DISPERLIT
ULTIMATE COLOR MADE EASY
DISPERLIT. PERFORMANCE WITHOUT COMPROMISE.
With Disperlit you are sure to get the best possible results, in any application. With many real advantages:
High color yield, brilliance and permanence. Superior pigment stability. Excellent transparency, similar to that of dyes. Extremely light-fast. Very easy to use. Exceptional dispersion, thanks to the fine grain
of the particles (solid, irregularly shaped granules with maximum size of approx. 0.7 – 0.8 mm).
DISPERLIT. THE PERFECT CHOICE FOR YOU.
Exceptional performance comes with many other benefits.From purchase to use, safeguarding the environment, expert assistance throughout the entireproduction process.
All Disperlit preparations are ready to use. Excellent price/quality ratio. Reduced delivery times. Pre- and post-sales assistance is always available, thorough and professional. The option of creating custom products to suit your specific needs. With granular particles, the problems of safety and environmental safeguarding
typically associated with managing powder formats have been eliminated.
DISPERLIT
ULTIMATE COLOR MADE EASY
DISPERLIT AW
High performance pigment preparations in an alkaline water/alcohol soluble acrylic resin. Particularly suitable for high quality printing inks, lacquering of aluminium foils, wood stain applications and other aqueous systems.
DISPERLIT EC
High performance pigment preparations in Ethylcellulose polymers. Particularly suitable for high quality printing inks and wood coatings.
DISPERLIT VK
High performance pigment preparations in Vinyl-Chloride Vinyl-Acetate Copolymer. Particularly suitable for high quality printing inks and solvent-based industrial ink jet.
ABOUT MIFAR.
MIFAR is a company dedicated exclusively to the research and manufacture ofhigh-performance, predispersed pigments. With 30 years’ experienceand its vision firmly focused on the future, MIFAR offers its customers the most innovative products, and is a real ‘solution provider’ ready to meet your every need. How? With ongoing, advanced research, a vast range of products, always in-stock(ensuring reduced delivery times), and with amazing technical assistancerenowned for its expertise and willingness to help.
77891TITANIUM DIOXIDE
P.WHITE 6 7-8 80 20
20710AZO
CONDENSATIONP. YELLOW 93 7 65 35
21108 DISAZO P. YELLOW 83 5 65 35
56280 ISOINDOLINONE P. YELLOW 110 7-8 65 35
20730AZO
CONDENSATION P. RED 166 7 60 40
20730AZO
CONDENSATION P. RED 166 7 60 40
HIGH TRANSPARENCY
12487 NAPHTHOL AS P. RED 184 5/6 60 40
51319 DIOXAZINE P. VIOLET 23 6-7 60 40
74160 PHTHALO BLUE P. BLUE 15:3 8 70 30
77266 CARBON BLACK P. BLACK 7 8 60 40
COLOUR INDEX
PIGMENT CLASS
GENERIC NAME
LIGHT FASTNESS1
COMPOSITION
PIGMENT % RESIN %
REMARKS
AW WHITE 6
AW YELLOW 93
AW YELLOW 83
AW YELLOW 110
AW SCARLET 166
AW SCARLET 166 HT
AW RED 184
AW VIOLET 23
AW BLUE 15:3
AW BLACK 7
1 Blue Wool Scale, 1-8 (8 best)Other colour index available. Ask for details.Colours are representation only and are in no way intended to convey the shade of the actual colour and shade.
DISPERLIT
ULTIMATE COLOR MADE EASY
DISPERLIT – AWPRODUCT RANGE. Concentrate pastes are obtained by using the following mix of solvents: ethanol, isopropanol, n-propanol, methoxypropanol or ethoxypropanol.
DISPERLIT
ULTIMATE COLOR MADE EASY
DISPERLIT – ECPRODUCT RANGE. It dissolves in a wide range of solvents such as aliphatic, alcohols, chlorinated solvents, esthers as ethyl acetate, buthyl acetate. It is practically insoluble in glycerin and propylene glycol.
77891TITANIUM DIOXIDE
P.WHITE 6 70 30
20710AZO
CONDENSATIONP. YELLOW 93 50 50
21100DIARYLIDE
m-XILIDIDEP. YELLOW 13 50 50
21108DIARYLIDE
DIMETHOXY CHLORANILIDE
P. YELLOW 83 50 50
20060AZO
CONDENSATION P. BROWN 23 50 50
15865:2 AZO 2B-TONER (Ca) P. RED 48:2 50 50
51345 DIOXAZINE P. VIOLET 37 50 50
74160 Cu-PHTHALOCYANINE P. BLUE 15:3 50 50
74260 Cu-PHTHALOCYANINE P. GREEN 7 50 50
77266 CARBON BLACK P. BLACK 7 50 50
COLOUR INDEX
PIGMENT CLASS GENERIC NAME
COMPOSITION
PIGMENT % RESIN %
REMARKS
EC WHITE 6
EC YELLOW 93
EC YELLOW 13
EC YELLOW 83
EC BROWN 23
EC RED 48:2
EC VIOLET 37
EC BLUE 15:3
EC GREEN 7
EC BLACK 7
Other colour index available. Ask for details.Colours are representation only and are in no way intended to convey the shade of the actual colour and shade.
77891TITANIUM DIOXIDE
P.WHITE 6 7-8 80 20
20710AZO
CONDENSATIONP. YELLOW 93 7 48 52
21108 DISAZO P. YELLOW 83 5 50 50
20735AZO
CONDENSATIONP. RED 144 7 40 60
20730AZO
CONDENSATION P. RED 166 7 50 50
56110DIKETO-PIRROLO-
PYRROLEP. RED 254 6-7 48 52
51345 DIOXAZINE P. VIOLET 37 6-7 48 52
74160 PHTHALO BLUE P. BLUE 15:3 8 50 50
74260 PHTHALO GREEN P. GREEN 7 8 45 55
77266 CARBON BLACK P. BLACK 7 8 50 50
COLOUR INDEX
PIGMENT CLASS
GENERIC NAME
LIGHT FASTNESS1
COMPOSITION
PIGMENT % RESIN %
REMARKS
VK WHITE 6
VK YELLOW 93
VK YELLOW 83
VK RED 144
VK SCARLET 166
VK RED 254
VK VIOLET 37
VK BLUE 15:3
VK GREEN 7
VK BLACK 7
1 Blue Wool Scale, 1-8 (8 best)Other colour index available. Ask for details.Colours are representation only and are in no way intended to convey the shade of the actual colour and shade.
DISPERLIT
ULTIMATE COLOR MADE EASY
DISPERLIT – VKPRODUCT RANGE. Concentrate pastes are obtained by using the following mix of solvents: ethyl acetate, MEK, MIBK, PMA.
DISPERLIT
ULTIMATE COLOR MADE EASY
SOLUBILITY AND PROCESS METHODDisperlit dispersions are ready to use and do not require milling: they can simply be added, under stirring, to the liquid base to be colored. Easily and quickly dissolved.
SOLUBILITY AND PROCESS METHOD
Disperlit dissolution is carried out using a simple stirrer of 10 to 20 HP (according to the batch size). For example, for a batch of around 200 Kg., 9 to 11 HP, for a batch of around 500/1000 Kg, 20 HP, use a saw “cowless” type agitator (high speed mixer), with a diameter which is 2/3 of the vessel diameter, running at 900 to 1400 rpm.
THE SYSTEMS TO BE USED CAN BE SELECTED FROM THE FOLLOWING:
1) The vessel contains the minimum amount of solvent to dissolve the chips and is stirred. The chips are added slowly at intervals to allow them to dissolve. After 45 minutes to 1 hour, when the chips are dissolved completely, add the remaining formula components and stir for a further 10 to 20 minutes.
2) Or, following chip solution at a high concentration, this intermediate solution is kept for making up final mixtures for specific requirements.
3) The minimum vehicle necessary to dissolve the chips is placed in the vessel (if more than one vehicle is being used, use the least viscous one). The agitator is switched on and the chips are trickle fed to the vessel. After an interval of 1 to 2 hours, complete batch preparation by adding the remaining components.
In all cases – remember that the chips must be dissolved/dispersed in the minimum amount of solvent/vehicle in order to have a mix of sufficient strength to ensure the best result. It is important to remember that before completing the product formulation, the chips must be completely dissolved.
The information herewith given is based on our present knowledge. Any conclusion and recommendation are made without liability on our part. Buyers and users are advised to make their own assessment under their own condition and for their own requirements. Standard terms and conditions (ST&C): all sales are subjected to Mifar’s ST&C in force at the date of this issue.
www.mifar.com