BUILDING SYSTEM TECHNICAL DATA FORT ZINC 100 Zinc Rich Epoxy Primer DESCRIPTION FORT ZINC 100 is a two-component, zinc rich epoxy primer with a high zinc content in the dry film. It cures to a hard wearing and highly weather resistant coating, offers cathodic protection of local mechanical damage. USES As a versatile, long-life primer on steel for epoxy, vinyl and acrylic coating system. Also can be used as shop riming and on-line application of containers. TECHNICAL DATA Colour/finish : Grey/flat Volume solid % : 47 + 1 Theoretical spreading rate : 11.75 at 40 micron dft Flash point : 30⁰C Specific gravity : 2.6 kg/ltr Surface dry : 30 minutes at 20⁰C Dry to touch : 3-4 hours at 20⁰C Fully cured : 7 days at 20⁰C VOC : 480 g/ltr CURING The curing period is dependent on ambient and surface temperatures. SURFACE PREPARATION Remove oil and grease thoroughly with suitable detergent. Remove salt and other contaminants by high pressure fresh water wash. Abrasive blasting to Sa 2.5 ISO8501-1:1988 with a sharp edged surface profile corresponding to Rugotest No.3, or ISO comparator, Medium (G) APPLICATION CONDITIONS Use only where application and curing can proceed at temperatures above 10⁰C . the temperature of the surface must also above this limit. The temperature of the paint itself should be 15⁰C or above. Apply only on a dry and clean surface with a temperature above the dew point to avoid condensation. In confined space provide adequate ventilation during application and drying. Note: If used as anticorrosive protection under insulation of high temperature equipment it is very important that NO moisture can penetrate during slow-down periods. This is to avoid risk of “wet corrosion” when the temperature rises. Film thickness: May be specified in another thickness than indicated depending on purpose and area of use. This will alter spreading rate and may influence amount of
Transcript of FORT ZINC 100 - Organix Bs Zinc 100.pdf · FORT ZINC 100 is a two-component, zinc rich epoxy primer...
BUILDING SYSTEM
TECHNICAL DATA
FORT ZINC 100 Zinc Rich Epoxy Primer
DESCRIPTION FORT ZINC 100 is a two-component, zinc rich epoxy primer with a high zinc content in the dry film. It cures to a hard wearing and highly weather resistant coating, offers cathodic protection of local mechanical damage.
USES As a versatile, long-life primer on steel for epoxy, vinyl and acrylic coating system. Also can be used as shop riming and on-line application of containers.
TECHNICAL DATA Colour/finish : Grey/flat Volume solid % : 47 + 1 Theoretical spreading rate : 11.75 at 40 micron dft Flash point : 30⁰C Specific gravity : 2.6 kg/ltr Surface dry : 30 minutes at 20⁰C Dry to touch : 3-4 hours at 20⁰C Fully cured : 7 days at 20⁰C VOC : 480 g/ltr CURING The curing period is dependent on ambient and surface temperatures. SURFACE PREPARATION Remove oil and grease thoroughly with suitable detergent. Remove salt and other contaminants by high pressure fresh water wash. Abrasive blasting to Sa 2.5 ISO8501-1:1988 with a sharp edged surface profile corresponding to Rugotest No.3, or ISO comparator, Medium (G)
APPLICATION CONDITIONS Use only where application and curing can proceed at temperatures above 10⁰C . the temperature of the surface must also above this limit. The temperature of the paint itself should be 15⁰C or above. Apply only on a dry and clean surface with a temperature above the dew point to avoid condensation. In confined space provide adequate ventilation during application and drying. Note: If used as anticorrosive protection under insulation of high temperature equipment it is very important that NO moisture can penetrate during slow-down periods. This is to avoid risk of “wet corrosion” when the temperature rises.
Film thickness: May be specified in another thickness than indicated depending on purpose and area of use. This will alter spreading rate and may influence amount of
ORGANIX BUILDING SYSTEMDubai, U.A.E, Tel: +971 42676951, Fax: +971 42676931Email: [email protected], www.organixbs.com
BUILDING SYSTEM
thinning necessary, drying time, and recoating interval. Normally the dry film thickness is 15-50 micron
Recoat Recoating intervals related to later conditions of exposure. If maximum recoating interval is exceeded, roughening of the surface is necessary to ensure inter-coat adhesion. Before recoating after exposure in contaminated environment, clean the surface thoroughly by high pressure water hosing and allow to dry. In addition, scrubbing with a stiff brush may be necessary to remove zinc corrosion products (white rust).
APPLICATION INFORMATION Mixing Ratio : 4:1 by volume Application method : Airless Spray Air Spray Brush Thinning : AT155 (5%) AT155 (15%) AT (5%) Pot Life : 8 hours (20⁰C) Nozzle orifice : 0.017” - 0.021” Nozzle Pressure : 150 bar/ 2200 psi Indicated film thickness, dry : 40 micron Indicated film thickness, wet : 75 micron Recoat interval min : 3 hour @ 20⁰C Service Temperature : Maximum, dry exposure only: 180⁰C Specifications For Specification please contact your OBS sales representative or contact our Technical Service Department [email protected]
WARNING! If you scrape sand or remove old paint, you may release lead dust. LEAD IS TOXIC, EXPOSURE TO LEAD DUST CAN CAUSE SERIOUS ILLNESS, SUCH AS BRAIN DAMAGE ESPECIALLY IN CHILDREN, PREGENANT WOMEN SHOULD ALSO AVOID EXPOSURE. Wear approved respirator to control lead exposure, clean up carefully with HEPA vacuum and wet mop
HEALTH AND SAFETY Handle with care, before and after use. Follow local safety regulations. All skin contact with resin product should be avoided. Barrier creams should be used and operatives should wear protective clothing. WARRANTY OBS warrants our products to be free of manufacturing defects in accord with applicable OBS quality control procedures. Liability for products proven defective, if any is limited to replacement of the defective product or the refund of the purchase price paid for the defective product as determined by OBS. NO OTHER GUARANTEE OF ANY KIND IS MADE BY OBS, EXPRESSED OR IMPLIED, STATUTORY, BY OPERATION OF LAW OR OTHERWISE, INCLUDING MERCHANTABLITY AND FITNESS FOR A PARTICULAR PURPOSE.