Crystalline polymers & Vibrational spectroscopy of polymers
description
Transcript of Crystalline polymers & Vibrational spectroscopy of polymers
Crystalline polymers
&
Vibrational spectroscopy of polymers
Glassy: molecules in a random coil conformation. For example fully amorphous PMMA and PPO
Crystalline: Polymer molecules show some degree of ordering. Depending on molecular symmetry (tacticity), molecular weight (kinetics) and branching, etc.
Lamellar growth direction ~10 µm
Lamella thickness
~100 – 200 Å
Microscopy image of a crystal of high density poly(ethylene) - viewed while “looking down” at the lamella.
10 m x 10 m
Lamella grows outwards
Several crystals of isotactic poly propylene G. Ellis*, M. A. Gómez and C. Marco
Polymers with some symmetry are usually polycrystalline. They are usually never completely crystalline but have some amorphous regions and “packing defects”.
competition between polymer chain stretching and coiling on one hand and on reduction in free energy for crystal formation on the other hand determines lamellar thickness.
Why is the lamellar crystal a basic unit?
Tk
gST
k
S
B
B
expratemelt crystal
exprate crystalmelt
1-
1-
is a microscopic frequency, g is negative by definition
Calculating the maximum net rate for a crystal of thickness l gives an estimate of the optimal thickness (fastest growing).
Lamellar thickness of PE grown from a melt
melt crystallization annealing
)(
20
0
cmv
mc TTH
TL
Lamellar Thickness:
Surface energy0mT
vH
Equilibrium melting Temperature
Enthalpy of fusion per unit volume
cT Crystallization temperature
Micellar Structures
When diblock copolymes are asymmetric, lamellar structures are not favoured.
Instead the shorter block segregates into small spherical phases known as “micelles”.
Density within phases is maintained close to bulk value.
Interfacial “energy cost”: (4r2)
Reduced stretching energy for shorter block
Exotic Morphologies
Molecular vibrations – vibrational spectroscopy
Restoring force (the bond): F=k(X2+X1)
m2
X2
m1
m1 m2
X1
equilibrium
F ma kx a d2x
d t2
md2x
d t2 kx d2x
d t2 k
mx
x(t) A cos 2 t k
m
k
Quantum Vibrational Motion
• molecular motion is quantized; vibrational quantum levels (quantum number “v”)
• energy absorbed is energy difference between two levels; for SHO, spacing is same between ALL adjacent levels.
Ev v 12
v 1
2
h
h2
2 12
k
Ev v1 h h
1
2k
Anharmonic Oscillator
• real molecules, vibrations “close to being” harmonic.
• relaxes the selection rules (overtones and combination bands)
• distorts the intensities of the transitions
• changes energy levels so that they come closer together as you go up the vibrational ladder.
• bond can “break”; not so with SHO.
Types of Vibrations
• molecular dipole moment must change during a vibration to be IR active.
• this oscillating dipole interacts with the oscillating E-M field of the photon, leading to absorption.
+ – + +
–
Stretching Vibrations Bending Vibrations
symmetric anti-symmetric rocking scissoring twisting waggingIn-Plane Out-of-Plane
Changes in bond length Changes in bond angle
Vibrational spectroscopy
anti-Stokes
Rayleigh Stokes
E
Virtual states
Excited stateGround state
-3500
400
22900
0
514
19400
3500
630
15900
Raman shift (cm-1)
wavelength (nm)
wavenumber (cm-1)
Raman scattering
Infrared absorption
3500
2850
Infrared is Rovibrational Spectroscopy
• Wavelengths between 0.8 µm to 1 mm.
• Associated with changes in nuclear motion (vibrations and rotations).
• In gas phase, rotational transitions are resolved; in liquid phase, they are broadened. Usually only focus on vibrational character.
• Energy is usually reported in wavenumbers (cm-1); also proportional to frequency
Near IR 0.8 - 2.5 µm 12800 - 4000 cm-
1
Mid-IR 2.5 - 50 µm 4000 - 200 cm-1
Far IR 50 - 1000 µm 200 - 10 cm-1
mostcommonly studied
1
c
The Raman Spectrum
A complete Raman spectrum consists of:
• a Rayleigh scattered peak (high intensity, same wavelength as excitation)
• a series of Stokes-shifted peaks (low intensity, longer wavelength)
• a series of anti-Stokes shifted peaks (still lower intensity, shorter wavelength)
• spectrum independent of excitation wavelength (488, 632.8, or 1064 nm)
Spectrum of CCl4, using an Ar+ laser at 488 nm.
Origin of Raman Effect - Classical
The oscillating electric field of the excitation light.
The induced dipole moment from this oscillating field.
The molecular polarizability changes with bond length.
The bond length oscillates at vibrational frequency.
Hence the polarizability oscillates at same frequency.
Substitute.
Remember trig identity.
Induced dipole has Rayleigh,Stokes, and anti-StokesComponents.
E E0 cos ext induced E E0 cos ex t
0 r req ddr
r req rmax cos vibt
0 ddr
rmax cos vibt
induced 0 ddr
rmax cos vibt
E0 cos ex t 0E0 cos ex t
E0rmaxddr
cos ex t cos vibt
cos x cosy 12
cos x y cos x y induced 0E0 cos ex t
E0rmax
2
ddr
cos ex vib t cos ex vib t
Infrared Spectroscopy Raman Spectroscopy
Interaction Absorption Scattering
Excitation Polychromatic Monochromatic
Frequency measurement Absolute Relative
Activity Dipole moment change Polarizability change
Band intensity
/Q0 /Q0
(/Q /Q)
Raman vs. IR
Compare IR and Raman
Spectra of PETN explosive. From D.N. Batchelder, Univ. of Leeds
Group frequencies
For large molecules - vibrations of some functional groups acts like independent oscillators i.e. always found at ~ same frequencies
Group cm-1
- C-H 2900-3000
- C=O 1700
- C-F 1100
- O-H 3600
- C-C - 900
Factors affecting group frequencies
• Center of Symmetry (i):determine IR active or Raman active.
• For IR active vibration an oscillating electric dipole must be generated.
• For Raman active vibration a change in polarizability of the molecule is produced, which gives rise to induced dipole.
Symmetry factor
• A molecule having a center of symmetry (i) has no permanent dipole moment, so a vibration symmetric to i (sym. mode) does not generate oscillating dipole and therefore it is an IR inactive vibration.
• But vibration anti-symmetric to i (anti-sym. mode) generates transient oscillating dipole, so it will be IR active vibration and show up in the spectrum.
Mutual exclusion rule • Symmetric mode vibration usually gives rise
to Raman scattering which causes changes in polarizability of molecule, and it is a Raman active vibration, showing up in the Raman spectrum.
• Mutual exclusion rule : For IR and Raman spectra, some lines missing in one would show up in the other, due to different symmetry requirement for each spectra. Thus, the information from IR data is complementary to that obtained from Raman.
General rule of symmetry
• Symmetry in molecule reduces the normal modes of vibrations and simplifies spectrum.
• CO2 : sym. stret. = 1340 cm-1 , IR
inactive, but Raman active.
assym. stret. = 2349 cm-1 , IR active.
IR vs. Raman : mutual exclusive.
Symmetry : IR shows only assym. stret.
Symmetry simplify spectra
Mechanical coupling
• Interaction between two vibrational modes through common atom or common bond: Such two identical groups are linked (or fused) by a common atom or a common bond.
• Induce mixing and redistribution of energy states, yielding new energy levels, one being higher and one lower in frequency.
Degrees of freedom
Always 3 N degrees of freedom (N = number of atoms in molecule) with 3N-6 (-5) vibrational degrees of freedom.
For polymers in practice we have 3n-6 modes (n=number of atoms in repeat unit) instead of 3N-6 ☺
Good
news
Quick IR Analysis Algorithm
Infrared spectra: It is important to remember that the absence of an absorption band can often provide more information about the structure of a compound than the presence of a band. Be careful to avoid focusing on selected absorption bands and overlooking others. Use the examples linked to the table to see the profile and intensity of bands. Remember that the absence of a band may provide more information than the presence of an absorption band.Look for absorption bands in decreasing order of importance:1. the C-H absorption(s) between 3100 and 2850 cm-1. An absorption above 3000 cm-1 indicates C=C, either alkene or aromatic. Confirm the aromatic ring by finding peaks at 1600 and 1500 cm -1 and C-H out-of-plane bending to give substitution patterns below 900 cm-1. Confirm alkenes with an absorption at 1640-1680 cm-1. C-H absorption between 3000 and 2850 cm-1 is due to aliphatic hydrogens. 2. the carbonyl (C=O) absorption between 1690-1760cm-1; this strong band indicates either an aldehyde, ketone, carboxylic acid, ester, amide, anhydride or acyl halide. The an aldehyde may be confirmed with C-H absorption from 2840 to 2720 cm-1.3. the O-H or N-H absorption between 3200 and 3600 cm-1. This indicates either an alcohol, N-H containing amine or amide, or carboxylic acid. For -NH2 a doublet will be observed.4. the C-O absorption between 1080 and 1300 cm-1. These peaks are normally rounded like the O-H and N-H peak in 3. and are prominent. Carboxylic acids, esters, ethers, alcohols and anhydrides all containing this peak.5. the CC and CN triple bond absorptions at 2100-2260 cm-1 are small but exposed.6. a methyl group may be identified with C-H absorption at 1380 cm -1. This band is split into a doublet for isopropyl(gem-dimethyl) groups. 7. structure of aromatic compounds may also be confirmed from the pattern of the weak overtone and combination tone
bands found from 2000 to 1600 cm-1.
This is a little recipe from Stanislau State University (California).
Some Raman Advantages
Here are some reasons why someone would prefer to use Raman Spectroscopy.
• Non-destructive to samples (minimal sample prep)
• Higher temperature studies possible (don’t care about IR radiation)
• Easily examine low wavenumber region: 100 cm-1 readily achieved.
• Better microscopy; using visible light so can focus more tightly.
• Easy sample prep: water is an excellent solvent for Raman. Can probe sample through transparent containers (glass or plastic bag).
A Raman disadvantage - Fluorescence
Spectrum of anthracene. A: using Ar+ laser at 514.5 nm. B: using Nd:YAG laser at 1064 nm.
Want to use short wavelength because scattering depends on 4th power of frequency.
…BUT…
Want to use long wavelength to minimize chance of inducing fluorescence.
What is it good for?
• Composition
• Co-ordination
• Conformation
Endgroups - example
CH2 and CH3 stretching and bending modes in saturated hydrocarbons. With increasing chain length the absorption from CH2 groups increases. Introduction to Mol. Spect. Academic press 1970
.
Molecules in motion. A presentation created by Dr Alexander Brodin