claddings was established depending on their oxidation level. Increase in a depending on their oxidation level. Increase in a yield stress in a transverse direction decrease in yield stress in a transverse direction decrease in plasticity to a zero value was observed up to ECR plasticity to a zero value was observed up to ECR value of ~ 8 - 9 %. The further oxidation of the value of ~ 8 - 9 %. The further oxidation of the claddings resulted in reducing strength.claddings resulted in reducing strength.
• Based on electron-microscopic researches change Based on electron-microscopic researches change of of –Zr layer failure character was established –Zr layer failure character was established depending on its structural – phase state determined depending on its structural – phase state determined by ECR value:by ECR value: