8/3/2019 Cswip3 1 Exam Question

1/4

Cswip3.1 Exam Question: MD SAZID ALAM

1. One of the following discontinuities, which is least likely to be the result of some improper welding technique?a. porosity

b. Laminationc. Lamellar teard. Crack

2. Which code gives pre qualified status to certain weld joint configuration

a. API 1104

b. AWS D1.1,

c. ASME Section IX

d. ANSI B31.1

e. None of the above

3. The tensile test can be used to provide values for which of the following?

a. Yield point b. Ultimate tensile strength

c. Modulus of elasticity

d. Elastic limite. All of the above

4. Under bead cracking is primarily caused by :

a. a source of hydrogen.

b. Restraint.

c. Excessive preheat.

d. All of the above.

e. None of the above

5. Which of the following discontinuities is associated with shrinkage stresses in the through -Thickness direction of thick plate?

a. crater cracks

b. lamellar tearsc. toe cracks s.

d. root cracks

e. none of the above

6. for the 2G position in pipe welding:

a. the axis of the pipe is vertical and the plane of the weld is horizontal.

b. The axis of the pipe is horizontal and plane of the weld is vertical.c. The pipe is not fixed.

d. The axis of the pipe and the plane of the weld are at 45 degree angle with the vertical plane.e. None of the above.

7. Which of the following weld is not considered applicable for an edge joint?

a. V-groove b. Plug

c. Edge-flange

d. U-groove

e. J-groove

8/3/2019 Cswip3 1 Exam Question

2/4

8. Which of the following is not a type of weld joint?

a. lap

b. T

c. Filletd. Butt

e. Edge

9. Double-groove joints always require

a. back gouging

b. special welding processes.

c. High deposition rate processes

d. Weld to be deposited from both sides of the joint

e. None of the above

10. Center line cracks can be caused by :

a. the use of preheat. b. A highly restrained weld joint

c. using the wrong polarityd. stress relief heat treatment.

e. The presence of incomplete side wall fusion.

11. To be most effective, visual inspection must be conducted:

a. before welding.

b. during welding

c. after welding.

d. All of the above

e. None of the above

12 A discontinuity is:a. always reject able

b. sometimes reject ablec. always a defectd. sometimes a defecte. b and d above

13. Which discontinuity occurs in the heat affected zone and can result from excess moisture in the

Weld zone?

a. longitudinal crackb. crater crackc. under bead crackd. Porosity e. transverse crack

14. A mega Pascal is equal to:

a. 1,000 Pa

b. 1,000, 000 Pa

c. 1,000 Kps.

d. a and b abovee. B and c above

15. Which of the conditions below can cause porosity in a weld?

a. Welder technique b. damp electrodesc. oily base metal

d. b and c above

e. all of the above

8/3/2019 Cswip3 1 Exam Question

3/4

16. The CAWI:

a. is responsible for determination of a wedments conformance to acceptable standards b .inspects weldments only under the direction of a CWI

c. cannot inspect critical weldmentsd. performs inspections the same as a CWIe. all of the above

17. A burn through many occurs if-------

a. the current is too low

b. the root face is too largec. the root gap is too larged. the arc voltage is too high

18. A solid inclusion in weld may be-----

a. entrapped gasb. entrapped slagc. lack of inter run fusiond. none of the above

19. A code of practice is-------------

a. A standard for workmanship quality only.

b. A set of rules for manufacturing a specific product.

c. A specification for the finished product.d. A code for the qualification of welding procedures and welders qualifications.

20. The principle purpose of a welder qualification test is.

a. to test the skill of the welder

b. to assess the weldability of the materialsc. to decide which NDT METHODS to use.

d. to give the welder practice before doing production welding.

21. The strength of a weld is determined by

a. Leg lengthb. Weld profilec. Weld widthd. Throat thickness

22. The main cause of undercut is: -----

a.

excessive ampsb. excessive OCVc. excessive travel speedd. too low current

8/3/2019 Cswip3 1 Exam Question

4/4

23. If a welding Inspector detects a type of imperfection not allowed by the application Standard he must always:---

a. request further NDEb. reject the weldc. prepare a concession requestd. only reject the weld if he considers it to be harmful.

24. A crack running along the centreline of a weld bead could be caused by.........

a. use of damp flux

b. lack of preheat

c. arc voltage being too high

d. weld bead being too deep and very narrow

25. Which of the following cutting methods is suitable for cutting stainless steel?

a. plasma b. oxy-acetylene

c. oxy-propane

d. it depends upon the thickness

---------------------------------------------------------------------------------------------------------------------------------------