聚脲防腐相关标准解读 SSPC Polyurea Coating...
6
1 美国SSPC聚脲防腐相关标准解读 SSPC Polyurea Coating Standards Richard Cui 崔晓明 2014 Ringier 中国涂料峰会 、0508 、上海 NOTES：因篇幅所限，没有详细注明所引用的文字、照片、在此真诚感谢相关的原料商、设备厂家、施工商及最终用户。 聚脲技术诞生二十八周年：聚脲3.0：新标准、新技术、新应用 1986年6月10日、 美国德州实验室 世界第一次成功喷涂聚脲： 基材/SPF泡沫、标准SPF喷涂设备 作为泡沫的防护包括防水应用 2013年12月26日美国SSPC正式发布聚脲及杂合体厚膜涂 料标准 . PAINT 45.历时4年的讨论与审核终于完成。 SSPC 油漆45 正式发布、标志着聚脲厚膜涂料进入了成熟 健康的发展阶段、同时也拉开了聚脲3.0 的大幕。 RICH崔先生 2009年10月加入SSPC.1.9 聚脲起草委员会、成为亚洲唯一成员 笔者2000年7月、创先总结：聚脲涂料体系、根据技术配方、分为五种： ①纯聚氨酯（PU/Pure Urethane）、 ②聚氨酯-聚脲（HPC/Hybrid Polyurea Coating）; ③纯聚脲/芳香族(PPC/Pure Polyurea Coating-Aromatic); (4TH): PAA/Polyaspatics +Aliphatic 脂肪族/聚天冬防腐装饰体系 (5th): 各种改性高性能重防护衬里体系(Modified PPC)… Plural Component Application for Polyureas and High Solid Coatings- Certification Program (3 Days) Level: Certification Duration: 3 Days/ 24 Hours, Includes Written Exam & Hands On Skills Assessment Exam Class Times: 8:00 - 5:00 Cost: Member $995, Non-Member $1195 Credits: 0.7 CEU’s Certification Term: 5 Years Polyurea History 聚脲涂料技术发展历程 • 1981 首先应用于汽车挡板部件 Developed for Automotive Fascia Parts • 1986 喷涂聚脲涂料配方成功研制 – Polyurea Spray Systems Developed • 1987 喷涂聚脲成套设备市场发布 – Polyurea Spray Equipment Introduced to Industry • 1988 喷涂聚脲涂料首个商业应用 – First Commercial Use 2000年美国培训认证、中国首次参与 卡士马大道1号 基本化学原理 Basic Chemistries 聚氨酯、纯聚脲、杂合体(HP)反应方程式 Physical properties and applications 物理指标及应用范围
Transcript of 聚脲防腐相关标准解读 SSPC Polyurea Coating...
1
美国SSPC聚脲防腐相关标准解读
SSPC Polyurea Coating Standards
Richard Cui 崔晓明
2014 Ringier 中国涂料峰会 、0508 、上海
NOTES：因篇幅所限，没有详细注明所引用的文字、照片、在此真诚感谢相关的原料商、设备厂家、施工商及最终用户。
聚脲技术诞生二十八周年：聚脲3.0：新标准、新技术、新应用
1986年6月10日、 美国德州实验室
世界第一次成功喷涂聚脲：
基材/SPF泡沫、标准SPF喷涂设备
作为泡沫的防护包括防水应用
2013年12月26日美国SSPC正式发布聚脲及杂合体厚膜涂料标准 . PAINT 45.历时4年的讨论与审核终于完成。
SSPC 油漆45 正式发布、标志着聚脲厚膜涂料进入了成熟、健康的发展阶段、同时也拉开了聚脲3.0 的大幕。
RICH崔先生 2009年10月加入SSPC.1.9
聚脲起草委员会、成为亚洲唯一成员
笔者2000年7月、创先总结：聚脲涂料体系、根据技术配方、分为五种：
①纯聚氨酯（PU/Pure Urethane）、 ②聚氨酯-聚脲（HPC/Hybrid Polyurea Coating）;
③纯聚脲/芳香族(PPC/Pure Polyurea Coating-Aromatic);
(4TH): PAA/Polyaspatics +Aliphatic 脂肪族/聚天冬防腐装饰体系
(5th): 各种改性高性能重防护衬里体系(Modified PPC)…
Plural Component Application for Polyureas
and High Solid Coatings-
Certification Program (3 Days)
Level: Certification
Duration: 3 Days/ 24 Hours, Includes Written Exam &
Hands On Skills Assessment Exam
Class Times: 8:00 - 5:00
Cost: Member $995, Non-Member $1195
Credits: 0.7 CEU’s
Certification Term: 5 Years
Polyurea History
聚脲涂料技术发展历程
• 1981 首先应用于汽车挡板部件
Developed for Automotive Fascia Parts
• 1986 喷涂聚脲涂料配方成功研制
– Polyurea Spray Systems Developed
• 1987 喷涂聚脲成套设备市场发布
– Polyurea Spray Equipment Introduced to
Industry
• 1988 喷涂聚脲涂料首个商业应用
– First Commercial Use 2000年美国培训认证、中国首次参与
卡士马大道1号
基本化学原理 Basic Chemistries
聚氨酯、纯聚脲、杂合体(HP)反应方程式
Physical properties and applications 物理指标及应用范围
2
双组份材料的类型
聚氨脂 – 常见的面漆 2K PU –Top Coats
Functions Applications Characteristics TypicalRatios
ViscosityRanges
Pot LifeRanges
ApplicationEquipment
DecorativeCoatings
Aircraft
Machine Tools
BusinessMachines
Railway Cars
Plastic Facia
Truck &Special Bodies
Clear coat onCars
Electric Motors& HeavyMachinery
WoodenFurniture
PlasticWindows forBuildings
Flexible
High Gloss
ImpactResistant
CorrosionResistant
Low Temp.Polymerization
1:1-15:1 50 - 200cps
30 min to 8hours
Air Spray(Conventionaland HVLP)
ProtectiveCoatings
Bridges
PetroleumTanks
Ships
Chemical &Abrasion Resistant
1:1 - 4:1 5,000 to30,000 cps
10 sec. To 8hours
Heated AirlessSpray
ASTM D16/Six Types of PU Coating :
Type V (2k /Polyol Based) and IV( 2k/Catalyst based)
影响材料性能指标的主要因素/举例
• 设备型号及系统配置
• 喷枪型号及配置
• 喷涂工艺参数：温度
• 喷涂工艺参数：压力
• 样品厚度
• 固化时间 0
100
200
300
400
500
600
1 hr
5 hrs
1 day
3 day
s
7 day
s
4 wee
ks
elo
ng
ati
on
(%
)
% elongation
Polyurea / Geotextile Elastomeric
Lining System 2005版本
1.02 Overview
A. This document specifies the installation of a polyurea geotextile lining systems items and
surfaces scheduled for primary and secondary containment over solid or earthen surfaces. It also
includes; definitions, quality assurance, project conditions, products, site preparation,
installation, and health & safety requirements.
B. This specification refers more specifically to aromatic based polyurea systems (may also include
some aliphatic polyurea systems) applied to a variety of geotextile fabrics. The polyurea
material is solvent free and capable of forming a continuous (seamless) membrane of the desired
thickness when spray applied to vertical and horizontally positioned geotextile materials.
C. The substrate and geotextile fabric must be dry prior to application. Application of the lining
system should not take place if precipitation or fog is expected imminently. Application should
not be done if the surface temperature is less than 5°F (3°C) above the dew point.
PDA -2002- 一个术语和两个应用指南
A closed-cell spray polyurethane foam together with a hybrid polyurea-polyurethane elastomeric topcoat have been used to restore the exterior of the
Superdome in New Orleans....
、 The new roof will consist of three layers:
500,000 square feet of galvanized 16-gauge fluted metal decking, mechanically attached to the existing steel support frame;
500,000 pounds of polyurethane foam, sprayed over the metal decking; and
20,000 gallons of elastomeric polyurethane coating, white in color, sprayed over the foam layer at a minimum dry film thickness of 46 mils. The coating system includes
a fire-resistant basecoat and white topcoat.
the $32 million contract , by September 2006.
ASTM D5469 - 00(2005) Standard Guide for Application of New
Spray Applied Polyurethane Foam and Coated Roofing Systems
Performance vs. Formulation
Standards Older SSPC coatings standards (1950-1990) were
primarily formulation-based
• Set requirements for coating ingredients
• “Recipe” for making a coating
• Little flexibility allowed in formulation
• No innovation or new materials • Performance-Based Standards
• • Beginning in 1990, the SRC recommended
• performance-based standards
• – establish minimum performance requirements
• for a product
• • Color retention (E*)
• • South Florida weathering (ASTM D 1014)
• – allows for flexibility in formulati
SSPC Standards
Review Committee
(SRC)
oversees SSPC
standards
development
Contents of Performance-Based
Standards
• Accelerated laboratory
testing for specific
qualities to meet
requirements of
expected service
environments
• Reference ASTM
standards
PDA 2011 年会资料
SSPC 聚脲相关标准
<
sspc油漆标准39>：
聚脲面漆/2K
世界目前唯一聚脲
面漆标准、
2004年SSPC发布
Thin film polyurea (6-9 mils)
• Two types – differentiated by dry time
– Type I – dry to touch ≤30 min
– Type II – dry to touch 30 min to 2 hours
3
PAA/Polyaspatics +Aliphatic
脂肪族/聚天冬防腐装饰体系+ Condor低压变比喷涂机
• 美国Elastomer Specialities公司，在研制低压喷涂聚脲弹性体技术方面，走在了前沿，推出了牌号为"Condor"的低压喷涂设备，它省去了主机加热器和管道加热器，缩小了设备体积。它采用静态混合杆替代对撞式混合室，减少了设备日常维护程序，消除了在多孔物体表面（例如：混凝土、泡沫）容易出现针孔的弊病，并大大简化了喷涂聚脲弹性体施工设备的配置，降低了日常维护费用。
SSPC-PS 28.01
两道涂层系统：2K MCU+聚脲面漆 Two-Coat Zinc-Rich PolyurethanePrimer/Aliphatic Polyurea
Topcoat System, Performance-Based
• SSPC-PS 28.01
• • Two-Coat Zinc-Rich Polyurethane
• Primer/Aliphatic Polyurea Topcoat System,
• Performance-Based
• – Primer must meet SSPC Paint 40 (zinc-rich
• moisture cure polyurethane primer)
• – Topcoat must meet SSPC Paint 39, Type II
• 钢结构涂装
I-84 Connecticut Bridge
2009 年发布, PAINT 40+ PAINT 39=PS 28.01
PS 28.02 Three-Coat Moisture-Cured Polyurethane Coating System,
Performance-Based
Jun-10
Paint
40
Zinc-Rich Moisture-Cure
Polyurethane Primer,
Performance-Based (new
April 2007)
Apr-07
Paint
41
Moisture-Cured Polyurethane
Primer or Intermediate Coat,
Micaceous Iron Oxide
Reinforced, Performance-
Based
Feb-08
SSPC-PS 28.02 三道涂层系统：
2K MCU 底漆、MCU PU中间漆及 1K MCU PU面漆
PAINT40+ PAINT41+PAINT 38= PS 28.02
100% solids/Zero VOC
1:1 mix ratio
Aliphatic / UV stable coating
70 D/ 12% /GLOSS 80+
Paint 36 Two-Component Weatherable Aliphatic Polyurethane
Topcoat, Performance-Based
Apr-06
Paint 38：Sngle-Package, Moisture Cure Aliphatic Polyurethane Topcoat, performance based Mar-2012
SSPC 油漆 36：双组分PU，脂肪族，面漆标准
SSPC 油漆 38：单组分PU，MCU，脂肪族，面漆标准
ＡＳＴＭ Ｄ１６， ＴＹＰＥ Ｖ
4
2K 底面合一DTM脂肪族聚脲涂料标准
混合使用期：
30分钟—2小时
DFT：150—225 微米
2K 底面合一DTM脂肪族聚脲涂料标准
根据配方不同
单组份或双组分喷涂设备
VOC 含量与稀释
2K 底面合一DTM脂肪族聚脲涂料标准
适用SSPC 6种防腐环境区域
2K 底面合一DTM脂肪族聚脲涂料标准
反应组分：聚醚氨与ISO树脂
2K 底面合一DTM脂肪族聚脲涂料标准
耐候测试
优先采用户外暴晒实验
5
DTM 附着力：600 PSI ASTM D 4541
2K 底面合一DTM脂肪族聚脲涂料标准
涂装间隔、修补附着力要求
2K 底面合一DTM脂肪族聚脲涂料标准
DTM 聚脲涂层物理指标 DTM 聚脲涂层耐候及防腐性能指标
SSPC新的聚脲标准- 2009-2013
油漆标准和施工规范-亚洲唯一的参与者
美国防护涂料协会(SSPC)发布新的聚脲应用标准
新的SSPC-PA 14补充了多组分涂料的应用说明 9月27日，在宾夕法尼亚州的匹兹堡——SSPC宣布了四个新的涂料应用标准（PA）之一，
其涉及到厚涂膜聚脲涂料的应用.
该标准由SSPC的C.1.9聚脲委员会起草，标题是“SSPC-PA 14：
多组分应用-多组分聚脲和聚氨酯厚涂膜涂料在混凝土和钢结构底材的应用”。
该标准适用于设施业主、承包商和涂料制造商，它在某种程度上类似
SSPC-PA1（“金属防护涂料的采购，施工和维护”）.PA14提供了这一补充应用说明，
是为了确保在使用多组分涂料时，被建议的最佳方式能被应用。
SSPC新的聚脲标准- 2009-2013
油漆标准和施工规范-亚洲唯一的参与者
2013年12月26日美国SSPC正式发布聚脲及杂合体厚膜涂料标准 . PAINT 45.
历时4年的讨论与审核终于完成。
SSPC 油漆45 正式发布、标志着聚脲厚膜涂料进入了成熟、健康的发展阶段、同时也拉开了聚脲3.0 的大幕。
RICH崔先生 2009年10月加入SSPC.1.9 聚脲起草委员会、成为亚洲唯一成员。
6
根据技术配方和性能、分为4种。
聚脲涂层线性固化收缩率小于1%
聚脲涂层 浸泡应用技术指标
聚脲3.0：新标准、新技术、新应用
Polyurea 3.0: standards, technology and application
1986年6月10日、 美国德州实验室世界第一次成功喷涂聚脲：基材/SPF泡沫、采用SPF喷涂设备、作为泡沫的防护防水应用。 如果十年作为一个应用年代划分、那么目前聚脲正在从2.5代向3.0 代的发展中。 本网站主要探讨和介绍国内外已经发布和正在制定有关的标准、已经出现的新技术和新应用，与广大聚脲防腐防水相关技术人员参考。
世界最早、最长：美国硅谷跨海高速公路、混凝土桥梁聚脲防护涂装技术 (1999—2002）