Construction 1Sika.pot Seal and Coating Innovative Systems with Sika ® Liquid Plastics.
-
Upload
kevin-hart -
Category
Documents
-
view
225 -
download
0
Transcript of Construction 1Sika.pot Seal and Coating Innovative Systems with Sika ® Liquid Plastics.
Co
nst
ruct
ion
www.sika.at
3Sika.pot
Innovative Seals
Products: 2K Polyurethan
„hot sprayed“ (60-70°C)
extremely fast hardening
Equipment: 2K Hot spraying equipment
Co
nst
ruct
ion
www.sika.at
4Sika.pot
Liquid Plastics Sikalastic®/Sikafloor®
Application areas:
Water retaining structures Water treatment plants
Seal below greening
Seal of rooftops
Seal of parking lots
Seal of bridges
Co
nst
ruct
ion
www.sika.at
6Sika.pot
Seal layer: Sikalastic® 821
Tensile elongation (DIN 53 504): 340 % Tensile strength (DIN 53 504): 5.4 N/mm² Shore A Stiffness (DIN 53 505): 73 Reaction time at 23°C: 20 - 25 sec. Crack bridging: dyn. 0.3 ± 0.1 mm stat. 1.0 mm Material consumption ca. 3 kg per m²
Co
nst
ruct
ion
www.sika.at
7Sika.pot
Liquid - Films Sheeting
Price + + + +Long-term experience +/- + +Application equipment + + + +Thermal stability + + - -Crack bridging + +/-Liability + + +/-Complicated connections + -Mechanical resistance + + -Seamless seal + +/-Performance + -
Comparison Liquid films – Bitumen sheeting
Co
nst
ruct
ion
www.sika.at
11
Sika.pot
Application areas:
Sikalastic® 830
Water treatment plants
Storage tanks
Ballast troughs
Digestion tanks
Large-scale washing machinery
Water retaining structures
Wearing protection
Co
nst
ruct
ion
www.sika.at
12
Sika.pot
Spray applied membrane: Sikalastic® 830
Breaking elongation (DIN 53 504): 77 % Tensile resistance (DIN 53 504): 19 N/mm²
Shore D stiffness (DIN 53 505): 70 Reaction time at 23°C: 60 - 70 sec. Crack bridging: stat. 0.3 mm
Consumption:1.05 kg/m² = 1 mmLayer thickness(ca. 20 % spraying loss to be
considered!)
Viscosity Comp. A: ca. 2500 mPasComp. B: ca. 2000 mPas
Abrasion Taber ca. 40 mg Mixing ratio A:B 2:1
Co
nst
ruct
ion
www.sika.at
13
Sika.pot
Arguments for Sikalastic® 830
High flexibility + tensile resistance Crack bridging Seamless seal Best adhesion to the substrate Abrasion resistant against mech.
damage Time-saving processing as a single layer High stability 3 mm in (1 AG) Large area coverage Suitable for complicated structures Extremely resiliant seal Chemically resistant
Co
nst
ruct
ion
www.sika.at
16
Sika.pot
Benefits of flat rooftops seal respectively greened or earth-covered seal with hot sprayed 2-K PUR-Liquid Foil
Execution of complicated connections, installations and details through seamless spraying
Extreme tensile elongation: 340% Extreme crack bridging (even at -20° C) Extreme tensile resistance and high chemical resistance (also oils
and fuels) Very good root strength Thermal stability: above mentioned properties are obtained across
the entire temperature range (mechanical load-bearing capacity even at +50°C)
High laying performance Good adhesion on all substrates (concrete, steel and bitumen)
and thus no underflow
Co
nst
ruct
ion
www.sika.at
17
Sika.pot
50.000 m²
Seal with wear layer (OS-F)
Car park A - St. Pölten:
Current References
Shot peening
Undercoat: Sikafloor® 156
Seal: Sikalastic® 821, ca. 3 kg/m²
Wear layer: Sikafloor® 350, ca. 1.5 kg/m²Sanding with quarz sand 0.3-0.8 mm
Seal: Sikafloor® 353
Co
nst
ruct
ion
www.sika.at
23
Sika.pot
Current ReferencesFinish arrival World Cup track Altenmarkt-Zauchensee
Co
nst
ruct
ion
www.sika.at
24
Sika.pot
Current ReferencesUnderground parking earth-covered Hugo Breitner Hof
Co
nst
ruct
ion
www.sika.at
25
Sika.pot
Current ReferencesUnderground parking earth-covered Hugo Breitner Hof
Co
nst
ruct
ion
www.sika.at
26
Sika.pot
Current ReferencesUnderground parking earth-covered Hugo Breitner Hof
Co
nst
ruct
ion
www.sika.at
45
Sika.pot
Substrates- Concrete
- Screed - cement-bound
- Anhydrite
- Magnesia- Asphalt
- Gypsum plasterboard
- Metals
- Different plastics