Exchange bias and coercivity of ferromagnetic/antiferromagnetic multilayers · Exchange bias and...
-
Upload
vuongthien -
Category
Documents
-
view
224 -
download
2
Transcript of Exchange bias and coercivity of ferromagnetic/antiferromagnetic multilayers · Exchange bias and...
![Page 1: Exchange bias and coercivity of ferromagnetic/antiferromagnetic multilayers · Exchange bias and coercivity of ferromagnetic/antiferromagnetic multilayers Klaus D. Usadel Universitat](https://reader033.fdocuments.net/reader033/viewer/2022051801/5ae2ca587f8b9a595d8da1c2/html5/thumbnails/1.jpg)
Exchange bias and coercivity
of ferromagnetic/antiferromagnetic multilayers
Klaus D. Usadel
Universitat Duisburg-Essen, Germany
Contents:
• exchange bias: introduction
• domain state model: results from MC simulations
• mean field approach for Ising AFM: coercivity and exchange bias
• generalisation to local vector spin models: dynamical consequences
• conclusions
Coworkers:
• U. Nowak, A. Misra, B. Beckmann, R. Stamps
![Page 2: Exchange bias and coercivity of ferromagnetic/antiferromagnetic multilayers · Exchange bias and coercivity of ferromagnetic/antiferromagnetic multilayers Klaus D. Usadel Universitat](https://reader033.fdocuments.net/reader033/viewer/2022051801/5ae2ca587f8b9a595d8da1c2/html5/thumbnails/2.jpg)
Exchange bias
• exchange bias (EB) = shifted hysteresis
loop
• first observation in Co/CoO partic-
les (Meiklejohn and Bean, Phys. Rev.
102,1413 (1956))
• typical for FM/AFM compounds like
multilayers, nanoparticles
• initial procedure: cooling the system in
an external field from above to below
Neel temperature of the AFM
• loop is shifted upwards and asymme-
tric; enhancement of the coercivity
TN
FCB
Hyst.
T
![Page 3: Exchange bias and coercivity of ferromagnetic/antiferromagnetic multilayers · Exchange bias and coercivity of ferromagnetic/antiferromagnetic multilayers Klaus D. Usadel Universitat](https://reader033.fdocuments.net/reader033/viewer/2022051801/5ae2ca587f8b9a595d8da1c2/html5/thumbnails/3.jpg)
Applications: sensors
H1 < 0H = 0H2 < H1
Sx
F(S
x)
-1 0 1
0
F(Sx) = −DS2x − BSx
The fields B− and B+ at which the magnetizati-
on of the FM switches are obtained from F ′ = 0
at Sx = 1 and Sx = −1, respectively:
B− = −2D,
B+ = 2D.
-1 -0.5 0 0.5 1external field
-1
-0.5
0
0.5
1
mag
netiz
atio
n
![Page 4: Exchange bias and coercivity of ferromagnetic/antiferromagnetic multilayers · Exchange bias and coercivity of ferromagnetic/antiferromagnetic multilayers Klaus D. Usadel Universitat](https://reader033.fdocuments.net/reader033/viewer/2022051801/5ae2ca587f8b9a595d8da1c2/html5/thumbnails/4.jpg)
Understanding EB: problems
• external field and exchange field of the FM interface layer polarizes the AFM interface layer
• why is the polarisation stable during a hysteresis cycle? why is the symmetry broken?
perfect interface
uncompensated compensated
rough interface
Domain wall formation
![Page 5: Exchange bias and coercivity of ferromagnetic/antiferromagnetic multilayers · Exchange bias and coercivity of ferromagnetic/antiferromagnetic multilayers Klaus D. Usadel Universitat](https://reader033.fdocuments.net/reader033/viewer/2022051801/5ae2ca587f8b9a595d8da1c2/html5/thumbnails/5.jpg)
Solution: domain walls in the AFM
• breaking the symmetry necessary for EB by introducing frozen domains
• perpendicular domain walls in the AFM due
to interface roughness
(Malozemoff, Phys. Rev. B 35, 3679 (1987))
• but: domain wall formation unlikely for large AFM thicknesses
• idea: introducing defects in the AFM to stabilize domains: d omain state model
(Miltenyi, Gierlings, Keller, Beschoten, Guntherodt,
Nowak, and Usadel, PRL 84, 4224 (2000))
![Page 6: Exchange bias and coercivity of ferromagnetic/antiferromagnetic multilayers · Exchange bias and coercivity of ferromagnetic/antiferromagnetic multilayers Klaus D. Usadel Universitat](https://reader033.fdocuments.net/reader033/viewer/2022051801/5ae2ca587f8b9a595d8da1c2/html5/thumbnails/6.jpg)
Experiments with diluted AFM
• Idea: generate defects in AFM:
– CoO → Co1−xMgxO
– interface layer without defects
– vary bulk dilution
FM: Co
AFM: CoO
CoMgO
⇒ bulk dilution enhances ex-
change bias(EB)
⇒ associated with EB is an en-
hancement of the coercivity
• see also:
Mewes et al., APL 76, 1057 (2000)
Shi et al., JAP 91, 7763 (2002)
Miltenyi, Gierlings, Keller, Beschoten, Guntherodt,
Nowak, Usadel, PRL 84, 4224 (2000)
![Page 7: Exchange bias and coercivity of ferromagnetic/antiferromagnetic multilayers · Exchange bias and coercivity of ferromagnetic/antiferromagnetic multilayers Klaus D. Usadel Universitat](https://reader033.fdocuments.net/reader033/viewer/2022051801/5ae2ca587f8b9a595d8da1c2/html5/thumbnails/7.jpg)
Local spin model
AFM
FM
x
zy
B
EB
M
H = HF + HAF + Hint
HF = −JF
∑
〈i,j〉
−→Si ·
−→Sj −
∑
i
(
DS2ix + SixB
)
HAF = JAF
∑
〈i,j〉
ǫiǫjσiσj −∑
i
ǫiσiB
Hint = −Jint
∑
i∈(int)
ǫiSixσi,
• D > 0; JAF = −JF/2;
Jint = +/ − JAF;
• Monte Carlo simulation, system
size up to 128 × 128 × (9 + 1)
up to 136000 MCS per hysteresis,
average over up to 10 runs
• local mean field theory
![Page 8: Exchange bias and coercivity of ferromagnetic/antiferromagnetic multilayers · Exchange bias and coercivity of ferromagnetic/antiferromagnetic multilayers Klaus D. Usadel Universitat](https://reader033.fdocuments.net/reader033/viewer/2022051801/5ae2ca587f8b9a595d8da1c2/html5/thumbnails/8.jpg)
Hysteresis of FM and AFM interface: MC simulations
• system cooled in a field
Bc = 0.25JF down to
kBT = 0.1JF
• AFM frozen in a domain
state with interface magne-
tization
• its irreversible part leads to
exchange bias
• BEB ≈ 0.03Jint
• D = 0.1JF
-0.3 -0.2 -0.1 0 0.1 0.2 0.3
B
-0.1
0
0.1
m (
AFM
Int
erfa
ce)
-0.3 -0.2 -0.1 0 0.1 0.2 0.3
-1
-0.5
0
0.5
1
m (
FM)
B+
B_
mI
![Page 9: Exchange bias and coercivity of ferromagnetic/antiferromagnetic multilayers · Exchange bias and coercivity of ferromagnetic/antiferromagnetic multilayers Klaus D. Usadel Universitat](https://reader033.fdocuments.net/reader033/viewer/2022051801/5ae2ca587f8b9a595d8da1c2/html5/thumbnails/9.jpg)
Structure of the AFM domains
TN
FCB
Hyst.
T
Staggered AFM magnetization after field cooling
above: large dilution, p = 0.5, small domains, below: small dilution, p = 0.3, larger domains.
![Page 10: Exchange bias and coercivity of ferromagnetic/antiferromagnetic multilayers · Exchange bias and coercivity of ferromagnetic/antiferromagnetic multilayers Klaus D. Usadel Universitat](https://reader033.fdocuments.net/reader033/viewer/2022051801/5ae2ca587f8b9a595d8da1c2/html5/thumbnails/10.jpg)
Magnetization reversal of the FM layer
θ = 8◦4
3
2
1
Magnetization mz
Magnet
ization
my
10-1
1
0
-1
• coherent rotation of the FM magnetization
• no asymmetry for θ → 0
• local FM spins−→S i =
−→S replaced by a
macro spin
F(Sx) = −NlDS2x − NlBSx − kBT Tr e−β(HAF+Hint)
F ′(Sx) = −2NlDSx − NlB − Jint
∑
i∈int
〈σi〉
F ′′(Sx) = −2NlD − βJ2int
⟨
(
∑
i∈int
(σi − 〈σi〉))2
⟩
• mint =∑
i∈int〈σi〉
• l number of FM monolayers
• N spins per FM monolayer
![Page 11: Exchange bias and coercivity of ferromagnetic/antiferromagnetic multilayers · Exchange bias and coercivity of ferromagnetic/antiferromagnetic multilayers Klaus D. Usadel Universitat](https://reader033.fdocuments.net/reader033/viewer/2022051801/5ae2ca587f8b9a595d8da1c2/html5/thumbnails/11.jpg)
Switching fields
H1 < 0H = 0H2 < H1
Sx
F(S
x)
-1 0 1
0
F ′(Sx) = −2NlDSx − NlB − Jintmint
Fields B− and B+ for magnetization switching
from F ′ = 0 at Sx = 1 and Sx = −1,
respectively:
B− = −2D − Jintmint
(
B−, Sx = 1)
/l,
B+ = 2D − Jintmint
(
B+, Sx = −1)
/l,
HH
1
�1
m0m0 � �(1)Jintm0 + �(1)Jintmint = m0 + mrev
mrev = χ(1)AFJintSx + χ
(2)AFB
![Page 12: Exchange bias and coercivity of ferromagnetic/antiferromagnetic multilayers · Exchange bias and coercivity of ferromagnetic/antiferromagnetic multilayers Klaus D. Usadel Universitat](https://reader033.fdocuments.net/reader033/viewer/2022051801/5ae2ca587f8b9a595d8da1c2/html5/thumbnails/12.jpg)
Hysteresis of FM and AFM interface: MC simulations
• system cooled in a field
Bc = 0.25JF down to
kBT = 0.1JF
• AFM frozen in a domain
state with interface magne-
tization
• its irreversible part leads to
exchange bias
• BEB ≈ 0.03Jint
• D = 0.1JF
-0.3 -0.2 -0.1 0 0.1 0.2 0.3
B
-0.1
0
0.1
m (
AFM
Int
erfa
ce)
-0.3 -0.2 -0.1 0 0.1 0.2 0.3
-1
-0.5
0
0.5
1
m (
FM)
B+
B_
mI
![Page 13: Exchange bias and coercivity of ferromagnetic/antiferromagnetic multilayers · Exchange bias and coercivity of ferromagnetic/antiferromagnetic multilayers Klaus D. Usadel Universitat](https://reader033.fdocuments.net/reader033/viewer/2022051801/5ae2ca587f8b9a595d8da1c2/html5/thumbnails/13.jpg)
Linear approximation
mint(B, Sx = ±1): AFM interface magnetization determines coercivity and EB
B± = ±2D−Jintmint(B±, Sx = ∓1)/l
mint = m0 + mrev
mrev = χ(1)AFJintSx + χ
(2)AFB
B± =±2D−Jintm0/l±J2
intχ(1)
AF/l
1+Jintχ(2)AF
/l
Beb = 12(B+ + B−) =
−Jintm0/l
1+Jintχ(2)
AF/l
Bc = 12(B+ − B−) =
2D+J2intχ
(1)
AF/l
1+Jintχ(2)
AF/l
0 0.5 1 1.5 2T/TN
(1)
0.02
0.06
0.10
0.14
Hc/J
AF
Hclin
Hcnum
⇒ dependence on the sign of JINT mean field approach
![Page 14: Exchange bias and coercivity of ferromagnetic/antiferromagnetic multilayers · Exchange bias and coercivity of ferromagnetic/antiferromagnetic multilayers Klaus D. Usadel Universitat](https://reader033.fdocuments.net/reader033/viewer/2022051801/5ae2ca587f8b9a595d8da1c2/html5/thumbnails/14.jpg)
MF approximation; no dilution
〈σi〉 = mi = tanh
(
β(
− JAF
∑
j mj + JintSx + B)
)
0 0.5 1 1.5 2T/TN
(1)
0.02
0.06
0.10
0.14
0.18
Hc/J
AF
L=1L=2L=3L=8
(a)
0 0.5 1 1.5 2T/TN
(1)
0.02
0.06
0.10
0.14
0.18
Hc/J
AF
L=1L=2L=3L=8
(b)
Coercive field as function of reduced temperature for different AFM layer thicknesses l.
left: Jint = −JAF right: Jint = JAF D/JF = 0.005
⇒ large increase of the coercivity in the vicinity of the Neel t emperature TN
(Scholten, Usadel, Nowak, Phys. Rev. B 71, 64413 (2005))
![Page 15: Exchange bias and coercivity of ferromagnetic/antiferromagnetic multilayers · Exchange bias and coercivity of ferromagnetic/antiferromagnetic multilayers Klaus D. Usadel Universitat](https://reader033.fdocuments.net/reader033/viewer/2022051801/5ae2ca587f8b9a595d8da1c2/html5/thumbnails/15.jpg)
Diluted systems
Local mean field equations:
mi = ǫitanh
(
β(
− JAF
∑
j
ǫjmj + JintSx + B)
)
Cooling : Iteration at a fixed temperature until a (metastable) self-consistent solution is
obtained, then reducing temperature in small steps.
![Page 16: Exchange bias and coercivity of ferromagnetic/antiferromagnetic multilayers · Exchange bias and coercivity of ferromagnetic/antiferromagnetic multilayers Klaus D. Usadel Universitat](https://reader033.fdocuments.net/reader033/viewer/2022051801/5ae2ca587f8b9a595d8da1c2/html5/thumbnails/16.jpg)
Coercivity and bias fields: different AFM dilution p
0.02
0.06
0.10
0.14
0.18
Hc/J
AF
p=0.p=0.1p=0.3p=0.6
0 0.5 1 1.5 2T/TN
(1,0)
0
0.01
0.02
0.03
0.04
0.05
Heb
/JA
F
l = 3 and Jint = −JAF
0.02
0.06
0.10
0.14
0.18
Hc/J
AF
p=0.p=0.1p=0.3p=0.6
0 0.5 1 1.5 2T/TN
(1,0)
0
0.01
0.02
0.03
0.04
0.05
Heb
/JA
F
l = 3 and JInt = JAF
• maximum of the coercivity independent of dilution: χmax = x/TN (x); x concentration of magnetic sites
![Page 17: Exchange bias and coercivity of ferromagnetic/antiferromagnetic multilayers · Exchange bias and coercivity of ferromagnetic/antiferromagnetic multilayers Klaus D. Usadel Universitat](https://reader033.fdocuments.net/reader033/viewer/2022051801/5ae2ca587f8b9a595d8da1c2/html5/thumbnails/17.jpg)
Generalization to AFM vector spins
Ho = −
∑
i
BSx(i) − D∑
i
Sx(i)2 + Hex
hα(i) = −∂
∂Sα(i)Ho + Jintσα(i)
hα(i) = −∂
∂Sα(i)Ho + Jintmα(i)
mα(i) = χ(1)αβ
Bβ + Jintχ(2)αβ
Sβ(i) + m0,α(i)
• separation of time scales and/or slow
variation in space: thermal average re-
stricted to the AFM
• AFM eqilibrium susceptibilities χ(1)αβ
and χ(2)αβ as response to external field
and exchange field
• Effective (free) energy of the FM layer:
F = Ho − Jint
∑
i
Sα(i)χ(1)αβ
Bβ −1
2J2int
∑
i
Sα(i)χ(2)αβ
Sβ(i) −∑
i
Sα(i)m0,α(i)
• enhanced moment; enhanced anisotropy
![Page 18: Exchange bias and coercivity of ferromagnetic/antiferromagnetic multilayers · Exchange bias and coercivity of ferromagnetic/antiferromagnetic multilayers Klaus D. Usadel Universitat](https://reader033.fdocuments.net/reader033/viewer/2022051801/5ae2ca587f8b9a595d8da1c2/html5/thumbnails/18.jpg)
F = Ho − Jint
∑
i
Sα(i)χ(1)αβ
Bβ −1
2J2int
∑
i
Sα(i)χ(2)αβ
Sβ(i) −∑
i
Sα(i)m0,α(i)
⇒ maximum lowering of symmetry occurs when only one component of the susceptibility tensor, χx,x,
is nonzero: Ising antiferromagnet
Ho = −
∑
i
BSx(i) −∑
i
DS2x(i) + Hex −
∑
i
Sα(i)m0,α(i)
• B = B[1 + (Jint/l)χ]
• D = D + [J2int/(2l)]χ = Bc/2
• strong dependence on temperature
• relatively weak anisotropy in the ferromagnet:
maximum value of hc/Jint ∼ 0.1 for
2D/Jint = 0.02. This corresponds to
(B/B)max ≈ 1.1 and (D/D)max ≈ 5.
Dynamical consequences:
⇒ domain wall width ∆ and domain wall
energy EDW :
(∆)max ≈
√
J/D;
(EDW )max ≈
√
JD
wall velocity vDW : vDW ∼ B∆.
Stamps, Usadel,Europhys. Lett., 74, 512 (2006)
![Page 19: Exchange bias and coercivity of ferromagnetic/antiferromagnetic multilayers · Exchange bias and coercivity of ferromagnetic/antiferromagnetic multilayers Klaus D. Usadel Universitat](https://reader033.fdocuments.net/reader033/viewer/2022051801/5ae2ca587f8b9a595d8da1c2/html5/thumbnails/19.jpg)
Conclusions
• Domain state model explains exchange bias and many effects associated with it without
explicitely assuming some net AFM interface magnetization
• frozen AFM interface magnetization leads to EB
• reversible part of the AFM interface magnetization leads to enhanced coercivity providing
the AFM is anisotropic
• for slow FM dynamics and slow spatial variation of its magnetization an effective FM
energy can be obtained after integrating out the AFM degrees of freedom