MIE 201Issued: April 2005Supercedes: November 2004
Glass Type – Alkaline Earth Boro-AluminosilicateForms Available – Fusion drawn sheetPrincipal Uses – Substrates for Active Matrix flatpanel displays
Properties
Where applicable, units are stated in Metric and English
MechanicalMetric English
Density (20oC, 68
oF) 2.37 g/cm
3 147.9 lb/ft
3
Young’s Modulus 70.9 GPa 10.3 MpsiPoisson’s Ratio 0.23 0.23Shear Modulus 28.9 GPa 4.2 Mpsi
Vickers Hardness 642(200 gm load, 25 sec dwell)
Thermal Expansion0 - 300
oC 31.8 x 10
-7/oC 17.7 x 10
-7/oF
(0 - 300oC) (32 - 572
oF)
Room Temperature 36.1 x 10-7
/oC 20.1 x 10
-7/oF
To Setting Point (25 - 670oC) (77 - 1238
oF)
Thermal Conductivity
Thermal Conductivity is a calculated value, and is equalto the product of the Thermal diffusivity multiplied bySpecific Heat multiplied by Density of the glass.
Specific Thermal Thermal ConductivityTemp (
oC) Heat Diffusivity (cal-cm/cm2-sec-
oK)
(cal/gm- oK) (cm2/sec)
23 0.176 0.00511 0.00213 50 0.185 0.00512 0.00225
100 0.201 0.00510 0.00244200 0.226 0.00507 0.00272300 0.244 0.00503 0.00291400 0.260 0.00499 0.00307600 0.288 0.00507 0.00344
ViscosityWorking Point (104 poises) 1321
oC 2410
oF
Softening Point (107.6 poises) 985oC 1805
oF
Annealing Point (1013 poises) 722oC 1332
oF
Strain Point (1014.5 poises) 666oC 1231
oF
DisplayTechnologies
Corning EAGLE2000™
AMLCD Glass SubstratesMaterial Information
MIE 201| 2
ElectricalLog10Volume Resistivity (ohm-cm)12.5 (250
oC, 482
oF)
10.5 (350oC, 662
oF)
8.5 (500oC, 932
oF)
Dielectric Constant: 5.181(20
oC/68
oF – 1 kHz)
Chemical
Weathering: 1Weathering is defined as corrosion by atmospheric-bornegases and vapor such as water and carbon dioxide. Glassesrated 1 will almost never show weathering effects, thoserated 2 will occasionally be troublesome, particularly ifweathering products cannot be removed, those rated 3require more careful consideration.
Durability:Durability is measured via weight loss per surfacearea after immersion. Values are highly dependent uponactual testing conditions. Data is reported for EAGLE2000
and Corning 1737 glasses run concurrently. Unlessotherwise noted, concentrations refer to weight percent.
Reagent Time Temp Weight Loss (mg/cm2) EAGLE
2000 Corning 1737
HCl – 5% 24 hrs 95oC 0.30 0.46
HNO3 – 1M 24 hrs 95oC 0.17 0.24
HF – 10% 20 min 22oC 3.71 6.34
NH4F:HF – 10% 20 min 22oC 0.75 1.17
1HF:10HNO3 3 min 25oC 1.35 2.01
1HF:100HNO3 3 min 25oC 0.40 0.46
DI H2O 24 hrs 95oC 0.00 0.01
Na2CO3 – 0.02N 6 hrs 95oC 0.14 0.17NaOH – 5% 6 hrs 95
oC 1.61 1.76
Total alkali content is approximately: 0.1 wt%(Typical < 0.05 wt%)
Optical RefractiveWavelength Index435.8 nm 1.5170480 nm 1.5131486.1 nm 1.5126546.1 nm 1.5090589.3 nm 1.5068643.8 nm 1.5050656.3 nm 1.5046
Birefringence Constant327 (nm/cm)/(kg/mm2)
Dielectric Constant
55.5
66.5
77.5
8
8.5
109.5
9
0 100 200 300 400 500 600
Temperature oC
200 Hz
1 kHz
10 kHz100 kHz
Die
lect
ric C
onst
ant
0.0001
0.001
0.01
0.1
1
10
0 100 200 300 400 500 600
Temperature oC
200 Hz
1 kHz
10 kHz
100 kHz
Dissipation Factor (Loss Tangent)
Dis
sipa
tion
Fact
or (L
oss
Tang
ent)
Loss Tangent: 0.40%(20
oC/68
oF – 1 kHz)
MIE 201| 3
Transmittance
UV Transmission
0
10
20
30
40
50
60
70
80
90
100
300 320 340 360 380 400
Wavelength (nm)
Tran
smis
sion
%
0.7 mm
0.5 mm
North America and all other CountriesCorning Display TechnologiesMP-HQ-W1Corning, NY 14831United StatesTelephone: +1 607-974-9000Fax: +1 607-974-7097Internet: www.corning.com/displaytechnologies
JapanCorning Japan K.K.Main OfficeNo. 35 Kowa Building, 1st Floor1-14-14, AkasakaMinato-Ku, Tokyo 107-0052 JapanTelephone: +81 3-5562-2260Fax: +81 3-5562-2263Internet: www.corning.co.jp
Nagoya Sales OfficeNagoya Bldg., 7 F4-6-18, Mei-eki, Nakamura-kuNagoya-shi, Aichi 450-0002 JapanTelephone: +81 52-561-0341Fax: +81 52-561-0348
ChinaCorning (China) Ltd., Shanghai Representative Office31/F, The Center989 Chang Le RoadShanghai 200031P.R. ChinaTelephone: +86 21-5467-4666Fax: +86 21-5407-5899
TaiwanCorning Display Technologies Taiwan Co., Ltd.Room #1203, 12F, No. 205Tun Hua North Road,Taipei 105, TaiwanTelephone: +886 2-2716-0338Fax: +886 2-2716-0339Internet: www.corning.com.tw
KoreaSamsung Corning Precision Glass Co., Ltd.20th Floor, Glass Tower Building946-1 Daechi-DongKangnam-Ku, Seoul 135-708KoreaTelephone: +82 2-3457-9846Fax: +82 2-3457-9888Internet: www.samsungscp.co.kr
Optical Transmission 0.7 mm
0.7mm
1009080706050403020100
Tran
smis
sion
%
200 250 300 350 400 450 500 550 600
Wavelength (nm)
EAGLE 2000 is a trademark of Corning Incorporated, Corning, N.Y.
©2005, Corning Incorporated
0.0000
0.1000
0.2000
0.3000
0.4000
0.5000
0.6000
0 500 1000 1500 2000 2500 3000
Wavelength (nm)A
bsor
banc
e (m
m-1
)
Optical Absorbance of EAGLE2000TM Glass