Panex 35 Pultruded Proles

Pultrusion is a cost-eective, continuous processfor producing ber-reinforced composite parts.Panex 35 carbon ber tows are fed into ourproprietary impregnation and curing processthat creates smooth carbon ber laminates thatprovide ecient laydown when building thick-ness. The specic ber alignment achieved withpultrusion delivers consistently better overallproperties in laminates than any other compositemanufacturing process.

Description

High-Strength

High-Stiness

Low Density

Corrosion Resistant

High Fiber Volume

Nearly Zero Void Content

Locked-in Filament Alignment

Performance Properties

Wind Energy (pre-cured carbon composite asthe structural member of the turbine blade)

Infrastructure Building & Repair

Oshore Drilling

Mining

Other Structural Reinforcement Applications

Product Applications

*Typical data based on a 1.55 mm thick at plate.

Plates: Composite Properties

Resin Type

Tensile Strength

Tensile Modulus

Density

Strain (elongation at break)

Epoxy

2350 MPa

155 GPa

1.6 g/cm

1.4%

Vinyl Ester

2100 MPa

150 GPa

1.6 g/cm

1.4%

Epoxy

340 ksi

22.5 Msi

0.058 lb/in

1.4%

Vinyl Ester

305 ksi

21.8 Msi

0.058 lb/in

1.4%

SI US

Zoltek Corporation | 3101 McKelvey Rd. | St. Louis, MO 63044

P: +1-314-291-5110 | F: +1-314-291-8536 | E: sales@zoltek.com | W: www.zoltek.com

7/27/2019 Datasheet Panex 35 Pultruded Profiles

2/2

PANEX is a registered trademark

of Zoltek Corporation

Panex 35 Pultruded Proles

Panex 35 Pultruded Proles are manufactured inaccordance with Zolteks written and publisheddata. A Certicate of Conformance is provided witheach shipment.

Certication

Obtain, read, and understand the Material SafetyData Sheet (MSDS) before use of this or any otheZoltek product.

Safety

Rods: Composite Properties

Resin Type

Tensile Strength

Tensile Modulus

Density

Strain (elongation at break)

Epoxy

2200 MPa

150 GPa

1.6 g/cm

1.4%

Vinyl Ester

2000 MPa

145 GPa

1.6 g/cm

1.4%

Epoxy

319 ksi

21.8 Msi

0.058 lb/in

1.4%

Vinyl Ester

290 ksi

21.0 Msi

0.058 lb/in

1.4%

SI US

*Typical data based on a 6.4 mm diameter rod.

Zoltek Corporation | 3101 McKelvey Rd. | St. Louis, MO 63044

P: +1-314-291-5110 | F: +1-314-291-8536 | E: sales@zoltek.com | W: www.zoltek.com 0213

Zolteks pultruded proles are produced with ourcommercial grade Panex 35 Continuous Tow

carbon ber. Our pultruded proles are typicallyproduced with a thermoset epoxy or vinyl esterresin in a proprietary low-cost, high-throughputprocess.

Available in plates, rods, tubes, or custom proleshapes.

About Panex 35 Pultrusion