CMP Datasheet (2003APR)1

The information given in this sheet is effective at the date shown above and subject to revision from time to time without notice.

CHUGOKU MARINE PAINTS, TODAY Chugoku Marine Paints (CMP) was founded in May 1917. CMP focused on the marine paint industry, which enabled them to give full attention to the Chugoku products and services geared to that particular industry. Our products became well established worldwide, and now Chugoku enjoys the confidence and trust of marine paint users all over the world. In more recent years Chugoku has expanded its horizons, and now we not only supply the shipping and ship building industries, but also other industrial areas, such as the construction and container industries, steel and electricity industries, wood products, the marine leisure market, the domestic sector, and many others. Now, Chugoku is focusing on an additional objective to harmonize man with nature. We look forward to the 21st century with confidence to make sure that we play a leading part in the development of our industry. We can achieve this by using our creativity and imagination to help to protect and conserve the environment for us all. This brings us to our 3 CMP principles:

Ecology - Harmony with the environment Inspired by nature, and our policy of improving the environment, we will

positively promote ecologically sound products, to help preserve and improve our surroundings. Quality - Development and production of consistently high quality

products Products, designed to meet customer needs, are manufactured to a consistent high

level of quality in many parts of the world. Innovation - Innovative technology - taking a global view

We search worldwide for the newest, most innovative technology. We know that our future depends not only on the continued development of Superior coatings, but also on the improvement of application systems. By using advanced techniques, such as robotics and computer systems, and active research of new materials, we can achieve a good harmony between market needs and the environment.


Research and development for the benefit of our customers and our environment Only a well-established and stable technology base can lead to the development of reliable products. Our policy regarding technical improvement has been practiced and applied strongly by all departments in our extensive research laboratories. The work and co-operation between all departments has resulted in new products and processes, some of which have taken number years to develop. Their efforts have led to a creation of new, novel, and environmentally friendly products, such as tin free anti-fouling paints, and water based container coatings. Chugoku has developed many paint systems, which offer excellent corrosion protection, whilst reducing the number of coats necessary, thus benefiting both customers and the environment. Chugoku’s technology has won praise from many research organizations, with whom we have co-operated. Our policy of improvement and co-operation with others will continue. An organization ensuring high quality products, worldwide Chugoku’s worldwide organization is linked together by advanced on-line communication systems, enabling us to respond quickly and efficiently to our customers’ requirements, and to the movements of our international markets. By using these systems, we can control all of our companies activities; from ordering raw materials and production planning to the receipt of orders and the delivery of finished products. Our confident approach to business is also reflected in our streamlined production facilities, which enables Chugoku to supply high quality products around the world.

TECHNICAL DATA (GENERAL)PRODUCT NAME DATA SHEET No.

SHOP PRIMER

EPICON ZINC RICH PRIMER B-2 (EPZR B-2) 1034CERABOND 2000 (CB2000) 1049ANZ PRIMER S (NZ S) 1050

OLEORESINOUS COATING

LZI PRIMER (LZI HB) 2100LZI PRIMER ZR-HB (LZI ZR HB) 2104AROSWAN QD HB (RWN HB) 2131DECK PAINT QD (QD DK) 2310HOLD SILVER (HL SILVER) 2341EVAMARINE (EM) 2400

VINYL COATING

VINYL AC-HB (V AC HB) 3001SILVAX SQ-K (SX SQ K) 3007SILVAX SQ-M (SX SQ M) 3008POLIBI T-1 (PB T-1) 3040

CHLORINATED RUBBER COATING

RAVAX AC-HB (RX AC HB) 4001RAVAX AC P (RX AC P) 4003HIPER AC (HP AC) 4005RAVAX PRIMER HB (RX P HB) 4101RAVAX FINISH (RX FC) 4400

ACRYLIC COATING

ACRI 700 PRIMER (ACR 700 P) 4006ACRI 700 FINISH (ACR 700 FC) 4038

EPOXY COATING

EPICON MARINE HB-AL (EPM HB-AL) 5001EPICON MARINE HB-CL (EPM HB-CL) 5101EPICON MARINE FINISH (EPM FC) 5400EPICON MARINE HB (EPM HB) 5402BISCON AC-HB (BC AC HB) 5601BISCON HB-NT L (BC HB NTL) 6135AUMEGUARD SX (UG SX) 6135HUMEGUARD MT (UG MT) 6167


POLYURETHAN PAINT

UNYMARINE (UM) 5510UNYMARINE TS (UM TS) 5525

TBT-FREE ANTIFOLING

Conventional TypeRAVAX AF (RX AF) 4010

Hydration TypeTFA-10 (TFA 10) 5871TFA FLAT (TFA F) 5873SEATENDER 7 (ST 7) 5950SEATENDER 10 (ST 10) 5955SEATENDER 12 (ST 12) 5957SEATENDER 15 (ST 15) 5960

Hydrolysis TypeSEA GRANDPRIX 500 (SGP 500) 5905SEA GRANDPRIX 1000 (SGP 1000) 5909SEA GRANDPRIX CF-10 (SGP CF10) 5917K

TANK & HEAVY DUTY COATING

Epoxy CoatingBANNOH 500 (B 500) 5055BANNOH 500 R (B 500R) 5072BANNOH 500 N (B 500N) 5073BANNOH 200 (B 200) 5127EPICON T-500 PRIMER H (EP T-500 H) 6020AEPICON T-500 (EP T-500) 6025EPICON T-800 HOLDING PRIMER (EP T-800 HP) 6035EPICON T-800 (EP T-800) 6037CLEANKEEP 5000 (CK 5000) 6072NOVA 1000 (NV 1000) 6180CNOVA 2000 (NV 2000) 6181NOVA 5000 (NV 5000 ) 6182NOVA 5000 BARRIER (NV 5000 BAR) 6182A

Tar-Epoxy CoatingBISCON HB (BC HB) 6110BISCON HB-200 (BC HB-200) 6112

Inorganic Zinc CoatingGALBON S-HB (GB S-HB) 6250

OtherAPERIA NO.3000 HB (AP 3000 HB) 6341


MISCELLANEOUS PAINT

SILVA SPAR NO.500 (SIS 500) 8000SILICON NO.400 PRIMER (SN 400 PR) 8009SILICON NO.400 SILVER (SN 400 SIL) 8010CERABEST (CB) 8052GALVANITE NO.200 PRIMER (GNT 200 P) 8220RUST INHIBITIVE OIL"CK" (RIO CK) 8250SWAN PRIMER (SW PR) 2418SWAN (SW) 2417

TECHNICAL DATA (ALPHABETICAL)PRODUCT NAME DATA SHEET No.

AACRI 700 FINISH (ACR 700 FC) 4038ACRI 700 PRIMER (ACR 700 P) 4006APERIA NO.3000 HB (AP 3000 HB) 6341

BBANNOH 200 (B 200) 5127BANNOH 500 (B 500) 5055BANNOH 500 N (B 500N) 5073BANNOH 500 R (B 500R) 5072BISCON AC-HB (BC AC HB) 5601BISCON HB (BC HB) 6110BISCON HB-200 (BC HB-200) 6112BISCON HB-NT L (BC HB NTL) 6135A

CCERABEST (CB) 8052CERABOND 2000 (CB2000) 1049ACLEANKEEP 5000 (CK 5000) 6072

DDECK PAINT QD (QD DK) 2310

EEPICON MARINE FINISH (EPM FC) 5400EPICON MARINE HB (EPM HB) 5402EPICON MARINE HB-AL (EPM HB-AL) 5001EPICON MARINE HB-CL (EPM HB-CL) 5101EPICON T-500 (EP T-500) 6025EPICON T-500 PRIMER H (EP T-500 H) 6020AEPICON T-800 (EP T-800) 6037EPICON T-800 HOLDING PRIMER (EP T-800 HP) 6035EPICON ZINC RICH PRIMER B-2 (EPZR B-2) 1034EVAMARINE (EM) 2400

GGALBON S-HB (GB S-HB) 6250GALVANITE NO.200 PRIMER (GNT 200 P) 8220

HHIPER AC (HP AC) 4005HOLD SILVER (HL SILVER) 2341

LLZI PRIMER (LZI HB) 2100LZI PRIMER ZR-HB (LZI ZR HB) 2104A

NNOVA 1000 (NV 1000) 6180CNOVA 2000 (NV 2000) 6181NOVA 5000 (NV 5000) 6182NOVA 5000 BARRIER (NV 5000 BAR) 6182ANZ PRIMER S (NZ S) 1050

TECHNICAL DATA (ALPHABETICAL)PRODUCT NAME DATA SHEET No.

PPOLIBI T-1 (PB T-1) 3040

RRAVAX AC P (RX AC P) 4003RAVAX AC-HB (RX AC HB) 4001RAVAX AF (RX AF) 4010RAVAX FINISH (RX FC) 4400RAVAX PRIMER HB (RX P HB) 4101ROSWAN QD HB (RWN HB) 2131RUST INHIBITIVE OIL"CK" (RIO CK) 8250

SSEA GRANDPRIX 1000 (SGP 1000) 5909SEA GRANDPRIX 500 (SGP 500) 5905SEA GRANDPRIX CF-10 (SGP CF10) 5917KSEATENDER 10 (ST 10) 5955SEATENDER 12 (ST 12) 5957SEATENDER 15 (ST 15) 5960SEATENDER 7 (ST 7) 5950SILICON NO.400 PRIMER (SN 400 PR) 8009SILICON NO.400 SILVER (SN 400 SIL) 8010SILVA SPAR NO.500 (SIS 500) 8000SILVAX SQ-K (SX SQ K) 3007SILVAX SQ-M (SX SQ M) 3008SWAN (SW) 2417SWAN PRIMER (SW PR) 2418

TTFA FLAT (TFA F) 5873TFA-10 (TFA 10) 5871

UUMEGUARD MT (UG MT) 6167UMEGUARD SX (UG SX) 6135HUNYMARINE (UM) 5510UNYMARINE TS (UM TS) 5525

VVINYL AC-HB (V AC HB) 3001


No. 1034 Oct. - 1999

(SHA) EPICON ZINC RICH PRIMER B-2 (EPZR B-2) EPICON ZINC RICH PRIMER B-2, a two-pack primer, based on a combination of metallic zinc, epoxy resin and hardener. It dries quickly and gives adequate preliminary protection of steel after sand - or shot-blasting. This primer is completely compatible with almost any type of paint and highly resistant to heat, oil, water and solvent. TECHNICAL DATA

Type

:

Epoxy zinc rich primer

Recommended Use

:

As a shop primer for protection of blast-cleaned steel plates used for underwater area of outer hull.

Mixing Ratio

:

Base : Hardener = 70 : 30 (by volume)

Colour

:

Green, Brown, Grey

Flash Point

:

Base : 10oC Hardener : 10oC

Solids by Volume

:

40 ± 2%

Coverage (Theoretical)

:

0.044 L/m2 ; 93 g/m2

Wet Film Thickness

:

-

Dry Film Thickness

:

18 µm

Drying Time

(at D.F.T. 18µm)

: Temperature 5oC 10oC 20oC 30oC

Surface Dry 8 min. 7 min. 4 min. 3 min.Hard Dry 4 hrs. 3 hrs. 2 hrs. 1.5 hrs.

Painting Interval (at D.F.T. 18µm)

:

Minimum* 24 hrs. 20 hrs. 16 hrs. 10 hrs.M aximum 180 days 180 days 180 days 150 days

Pot Life

: 72 hrs. 60 hrs. 48 hrs. 24 hrs.

Thinner

:

EPICON THINNER

Method of Application

:

Airless spray, Brush, Roller

Condition for Airless Spray

:

Temperature Minimum 5°C Humidity Maximum 85% R.H. For Airless spray;

Tip No. GRACO 719 Paint Output Pressure 8.2 ~ 11.0 MPa (g) Viscosity 9 ~ 13 sec. (Ford Cup No.4) Thinning 10 ~ 25% by volume

Preferable Preceding Coats

:

-

Preferable Subsequent Coats

:

Most of our products or the equivalents except oleoresinous paints.

Packing

:

Two pack product

Note : * Minimum painting interval for touch up is 4 hours at 20oC.


No. 1049A Jan. - 2003

(SHA) CERABOND 2000 (CB 2000) CERABOND 2000, is a combination of heat resistance alloy and heat resistant silicate solution producing an inorganic rust-preventive coat mechanically adhered to the steel and giving an effective and long-term protection against corrosion without suffering from blistering and loss of adhesion. It is compatible with organic overcoatings as well as with inorganic overcoatings. CERABOND 2000 is extremely resistant to heat (up to 800°C) and secondary surface preparation cost can be decreased. It has excellent welding and cutting properties and presents no health hazard to the welder. CERABOND 2000 has been approved by Lloyd’s Resister of Shipping as a shop primer which is suitable for welding. TECHNICAL DATA

Type

:

Fast weldable &Ultra heat resistant shop primer

Recommended Use

:

As a shop primer for temporary protection of blast-cleaned steel, as a general purpose rust-preventing primer for organic and inorganic over coating, and also as a heat resistant paint.

Mixing Ratio

:

Paste : Base = 39 : 61 (by volume)

Colour

:

Green, Grey, Brown

Flash Point

:

Paste : 23°C Base : 15°C

Solids by Volume

:

36 ± 2%


:

0.044 L/m2

Wet Film Thickness

:

42 µm

Dry Film Thickness

:

15 µm

Drying Time

(at D.F.T. 15µm)


Surface Dry 3 min. 3 min. 2 min. 2 min.Hard Dry 2 hrs. 1.5 hrs. 1 hr. 1 hr.


:

Min.(Organic) 14 days 10 days 7 days 7 days (Inorganic) 16 hrs. 8 hrs. 4 hrs. 4 hrs.M aximum 180 days 180 days 180 days 180 days

Pot Life

: 36 hrs. 30 hrs. 24 hrs. 15 hrs.

Thinner

:

INORGANIC SHOP PRIMER THINNER, INORGANIC SHOP PRIMER THINNER S


:

Airless spray, Brush


:

Temperature 0 ~ 40oC Humidity 50 ~ 90% R.H. For Airless spray;

Tip No. GRACO 617 ~ 923 Paint Output Pressure 4.4 ~ 8.9 MPa(g) Viscosity 9 ~11 sec. (Ford Cup No.4) Thinning 5 ~ 15% ( by volume)


:

Most our products or the equivalents. However, when oleoresinous paints are applied please consult us.

Packing

:

Two pack product

Notes : * Expected life for outdoor exposure (under normal conditions) : about 6 months * Oleoresinous coating system over CERABOND 2000 is not recommended on high humid (often sweaty) or underwater areas.


No. 1050 Oct. - 1999

(SHA) NZ PRIMER S (NZ S) NZ PRIMER S, based on a combination of epoxy resin, rust-preventive pigments and hardener, is quick drying and gives adequate preliminary protection of blast-cleaned steel plates. It is compatible with almost any type of priming coat and highly resistant to heat, oil, water and solvents. TECHNICAL DATA

Type

:

Non zinc type epoxy shop primer

Recommended Use

:

As a shop primer for protection of blast-cleaned steel plates. Especially suitable for steel plates subject to prolonged weathering.

Mixing Ratio

:


Colour

:

Red brown

Flash Point

:


Solids by Volume

:

24 ± 2%


:

0.091 L/m2 ; 103 g/m2

Wet Film Thickness

:

-

Dry Film Thickness

:

22 µm

Drying Time

(at D.F.T. 35µm)


Surface Dry 8 min. 7 min. 4 min. 3 min.H ard Dry 4 hrs. 3 hrs. 2 hrs. 1 hr.

Painting Interval

(at D.F.T. 35µm)

: Minimum 24 hrs. 20 hrs. 16 hrs. 8 hrs.

M aximum 150 days 120 days 120 days 90 days Pot Life

: 72 hrs. 72 hrs. 48 hrs. 24 hrs.

Thinner

:

EPICON THINNER


:



:


Tip No. GRACO 719 Paint Output Pressure 8.8 ~ 11.8 MPa(g) Viscosity 9 ~ 10 sec. (Ford Cup No.4) Thinning 10 ~ 25% by volume


:

Any one of our products and/ or the equivalent, e.g.:, Oleoresinous paint, Chlorinated rubber paint, Vinyl paint, Epoxy paint, Tar-epoxy paint

Packing

:

Two pack product

Note : * Expected life for outdoor exposure [under normal conditions] : about 4 months


No. 2100 Mar. - 2003

(SHA)

LZI PRIMER (LZI) LZI PRIMER, is an alkyd resin based red lead and zinc chromate primer with carefully selected rust-preventing pigments. It dries quickly, offering effective rust-prevention and excellent resistance to impact and bending. TECHNICAL DATA

Type

:

Alkyd resin primer

Recommended Use

:

As a rust-preventing primer for inside of superstructure, deck, hold, and other steel structures

Colour

:

Reddish brown

Flash Point

:

43oC

Solids by Volume

:

52 ± 2%


:

0.058 ~ 0.077 L/m2 ; 81 ~ 108 g/m2

Wet Film Thickness

:

58 ~ 77µm

Dry Film Thickness

:

30 ~ 40 µm

Drying Time

(at D.F.T. 35µm)


Surface Dry 4 hrs. 2 hrs. 1 hr. 30 min.H ard Dry 18 hrs. 12 hrs. 6 hrs. 3 hrs.

Painting Interval

(at D.F.T. 35µm)


M aximum 120 days 100 days 90 days 60 days Thinner

:

MARINE THINNER


:



:


Tip No. GRACO 719 Paint Output Pressure 10.7 ~ 13.8 MPa(g) Viscosity 120 sec. (Ford Cup No. 4) Thinning 0 ~ 5% by volume


:

NZ PRIMER, etc.


:

EVAMARINE, Alkyd resin based paints

Packing

:

One pack product


No. 2131 Mar. - 2000

(SHA)

ROSWAN QD HB (RWN HB) ROSWAN QD HB is a white coloured high-build type paint, based on alkyd resin. Being white colour, it is especially recommended for use as a primer for white and light-coloured finishes. TECHNICAL DATA

Type

:

Alkyd resin primer, High-build

Recommended Use

:

As a rust-preventing primer on inside and outside of superstructure and other steel structures.

Colour

:

White, Tint colour

Flash Point

:

36oC

Solids by Volume

:

47 ± 2%


:

0.064 ~ 0.170 L/m2 ; 88 ~ 235 g/m2

Wet Film Thickness

:

64 ~ 170 µm

Dry Film Thickness

:

30 ~ 80 µm

Drying Time

(at D.F.T. 70µm)


Surface Dry 6 hrs. 3 hrs. 1.5 hrs. 45 min.Hard Dry 24 hrs. 14 hrs. 7 hrs. 4 hrs.


:

Minimum 48 hrs. 30 hrs. 20 hrs. 16 hrs.Maximum 120 days 100 days 90 days 60 days

Thinner

: MARINE THINNER


:

Airless spray, Brush*, Roller


:


Tip No. GRACO 719 Paint Output Pressure 14.7 ~ 17.7 MPa(g) Viscosity 120 sec. (Ford Cup No. 4) Thinning 0 ~ 5% by volume


:

NZ PRIMER, LZI PRIMER, etc.


:

EVAMARINE, Alkyd resin based paints

Packing

:

One pack product

Note : * Sufficient thickness is difficult to obtain by brush.


No. 2310 Oct. - 1999 (SHA) DECK PAINT QD (QD DK) DECK PAINT QD, based on alkyd resin, is designed to provide good protection to deck areas which are subject to severe conditions such as heavy wear and strong sunlight. TECHNICAL DATA

Type

:

Alkyd resin deck paint

Recommended Use

:

As a finish coat on steel decks

Colour

:

Reddish brown, Green, Grey

Flash Point

:

44oC

Solids by Volume

:

52 ± 2%


:

0.057 ~ 0.076 L/m2 ; 69 ~ 92 g/m2

Wet Film Thickness

:

57 ~ 76 µm

Dry Film Thickness

:

30 ~ 40 µm

Drying Time

(at D.F.T. 35µm)


Surface Dry 4 hrs. 2 hrs. 1 hr. 30 min.Hard Dry 18 hrs. 10 hrs. 6 hrs. 3 hrs.


:

Minimum* 30 hrs. 20 hrs. 16 hrs. 10 hrs.Maximum - - - -

Thinner

: MARINE THINNER


:



:


Tip No. GRACO 615, 717 Paint Output Pressure 10.7 ~ 13.8 MPa(g) Viscosity 100 sec. (Ford Cup No.4) Thinning 0 ~ 5% by volume


:

LZI PRIMER, RED LEAD PRIMER QD, Alkyd resin based primer


:

-

Packing

:

One pack product

Note : * Requires 16 hours drying time (at 20oC) before it is dry enough to walk on.


No. 2341 Oct. - 1999 (SHA) HOLD SILVER (HL SILVER) Holds suffer from corrosion as much as most other areas. HOLD SILVER is based on oil and synthetic petroleum resin. TECHNICAL DATA

Type

:

Oleo resinous hold paint

Recommended Use

:

As a finishing coat in ship’s holds (cargo hold)

Colour

:

Silver

Flash Point

:

29oC

Solids by Volume

:

45 ± 2%


:

0.033 ~ 0.056 L/m2 ; 33 ~ 56 g/m2

Wet Film Thickness

:

33 ~ 56 µm

Dry Film Thickness

:

15 ~ 25 µm

Drying Time

(at D.F.T. 20µm)




:

Minimum 35 hrs. 24 hrs. 15 hrs. 10 hrs.Maximum - - - -

Thinner

: MARINE THINNER


:



:


Tip No. GRACO 713, 715 Paint Output Pressure 10.7 ~ 13.8 MPa(g) Viscosity 33 sec. (Ford Cup No.4) Thinning -


:

LZI PRIMER, RED LEAD PRIMER QD, Alkyd resin based primer


:

-

Packing

:

One pack product

Notes: Resistance to certain cargoes is limited. Please contact us.

Waiting time before the first cargo loading Temp. 10oC 20oC 30oC (Days) 50 40 30


No. 2400 Oct. - 1999 (SHA) EVAMARINE (EM) EVAMARINE is an alkyd resin based paint with excellent adhesion property, weathering resistance and excellent colour retention. TECHNICAL DATA

Type

:

Alkyd resin finish paint

Recommended Use

:

As a finishing coat on exterior wood and steel surfaces

Colour

:

White, As specified

Flash Point

:

43oC

Solids by Volume

:

49 ± 2%


:

0.051 ~ 0.071 L/m2 ; 61 ~ 85 g/m2

Wet Film Thickness

:

51 ~ 71 µm

Dry Film Thickness

:

25 ~ 35 µm

Drying Time

(at D.F.T. 35µm)


Surface Dry 4 hrs. 3 hrs. 2 hrs. 1.5 hrs.Hard Dry 30 hrs. 16 hrs. 8 hrs. 6 hrs.


:


Thinner

: MARINE THINNER


:



:




:

LZI PRIMER, etc.


:

-

Packing

:

One pack product


No. 2417 Dec. - 2000

(SHA)

SWAN (SW) SWAN is a water base paint having outstanding durability. It provide smooth and odd-less film with quick dry. SWAN shows good adhesion to steel surface. TECHNICAL DATA

Type

:

Water base finish paint

Recommended Use

:

As a finish coat for exterior and interior surface of marine and steel structures

Colour

:

White, Light colours

Flash Point

:

Non flammable

Solids by Volume

:

40 ± 2%


:

0.103 L/m2 ; 129 g/m2

Wet Film Thickness

:

103 µm

Dry Film Thickness

:

40 µm

Drying Time

(at D.F.T. 40µm)


Surface Dry 1.5 hrs. 1 hr. 30 min. 20 min.Hard Dry 5 hrs. 4 hrs. 3 hrs. 1.5 hrs.

Painting Interval

(at D.F.T. 40µm)

:


Thinner

:

Fresh water


:

Airless spray, Air spray, Brush


:


Tip No. GRACO 515, 617, 719 Paint Output Pressure 14.7 ~ 17.7 MPa(g) Viscosity 3 ~ 4 Pa.s Thinning 0 ~ 3% by volume


:

SWAN PRIMER, CERABEST


:

-

Packing

:

One pack product

Notes: 1. Drying and curing is favored good ventilation to assist evaporation of water.2. Paint can should be closed after application to prevent skinning.3. Do not storage the paint below -5oC nor over 40oC4. Do not mix other water based paints and coloring compounds.


No. 2418 Dec. - 2000

(SHA)

SWAN PRIMER (SW PR) SWAN PRIMER is a water based anti-rust primer. It provide smooth and odd-less film with quick dry. It has excellent rust-preventing property, adhesion, weathering resistance and other physical properties. SWAN PRIMER is suitable for protection of steel surface. TECHNICAL DATA

Type

:

Water base anti-rust primer

Recommended Use

:

As a anti-rust primer of marine and steel structures.

Colour

:

Light Grey

Flash Point

:

Non flammable

Solids by Volume

:

38 ± 2%


:

0.092 ~ 0.118 L/m2 ; 110 ~ 142 g/m2

Wet Film Thickness

:

92 ~ 118 µm

Dry Film Thickness

:

35 ~ 45 µm

Drying Time

(at D.F.T. 40µm)


Surface Dry 1 hr. 50 min. 30 min. 20 min.Hard Dry 2.5 hrs. 2 hrs. 1.5 hrs. 1 hr.

Painting Interval

(at D.F.T. 40µm)

:


Thinner

:

Fresh water


:

Airless spray, Air spray, Brush


:


Tip No. GRACO 515, 617, 719 Paint Output Pressure 14.7 ~ 17.7 MPa(g) Viscosity 3 ~ 4 Pa.s Thinning 0 ~ 3% by volume


:

CERABOND 2000, EPICON ZINC RICH PRIMER, CERABEST


:

SWAN

Packing

:

One pack product

Notes: 1. Drying and curing is favored good ventilation to assist evaporation of water.2. Paint can should be closed after application to prevent skinning.3. Do not storage the paint below -5oC nor over 40oC4. Do not mix other water based paints and coloring compounds.


No. 3001 Oct. - 1999

(SHA) VINYL AC-HB (V AC HB) VINYL AC-HB, based on vinyl chloride resin and aluminium pigment, provides an effective protection against corrosion. It adheres well to subsequent anti-fouling paint as well as to various types of primers. It is quick drying and forms a tough yet flexible film which is highly resistant to weather, sea water and cathodic protection. TECHNICAL DATA

Type

:

Vinyl primer, high-build

Recommended Use

:

Steel ship’s hull and other steel structures

Colour

:

S (Silver), SR (Pinkish silver)

Flash Point

:

19oC

Solids by Volume

:

22 ± 2%


:

0.113 ~ 0.272 L/m2 ; 121 ~ 291 g/m2

Wet Film Thickness

:

113 ~ 272 µm

Dry Film Thickness

:

25 ~ 60 µm

Drying Time

(at D.F.T. 60µm)


Surface Dry 50 min. 40 min. 30 min. 20 min.Hard Dry 5 hrs. 4 hrs. 3 hrs. 2 hrs.


:

Minimum 6 hrs. 5 hrs. 4 hrs. 3 hrs.M aximum - - - -

Thinner

:

VINYL THINNER


:

Airless spray

Condition for Application

:


Tip No. GRACO 719, 721 Paint Output Pressure 14.7 ~ 17.7 MPa(g) Viscosity 1.5 Pa.s Thinning 5~ 10% by volume


:

ETCHING PRIMER H, NZ PRIMER, EPICON ZINC RICH PRIMER, EPICON MARINE HB-AL, etc.


:

VINYL AF, POLIBI T-1, TFA-10, TFA-20, TFA-30, etc.

Packing

:

One pack product


No. 3007 Jan. - 2001 (SHA) SILVAX SQ-K (SX SQ K) SILVAX SQ-K, modified vinyl paint, forms a practically impervious barrier against water and provides an excellent key for subsequent anti-fouling paints. TECHNICAL DATA

Type

:

Modified vinyl anti-corrosive paint.

Recommended Use

:

Anti-corrosive for steel ships bottom, Binder-coat for anti-fouling paint

Colour

:

S (Silver), SR (Pink Silver)

Flash Point

:

19oC

Solids by Volume

:

30 ± 2%


:

0.133 ~ 0.266L/m2 ; 144 ~ 288 g/m2

Wet Film Thickness

:

133 ~ 266 µm

Dry Film Thickness

:

40 ~ 80 µm

Drying Time

(at D.F.T. 80µm)


Surface Dry 1.5 hrs. 1 hr. 40 min. 30 min.Hard Dry 12 hrs. 10 hrs. 8 hrs. 6 hrs.

Painting Interval

(at D.F.T. 80µm)

:

Minimum (AC) 12 hrs. 10 hrs. 8 hrs. 6 hrs.Minimum (AF) 15 hrs. 12 hrs. 9 hrs. 8 hrs.Maximum (AC) - - - -M aximum (AF) 7 days 7 days 7 days 7 days

Thinner

:

VINYL THINNER


:


Condition of Application

:

Temperature Minimum 0oC Humidity Maximum 85% R.H. For Airless spray;

Tip No. GRACO 719, 721 Paint Output Pressure 11.7 ~ 14.7 MPa (g) Viscosity 80 sec. (Ford Cup No. 4) Thinning 0 ~ 10% by volume


:

BISCON AC-QL, BISCON AC-AL, BANNOH 500, etc.


:

SEA GRANDPRIX series

Packaging

:

One pack product

Note : Before application of subsequent coat, clean the surface by fresh water washing or other means if surface is

contaminated by chalking or impurities.


No. 3008 Jun. - 2001 (SHA) SILVAX SQ-M (SX SQ M) SILVAX SQ-M, modified vinyl paint, forms a practically impervious barrier against water and provides an excellent key for subsequent anti-fouling paints. TECHNICAL DATA

Type

:

Modified vinyl anti-corrosive paint.

Recommended Use

:

Anti-corrosive for steel ships bottom, Binder-coat for anti-fouling paint

Colour

:

S (Silver Brown), R (Red Silver Brown)

Flash Point

:

19 oC

Solids by Volume

:

36 ± 2%


:

0.111 ~ 0.208 L/m2 ; 124 ~ 233 g/m2

Wet Film Thickness

:

111 ~ 208 µm

Dry Film Thickness

:

40 ~ 75 µm

Drying Time

(at D.F.T. 75µm)


Surface Dry 1 hr. 45 min. 30 min. 25 min.H ard Dry 8 hrs. 6.5 hrs. 5 hrs. 4 hrs.

Painting Interval

(at D.F.T. 75µm)

:

Minimum (AC) 8 hrs. 6.5 hrs. 5 hrs. 4 hrs.Minimum (AF) 14 hrs. 11 hrs. 8 hrs. 7 hrs.Maximum (AC) - - - -M aximum (AF) 7 days 7 days 7 days 7 days

Thinner

:

VINYL THINNER


:



:

Temperature Minimum 0 oC Humidity Maximum 85% R.H. For Airless spray;

Tip No. GRACO 719, 721 Paint Output Pressure 11.7 ~ 14.7 MPa(g) Viscosity 80 sec. (Ford Cup No. 4) Thinning 0 ~ 10% by volume


:

BISCON AC-HB, BISCON AC-QL HB, SILVAX SQ-M, etc.


:

MARINE STAR 10, 20 series, TFA-10 series, SILVAX SQ-M

Packaging

:

One pack product

Note : Before application of subsequent coat, clean the surface by fresh water washing or other means if surface

is contaminated by chalking or impurities.


No. 3040 Oct. - 1999

(SHA) POLIBI T-1 (PB T-1) POLIBI T-1 is a vinyl chloride resin based paint, providing excellent adhesion property, durability, weathering resistance and gloss retention. It is quick drying and easy to apply. Recommended as a finishing coat on the inside and outside of superstructures. TECHNICAL DATA

Type

:

Vinyl finish paint

Recommended Use

:

Finish coat of vinyl system on the ship’s inside and outside superstructures area and other steel structures.

Colour

:

White, As specified

Flash Point

:

7oC

Solids by Volume

:

28 ± 2%


:

0.072 ~ 0.108 L/m2 ; 77 ~ 116 g/m2

Wet Film Thickness

:

72 ~ 108 µm

Dry Film Thickness

:

20 ~ 30 µm

Drying Time

(at D.F.T. 25µm)


Surface Dry 30 min. 25 min. 20 min. 15 min.Hard Dry 3 hrs. 2.5 hrs. 2 hrs. 1.5 hrs.

Painting Interval

(at D.F.T. 25µm)

:

Minimum 5 hrs. 4 hrs. 3 hrs. 2hrs.M aximum - - - -

Thinner

:

VINYL THINNER


:



:


Tip No. GRACO 719 Paint Output Pressure 11.7 ~ 14.7 MPa(g) Viscosity 30 sec. (Ford Cup No.4) Thinning 6 ~ 12% by volume


:

VINYL RED LEAD PRIMER, VINYL RED LEAD PRIMER HB, VINYL AC


:

-

Packing

:

One pack product


No. 4001 Oct. - 1999 (SHA) RAVAX AC HB (RX AC HB) RAVAX AC HB is a chlorinated rubber paint giving a high-build quick drying, effective protection against corrosion. It affords good adhesion between the films as well as to shop primers and subsequent coats. It also possesses sea water resistance and shows good adhesion to subsequent coats even after prolonged weathering. TECHNICAL DATA

Type

:

Chlorinated rubber anti-corrosive paint, high build

Recommended Use

:


Colour

:

SR (Pinkish Silver), S (Silver)

Flash Point

:

27oC

Solids by Volume

:

42 ± 2%


:

0.095 ~ 0.179 L/m2 ; 124 ~ 232 g/m2

Wet Film Thickness

:

95 ~ 179 µm

Dry Film Thickness

:

40 ~ 75 µm

Drying Time

(at D.F.T. 60µm)


Surface Dry 1 hr. 45 min. 30 min. 25 min.Hard Dry 6 hrs. 4.5 hrs. 3 hrs. 2.5 hrs.

Painting Interval

(at D.F.T. 60µm)

:


Thinner

:

RAVAX THINNER


:



:




:

NZ PRIMER, CERABOND 2000, EPICON ZINC RICH PRIMER, etc.


:

RAVAX AF, RAVAX FINISH, TFA-10. 20. 30, etc.

Packing

:

One pack product


No. 4005 Oct. - 1999

(SHA) HIPER AC (HP AC) HIPER AC is a special synthetic resin paint giving a high-build quick drying, effective protection against corrosion. It possesses good sea water resistance and shows good adhesion to subsequent coats. TECHNICAL DATA

Type

:

Special synthetic resin anti-corrosive paint

Recommended Use

:

Anti-corrosive paint for repair ships and steel ship’s hull

Colour

:

S (Silver), SR (Silver red)

Flash Point

:

27oC

Solids by Volume

:

43 ± 2%


:

0.142 ~ 0.235 L/m2 ; 184 ~ 306 g/m2

Wet Film Thickness

:

142 ~ 235 µm

Dry Film Thickness

:

60 ~ 100 µm

Drying Time

(at D.F.T. 80µm)


Surface Dry 1 hr. 45 min. 30 min. 25 min.H ard Dry 8 hrs. 6 hrs. 4 hrs. 3 hrs.

Painting Interval

(at D.F.T. 80µm)

:

Minimum (AC) 8 hrs. 6 hrs. 4 hrs. 3 hrs.Minimum (AF) 12 hrs. 8 hrs. 6 hrs. 5 hrs.M aximum - - - -

Thinner

:

RAVAX THINNER


:



:

Temperature Minimum 0oC Humidity Maximum 85% R.H. For Airless spray;

Tip No. GRACO 621, 623 Paint Output Pressure 11.7 ~ 14.7 MPa(g) Viscosity 1.6 Pa.s Thinning 0 ~ 5% by volume


:



:

TFA series, SEATENDER series, SEA GRANDPRIX series

Packing

:

One pack product


No. 4006 Dec. - 2000

(SHA) ACRI 700 PRIMER (ACR 700 P) ACRI 700 PRIMER is an effective anti-corrosive primer based on acrylic resin and drying by evaporation of the solvents. It can be applied directly on to bare steel or existing paint film such as acrylic, chlorinated rubber and alkyd. It has good workability and it is possible to obtain thick coat especially by spray application. TECHNICAL DATA

Type

:

Acrylic anti-corrosive primer

Recommended Use

:

Anti-corrosive primer on the ship’s topside, superstructure

Colour

:

S (Silver Brown), R (Red Silver Brown)

Flash Point

:

24oC

Solids by Volume

:

40 ± 2%


:

0.100 ~ 0.200 L/m2 ; 115 ~ 230 g/m2

Wet Film Thickness

:

100 ~ 200 µm

Dry Film Thickness

:

40 ~ 80 µm

Drying Time

(at D.F.T. 60µm)


Surface Dry 1.5 hrs. 1.2 hrs. 1 hr. 0.5 hr.Hard Dry 12 hrs. 9 hrs. 7 hrs. 6 hrs.

Painting Interval

(at D.F.T. 60µm)

:


Thinner

:

RAVAX THINNER


:



:




:

NZ PRIMER, CERABOND 2000, EPICON ZINC RICH PRIMER, existing Acrilic, CR paint, etc.


:

ACRI 700 FINISH

Packing

:

One pack product


No. 4010 Dec. - 1999

(SHA) RAVAX AF (RX AF) RAVAX AF is a special synthetic resin based anti-fouling paint with a high content of antifoulant, providing extended effective protection against fouling, results in fuel saving and elimination of lost time due to reduction in speed resulting from fouling. It has excellent adhesion to RAVAX AC. TECHNICAL DATA

Type

:

Special synthetic resin anti-fouling paint

Recommended Use

:

Anti-fouling finish of chlorinated rubber system on steel ship’s bottom areas

Colour

:

Dark red brown

Flash Point

:

24oC

Solids by Volume

:

50 ± 2%


:

0.070 ~ 0.090 L/m2 ; 116 ~ 149 g/m2

Wet Film Thickness

:

70 ~ 90 µm

Dry Film Thickness

:

35 ~ 45 µm

Drying Time

(at D.F.T. 40µm)


Surface Dry 45 min. 30 min. 20 min. 15 min.H ard Dry 6 hrs. 4.5 hrs. 3 hrs. 2 hrs.

Painting Interval

(at D.F.T. 40µm)

:


Dry To Launch

(at D.F.T. 40µm)

:


Thinner

:

RAVAX THINNER


:



:




:

RAVAX AC, SILVER SQ, etc.


:

-

Packing

:

One pack product


No. 4038 Dec. - 2000

(SHA)

ACRI 700 FINISH (ACR 700 FC) ACRI 700 FINISH is a finish coat based on acrylic resin and drying evaporation on the solvents. It has excellent adhesion property, weathering resistance and gloss and colour retention. TECHNICAL DATA

Type

:

Acrylic finish paint

Recommended Use

:

Finishing coat on ship’s topside, superstructure

Colour

:

White, As specified

Flash Point

:

24oC

Solids by Volume

:

37 ± 2%


:

0.081 ~ 0.135 L/m2 ; 99 ~ 165 g/m2

Wet Film Thickness

:

81 ~ 135 µm

Dry Film Thickness

:

30 ~ 50 µm

Drying Time

(at D.F.T. 35µm)


Surface Dry 1.5 hrs. 1 hr. 0.5 hr. 0.5 hr.Hard Dry 10 hrs. 8 hrs. 6 hrs. 4 hrs.

Painting Interval

(at D.F.T. 35µm)

:


Thinner

:

RAVAX THINNER


:



:


Tip No. GRACO 719 Paint Output Pressure 11.7 ~ 14.7 MPa(g) Viscosity 60 sec. (Ford Cup No.4) Thinning 0 ~ 10% by volume


:

ACRI 700 PRIMER, BANNOH 200


:

-

Packing

:

One pack product


No. 4101 Dec. - 2000

(SHA) RAVAX PRIMER HB (RX P HB) RAVAX PRIMER HB is an effective anti-rust primer based on chlorinated rubber, red lead and red iron oxide, drying by evaporation of solvents. It has excellent rust-preventing and adhesion properties, weathering and oil resistance and other physical properties. TECHNICAL DATA

Type

:

Chlorinated rubber anti-rust primer, high-build

Recommended Use

:

As an anti-rust primer on the superstructure of ships and other steel structure

Colour

:

Reddish brown

Flash Point

:

26oC

Solids by Volume

:

43 ± 2%


:

0.094 ~ 0.187 L/m2 ; 130 ~ 260 g/m2

Wet Film Thickness

:

94 ~ 187 µm

Dry Film Thickness

:

40 ~ 80 µm

Drying Time

(at D.F.T. 80µm)


Surface Dry 1.5 hrs. 1.2 hrs. 1 hr. 30 min.Hard Dry 12 hrs. 9 hrs. 7 hrs. 6 hrs.

Painting Interval

(at D.F.T. 80µm)

:


Thinner

:

RAVAX THINNER


:



:




:



:

RAVAX FINISH, etc.

Packing

:

One pack product


No. 4400 Dec. - 2000 (SHA) RAVAX FINISH (RX FC) RAVAX FINISH, base on a chlorinated rubber vehicle, physically dries by evaporation of the solvents. It has excellent adhesion property, weathering resistance and gloss and colour retention. It is also highly resistant to the influence of salt water, oil and chalking. Although standard dry film thickness is 35 microns per coat, it is possible to obtain a maximum of 50 microns dry film thickness per coat. TECHNICAL DATA

Type

:

Chlorinated rubber finish paint

Recommended Use

:

As an finishing coat on interior and exterior of superstructures

Colour

:

White, As specified

Flash Point

:

26°C

Solids by Volume

:

42 ± 2%


:

0.072 ~ 0.120 L/m2 ; 95 ~ 158 g/m2

Wet Film Thickness

:

72 ~ 120 µm

Dry Film Thickness

:

30 ~ 50 µm

Drying Time

(at D.F.T. 35µm)


Surface Dry 60 min. 50 min. 30 min. 20 min.Hard Dry 6 hrs. 5 hrs. 4 hrs. 3.5 hrs.

Painting Interval

(at D.F.T. 35µm)

:


Thinner

:

RAVAX THINNER


:



:


Tip No. GRACO 719 Paint Output Pressure 11.7 ~ 14.7 MPa(g) Viscosity 100 sec. (Iwata Cup) Thinning 0 ~ 5% by volume


:

RAVAX PRIMER, etc.


:

-

Packing

:

One pack product


No. 5001 Oct. - 1999

(SHA)

EPICON MARINE HB-AL (EPM HB AL) EPICON MARINE HB-AL is a combination of epoxy resin and a curing agent containing aluminium pigment. It possesses excellent physical properties such as adhesion, toughness, impact and abrasion resistance, sea-water and water-resistance. It is suitable for underwater areas. TECHNICAL DATA

Type

:

Epoxy/Polyamide anti-corrosive paint, high-build

Recommended Use

:

Primer on EPICON MARINE system on the steel ship’s outer shell and under water areas and other steel structures

Mixing Ratio

:


Colour

:

R (Reddish Silver), W (Silver)

Flash Point

:

Base : 23oC ; Hardener : 28oC

Solids by Volume

:

52 ± 2%


:

0.096 ~ 0.240 L/m2 ; 115 ~ 288 g/m2

Wet Film Thickness

:

96 ~ 240 µm

Dry Film Thickness

:

50 ~ 125 µm

Drying Time

(at D.F.T. 100µm)


Surface Dry 3.5 hrs. 2.5 hrs. 1.5 hrs. 1 hr.Hard Dry 38 hrs. 28 hrs. 16 hrs. 12 hrs.

Painting Interval

:

Minimum 24 hrs. 18 hrs. 10 hrs. 8 hrs.Max imum* - - - -

Pot Life

: 24 hrs. 18 hrs. 12 hrs. 8 hrs.

Thinner

:

EPICON THINNER


:

Airless spray


:


Tip No. GRACO 719, 721 Paint Output Pressure 14.7 ~ 17.7 MPa(g) Viscosity 170 sec. (Ford Cup No. 4) Thinning 0 ~ 5% by volume


:

NZ PRIMER, EPICON ZINC RICH PRIMER, CERABOND 2000, etc.


:

EPICON MARINE FINISH, EPICON MARINE HB, etc.

Packing

:

Two pack product

Notes: Please refer to the painting specification.


No. 5400 Oct. - 1999 (SHA) EPICON MARINE FINISH (EPM FC) EPICON MARINE FINISH, based on a combination of epoxy resin and polyamide curing agent, has excellent durability, and adhesion property. It is a protective finish coat for steel ships, bridges and steel structures. TECHNICAL DATA

Type

:

Epoxy/ Polyamide finish coat

Recommended Use

:

Finish coat of EPICON MARINE system of steel ships, bridges and other steel structures

Mixing Ratio

:


Colour

:

White, As specified

Flash Point

:

Base : 24°C ; Hardener : 28°C

Solids by Volume

:

51 ± 2%


:

0.059 ~ 0.098 L/m2 ; 72 ~ 120 g/m2

Wet Film Thickness

:

59 ~ 98 µm

Dry Film Thickness

:

30 ~ 50 µm

Drying Time

(at D.F.T. 40µm)



Painting Interval

(at D.F.T. 40µm)


Max imum - - - - Pot Life

: 24 hrs. 24 hrs. 18 hrs. 12 hrs.

Thinner

:

EPICON THINNER


:

Airless spray


:


Tip No. GRACO 619, 719 Paint Output Pressure 14.7 ~ 17.7 MPa (g) Viscosity 60 sec. (Ford Cup No.4) Thinning 0 ~ 5% by volume


:

BANNOH 200, BANNOH 500, EPICON MARINE HB-AL, EPICON MARINE HB-CL, etc


:

-

Packing

:

Two pack product


No. 5510 Dec. - 2000

(SHA) UNYMARINE (UM FC) UNYMARINE, based on polyurethane resin, has excellent gloss retention, durability and chemical resistance, etc. It is suitable for protection of outside of superstructure of steel ships. TECHNICAL DATA

Type

:

Polyurethane paint

Recommended Use

:

Glossy finish coat on outside of superstructure, deck and fittings

Mixing Ratio

:


Colour

:

White, As specified

Flash Point

:

Base : 18oC , Hardener : 30oC

Solids by Volume

:

51 ± 2%


:

0.059 ~ 0.098 L/m2 ; 73 ~ 122 g/m2

Wet Film Thickness

:

59 ~ 98 µm

Dry Film Thickness

:

30 ~ 50 µm

Drying Time

(at D.F.T 40µm)


Surface Dry 2 hrs. 1 hr. 40 min. 20 min.Hard Dry 16 hrs. 12 hrs. 8 hrs. 6 hrs.

Painting Interval

(at D.F.T. 40µm)

:


Pot Life

: 24 hrs. 20 hrs. 16 hrs. 8 hrs.

Thinner

:

UNYMARINE THINNER


:



:


Tip No. GRACO 515, 615, 715, 813 Paint Output Pressure 11.7 ~ 14.7 MPa(g) Viscosity 25 ~ 35 sec. (Ford Cup No.4) Thinning 5 ~ 15% by volume


:

BANNOH 500, BANNOH 200, etc.


:

-

Packing

:

Two pack product

Note: Please refer to the painting specifications.


No. 5525 Mar. - 2003

(SHA) UNY MARINE TS (UM TS) UNY MARINE TS, based on a acryl polyole resin and non-yellowing poly-isocyanate resin, has excellent physical properties such as excellent gloss retention, adhesion, impact resistance, abrasion resistance, etc. TECHNICAL DATA

Type

:

Polyurethane paint

Recommended Use

:

Glossy finish coat on outside of structure

Mixing Ratio

:


Colour

:

Black, White

Flash Point

:


Solids by Volume

:

55 ± 2%


:

0.055 ~ 0.073 L/m2 ; 71 ~ 95 g/m2

Wet Film Thickness

:

55 ~ 73 µm

Dry Film Thickness

:

30 ~ 40 µm

Drying Time

(at D.F.T 40µm)


Surface Dry 1 hr. 50 min. 30 min. 10 min.Hard Dry 20 hrs. 16 hrs. 10 hrs. 7 hrs.

Painting Interval

(at D.F.T. 40µm)

:


Pot Life

: 24 hrs. 20 hrs. 16 hrs. 8 hrs.

Thinner

:

UNYMARINE THINNER


:



:




:

EPICON MARINE UNDERCOAT M, BANNOH, etc.


:

-

Packing

:

Two pack product


No. 5601 Dec. - 1999

(SHA) BISCON AC-HB (BC AC HB) BISCON AC-HB, based on epoxy resin / coal tar combination and a curing agent, is a high-build type paint with excellent physical properties such as adhesion, toughness, impact and abrasion resistance, etc. It is also resistant to both water and sea-water and highly resistant to cathodic protection. BISCON AC-HB is suitable as a protective coating for steel ship’s bottom and under water area. TECHNICAL DATA

Type

:

Epoxy / Coal tar / Polyamide anti-corrosive paint, high-build

Recommended Use

:

Anti-corrosive for steel ship’s bottom

Mixing Ratio

:


Colour

:

Black, Brown

Flash Point

:


Solids by Volume

:

58 ± 2%


:

0.172 ~ 0.345 L/m2 ; 209 ~ 417 g/m2

Wet Film Thickness

:

172 ~ 345 µm

Dry Film Thickness

:

100 ~ 200 µm

Drying Time

(at D.F.T. 200µm)


Surface Dry 8 hrs. 3.5 hrs. 2.5 hrs. 1.5 hrs.Hard Dry 57 hrs. 36 hrs. 22 hrs. 15 hrs.


:

Minimum* 30 hrs. 22 hrs. 14 hrs. 11 hrs.M aximum 7 days 5 days 5 days 3 days

Pot Life

: 14 hrs. 10 hrs. 8 hrs. 6 hrs.

Thinner

:

EPICON THINNER


:

Airless spray


:


Tip No. GRACO 623 Paint Output Pressure 14.7 ~ 17.7 MPa(g) Viscosity 1.2 ~ 1.8 Pa.s Thinning 0 ~ 5% by volume


:

NZ PRIMER, EPICON ZINC RICH PRIMER, CERABOND 2000, etc.


:

SILVAX SQ-HB, SILVAX SQ-K, SILVAX SQ-M, etc.

Packing

:

Two pack product

Note : * If the painted surface will be exposed indirect sunlight, the succeeding coat should be applied after

minimum painting interval and possibly within 1 days to keep adhesion.


No. 5871 Mar. - 2003

(SHA) TFA-10 (TFA 10) TFA-10 is a tin free erodable anti-fouling paint with self-polishing action in service and long protection against marine organisms. The specific vehicle composition provides a unique hydrating mechanism during operation, resulting in long lasting anti-fouling performance. TECHNICAL DATA

Type

:

Tin free self-polishing anti-fouling paint

Recommended Use

:

Anti-fouling paint on steel ship’s bottom for world-wide service with extended drydocking interval

Colour

:

Dark Red, Light Red

Flash Point

:

23oC

Solids by Volume

:

55 ± 2%


:

0.182 ~ 0.273 L/m2 ; 340 ~ 510 g/m2

Wet Film Thickness

:

182 ~ 273 µm

Dry Film Thickness

:

100 ~ 150 µm

Drying Time

(at D.F.T. 100µm)


Surface Dry 3 hrs. 2 hrs. 1 hr. 30 min.H ard Dry 12 hrs. 8 hrs. 5 hrs. 4 hrs.

Painting Interval

(at D.F.T. 100µm)


M aximum - - - - Dry to launch

(at D.F.T. 100µm)


M aximum - - - - Thinner

:

RAVAX THINNER


:



:


Tip No. GRACO 621(721) ~ 635(735) Paint Output Pressure 11.7 ~ 14.7 MPa(g) Viscosity 90 sec. (For Cup No.4) Thinning 0 ~ 5% by volume


:

SILVAX SQ, VINYL AC, HIPER AC, RAVAX AC, TFA series, SEATENDER series, etc.


:

-

Packing

:

One pack product


No. 5873 Jan. - 2003

(SHA) TFA FLAT (TFA F) TFA FLAT, is a tin free anti-fouling paint with self-polishing action. The product is used for fouling control on flat bottom. TECHNICAL DATA

Type

:

Tin free self polishing anti-fouling paint

Recommended Use

:

Anti-fouling paint on steel ship’s bottom for world-wide service with extended drydocking interval

Colour

:

Red brown (Pink & Red)

Flash Point

:

23oC

Solids by Volume

:

52 ± 2%


:

0.095 ~ 0.190 L/m2 ; 179 ~ 357g/m2

Wet Film Thickness

:

95 ~ 190µm

Dry Film Thickness

:

50 ~ 100µm

Drying Time

(at D.F.T. 100µm)



Painting Interval

(at D.F.T. 100µm)

:


Dry to launch

(at D.F.T. 100µm)

:


Thinner

:

RAVAX THINNER


:



:


Tip No. GRACO 621(721) ~ 633(733) Paint Output Pressure 11.7 ~ 14.7 MPa(g) Viscosity 90 sec. (Ford Cup No.4) Thinning 0 ~ 5% by volume


:

SILVAX SQ, VINYL AC, RAVAX AC-HB, RAVAX AC-P, etc.


:

-

Packing

:

One pack product


No. 5905 Sep. - 2000

(SHA) SEA GRANDPRIX 500 (SGP 500) SEA GRANDPRIX 500 is a tin free self polishing antifouling paint based on the specific polymer with highly hydrolysis activity. Excellent antifouling effect is derived from the highly active polymer which ensures maximum effectiveness and leaching of the biocides. Activation at the surface is maintained by control of hydrolysis thus providing long term antifouling protection commensurate with applied film thickness. TECHNICAL DATA

Type

:

Tin free self polishing copolymar antifouling paint

Recommended Use

:

Antifouling paint on steel ship’s bottom for world wide service with extended dry-docking interval.

Colour

:

Red brown (Light red & Red)

Flash Point

:

27oC

Solids by Volume

:

45 ± 2%


:

0.167 ~ 0.333 L/m2 ; 276 ~ 552 g/m2

Wet Film Thickness

:

167 ~ 333 µm

Dry Film Thickness

:

75 ~ 150 µm

Drying Time

(at D.F.T. 100µm)



Painting Interval

(at D.F.T. 100µm)

:


Dry to launch

(at D.F.T. 100µm)

:


Thinner

:

RAVAX THINNER


:



:


Tip No. GRACO 621~ 723 Paint Output Pressure 11.7 ~ 14.7 MPa (g) Viscosity 1.5 ~ 2.5 Pa.s Thinning 0 ~ 5% by volume


:

SILVAX SQ-K, VINYL AC-HB, HIPER AC, RAVAX AC-HB, BANNOH 500 N, BANNOH 500 R, etc.


:

-

Packing

:

One pack product


　　

SEA GRANDPRIX 660 HS（SGP 660 HS）

Mar.2010　

No. 5904B

　

SEA GRANDPRIX 660 HS is a tin free antifouling paint with self polishing action in service and long protection against marine organisms. The specific vehicle composition provides an advanced fusion technology during operation , resulting in long lasting antifouling performance.

TECHNICAL DATA

Type Tin free self polishing antifouling paint

Recommened

Use

Antifouling paint on steel ship's bottom for world wide service with extended dry-docking interval.

Color : Brown, Light brown Flash Point : 23.0 [degC] Density : 1.93 [g/mL] Solid by volume : 67 (+-2) [volume %] VOC : 292 [g/L] Coverage(Theoretical): 0.112 - 0.224 [L/m

2

]

Information

Film Thickness : WET 112 - 224 [micron]DRY 75 - 150 [micron]

　

(DFT 100microns) 5 oC 10 oC 20 oC 30 oC

Drying Time Surface Dry 3hrs. 2hrs. 1hr. 30mins.Hard Dry 12hrs. 8hrs. 5hrs. 4hrs.

Painting Interval Min 12hrs. 8hrs. 5hrs. 4hrs.Max - - - -

Dry to Launch Min 24hrs. 18hrs. 12hrs. 10hrs.

Method of Application : Airless spray, Brush, Roller Weather : Temperature:Minimum 0

degC, Humidity:Maximum 85 %RH, Dew Point +Minimum - degC

For Airless Spray : Viscosity : (Fc#4)90[sec] Tip No. : (GRACO)621(721) - 635(735) Paint Output Pressure: 11.7 - 14.7[MPa] Spray Speed : 60 - 80[cm/sec]

Thinner : CR/ACRI THINNER A, Thinning: 0 - 5 % by Volume

Preceding Coats : SILVAX SQ-K, SILVAX SQ-M, VINYL AC-HB, RAVAX AC HB, RAVAX AC-P, HIPER AC, BANNOH 500N, BANNOH 500R

Conditionof

Application

Subsequent Coats : -

Packaging One pack product

Notes 1.There is a risk of antifoulings becoming fouled when ships are stationary for two consecutive weeks or more,particularly in areas with a high risk of fouling.2.Density and VOC are calculated from the formula of representative paint color(Brown) without thinner. And there are various value depending on color and such.


No. 5909 Sep. - 2000

(SHA) SEA GRANDPRIX 1000 (SGP 1000) SEA GRANDPRIX 1000 is a tin free self polishing antifouling paint based on the specific polymer with highly hydrolysis activity. Excellent antifouling effect is derived from the highly active polymer which ensures maximum effectiveness and leaching of the biocides. Activation at the surface is maintained by control of hydrolysis thus providing long term antifouling protection commensurate with applied film thickness. TECHNICAL DATA

Type

:

Tin free self polishing copolymer antifouling paint

Recommended Use

:


Colour

:

Red brown (Light red & Red), As specified

Flash Point

:

27oC

Solids by Volume

:

44 ± 2%


:

0.170 ~ 0.340 L/m2 ; 289 ~ 578 g/m2

Wet Film Thickness

:

170 ~ 340 µm

Dry Film Thickness

:

75 ~ 150 µm

Drying Time

(at D.F.T. 100µm)



Painting Interval

(at D.F.T. 100µm)

:


Dry to launch

(at D.F.T. 100µm)

:


Thinner

:

RAVAX THINNER


:



:


Tip No. GRACO 621 ~ 723 Paint Output Pressure 11.7 ~ 14.7 MPa (g) Viscosity 1.5 ~ 2.5 Pa.s Thinning 0 ~ 5% by volume


:

SILVAX SQ-K, VINYL AC-HB, HIPER AC, RAVAX AC-HB, BANNOH 500 N, BANNOH 500 R, etc.


:

-

Packing

:

One pack product


No. 5917K Sep. - 2002

(SHA) SEA GRANDPRIX CF 10 (SGP CF10) SEA GRANDPRIX CF-10, tin and copper free self polishing antifouling paint based on the specific polymer, is designed for the overseas ships. Excellent antifouling effect is derived from the highly active hydrolysis polymer which ensures maximum effectiveness and leaching of the biocides. Activation at the surface is maintained by control of hydrolysis thus providing long term antifouling protection commensurate with the applied film thickness. TECHNICAL DATA

Type

:

Tin and copper free self polishing copolymer antifouling

Recommended Use

:


Colour

:

Red, Light red

Flash Point

:

26.7oC

Solids by Volume

:

45 ± 2%


:

0.167 L/m2

Wet Film Thickness

:

167 ~ 356 µm

Dry Film Thickness

:

75 ~ 160 µm

Drying Time

(at D.F.T. 100µm)



Painting Interval

(at D.F.T. 100µm)

:


Dry to launch

(at D.F.T. 100µm)

:


Thinner

:

RAVAX THINNER


:



:


Tip No. GRACO 621 ~ 723 Paint Output Pressure 11.7 ~ 14.7 MPa (g) Viscosity 1.5 ~ 2.5 Pa.s Thinning 0 ~ 5% by volume


:

BANNOH 500 N, SILVAX SQ-K, HIPER AC, etc.


:

-

Packing

:

One pack product

Note: There is a risk of antifouling becoming fouled when ships are stationary for three consecutive

weeks or more, particularly in areas with a high risk of fouling.


No. 5950 May - 1997

(SHA) SEATENDER 7 (ST 7) SEATENDER 7 is a tin free anti-fouling paint. The product is used for fouling control on ship bottom. TECHNICAL DATA

Type

:

Tin free anti-fouling paint

Recommended Use

:

Anti-fouling paint on steel ship’s bottom for world wide service with extended dry-docking interval.

Colour

:

Red brown

Flash Point

:

26oC

Solids by Volume

:

49 ± 2%


:

0.153 L/m2 ; 276 g/m2

Wet Film Thickness

:

153 µm

Dry Film Thickness

:

75 µm

Drying Time

(at D.F.T. 100µm)


Surface Dry 45 min. 30 min. 20 min. 15 min.Hard Dry 6 hrs. 4.5 hrs. 35 hrs. 2 hrs.

Painting Interval

(at D.F.T. 100µm)

:


Dry to launch

(at D.F.T. 100µm)

:


Thinner

:

RAVAX THINNER


:



:


Tip No. GRACO 621, 629 Paint Output Pressure 11.7 ~ 14.7 MPa (g) Viscosity 60 ~ 80 sec. (Ford Cup No. 4) Thinning 0 ~ 5% by volume


:

SILVAX SQ, VINYL AC, RAVAX AC, etc.


:

-

Packing

:

One pack product


No. 5955 May - 1997

(SHA) SEATENDER 10 (ST 10) SEATENDER 10 is a tin free erodable anti-fouling paint. The product is used for fouling control on ship bottom. TECHNICAL DATA

Type

:

Tin free erodable anti-fouling paint

Recommended Use

:

Anti-fouling paint on steel ship’s bottom for world wide service with extended dry-docking interval.

Colour

:

Dark Red, Light Red

Flash Point

:

23oC

Solids by Volume

:

52 ± 2%


:

0.095 ~ 0.190 L/m2 ; 179 ~ 357 g/m2

Wet Film Thickness

:

95 ~ 190 µm

Dry Film Thickness

:

50 ~ 100 µm

Drying Time

(at D.F.T. 100µm)



Painting Interval

(at D.F.T. 100µm)

:


Dry to launch

(at D.F.T. 100µm)

:


Thinner

:

RAVAX THINNER


:



:


Tip No. GRACO 621(721), 633(733) Paint Output Pressure 11.7 ~ 14.7 MPa (g) Viscosity 90 sec. (Ford Cup No. 4) Thinning 0 ~ 5% by volume


:

SILVAX SQ, VINYL AC, RAVAX AC


:

-

Packing

:

One pack product


No. 5957 May - 1997

(SHA) SEATENDER 12 (ST 12) SEATENDER 12 is a tin free anti-fouling paint with polishing action in service and long protection against marine organisms. The specific vehicle composition provides long lasting anti-fouling performance and polishing action. TECHNICAL DATA

Type

:


Recommended Use

:

Anti-fouling paint on steel ship’s bottom for world-wide service with extended dry-docking interval.

Colour

:

Dark Red, Light Red

Flash Point

:

23oC

Solids by Volume

:

51 ± 2%


:

0.196 ~ 0.294 L/m2 ; 350 ~ 525 g/m2

Wet Film Thickness

:

196 ~ 294 µm

Dry Film Thickness

:

100 ~ 150 µm

Drying Time

(at D.F.T. 100µm)



Painting Interval

(at D.F.T. 100µm)

:


Dry to launch

(at D.F.T. 100µm)

:


Thinner

:

RAVAX THINNER


:



:


Tip No. GRACO 621(721) ~ 635(735) Paint Output Pressure 11.7 ~ 14.7 MPa (g) Viscosity 90 sec. (Ford Cup No. 4) Thinning 0 ~ 5% by volume


:

SILVAX SQ, VINYL AC, RAVAX AC, TFA, SEATENDER, etc.


:

-

Packing

:

One pack product


No. 5960 May - 1997

(SHA) SEATENDER 15 (ST 15) SEATENDER 15 is a tin free anti-fouling paint with polishing action in service and long protection against marine organisms. The specific vehicle composition provides long lasting anti-fouling performance and polishing action. TECHNICAL DATA

Type

:


Recommended Use

:

Anti-fouling paint on steel ship’s bottom for world-wide service with extended dry-docking interval.

Colour

:

Dark Red, Light Red

Flash Point

:

23oC

Solids by Volume

:

51 ± 2%


:

0.196 ~ 0.294 L/m2 ; 350 ~ 525 g/m2

Wet Film Thickness

:

196 ~ 294 µm

Dry Film Thickness

:

100 ~ 150 µm

Drying Time

(at D.F.T. 100µm)



Painting Interval

(at D.F.T. 100µm)

:


Dry to launch

(at D.F.T. 100µm)

:


Thinner

:

RAVAX THINNER


:



:


Tip No. GRACO 621(721) ~ 635(735) Paint Output Pressure 11.7 ~ 14.7 MPa (g) Viscosity 90 sec. (Ford Cup No. 4) Thinning 0 ~ 5% by volume


:

SILVAX SQ, VINYL AC, RAVAX AC, HIPER AC, TFA, SEATENDER, etc. Existing AF: SEAFLO


:

-

Packing

:

One pack product


No. 6072 Jan. - 2001 (SHA) CLEANKEEP 5000 CLEANKEEP 5000, solvent-free epoxy paint, is designed as a protective coating of drinking water tank. CLEANKEEP 5000 is friendly to the environment as it provides no solvent, no heavy metal and less wasted material while coating. CLEANKEEP 5000 could be coated by airless spray. TECHNICAL DATA

Type

:

Solventfree epoxy coating

Recommended Use

:

Fresh water tank, Drinking water tank

Mixing Ratio

:


Colour

:

Cream

Flash Point

:

Base : <250oC Hardener : 155oC

Solids by Volume

:

100%


:

0.300 L/m2 ; 444 g/m2

Wet Film Thickness

:

300 µm

Dry Film Thickness

:

300 µm

Drying Time (at D.F.T 300µm)

: Temperature 10oC 20oC 30oC

Surface Dry 45 hrs. 18 hrs. 11 hrs. Hard Dry 4 days 32 hrs. 24 hrs.

Painting Interval (at D.F.T 300µm)

:

Minimum 4 days 32 hrs. 24 hrs. M aximum 14 days 14 days 14 days

Pot Life

: 1.5 hrs. 1 hr. 45 min.

Thinner

:

EPICON THINNER ( for cleaning only)


:



:


Tip No. GRACO 619 ~ 721 Paint Output Pressure 23.5 ~ 33.4 MPa (g) Viscosity 30 ~ 40 poise by Rion viscidity meterThinning -


:

WELBOND, CERABOND 2000, EPICON ZINC RICH PRIMER, NZ PRIMER


:

-

Packaging

:

Two pack product

Notes: Certificated by the test of quality of Drinking Water as follows:

- Hiroshima City Research Laboratory of Public Health - JAPAN

- Public Utilities Board - Singapore

- WRAS (Water Regulations Advisory Scheme recognized by Ministry of Defense UK)


No. 6110 Oct. - 1999 (SHA) BISCON HB (B/C HB) BISCON HB, high-build epoxy/ coal tar paint, gives in one cross-layer, a film thickness of 200 ~ 300 microns. The advantages of BISCON HB include better mechanical properties such as adhesion, toughness and abrasion resistance, etc. It also offers chemical resistance to salt-water, crude oil, alkalis and dilute acids. It is suitable for protective coating of crude oil tanks, ballast tanks interior and underwater areas, etc. BISCON HB has been approved as a Corrosion Control System by Lloyd’s Register of Shipping. TECHNICAL DATA

Type

:

Epoxy/coal tar anti (one coat system) tank coating, high-build

Recommended Use

:

Crude oil tank, Ballast tank, Void space, Cofferdam, Cargo hold, Underwater areas, other steel structures, etc.

Mixing Ratio

:


Colour

:

Black, Brown

Flash Point

:


Solids by Volume

:

67 ± 2%


:

0.186 ~ 0.373 L/ m 2 ; 236 ~ 473 g/m 2

Wet Film Thickness

:

186 ~ 373 µm

Dry Film Thickness

:

125 ~ 250 µm

Drying Time

(at D. F. T. 250µm)


Surface Dry 5 hrs. 4 hrs. 3 hrs. 1 hr.Hard Dry 44 hrs. 30 hrs. 16 hrs. 12 hrs.

Painting Interval (at D. F. T. 250µm)

:

Minimum 44 hrs. 30 hrs. 16 hrs. 12 hrs.M aximum* 7 days 5 days 5 days 2 days

Pot Life

: 10 hrs. 90 hrs. 7 hrs. 5 hrs.

Thinner

:

EPICON THINNER


:



:


Tip No. GRACO 623 Paint Output Pressure 14.7 ~ 17.7 MPa(g) Viscosity 1.5 ~2.0 Pa.s Thinning 0 ~ 5% by volume


:

CERABOND 2000, EPICON ZINC RICH PRIMER, NZ PRIMER


:

-

Packaging

:

Two pack product

Notes: In confined spaces such as tank insides ventilation is required during application and curing to removed

solvent vapours are promote curing. * If there is a possibility that the painted surface will be in direct sunlight, the succeeding coat should be applied as soon as possible after the minimum painting interval. Waiting time before the first cargo loading Temp. 10oC 20oC 30oC (Days) 24 14 9


No. 6112 Oct. - 1999

(SHA)

BISCON HB-200 (BC HB-200) BISCON HB-200, high-build epoxy / coat tar paint, gives in one cross-layer, a film thickness of 200 ~ 300 microns. The advantages of BISCON HB-200 include better mechanical properties such as adhesion, toughness and abrasion resistance, etc. It also offers chemical resistance to salt-water, alkalis and dilute acids. It is suitable for protective coating of ballast tanks interior and underwater areas, etc. TECHNICAL DATA

Type

:

Epoxy / coal tar (one coat system) tank coating, high-build

Recommended Use

:

Ballast tank, Void space, Cofferdam, Cargo hold, Underwater area etc.

Mixing Ratio

:


Colour

:

Black, Brown

Flash Point

:

Base : 23°C , Hardener : 13°C

Solids by Volume

:

67 ± 2%


:

0.187 ~ 0.373 L/m2 ; 247 ~ 492 g/m2

Wet Film Thickness

:

187 ~ 373 µm

Dry Film Thickness

:

125 ~ 250 µm

Drying Time

(at D.F.T. 250µm)


Surface Dry 6 hrs. 5 hrs. 4 hrs. 2 hrs.Hard Dry 48 hrs. 36 hrs. 18 hrs. 13 hrs.

Painting Interval

(at D.F.T. 250µm)

:

Minimum 48 hrs. 36 hrs. 18 hrs. 13 hrs.Maximum* 7 days 5 days 5 days 2 days

Pot Life

: 14 hrs. 10 hrs. 8 hrs. 6 hrs.

Thinner

:

EPICON THINNER


:



:




:

CERABOND 2000, NZ PRIMER, EPICON ZINC RICH PRIMER


:

-

Packing

:

Two pack product

Notes: In confined spaces such as tank insides ventilation is required during application and curing to remove solvent vapours are promote curing. * If there is a possibility that the painted surface will be in direct sunlight, the succeeding coat should be applied as soon as possible after the minimum painting interval. Waiting time before the first cargo loading Temp. 10oC 20oC 30oC (Days) 24 14 9 “BISCON QL HB-200” is selected for the application at cold weather.


No. 6135A Oct. - 1999

(SHA) BISCON HB-NT L (BC HB NT L) BISCON HB-NT L is a modified epoxy paint. It gives excellent physical properties such as adhesion, toughness and abrasion resistance, etc. and chemical resistance to water, salt water and crude oil. TECHNICAL DATA

Type

:

Modified epoxy paint

Recommended Use

:

Cargo hold, Inside and outside of accommodation space, Void space, Cofferdam, Engine room, Pipe line. Other steel structures, etc.

Mixing Ratio

:


Colour

:

Grey, Black, White, Red brown, Green

Flash Point

:


Solids by Volume

:

57 ± 2%


:

0.176 ~ 0.439 L/m2 ; 239 ~ 597 g/m2

Wet Film Thickness

:

176 ~ 439 µm

Dry Film Thickness

:

100 ~ 250 µm

Drying Time

(at D.F.T. 250µm)


Surface Dry 4.5 hrs. 3.5 hrs. 2.5 hrs. 1.5 hrs.Hard Dry 44 hrs. 27 hrs. 17 hrs. 12 hrs.


:

Minimum* 44 hrs. 27 hrs. 17 hrs. 12 hrs.Maximum - - - -

Pot Life

: 24 hrs. 14 hrs. 8 hrs. 5 hrs.

Thinner

:

EPICON THINNER


:



:


Tip No. GRACO 623 Paint output Pressure 14.7 ~ 17.7 MPa(g) Viscosity 1.5 ~2.0 Pa.s Thinning 0 ~ 5% by volume


:

WELBOND, CERABOND, NZ PRIMER, EPICON ZINC RICH PRIMER


:

-

Packing

:

Two pack product

Notes : In confined spaces such as tank insides, ventilation is required during application and curing to remove

solvent vapours and promote curing. Waiting time before the first cargo loading Temp. 10oC 20oC 30oC (Days) 20 12 7


No. 6135H May - 2000

(SHA) UMEGUARD SX (UG SX) UMEGUARD SX, surface tolerant paint, is a modified epoxy paint. It gives excellent physical properties such as adhesion, toughness and abrasion resistance, etc. and chemical resistance to water, salt water and crude oil. TECHNICAL DATA

Type

:

Modified epoxy paint

Recommended Use

:

Cargo hold, Inside and outside of accommodation space, Void space, Cofferdam, Engine room, Pipe line. Other steel structures, etc.

Mixing Ratio

:


Colour

:

Grey, Black, White, Red brown, Green

Flash Point

:


Solids by Volume

:

58 ± 2%


:

0.172 ~ 0.431 L/m2 ; 230 ~ 578 g/m2

Wet Film Thickness

:

172 ~ 431 µm

Dry Film Thickness

:

100 ~ 250 µm

Drying Time

(at D.F.T. 250µm)


Surface Dry 4.5 hrs. 3.5 hrs. 2.5 hrs. 1.5 hrs.Hard Dry 44 hrs. 27 hrs. 17 hrs. 12 hrs.


:

Minimum* 38 hrs. 20 hrs. 14 hrs. 10 hrs.M aximum - - - -

Pot Life

: 24 hrs. 14 hrs. 8 hrs. 5 hrs.

Thinner

:

EPICON THINNER


:



:


Tip No. GRACO 623 Paint Output Pressure 14.4 ~ 17.7MPa(g) Viscosity 1.5 ~2.0 Pa.s Thinning 0 ~ 5% by volume


:

CERABOND 2000, NZ PRIMER, EPICON ZINC RICH PRIMER, etc.


:

-

Packing

:

Two pack product

Note : In confined spaces such as tank insides, ventilation is required during application and curing to remove

solvent vapours and promote curing.


No. 6180C Jan. - 2003 (SHA) NOVA 1000 (NV 1000) NOVA 1000 is tar free modified epoxy paint, based on modified epoxy, pigmentation. It gives excellent physical properties such as adhesion, toughness and abrasion resistance, etc. and chemical resistance to water, salt water and oils. It is suitable for protection of water tank interior. TECHNICAL DATA

Type

:

Tar free modified epoxy paint

Recommended Use

:

Ballast water tank, Crude oil tank, Cargo hold, Void space, Cofferdam

Mixing Ratio

:


Colour

:

Light grey, Cream

Flash Point

:


Solids by Volume

:

70 ± 2%


:

0.143 ~ 0.357 L/m2 ; 190 ~ 475 g/m2

Wet Film Thickness

:

143 ~ 357 µm

Dry Film Thickness

:

100 ~ 250 µm

Drying Time

(at D.F.T. 250µm)

:

Temperature 10oC 20oC 30oCSurface Dry 7 hrs. 4 hrs. 2 hrs.Hard Dry 28 hrs. 15 hrs. 10 hrs.

Painting Interval

(at D.F.T. 250µm)

:

Minimum 28 hrs. 15 hrs. 10 hrs.Maximum 15 days 10 days 7 days

Pot Life

:

10 hrs. 6 hrs. 4 hrs.

Thinner

:

EPICON THINNER


:

Airless spray


:


Tip No. GRACO 621, 623 Paint Output Pressure 14.7 ~ 17.7 MPa(g) Viscosity 1.5 ~2.0 Pa.s Thinning 0 ~ 7% by volume


:

CERABOND 2000, EPICON ZINC RICH PRIMER, NZ PRIMER


:

-

Packing

:

Two pack product

Notes: In confined spaces such as tank insides, ventilation is required during application and curing to remove

solvent vapours and promote curing. If there is a possibility that the painted surfaced will be in direct sunlight, the succeeding coat should be applied as soon as possible after the minimum painting interval.


No. 6181 May - 2002 (SHA) NOVA 2000 (NV 2000) NOVA 2000 is tar free high solid modified epoxy paint, based on modified epoxy, pigmentation. It gives excellent physical properties such as adhesion, toughness and abrasion resistance, etc. and chemical resistance to water, salt water and oils. It is suitable for protection of water tank interior. TECHNICAL DATA

Type

:

Tar free high solid modified epoxy paint

Recommended Use

:

Ballast water tank, Crude oil tank, Cargo hold, Void space, Cofferdam

Mixing Ratio

:


Colour

:

Light grey, Cream

Flash Point

:


Solids by Volume

:

80 ± 2%


:

0.156 ~ 0.313 L/m2 ; 223 ~ 447 g/m2

Wet Film Thickness

:

156 ~ 313 µm

Dry Film Thickness

:

125 ~ 250 µm

Drying Time

(at D.F.T. 250µm)


Surface Dry 12 hrs. 6 hrs. 4 hrs. Hard Dry 24 hrs. 15 hrs. 12 hrs.


:

Minimum 24 hrs. 15 hrs. 12 hrs. M aximum 15 days 10 days 7 days

Pot Life

: 5 hrs. 3 hrs. 2 hrs.

Thinner

:

EPICON THINNER


:

Airless spray


:


Tip No. GRACO 621, 623 Paint Output Pressure 14.7 ~ 17.7 MPa(g) Viscosity 1.5 ~2.0 Pa.s Thinning 0 ~ 7% by volume


:

CERABOND 2000, NZ PRIMER, EPICON ZINC RICH PRIMER,


:

-

Packing

:

Two pack product

Notes : In confined spaces such as tank insides, ventilation is required during application and curing to remove

solvent vapours and promote curing. If there is a possibility that the painted surfaced will be in direct sunlight, the succeeding coat should be applied as soon as possible after the minimum painting interval.


No. 6182 Nov. - 2000 (SHA) NOVA 5000 (NV 5000) NOVA 5000, solvent-free epoxy tank coating, is designed as a protective coating of ballast water tanks and cargo oil tanks. It has excellent water/sea-water resistance and has also superior crude oil resistance. NOVA 5000 is eco-friendly to the environment as it contains no solvent, no heavy metal. NOVA 5000 can be coated by conventional airless spray. TECHNICAL DATA

Type

:

Solvent-free epoxy coating

Recommended Use

:

Ballast water tank, Crude oil tank, Void space, Cofferdam, Hold of ships, Bridges, Underground pipes, Port facilities, etc.

Mixing Ratio

:


Colour

:

Light Grey

Flash Point

:

Base : 250< °C , Hardener : 155°C

Solids by Volume

:

100%


:

0.300 L/m2 ; 399 g/m2

Wet Film Thickness

:

300 µm

Dry Film Thickness

:

300 µm

Drying Time

(at D.F.T. 300µm)

:

Temperature 10oC 20oC 30oCSurface Dry 45 hrs. 18 hrs. 11 hrs.Hard Dry 3 days 24 hrs. 16 hrs.

Painting Interval

(at D.F.T. 300µm)

:

Minimum 3 days 24 hrs. 16 hrs.Maximum 14 days 14 days 14 days

Pot Life

:

1.5 hrs. 1 hr. 45 min.

Thinner

:

EPICON THINNER (for cleaning purpose)


:



:


Tip No. GRACO 619 ~ 721 Paint Output Pressure 23.5 ~ 33.4 MPa(g) Viscosity - Thinning -


:

CERABOND 2000, EPICON ZINC RICH PRIMER, NZ PRIMER-


:

-

Packing

:

Two pack product


No. 6341 Oct. - 1999 (SHA) APERIA No. 3000 HB (AP 3000 HB) APERIA No. 3000 HB, based on a special tar pitch and synthetic resin combination, gives in one cross-layer, a film thickness of 200 microns. It has good physical properties such as excellent adhesion, toughness, and abrasion resistance and good resistance to water and salt water. It is suitable for protective coating of steel surface. APERIA No. 3000 HB is an economical protective coating compared with epoxy and coal tar paint. TECHNICAL DATA

Type

:

Bituminous paint, high-build type

Mixing Ratio

:


Colour

:

Black

Flash Point

:

11oC

Solids by Volume

:

50 ± 2%


:

0.200 ~ 0.400 L/ m 2 ; 260 ~ 520 g/m 2

Wet Film Thickness

:

200 ~ 400 µm

Dry Film Thickness

:

100 ~ 200 µm

Drying Time

(at D. F. T. 200µm)


Surface Dry 5 hrs. 4 hrs. 3 hrs. 2 hrs.H ard Dry 24 hrs. 22 hrs. 21 hrs. 20 hrs.

Painting Interval

(at D. F. T. 200µm)

: Minimum 24 hrs. 22 hrs. 21 hrs. 20 hrs.Maximum - - - -

Thinner

: APERIA No. 3000 THINNER


:



:


Tip No. GRACO 621, 623 Paint Output Pressure 14.7 ~ 17.7 MPa(g) Viscosity 1.6 ~ 1.8 Pa.s Thinning 0 ~ 5% by volume


:

CERABOND 2000, EPICON ZINC RICH PRIMER, NZ PRIMER, etc.


:

-

Packaging

:

One pack product

Note : In confined spaces such as tank insides and void spaces, etc., ventilation is required during application and

curing to remove vapour and promote hardening.


No. 8009 Mar. - 2000

(SHA) SILICON No. 400 PRIMER (SN 400 PR) SILICON No.400 PRIMER is a silicon resin primer based on a combination of silicon resin, pigments and curing accelerator. It has the following characteristics. 1. It has excellent heat resistance. It withstands temperature up to 400oC. 2. It has excellent adhesion to metal surface. 3. It has excellent weathering resistance. TECHNICAL DATA

Type

:

Silicon resin heat resisting paint

Recommended Use

:

Boiler, Cylinder of engine, inside of exhaust pipes, Radiator, Stove, Oil burner, etc.

Mixing Ratio

:

Base : Curing accelerator * = 73 : 1 (by volume)

Colour

:

White

Flash Point

:

Base : 19oC Curing accelerator : 38oC

Solids by Volume

:

38 ± 2%


:

0.053 ~ 0.079 L/m2 ; 72 ~ 108 g/m2

Wet Film Thickness

:

53 ~ 79 µm

Dry Film Thickness

:

20 ~ 30 µm

Drying Time

(at D.F.T. 25µm)


Surface Dry 1 hr. 50 min. 30 min. 20 min.Hard Dry 7 hrs. 5 hrs. 3 hrs. 1 hr.


:


Pot Life

: 32 hrs. 28 hrs. 24 hrs. 16 hrs.

Thinner

:

SILICON THINNER


:



:


Tip No. GRACO 415 Paint Output Pressure 8.8 ~ 11.8 MPa(g) Viscosity 25 ~ 35 sec. (Ford Cup No. 4) Thinning 5 ~ 10% by volume


:

-


:

SILICON No. 400 SILVER, SILICON No. 400 ENAMEL

Packing

:

Two pack product

Note : Paint film should be backed for 2 hours at 200oC to complete curing.


No. 8010 Mar. - 2000

(SHA) SILICON No. 400 SILVER (SN 400 SIL) SILICON No.400 SILVER is a silicon resin aluminium paint based on a combination of silicon resin and aluminium pigment. It has the following characteristics. 1. It has excellent heat resistance. It withstands temperature up to 400°C. 2. It has excellent adhesion to SILICON No.400 PRIMER. 3. It has excellent weathering resistance. TECHNICAL DATA

Type

:

Silicon resin heat resisting aluminium paint

Recommended Use

:

Boiler, Cylinder of engine, inside of exhaust pipes, Radiator, Stove, Oil burner, etc.

Colour

:

Silver

Flash Point

:

22.3oC

Solids by Volume

:

25 ± 2%


:

0.040 ~ 0.080 L/m2 ; 43 ~ 86 g/m2

Wet Film Thickness

:

40 ~ 80 µm

Dry Film Thickness

:

10 ~ 20 µm

Drying Time

(at D.F.T. 15µm)


Surface Dry 1 hr. 50 min. 30 min. 20 min.Hard Dry 7 hrs. 5 hrs. 3 hrs. 1 hr.

Painting Interval

(at D.F.T. 15µm)

:


Thinner

:

SILICON THINNER


:



:


Tip No. GRACO 415 Paint Output Pressure 8.8 ~ 11.8 MPa(g) Viscosity 10 ~ 20 sec. (Ford Cup No. 4) Thinning 5 ~ 10% by volume


:

SILICON No. 400 PRIMER


:

-

Packing

:

One pack product


No. 8220 Oct. - 1999 (SHA) GALVANITE No.200 PRIMER (GNT 200P) GALVANITE No.200 PRIMER is used for painting galvanized steel on superstructure, tank and other parts. It is highly effective paint system with excellent adhesion property on galvanized steel surface, and has excellent salt water resistance. TECHNICAL DATA

Type

:

Epoxy resin paint

Recommended Use

:

As a primer on galvanized steel

Mixing Ratio

:


Colour

:

White

Flash Point

:

Base : 17OC , Hardener : 6oC

Solids by Volume

:

38 ± 2%


:

0.079 ~ 0.131 L/m2 ; 107 ~ 178 g/m2

Wet Film Thickness

:

39 ~ 131µm

Dry Film Thickness

:

30 ~ 50 µm

Drying Time

(at D.F.T. 40µm)



Painting Interval

(at D.F.T. 40µm)

:


Pot Life

:

36 hrs. 30 hrs. 24 hrs. 12 hrs.

Thinner

:

GALVANITE No. 200 THINNER


:



:


Tip No. GRACO 719, 619 Paint Output Pressure 10.7 ~ 13.8 MPa(g) Viscosity 55 ~ 65 sec. (Ford Cup No. 4) Thinning 5 ~ 10% by volume


:

-


:

EVAMARINE, RAVAX PRIMER, EPICON MARINE, etc.

Packing

:

Two pack product


No. 8250 Oct. - 1999 (SHA) RUST INHIBITIVE OIL ″CK″ (RIO CK) RUST INHIBITIVE OIL ″CK″, based on special petroleum resin and mineral spirit, is a temporary protective primer for fuel oil tanks. TECHNICAL DATA

Type

:

Petroleum resin

Colour

:

Clear

Flash Point

:

43OC

Solids by Volume

:

43 ± 2%


:

0.043 L/m2 ; 40 g/m2

Wet Film Thickness

:

41µm

Dry Film Thickness

:

20 µm

Drying Time

(at D.F.T. 20µm)


Surface Dry 1 hr. 30 min. 15 min. 5 min.Hard Dry 4 hrs. 2 hrs. 1 hr. 30 min.

Painting Interval

:

Minimum - - - -Maximum - - - -

Thinner

:

MARINE THINNER


:



:


Tip No. GRACO 615, 717 Paint Output Pressure 10.7 ~ 13.8 MPa(g) Viscosity 90 sec. (Ford Cup No. 4) Thinning -


:

-


:

-

Packing

:

One pack product

Notes: The ingredients of this product will be dissolved by the fuel oil but they do not affect the quality of the fuel oil

at all.


No. 2104A Oct. - 1999

(SHA) LZI PRIMER ZR-HB (LZI ZR HB) LZI PRIMER ZR-HB, based on alkali-resistance synthetic resin, contains special compound which can make zinc surfaces stable. It has excellent adhesion property on zinc rich shop primer, as well as salt-water and weathering resistance. TECHNICAL DATA

Type

:

Special synthetic resin primer

Recommended Use

:

As the 1st coat of primer, when a conventional paint system is specified on zinc shop primer.

Colour

:

Dark brown

Flash Point

:

36oC

Solids by Volume

:

49 ± 2%


:

0.061 ~ 0.143 L/m2 ; 83 ~ 196 g/m2

Wet Film Thickness

:

61 ~ 143 µm

Dry Film Thickness

:

30 ~ 70 µm

Drying Time

(at D.F.T. 70µm)


Surface Dry 6 hrs. 3 hrs. 1.5 hrs. 45 min.Hard Dry 24 hrs. 14 hrs. 7 hrs. 4 hrs.


:


Thinner

: MARINE THINNER


:

Airless spray, Brush*, Roller

Condition for application

:


Tip No. GRACO 719 Paint output pressure 14.7 ~ 17.7 MPa(g) Viscosity 1.0 ~ 2.0 Pa.s Thinning 0 ~ 5% by volume


:

EVABOND, WELBOND, NZ PRIMER etc.


:

EVAMARINE, EVAMARINE HB, Alkyd resin based paints

Packing

:

One pack product

Note : * Sufficient thickness is difficult to obtain by brush.


No. 4003 May - 1997 (SHA) RAVAX AC P (RX AC P) RAVAX AC P, based on chlorinated rubber, dries quickly and provides effective protection against corrosion and good adhesion between the film as well as to shop primers and subsequent coats. It also possesses sea water resistance and shows good adhesion to subsequent coats even after prolonged weathering. TECHNICAL DATA

Type

:

Chlorinated rubber anti-corrosive paint, high build

Recommended Use

:


Colour

:

SR (Pinkish Silver), S (Silver)

Flash Point

:

27oC

Solids by Volume

:

42 ± 2%


:

0.095 ~ 0.179 L/m2 ; 124 ~ 232 g/m2

Wet Film Thickness

:

95 ~ 179 µm

Dry Film Thickness

:

40 ~ 75 µm

Drying Time

(at D.F.T. 60µm)


Surface Dry 1 hr. 45 min. 30 min. 25 min.H ard Dry 6 hrs. 4.5 hrs. 3 hrs. 2.5 hrs.

Painting Interval

(at D.F.T. 60µm)

:


Thinner

:

RAVAX THINNER


:



:




:



:

RAVAX AF, RAVAX FINISH, TFA-10. 20. 30, etc.

Packing

:

One pack product


No. 5055 Dec. - 2000

(SHA) BANNOH 500 (B 500) BANNOH 500 is a multi-purpose primer, which gives excellent physical properties such as toughness, abrasion resistance and adhesion, etc., and has excellent flexibility, resistance to sea water and catholic protection. It is suitable for most areas of ship. TECHNICAL DATA

Type

:

Pure epoxy paint

Recommended Use

:

Anti-corrosive for ship’s hull, exposed decks, superstructures and ballast water tanks, etc.

Mixing Ratio

:


Colour

:

Grey , Red brown

Flash Point

:


Solids by Volume

:

63 ± 2%


:

0.159 ~ 0.317 L/m2 ; 208 ~ 416 g/m2

Wet Film Thickness

:

159 ~ 317 µm

Dry Film Thickness

:

100 ~ 200 µm

Drying Time

(at D.F.T. 200µm)


Surface Dry 7 hrs. 5.5 hrs. 4 hrs. 2.5 hrs.H ard Dry 24 hrs. 18 hrs. 10 hrs. 8 hrs.

Painting Interval

(at D.F.T. 200µm)

:

Minimum 24 hrs. 18hrs. 10 hrs. 8 hrs.M aximum* - - - -

Pot Lift

: 18 hrs. 14 hrs. 7 hrs. 4 hrs.

Thinner

:

EPICON THINNER


:



:


Tip No. GRACO 623 Paint Output Pressure 14.7 ~ 17.7 MPa(g) Viscosity 1.2 ~1.8 Pa.s Thinning 0 ~ 5% by volume


:

CERABOND 2000, EPICON ZINC RICH PRIMER, etc.


:

BANNOH 500 N, SILVAX SQ-K, SILVAX SQ-M, EPICON MARINE HB, etc.

Packing

:

Two pack product

Note : Kindly consult with CMP sales office.


No. 5073 Dec. - 2000

(SHA) BANNOH 500 N (B 500 N) BANNOH 500 N is tar free, epoxy anti-corrosive primer, based on pure epoxy resin and pigmentation. It gives excellent physical properties such as toughness and abrasion resistance, adhesion, especially excellent adhesion with anti-fouling paint. TECHNICAL DATA

Type

:

Pure epoxy paint

Recommended Use

:

Anti-corrosive paint for ship’s bottom

Mixing Ratio

:


Colour

:

Plum

Flash Point

:

Base : 22oC , Hardener : 23.5oC

Solids by Volume

:

60 ± 2%


:

0.125 ~ 0.292 L/m2 ; 169 ~ 394 g/m2

Wet Film Thickness

:

125 ~ 292 µm

Dry Film Thickness

:

75 ~ 175 µm

Drying Time

(at D.F.T. 100µm)


Surface Dry 5 hrs. 4 hrs. 3 hrs. 2 hrs.H ard Dry 18 hrs. 15 hrs. 8 hrs. 6 hrs.

Painting Interval

(at D.F.T. 100µm)

:

Minimum 18 hrs. 15 hrs. 8 hrs. 6 hrs.M aximum* - - - -

Pot Lift

: 18 hrs. 14 hrs. 7 hrs. 4 hrs.

Thinner

:

EPICON THINNER


:



:




:

BANNOH 500


:

SEA GRANDPRIX 500,1000,2000, etc.

Packing

:

Two pack product

Note : * Please refer to the painting specifications.


No. 5101 Oct. - 1999

(SHA)

EPICON MARINE HB-CL (EPM HB CL) EPICON MARINE HB-CL is a combination of epoxy resin/ rust-preventive pigment and a curing agent. It has excellent adhesion property, toughness, impact and abrasion resistance, and effective rust-preventing properties. It is suitable for protection of superstructures and exposed deck of steel ships, bridges and steel structures. TECHNICAL DATA

Type

:

Epoxy/ Polyamide rust-preventing paint high-build

Recommended Use

:

Primer of EPICON MARINE system on inside and outside of superstructures, exposed deck of steel ship’s, bridge and other steel structures.

Mixing Ratio

:


Colour

:

R (Reddish orange), W (Light orange)

Flash Point

:


Solids by Volume

:

54 ± 2%


:

0.093 ~ 0.231 L/m2 ; 120 ~ 300 g/m2

Wet Film Thickness

:

93 ~ 231µm

Dry Film Thickness

:

50 ~ 125µm

Drying Time

(at D.F.T. 100µm)



Painting Interval

(at D.F.T. 100µm)



: 24 hrs. 18 hrs. 12 hrs. 8 hrs.

Thinner

:

EPICON THINNER


:

Airless spray


:


Tip No. GRACO 719, 721 Paint Output Pressure 14.7 ~ 17.7 MPa (g) Viscosity 100 sec. (Ford Cup No. 4) Thinning 0 ~ 5% by volume


:



:

EPICON MARINE FINISH, EPICON MARINE HB, etc.

Packing

:

Two pack product


No. 5072 Aug. - 2000

(SHA) BANNOH 500 R (B 500 R) BANNOH 500 R is a tar free, epoxy anti-corrosive primer, based on pure epoxy resin and pigmentation. It gives excellent physical properties such as toughness and abrasion resistance, adhesion, especially excellent adhesion with anti-fouling paint. It is suitable for outside hull, deck and superstructure of ships. TECHNICAL DATA

Type

:

Pure epoxy paint

Recommended Use

:

Anti-corrosive paint for repair ships

Mixing Ratio

:


Colour

:

Grey

Flash Point

:

Base : 22oC , Hardener : 23.5oC

Solids by Volume

:

60 ± 2%


:

0.292 L/m2 ; 394 g/m2

Wet Film Thickness

:

292 µm

Dry Film Thickness

:

175 µm

Drying Time

(at D.F.T. 175µm)


Surface Dry 5 hrs. 4 hrs. 3 hrs. 2 hrs.Hard Dry 24 hrs. 20 hrs. 10 hrs. 8 hrs.


:

Minimum* - - - -M aximum* - - - -

Pot Lift

: 18 hrs. 14 hrs. 7 hrs. 4 hrs.

Thinner

:

EPICON THINNER


:



:


Tip No. GRACO 423, 425, 427 Paint Output Pressure 14.7 ~ 17.7 MPa(g)

Viscosity 1.6 ~2.0 Pa.s Thinning 0 ~ 5% by volume


:

EPICON ZINC RICH PRIMER, etc.


:

SEA GRANDPRIX 500,1000,2000, RAVAX FINISH, EPICON MARINE FINISH, etc.

Packing

:

Two pack product

Note : * Please refer to the painting specification.


No. 5402 Dec. - 2000 (SHA) EPICON MARINE HB (EPM HB) EPICON MARINE HB, based on a combination of epoxy resin and polyamide curing agent, has high-build excellent durability and adhesion properties. It is suitable as a finish coat for protection of steel ships, bridges and steel structures. TECHNICAL DATA

Type

:

Epoxy/ Polyamide finish coat, high-build

Recommended Use

:

Finish coat of EPICON MARINE system of steel ships, bridges and other steel structures

Mixing Ratio

:


Colour

:

White, As specified

Flash Point

:

Base : 23°C ; Hardener : 28°C

Solids by Volume

:

58 ± 2%


:

0.086 ~ 0.172 L/m2 ; 107 ~ 214 g/m2

Wet Film Thickness

:

86 ~ 172 µm

Dry Film Thickness

:

50 ~ 100 µm

Drying Time

(at D.F.T. 100µm)



Painting Interval

(at D.F.T. 100µm)



: 24 hrs. 12 hrs. 12 hrs. 8 hrs.

Thinner

:

EPICON THINNER


:

Airless spray


:


Tip No. GRACO 719, 721 Paint Output Pressure 8.2 ~ 11.0 MPa (g) Viscosity 1.5 Pa.s Thinning 0 ~ 5% by volume


:

BANNOH 200, BANNOH 500, etc


:

-

Packing

:

Two pack product

Note : *.Please refer to the painting specifications.


No. 5127 Dec. - 2000

(SHA)

BANNOH 200 (BNN 200) BANNOH 200, based on a combination of modified epoxy resin and rest-preventive pigment, has excellent adhesion property, toughness and effective rust-preventive property. It is suitable for protection of superstructures and exposed deck of steel ships. TECHNICAL DATA

Type

:

Modified epoxy rust-preventive paint, high-build

Recommended Use

:

Primer on inside and outside of superstructures, exposed deck of steel ships and other steel structures

Mixing Ratio

:


Colour

:

White, Grey, Green, Blue, Reddish brown, Black

Flash Point

:


Solids by Volume

:

59 ± 2%


:

0.169 ~ 0.339 L/m2 ; 227 ~ 454 g/m2

Wet Film Thickness

:

169 ~ 339 µm

Dry Film Thickness

:

100 ~ 200 µm

Drying Time

(at D.F.T. 200µm)




:

Minimum 24 hrs. 18 hrs. 10 hrs. 8 hrs.M aximum* - - - -

Pot Life

: 18 hrs. 14 hrs. 7 hrs. 4 hrs.

Thinner

:

EPICON THINNER


:



:




:

CERABOND 2000, EPICON ZINC RICH PRIMER, etc.


:

EVAMARINE, RAVAX FINISH, ACRI 700 FINISH, UNYMARINE TS, EPICON MARINE HB, POLIBI-T-1, etc.

Packing

:

Two pack product

Note: * Please refer to the painting specifications.


No. 6020A Oct. - 1999

(SHA) EPICON T-500 PRIMER H (EP T-500 H) EPICON T-500 PRIMER H, based on a combination of epoxy resin and hardener, has excellent physical properties such as adhesion, toughness, abrasion resistance, etc. and chemical resistance to saltwater, petroleum products, crude oil, alkalis and weak acids. It is particularly compatible with EPICON T-500 and useful as a high build type holding primer for product carrier and tank interiors. TECHNICAL DATA

Type

:

Epoxy tank coating, high-build

Recommended Use

:

As a primer for product carrier tank interiors and useful as holding primer

Mixing Ratio

:


Colour

:

Pinkish Brown

Flash Point

:


Solids by Volume

:

33 ± 2%


:

0.074 ~ 0.152L/m2 ; 86 ~ 176 g/m2

Wet Film Thickness

:

74 ~ 152 µm

Dry Film Thickness

:

25 ~ 50 µm

Drying Time

(at D.F.T. 50µm)

:

Temperature 10oC 20oC 30oCSurface Dry 90 min. 40 min. 20 min.Hard Dry 16 hrs. 8 hrs. 4 hrs.

Painting Interval

(at D.F.T. 50µm)

:

Minimum 16 hrs. 12 hrs. 8 hrs.Maximum 15 days 15 days 15 days* (7) days (5) days (3) days

Pot Life

:

16 hrs. 10 hrs. 6 hrs.

Thinner

:

EPICON T-500 THINNER


:



:

Temperature Minimum 10°C Humidity Maximum ** 85% R.H. For Airless spray;



:



:

EPICON T-500

Packing

:

Two pack product

Notes: * In case of outdoor exposure. ** Dew point + Min. 5oC


No. 6035 Oct. - 1999

(SHA) EPICON T-800 HOLDING PRIMER (EP T-800 HP) EPICON T-800 HOLDING PRIMER, based on a combination of epoxy phenolic resin, rust-preventive pigments and hardener, has chemical resistance to salt-water, petroleum products, crude oil, alkalis and weak acids. It is particularly compatible with EPICON T-800 and useful as a holding primer for products carrier tank interiors. TECHNICAL DATA

Type

:

Epoxy phenolic holding primer

Recommended Use

:

As a holding primer for product carrier tank interiors

Mixing Ratio

:


Colour

:

Pinkish brown

Flash Point

:


Solids by Volume

:

35 ± 2%


:

0.072 L/m2 ; 82 g/m2

Wet Film Thickness

:

72 µm

Dry Film Thickness

:

25 µm

Drying Time

(at D.F.T. 25µm)


Surface Dry 15 min. 10 min. 6 min.Hard Dry 3 hrs. 2 hrs. 1.5 hrs.


: Minimum 16 hrs. 8 hrs. 5 hrs.

Maximum* 15 days 15 days 15 days(7) days (5) days (3) days

Pot Life

: 24 hrs. 16 hrs. 12 hrs. Thinner

:



:



:


Tip No. GRACO 719 Paint Output Pressure 8.8 ~ 11.8 MPa(g) Viscosity 9 ~ 10 sec. (For Cup No. 4) Thinning 0 ~ 20% by volume


:

CERABOND 2000


:

EPICON T-800

Packing

:

Two pack product

Notes: *In case of outdoor exposure.

** On steel: Dew point + Min. 5oC.


No. 6037 Nov. - 2000 (SHA) EPICON T-800 (EP T-800) EPICON T-800, a high-build type epoxy phenolic coating, has excellent physical properties such as adhesion, toughness, abrasion resistance, etc. as well as chemical resistance to salt-water, fresh water, petroleum products, crude oil, alkalis and weak acids. It is suitable as a protective coating for tank interiors. Airless spray can build a dry film thickness of 75 ~ 125 microns per coat. TECHNICAL DATA

Type

:

Epoxy phenolic tank coating, high-build

Recommended Use

:

Cargo oil tank, chemical tank, etc.

Mixing Ratio

:


Color

:

Red brown, Grey, Light grey, White

Flash Point

:


Solids by Volume

:

57 ± 2%


:

0.132 ~ 0.219 L/m2 ; 175 ~ 292 g/m2

Wet Film Thickness

:

132 ~ 219 µm

Dry Film Thickness

:

75 ~ 125 µm

Drying Time

(at D.F.T. 100µm)


Surface Dry 2.5 hrs. 1.5 hrs. 30 min. Hard Dry 24 hrs. 12 hrs. 6 hrs.


:

Minimum 24 hrs. 16 hrs. 14 hrs. Maximum 10 days 7 days 5 days * (4) days (3) days (2) days

Pot Life

: 7 hrs. 5 hrs. 3 hrs.

Thinner

:



:



:




:

CERABOND2000, EPICON ZINC RICH PRIMER, EPICON T-800 HOLDING PRIMER, EPICON T-800


:

EPICON T-800

Packaging

:

Two pack product

Notes:* In case of outdoor exposure ** On steel : Dew point + Min. 5oC On paint film : Dew point + Min. 3oC


No. 6025 Dec. - 1999

(SHA) EPICON T-500 (EP T-500) EPICON T-500, a high build type epoxy coating, has excellent physical properties such as adhesion, toughness, abrasion resistance, etc. as well as chemical resistance to salt water, fresh water, petroleum products, crude oil, alkalis and weak acids. It is suitable as a protective coating for tank interiors. Airless spray can build a dry film thickness of 75 ~ 125 microns per coat. TECHNICAL DATA

Type

:

Epoxy tank coating, high-build

Recommended Use

:

Cargo oil tank, fresh water tank, hold, solvent tank, chemical tank, etc.

Mixing Ratio

:


Colour

:

Red brown, Grey, Light grey, White

Flash Point

:


Solids by Volume

:

58 ± 2%


:

0.130 ~ 0.216 L/m2 ; 179 ~ 299 g/m2

Wet Film Thickness

:

130 ~ 216 µm

Dry Film Thickness

:

75 ~ 125 µm

Drying Time

(at D.F.T. 125µm)


Surface Dry 3.5 hrs. 2.5 hrs. 1.5 hrs. 30 min.Hard Dry 36 hrs. 24 hrs. 12 hrs. 6 hrs.


: Minimum 36 hrs. 24 hrs. 12(16) hrs. 6(14) hrs.

Maximum* 10 days 10 days 7 days 5 days Pot Life

: 10 hrs. 7 hrs. 5 hrs. 3 hrs.

Thinner

:



:



:

Temperature Minimum 5(10)°C Humidity Maximum ** 85% R.H. For Airless spray;

Tip No. GRACO 619 ~ 621 Paint Output Pressure 14.7 ~ 17.7 MPa(g) Viscosity 1.0 ~ 1.5 Pa.s Thinning 0 ~ 5% by volume


:

CERABOND 2000, EPICON ZINC RICH PRIMER, NZ PRIMER, EPICON T-500 PRIMER H, etc.


:

EPICON T-500

Packing

:

Two pack product

Notes: Shown above “( )” are for tank coating of product carrier, please refer to Chugoku’s catalogue “Product Carrier Tank Coating” in detail. * Maximum painting interval is 3 days at 20°C when it is exposed outdoors. ** On steel : Dew point + Min. 5oC.

On paint film : Dew point + Min. 3oC Waiting time before the first cargo loading Temp. 10oC 20oC 30oC (Days) 18 10 6


No. 6167 Apr. - 2001 (SHA) UMEGUARD MT (UG MT) UMEGUARD MT, is a high solid, modified epoxy paint which is specially designed for steel surfaces prepared by high pressure fresh water cleaning. The surface does not need to be completely dry, and may be slightly damp during application. This product has excellent tolerance for poor surfaces, and has good anti-corrosive properties. TECHNICAL DATA

Type

:

Epoxy / Special polyamine surface tolerant coating

Recommended Use

:

Deck, Topside, Superstructure, Inland construction, Ballast tank

Mixing Ratio

:


Colour

:

Light Grey, Reddish Brown

Flash Point

:

15oC

Solids by Volume

:

82 ± 2%


:

0.121 ~ 0.241 L/m2 ; 182 ~ 363 g/m2

Wet Film Thickness

:

121 ~ 243 µm

Dry Film Thickness

:

100 ~ 200 µm

Drying Time

(at D.F.T. 100µm)


Surface Dry 19 hrs. 11 hrs. 8 hrs.Hard Dry 21 hrs. 15 hrs. 10 hrs.

Painting Interval

(at D.F.T. 100µm)

:

Minimum* 48 hrs. 24 hrs. 16 hrs.Maximum 14 days 7 days 7 days

Pot Life

: 4.5 hrs. 3 hrs. 2 hrs.

Thinner

:

EPICON THINNER


:



:

Temperature Minimum 20oC (Recommended) Humidity Maximum 95% R.H. For Airless Spray;

Tip No. GRACO 621 ~ 623 Paint Output Pressure 14.7 ~ 17.7 MPa(g) Viscosity 1.5 ~ 2.5 Pa.s Thinning 0 ~ 5% by volume


:

CERABOND 2000, EPICON ZINC RICH PRIMER


:

UMEGUARD MT

Packing

:

Two pack product

Note: In confined spaces such as tank inside, ventilation is required during application and curing to remove solvent

vapours and promote curing.


No. 6182A Dec. - 2000 (SHA) NOVA 5000 BARRIER (NV 5000 B) NOVA 5000 BARRIER, solvent-free epoxy putty, is designed as a protective coating of ballast water tanks and cargo oil tanks, It has excellent water/sea-water resistance and has also superior crude oil resistance, besides excellent adhesion even on simply treated or/and slightly dump surface. NOVA 5000 BARRIER is eco-friendly to the environment as it contains no solvent, no heavy metal. TECHNICAL DATA

Type

:

Solvent-free epoxy putty

Recommended Use

:

Ballast water tank, Crude oil tank, Void space, Cofferdam, Hold of ships, Bridges, Underground pipes, Port facilities, etc.

Mixing Ratio

:


Colour

:

Grey

Flash Point

:

Base : 250<°C , Hardener : 155°C

Solids by Volume

:

100%


:

0.300 L/m2 ; 648 g/m2

Wet Film Thickness

:

300 µm

Dry Film Thickness

:

300 µm

Drying Time

(at D.F.T. 300µm)

:

Temperature 10oC 20oC 30oCSurface Dry 8 hrs. 4 hrs. 2 hrs.Hard Dry 24 hrs. 12 hrs. 8 hrs.

Painting Interval

(at D.F.T. 300µm)

:

Minimum 24 hrs. 12 hrs. 8 hrs.Maximum 15 days 7 days 7 days

Pot Life

:

1.5 hrs. 1 hr. 45 min.

Thinner

:

EPICON THINNER (for cleaning purpose)


:

Brush, Roller, Spatula, Hands


:

Temperature 10°C Humidity Maximum 85% R.H. Thinning Not recommended


:

-


:

-

Packing

:

Two pack product


No. 6250 Oct. - 1999

(SHA) GALBON S-HB (GB S-HB) GALBON S-HB is an alcohol soluble inorganic zinc coating based on a combination of ethyl silicate and selected zinc dust. It gives excellent protection against corrosion and prolonged weather resistance, and is highly resistance to oil and solvent as well as fresh and salt water. GALBON S-HB withstands temperature of up to 400°C. A film thickness of 50 ~ 100 microns can be built in one application. GALBON S-HB is recommended as a top coating over GALBON S or CERABOND 2000. TECHNICAL DATA

Type : Inorganic zinc silicate alcohol soluble and self-curing, high-build type

Recommended Use : As a protective coating for oil tanks, solvent tanks, ballast tanks, outside hull, deck, heating pipes, holds, other steel structures, etc.

Mixing Ratio : Base : Powder = 7 : 3 (by weight)

Colour : Grey

Flash Point : Base : 15oC Powder : Non flammable

Solids by Volume : 60 ± 2%

Coverage (Theoretical) : 0.083 ~ 0.125 L/m2 ; 220 ~ 330 g/m2

Wet Film Thickness : 83 ~ 125 µm

Dry Film Thickness : 50 ~ 75 µm

Drying Time (at D.F.T. 65µm)

: Temperature 5oC 10oC 20oC 30oCSurface Dry 40 min. 30 min. 20 min. 10 min.Hard Dry 6 hrs. 5 hrs. 4 hrs. 3 hrs.


: Minimum 72 hrs. 32 hrs. 24 hrs. 18 hrs.Maximum - - - -

Pot Life : 14 hrs. 10 hrs. 7 hrs. 5 hrs. Thinner : GALBON S-HB THINNER

Method of Application : Airless spray, Brush, (only for touch-up)

Condition for Application : Temperature 5°C Humidity 50 ~ 95% R.H. For Airless spray; Pump Ratio 1:23, 1:28

Tip No. GRACO 419 ~ 519 Paint Output Pressure 9.8 MPa(g) Viscosity 10 ~ 12 sec. (Ford Cup No. 4) Thinning 0 ~ 5% by volume

Surface Preparation : The particular properties of this product require a very careful surface preparation of the steel which must be blast-cleaned to SSPC-SP 10 or SIS Sa 2.5

Preferable Preceding Coats : GALBON S, GALBON SP, CERABOND 2000

Preferable Subsequent Coats : Any one of our products and/or the equivalent, e.g. Inorganic zinc paint, Chlorinated rubber paint, Epoxy paint, Tar-epoxy paint

Packing : Two pack product Note: In case an organic top coat is applied, dry film thickness of GALBON S-HB should be controlled at 50 ~ 100

microns. Recommended dry film thickness is 65 microns.


No. 8000 Oct. - 1999

(SHA) SILVA SPAR No.500 (SIS 500) SILVER SPAR No.500 is an alkyd resin based aluminium paint with outstanding heat resisting and rust-preventing properties. It presents a beautiful appearance. SILVA SPAR No.500 successfully withstands temperature of up to 150°C. TECHNICAL DATA

Type

:

Alkyd / Aluminium heat resisting paint

Recommended Use

:

As a protective coating on steel surfaces reaching high temperature

Mixing Ratio

:

Varnish : Aluminium paste = 86 : 14 (by volume)

Colour

:

Metallic Silver

Flash Point

:

Varnish : 35oC ; Aluminium paste : 43oC

Solids by Volume

:

42 ± 2%


:

0.035 ~ 0.059 L/m2 ; 35 ~ 59 g/m2

Wet Film Thickness

:

35 ~ 59 µm

Dry Film Thickness

:

15 ~ 25 µm

Drying Time

(at D.F.T. 20µm)



Painting Interval

(at D.F.T. 20µm)

:


Pot Life

: 32 hrs. 24 hrs. 16 hrs. 8 hrs.

Thinner

:

MARINE THINNER


:



:


Tip No. GRACO 713 Paint Output Pressure 10.7 ~ 13.8 MPa(g) Viscosity 40 sec. (Iwata Cup) Thinning -


:

LZI PRIMER, Alkyd resin based primer


:

-

Packing

:

Two pack product


No. 8052 Jun. – 2001

(SHA) CERABEST (CB) CERABEST is a combination of strictly selected heat resistant alloys and heat resistant silicate solution. It has excellent heat resistance at high temperatures up to 800oC, and has excellent adhesion to inorganic zinc shop primer. TECHNICAL DATA

Type

:

Ultra heat resistant paint

Recommended Use

: As a topcoat of inorganic shop primer to prevent from the heat

damages of steel structures, such as Ship’s super structures Mixing Ratio

:

Paste : Base = 42 : 58 (by volume)

Colour

:

Grey

Flash Point

:

Paste : 18°C ; Base : 13°C ,

Solids by Volume

:

42 ± 2%


:

0.071 L/m2

; 107 g/m2 Wet Film Thickness

:

-

Dry Film Thickness

:

30 µm

Drying Time

(at D.F.T. 30µm)



Painting Interval

(at D.F.T. 30µm)

:

Minimum Organic 14 days 10 days 7 days 7 daysMaximum 180 days 180 days 180 days 180 days

Pot Life

:

30 hrs. 24 hrs. 16 hrs. 10 hrs.

Thinner

:

INORGANIC SHOP PRIMER THINNER INORGANIC SHOP PRIMER THINNER S


:

Airless spray, Air spray


:

Temperature 5 ~ 30°C

Humidity 50 ~ 90% R.H. For Airless spray;

Tip No. GRACO 619 ~ 719 Paint Output Pressure 8.8 ~ 11.8 MPa(g) Viscosity 9 ~ 10 sec. (IWATA Cup No. 2) Thinning 0 ~ 5% by volume


:

Inorganic shop primer


:

Epoxy paint, Tar-epoxy paint, Non-tar-epoxy paint, Chlorinated rubber primer, Alkyd primer

Packing

:

Two pack product

Notes: 1. To obtain homogenous mixture stir the PASTE well prior to adding the BASE.2. To prevent from nozzle clogging, put 80 mesh filter on the suction inlet.3. To prevent from pigment setting, keep stirring the mixture during the application.4. Since the paint mixture reacts with moisture, use up the mixture as soon as possible under high humid

condition.5. Use the specified thinner.6. Take 7 days for aging before application of subsequent coat at below 10oC since curing of the product

becomes considerably slow at low temperature.


GENERAL INSTRUCTION

for SURFACE PREPARATION & PAINTING

SURFACE PREPARATION For the protection of steel with paint, careful surface preparation is of the utmost importance. If this surface preparation is neglected, the performance of the paint cannot be ensured. 1. Surface Preparation of Bare Steel (Pre-Fabrication Treatment)

a) Oil and grease are to be removed by thinner wiping after scraping away firmly adhering impurities.

b) Corrosive salts and sulfate on the steel surface are to be removed by fresh-water washing. The surface is then to be dried with dry waste cloth or dry compressed air.

c) All mill scale, rust and foreign matters are to be removed by shot-, grit- or sand-blasting. Finally, the surface should be cleaned by a vacuum cleaner or by blowing with compressed air.

Bare steel surfaces rust rapidly when exposed to the air, and therefore should be painted with a

shop primer as soon as possible, in order to prevent rusting during storage, fabrication and fitting out. The main function of shop primers is to provide steel with temporary protection against rusting during fabrication and fitting out and they must be suitable for application in the course of shipyard practice and must not interfere with other construction processes. Consequently, rapid drying (to allow handling in a short time after application), non-toxic, and good welding or gas-cutting properties are required for shop primers. They must also be compatible with any subsequent paint. The following shop primers have been mainly manufactured and marketed by Chugoku Marine Paints Ltd in the Asian region, except Japan & Korea.

Shop primer Standard Grade of

Pre-Fabrication Treatment

Applicable Subsequent Paint

NZ PRIMER S (Epoxy non-zinc shop primer)

ISO Sa 2.5 or equivalent Any of our organic resin based paints, e.g. oleoresinous paint, or equivalent, chlorinated rubber paint, vinyl paint, epoxy paint, tar-epoxy paint.

EPICON ZINC RICH PRIMER (Epoxy zinc rich shop primer)

ISA Sa 2.5 or equivalent

CERABOND 2000 (Inorganic zinc shop primer)

ISO Sa 2.5 or equivalent Most of our organic resin based paints. However, when oleoresinous paints or equivalent are applied, please consult us first.

Notes : 1. ISO = International Standard

2. *Oleoresinous paint on CERABOND 2000 is not recommended for high humidity (often sweaty) areas or for immersed areas, due to the possible adhesive failure caused by chemical reaction between the oleoresinous vehicle and metallic zinc.


2. Surface Preparation of Shop Primed Surface (Secondary Surface Preparation or Post-Fabrication Treatment)

Water and moisture, oil and grease, white rust, chalk marks, unsuitable marking paint and other contaminants should be removed by thinner wiping, or other proper cleaning methods. If the shop primed surface has been damaged during rolling, cutting or welding, or suffered mechanical abrasion in handling and transport, the affected areas should be cleaned by wire brush or disc sander and touched-up. The entire surface must be cleaned by washing, if necessary, before subsequent paints are applied.

Surface Preparation Grade (Post-Fabrication Treatment Grade) according to the type of

subsequent paint: Outer Hull (Including tank internals) Epoxy, tar-epoxy ISO St 3 Vinyl, chlorinated rubber, acrylic ISO St 3 Oleoresinous Between ISO St 3 and 2 Interior Epoxy, tar-epoxy ISO St 3 Vinyl, chlorinated rubber, acrylic Between ISO St 3 and 2 Oleoresinous Between ISO St 3 and 2 3. Surface Preparation for Old Paint Film

The surface must be cleaned by scraping, and/or thinner wiping and/or fresh water washing to remove salt, dirt, oil and grease and other impurities. All rust, oil, loose paint and other impurities should be removed by disc sander, wire brush or other suitable method after which a specified paint system should be applied.


PAINTING 1. Weather Conditions Full advantage should be taken of weather conditions to carry out painting when the weather is

favorable. Paints should never be applied on a wet surface. Not only should painting be avoided in rain, sleet or fog, but also attention must be paid to the presence of condensation on the surface.

Generally, painting should be done at over 0 ~5°C and below 85% R.H. condition. However, below 5°C some paints such as epoxy slow down dramatically or even stop curing. Other paints such as chlorinated rubber, acrylic and vinyl paints are quite applicable at temperatures even below 0°C if the surface is clean and free from ice or frost.

Painting should not be carried out when the surface temperature is less than 3°C above the dew point, no matter what the R.H. is at that time.

Particulars are mentioned in INSTRUCTIONS FOR APPLICATION OF EPOXY & TAR-EPOXY HULL COATING, EPOXY & TAR-EPOXY TANK COATING or INORGANIC ZINC COATING.

2. Preparation & Storage

a) Some paint components, although perfectly stable at normal temperature, will react together at higher temperatures, causing thickening etc. Some paints such as water based paints and emulsions are affected by frost. Because of this, paint should not be stored where temperatures can become excessively high or low.

b) Shelf life If stored in normal conditions, Oleoresinous 18 months min., subject to re-inspection thereafter. Chlorinated rubber, vinyl tar, epoxy, tar-epoxy 12 months min., subject to re-inspection thereafter. Inorganic zinc 6 months min., subject to re-inspection thereafter. c) When paints are left standing they normally tend to separate slightly. This is caused by

different specific gravities of the ingredients. Therefore, before using, all paint must be carefully stirred until a homogeneous mixture is obtained. Stirring should be done from time to time in order to prevent such separation while painting.

d) Once opened, some paints rapidly form a skin on the surface. Generally the quick-drying

types have this tendency, which is of course not a fault of the paint but is due to the natural process of drying. The skin must be removed before painting. This precaution applies particularly when spraying the material, because small particles of skin would soon clog the gun.


brushing or to bring paint to spraying consistency. Do not exceed the amount of thinner specified by the manufacturer.

3. Film Thickness

The dry film thickness of a shop primer on a blasted steel surface should be measured as follows: place a smooth steel panel on the blasted steel surface, apply the shop primer and measure the dry film thickness on the steel panels by an adequate electromagnetic thickness meter.

4. Application Method

a) Brush The paint should be applied on the surface by lengthwise and crosswise movements of the

brush. Tough surfaces, rivet heads, edges and angles should be given special attention. b) Roller

Cover the surface of the roller by spreading the paint. Paint at a slow and even space up and down and across. Do not spread the paint excessively. Particular care should be taken when painting rivet heads and welding seams.

c) Airless Spray Most CHUGOKU products can be applied by airless spray, which is still a more effective

and economical method than conventional spraying, especially on large areas. The method is quicker and the paint can be applied in thicker coats.

The use of an airless spray requires more of a routine than a conventional spray, and great caution must be exercised in handling the gun due to the very high pressures involved.

5. Cleaning of Tools The tools should be cleaned immediately after use. This is particularly important when working

with quick-drying or two component paints. Spray equipment should be cleaned after use by flushing with adequate thinner. Special care should be taken in cleaning the nozzles.


GENERAL INSTRUCTION FOR APPLICATION of EPOXY & TAR-EPOXY COATINGS CLEANING PRIOR TO PAINTING (SECONDARY SURFACE PREPARATION) In surface preparation and cleaning of the surface, special attention should be given to the welded parts and edges of steel construction. Dust spatter, slag, etc. should be removed. 1. Damaged parts Rusty parts should be cleaned by disc sander or other suitable method to the grade ISO St 3.

Welding spatter, slag and other foreign matter should be removed by scraper, scaling hammer or suitable tools. Areas burned by welding or other heat treatment, including adjacent areas, should be cleaned by disc sander, blasting or suitable tools to ISO St 3 or Sa 2.5.

Welding parts should be cleaned by power brush or other suitable method. 2. Undamaged Parts

Oil, moisture, dust or other foreign matter should be removed by thinner, power brush, disc sander, compressed air or vacuum cleaner, etc.

After cleaning, a subsequent coat should be applied as soon as possible. MIXING OF MATERIALS 1. Mixing

Base and hardener should be mixed in the specific proportions and ensure a homogeneous state. Since poor mixing may impair its drying property, mixing should be done by a pneumatic mixing machine or the like.

2. Thinning Thinner may be added in spray application, but should never exceed the specified amount. 3. Aging/Induction When indicated necessary before application, the mixed material should be aged for at least as

long as the specified period. Insufficient aging causes blooming. 4. POT LIFE The mixture should be used within the specified pot life.


PAINTING Airless spray is the most recommended method to obtain a uniform and specified film thickness. In this respect cross-spraying is also recommended. If the film thickness is found insufficient, an additional coat should be applied on these parts. Edges, corners, welding seams, scallops and underside of longitudinal should be touched up prior to spraying. In particular, underside of longitudinal must be painted carefully, for it is difficult to obtain sufficient film thickness. Keep to the overcoating intervals as specified. If the maximum overcoating interval is exceeded, the surface to be coated should be roughened by sand paper, disc sander or other adequate tools before application of the subsequent coat. CONTROL OF FILM THICKNESS Film thickness should be controlled at the recommended mean value, unless otherwise specified. WEATHER CONDITION Generally, painting should be done at over 5°C and below 85% R.H. condition. Painting should not be carried out when the surface temperature is less than 3°C above the dew point, no matter what the R.H. is at the time. PROTECTION OF PAINT FILM 1. Painted surfaces should be kept free from water or other liquid before drying through. 2. Painted surfaces should be kept free from welding sparks or dirt during and before the paint film

is touch dry. 3. Painted surface should be arranged to prevent possible damage by foot traffic, particularly in

tank’s interior. PRECAUTIONS FOR FIRE HAZARD AND HEALTH 1. Solvents are flammable, so attention must be given to prevent fire hazard. When painting is

carried out in confined spaces such as a tank’s interior, sufficient ventilation should be provided during painting and during the drying process.

2. To prevent contamination of the skin, protective gloves and clothing should be worn. Should

paint stain the skins, it should be wiped off with a suitable thinner and then the area to be washed with lukewarm water and soap.

3. For more specific information about each product, please ask for a Health and Safety Data sheet.


GENERAL INSTRUCTION FOR APPLICATION of INORGANIC ZINC COATINGS CLEANING PRIOR TO PAINTING (SECONDARY SURFACE PREPARATION) The surface should be cleaned by sweep blasting or power tool cleaning after removing oil and grease. Damaged and welded parts should be cleaned by blasting. If this is impossible, these parts should be treated by disc sander and power brush to the grade of ISO St 3, and then touched up with GALBON S or GALBON S-HB, especially when GALBON L is applied. MIXING OF MATERIALS 1. Mixing The base and powder should be mixed in the specified proportion by gradually adding zinc dust

into the base. Mixing should be done thoroughly to ensure proper mixing and a homogenous condition. As the mixture tends to separate, mixing should be constantly carried out during painting. Prior to painting, it is recommended that the mixture is to be filtered through an 80 mesh screen.

2. Aging/Induction If indicated, the specified time should be kept for aging. When aging is insufficient, paint

failures are likely to occur. 3. Pot life The mixture should be used within the specified pot life. The quality will be impaired if left

longer than the pot life. PAINTING 1. Painting equipment Special care is needed for application of inorganic zinc coatings. It is recommended to apply by

the equipment mentioned below. Cross spraying (double spraying) is highly recommended to obtain a uniform and specified film thickness. The painting equipment should be clean and kept in good condition.

For air spray application of GALBON S and GALBON S-HB:

a) Air spray equipment with pressure paint pot and an agitator; b) Air compressor capable of supplying sufficient volume of air continuously at 80 psi (5-6

kgf/cm2) to the nozzle of each gun (of BINKS or DEVILBISS); c) Air hose for gun of ID 5/16 inches (8mm); d) Paint hose of ID ½ inches (13mm); and e) Spray gun such as BINKS No. 18 with No. 66 paint nozzle and No. 63 PB air nozzle.


For airless spraying of GALBON (GALBON S and GALBON S-HB can be applied by conventional airless equipment.) a) King Slurry Unit (Graco Inc., USA); b) Spee-Flo Hydroairless (Spee-Flo Co., Japan); c) Airpon (Nagano Keiki Seisakusho Ltd., Japan); d) ALS-81 (Iwata Aircompressor Mfg. Co., Ltd., Japan); e) or the equivalent.

2. Additional coat If the applied film thickness is found to be insufficient, an additional coat should be applied. CONTROL OF FILM THICKNESS Film thickness should be controlled at the recommended mean value, unless otherwise specified. Film thickness should be measured by a wet and/or dry film thickness gage. WEATHER CONDITION Alcohol based type (GALBON S and GALBON S-HB) Temperature 0 - 50°C Humidity 50 - 95% R.H. TOUCH UP Small damaged parts, holidays and cracking should be treated with a scraper, disc sander or power brush to ISO St 3, and be painted according to the recommended painting scheme, unless otherwise specified. WARNING GALBON S and GALBON S-HB are inflammable. Keep away from sparks and flames during application. Adequate ventilation should be provided during application and in the process of drying GALBON.


CONVERSION TABLES To convert From To Multiply by Distance: mil micron 25 micron mil 0.04 inches centimeter 2.54 centimeter inches 0.3937 feet meter 0.3048 meter feet 3.2808 yards meter 0.9144 meter yards 1.0936 nautical mile kilometer 1.8530 kilometer nautical mile 0.5396 Area: square feet square meter 0.0929 square meter square feet 10.764 Volume: US Gallon Liter 3.785 liter US Gallon 0.264 liter cu.ft. 0.0353 cu.ft. liter 28.32 Imperial gallon liter 4.550 liter Imperial gallon 0.220 Area/Volume: m²/liter sq.ft/US gallon 40.74 sq.ft/US gallon m²/liter 0.0245 m²/liter sq.ft./Imperial gallon 48.93 sq.ft./Imperial gallon m²/liter 0.0204 Weight: lbs kg 0.4536 kg lbs 2.2046 Density: kg/liter lbs/US gallon 8.3440 lbs/US gallon kg/liter 0.1198 V.O.C.: g/liter lbs/US gallon 0.0083 Pressure: atm. bar 1.0130 atm. kp/cm² 1.0330 atm. p.s.i. 14.70 bar atm. 0.9870 bar kp/cm² 1.020 bar p.s.i. 14.50 kp/cm² atm. 0.968 kp/cm² bar 0.981 kp/cm² p.s.i. 14.22 kp/cm² Mpa 0.098 p.s.i. atm. 0.068 p.s.i. bar 0.069 p.s.i. kp/cm² 0.070


To convert From To Calculate Temperature: Celsius Fahrenheit (9/5 × °C) + 32 Fahrenheit Celsius 5/9 × (°F - 32) Film thickness: Wet Dry wft × VS % 100 Dry Wet dft × 100 VS % Notes: - atm. is so called physical atmosphere the technical atmosphere, at, is identical to kp/cm² - The so-called kilogram forces/cm² is considered equal to Kp/cm²

- wft = Wet film thickness, dft = Dry film thickness, VS% = Volume Solids CALCULATION OF Theoretical Spreading Rate (on completely smooth surface) In m² per liter = VS % × 10 In sq.ft. per US gallon = VS % × 16.04 desired DFT (micron) desired DFT (mil) Theoretical Paint Consumption (on completely smooth surface) In liter = area (m) × desired DFT (micron) VS % × 10 In US gallon = area (sq.ft.) × desired DFT (mil) VS % × 16.04 Practical consumption = area × consumption factor theoretical spreading rate Theoretical spreading rate = VS % × 10 DFT


FORMULAS FOR ESTIMATING SURFACE AREAS OF SHIPS Bottom (incl. Boottop): A = ((2 × d) + B) × Lpp × P where d = draught maximum (as per Lloyd’s) B = breath extreme (as per Lloyd’s) Lpp = length between perpendiculars (as per Lloyd’s) P = 0.90 for big tankers, 0.85 for bulk carriers, 0.70- 0.75 for dry cargo liners or A = Lpp × (Bm + 2 × D) × V Bm × Lpp × D where D = mean draft at paint line (m) Bm = breath moulded (m) Lpp = length between perpendiculars V = displacement (cubic meter) corresponding to the draft Boottop: A = 2 × h × (Lpp + 0.5 × B) where h = width of boottop (to be informed by owner) Lpp = length between perpendiculars (as per Lloyd’s) B = breath extreme (as per Lloyd’s) Topsides: A = 2 × H × (Loa + 0.5 × B) where H = height of topsides (depth - draught) (as per Lloyd’s) Loa = length overall (as per Lloyd’s) B = breath extreme (as per Lloyd’s)


Relation between dew point, relative humidity and air temperature

Air temp. in °C

Dew point in °C at a relative humidity 50% 55% 60% 65% 70% 75% 80% 85% 90%

5 -4.1 -2.9 -1.8 -0.9 0.0 0.9 1.8 2.7 3.66 -3.2 -2.1 -1.0 -0.1 0.9 1.8 2.8 3.7 4.57 -2.4 -1.3 -0.2 0.8 1.8 2.8 3.7 4.6 5.58 -1.6 -0.4 0.8 1.8 2.8 3.8 4.7 5.6 6.5

9 -0.8 0.4 1.7 2.7 3.8 4.7 5.7 6.6 7.5 10 0.1 1.3 2.6 3.7 4.7 5.7 6.7 7.6 8.411 1.0 2.3 3.5 4.6 5.6 6.7 7.6 8.6 9.412 1.9 3.2 4.5 5.6 6.6 7.7 8.6 9.6 10.413 2.8 4.2 5.4 6.6 7.6 8.6 9.6 10.6 11.414 3.7 5.1 6.4 7.5 8.6 9.6 10.6 11.5 12.415 4.7 6.1 7.3 8.5 9.5 10.6 11.5 12.5 13.416 5.6 8.0 8.3 9.5 10.5 11.6 12.5 13.5 14.417 6.5 7.9 9.2 10.4 11.5 12.5 13.5 14.5 15.318 7.4 8.8 10.2 11.4 12.4 13.5 14.5 15.4 16.319 8.3 9.7 11.1 12.3 13.4 14.5 15.5 16.4 17.320 9.3 10.7 12.0 13.3 14.4 15.4 16.4 17.4 18.321 10.2 11.6 12.9 14.2 15.3 16.4 17.4 18.4 19.322 11.1 12.5 13.8 15.2 16.3 17.4 18.4 19.4 20.323 12.0 13.5 14.8 16.1 17.2 18.4 19.4 20.3 21.324 12.9 14.4 15.7 17.0 18.2 19.3 20.3 21.3 22.325 13.8 15.3 16.7 17.9 19.1 20.3 21.3 22.3 23.226 14.8 16.2 17.6 18.8 20.1 21.2 22.3 23.3 24.227 15.7 17.2 18.6 19.8 21.1 22.2 23.2 24.3 25.228 16.6 18.1 19.5 20.8 22.0 23.2 24.2 25.2 26.229 17.5 19.1 10.5 21.7 22.9 24.1 25.2 26.2 27.230 18.4 20.0 21.4 22.7 23.9 25.1 26.2 27.2 28.2

To allow a sensible safety margin, normally the substrate temperature must be at least 3 degrees centigrade above the dew point. The dew point is the temperature of a given air-water vapour mixture at which condensation starts, because at that temperature the maximum water content of the air reached.

Europe Belgium Contact CHUGOKU PAINTS B.V., Netherlands Canary Islands Contact H.M. PAINTS, S.A.L., Spain or CHUGOKU PAINTS B.V., Netherlands Croatia CHUGOKU PAINTS B.V., Netherlands Denmark Agent FALCK FORMCO APS Hans Edvard Teglersvej 7 2 T. 292 Charlottenlund Denmark Phone:45-39-628511 Fax:45-39-622840 Telex:19550 FORMCO DK Finland Contact CHUGOKU PAINTS B.V., Netherlands Germany CHUGOKU PAINTS (GERMANY) G.m.b.H. Johannisbollwerk 19, 20459 Hamburg Phone:49-40-317-964-80 Fax:49-40-317-964-76 E-mail: [email protected] Greece CHUGOKU MARINE PAINTS (HELLAS), S.A. 8 Kanari Street, Piraeus 185 38, Greece Phone:30-(210)4522489/4522571/4287085/4535089 /4180867/4287085,6 Fax:30-(210)4180868 E-mail: [email protected] Italy Licensee/Agent BOAT S.p.A Via Maccagi 19,16121 Genova, Italy Phone:39-(010)55005 Fax:39-(010)5500298/288 E-mail: [email protected] Licensee COLORFICIO ATTIVA S.r.I. Via Argine. Polcevera 16 D-16161, Genova, Italy Phone:39-(010)7456841 Fax:39-(010)7456946 Malta CALMARINE SERVICES, LTD. "Casa Roma" 48 Sir Augustus Bartoto Street, Ta' Xbiex MSD 11, Malta Phone:356-346365/323779 Fax:356-346367 Monaco Contact CAMREX CHUGOKU LTD., U. K. Netherlands CHUGOKU PAINTS B.V. (Sales & Factory) Sluisweg 12, P.O.Box 73, 4793ZH Fijnaart, Netherlands Phone:31-(167)526100 Fax:31-(167)522059 Telex:74385 CHUGOKU NL E-mail: [email protected]

Norway Licensee STAR MALING-OG LAKKFABRIKK A/S P.O.Box 593, 3412 Lierstranda, Norway Phone:47-(32)841500 Fax:47-(32)841670 Agent (Yacht Paints) Sola Shipping as Industriveien 6, 1473 Skarer, Norway Phone:47-67-904200 Fax:47-67-906520 E-mail: [email protected] Portugal Contact CHUGOKU PAINTS B.V., Netherlands Spain Agent H. M. PAINTS, S.A.L. Avda. San Pablo, 28 Edifcio 1-3rd floor 28820-Coslada, Madrid, Spain Phone:34-(91)669-0334,0445 Fax:34-(91)669-0397 E-mail:[email protected] Sweden Agent SWEDE HOLDING HornSimpa AB Nybingsbo 45 SE-793 97 Siljansnas, Sweden Phone & Fax:46-(247)20010 E-mail: [email protected] Switzerland Contact CAMREX CHUGOKU LTD., U. K. Turkey CHUGOKU PAINTS B.V. ( Turkish office) Istanbul Deri End.Serb.Bol. Nuzhet Kodalak Sok. No. 11 kat. 6 81464 Tuzla Istanbul, Turkey Phone: 0090-216-394-0713 Fax:0090-216-394-0716 E-mail:[email protected] U. K. CAMREX CHUGOKU LTD. Norris House, 4 Norris Street, London, SW1Y 4RJ, U. K. Phone:44-(20)7925-2535 Fax:44-(20)7925-2447 Telex:28851 CMPLDN G Africa South Africa Marine & Heavy Duty Coatings Licensee (Cape Town) DEKRO PAINTS (PTY) LTD. 24 Fabriek Street, P.O.Box 131, Kuilsriver 7580, South Africa Phone:27-(21)903-3131 Fax:27-(21)903-2307 Agent/Stock (Cape Town) MARINECOTE (PTY) LTD. 24 Fabriek Street, P.O.BOX 131, Kuilsriver 7580, South Africa Phone:27-(21)903-3131 Fax:27-(21)903-2307

15.Apr..2003

Agent/Stock (Durban) MARINECOTE (PTY) LTD. 41 Livingstone Road, Pinetown 3610 P.O.Box 23, New Germany 3620, South Africa Phone:27-31-7027353 Fax:27-31-7010895 Middle East U. A. E. Chugoku Marine Paints(Singapore),PTE.,Ltd. Dubai Office Shipping Tower, 6th Floor, Al Mina Road Al Rifa'a, P.O. Box 464, Dubai, United Arab Emirates Phone:971-4-393-8236 Fax:971-4-393-4268 Telex: 45495 STALCO EM E-mail: [email protected] Stock STALCO, Dubai Shipping Tower, 7th Floor Al Mina Road Al Rifa'a, P.O.Box 464, Dubai, United Arab Emirates Phone:971-4-555666 Fax:971-4-555888 Telex:45495 STALCO EM North America U.S.A. CMP COATINGS, INC. (Head Quarter & Factory) 1610 Engineers Road, Belle Chasse, Louisiana, 70037, U.S.A. Tel: 1 – (504) 392-4817 Fax: 1 – (504) 392-2979 E-mail : [email protected] (New York Container Sales) Mr. Jeffrey McKenna 1664 Hidden Lane, Lakewood, New Jersey, 08701 U.S.A. Tel: 1 - (732) 901-8849 Fax: 1 - (732) 901-9447 (New York Marine Sales) Mr. Glen Dempsey 950 Beacon Avenue, Brick, New Jersey 08723 U.S.A. Tel: 1 – (732) 451-0365 Fax: 1 – (732) 451-0265 Licensee SIMPSON COATINGS GROUP 111 South Maple Avenue, South San Francisco, California, 94080 U.S.A. **** Contact CMP COATINGS, INC. (Head Quarter) **** Stock ATLANTIC STEAMERS 1100 Adams Street, Hoboken, New Jersey, 07030 U.S.A. **** Contact CMP COATINGS, INC. (Head Quarter) **** Stock CALIFORNIA GENERAL / Long Beach 440 North Marine Avenue, Wilmington, California, 90748 U.S.A. **** Contact CMP COATINGS, INC. (Head Quarter) **** Stock VANCOUVER WAREHOUSE AND DISTRIBUTION COMPANY 1101 West 11th Street, Vancouver, WA 98660 U.S.A. **** Contact CMP COATINGS, INC. (Head Quarter) ****

Curacao Stock controlled by CPBV CURACAO MARINE PAINTS P.O. 765, Seru Loraweg, 104, Curacao, Netherland Antilles **** Contact CMP COATINGS, INC. (Head Quarter) **** Oceania Australia Licensee/Agent SUPALUX PAINT CO. PTY. LTD. 9-11 Tipping Road, Kewdale, P.O.Box 151 Clovedale, Western Australia 6105 Phone:61-8(9)3532293 Fax:61-8(9)3531131 New Zealand Licensee/Agent JACOBSEN MANUFACTURING LTD. 7 Akatea Road, Glendene, Auckland 8, New Zealand P.O.Box 83174 Auckland 8, New Zealand Phone:64-(9)818-7410 Fax:64-(9)818-7862 Asia China CHUGOKU MARINE PAINTS (SHANGHAI), LTD. (Sales Office) Room F.19th Floor, Zhao Feng Shi Mao Building, No.369 Jiang Su Road, Shanghai 200050, China Phone:86-(21)62268180 Fax:86-(21)62268468 E-mail: [email protected] (Factory) 5678 Caoan Road, Anting, Jiading, Shanghai, China, Post Code 201805 Phone:86-(21)59572123 Fax:86-(21)59579678 CHUGOKU MARINE PAINTS (GUANG DONG), LTD. (Sales Office & Factory) Industrial Development Area, Lunjiao, Shunde, Guangdong, 528308, China (Sales) Phone:86-765-7736170/6057 Fax:86-765-7736171 (Factory) Phone:86-765-7733451, Fax:86-765-7733452 E-mail : [email protected] Stock DALIAN COSCO MARINE ENGINEERING CO., LTD. 80, Zhongyuan Road, Dalian, China Post Code:116113 Phone:86-411-7606060 Fax:86-411-7606580 Stock TIANJIN OCEAN SHIPPING CO. QINHUANGDAO MARINE MATERIAL SUPPLY CO. No.129, Donggang Road, Qinhuangdao, Hebei, China. 066003 Post Code : 066003 Tel : 86(335)-3040146 Fax: 86 ( 335)-3031393 Stock COSCO QINGDAO OCEAN-GOING SHIPS SUPPLY CO. No.3 Banghai Mid. Road, Qingdao, China

Post Code: 266045 Phone:86-532 4888752 Fax:86-532 4888152 Stock CHENGXI SHIPYARD CHENGXI MARINE BONDED WAREHOUSE CO.,LTD. No.1, Hengshan Road, Jiangyin, Jiangsu, China. Post Code : 214433 Tel & Fax : 86 ( 510)-6118649 Stock CHINA MARINE BUNKER SUPPLY NANTONG CO. 120 Renmin Road(W) Nantong, China Pose Code: 226005 Phone:86-513 3527 039 Fax:86-513 3511 602 Stock SHANGHAI ZHONGZHOU MARINE PAINTS BONDED WAREHOUSE He Xiang Qiao Town The End of Jiang Chuan Road Min. Hang District, Shanghai, China Post Code: 201111 Phone: 86-21 64305126 Fax:86-21 64305126 Stock COSCO GUANGZHOU SHIPSTORES SUPPLY CO., LTD. 139 Gang Wan Road, Huang pu, Guangzhou, China Post Code:510700 Phone:86-20-8227-3646, Fax:86-20-8227-1356 Taiwan CHUGOKU MARINE PAINTS (TAIWAN),LTD. 9F- 3A, No.57, Fu Hsing N. Rd., Taipei, Taiwan, R.O.C. Phone: 886-2-27511422 Fax: 886-2-27517647 E-mail : [email protected] CHUGOKU MARINE PAINTS (TAIWAN) ,LTD. (Kaohsiung Office) 4th Floor, No.5, Lane 25, Li Chun RoadHsiao Kang District, Kaohsiung, Taiwan, R.O.C. Phone:886-(7)8033785 Fax:886-(7)8035126 E-mail: [email protected] CMP Green Processing Technology Co.,Ltd. 9F- 3A, No.57, Fu Hsing N. Rd., Taipei, Taiwan, R.O.C. Phone: 886-2-27763157 Fax:886-2-27517647 E-mail : [email protected] Agent YEE FOO MARINE INDUSTRIAL CO., LTD. 6th Floor, Ya-Hsin Bldg., No.3, Sec.3, Ming Sheng East Rd., Taipei, Taiwan, R.O.C. Phone:886-(2)25039291 Fax:886-(2)25036645/(2)25082934 Agent/Stock YEE FOO MARINE INDUSTRIAL CO., LTD. (Kaohsiung Office) 9F-11, Chi-An Bldg., No.472, Chung Shan 2nd Road, Kaohsing, Taiwan, R.O.C. Phone:886-(7)2510265/(7)2152610 Fax:886-(7)2158933 Hong Kong CHUGOKU MARINE PAINTS (HONG KONG), LTD.

Unit 5-6 P, 23 Floor, Island Place Tower, 510 King's Road, North Point, Hong Kong Phone:852-2576 6376 Fax:852-2576 3607 E-mail：[email protected] India CHUGOKU JENSON & NICHOLSON, LTD. Mackinnon Mackenzie Building, 4 Shoorji Vallabhdas Marg Ballard Estate, MUMBAI 400001 Phone:91-(22)2632325/2632625 Fax:91-(22)2632322 E-mail: [email protected] Indonesia P.T. CHUGOKU PAINTS INDONESIA (Head Office) 8F, Midplaza 1 Bldg., Jalan Jendral Sudirman Kav 10-11, Jakarta 10220, Indonesia Phone:62-(21)5700515 Fax:62-(21)5733787 Telex:65067 MIDPLAZA IA E-mail : [email protected], [email protected] (Factory) Jl. Industri VIII, Desa Pasir Jaya Kec. Jati Uwung Tangerang, Indonesia Phone:62-(21)5902005/5902006 Fax:62-(21)5902007 Agent P. T. CHANDRAMAHKOTA PRIMA 8F, Midplaza 1 Bldg., Jalan Jendral Sudirman Kav 10-11, Jakarta 10220, Indonesia Phone:62-(21)5700515 Fax:62-(21)5733787 Telex:65067 MIDPLAZA IA Japan CMP HOLDINGS PTE., LTD. (Tokyo Office) Sakurada Bldg., 1-3, Nishishinbashi 1-chome, Minato-ku, Tokyo, 105-0003, Japan Phone:81-(3)3506-5858 Fax:81-(3)5511-8542 Telex:2225420 CMP J Korea CHUGOKU-SAMHWA PAINTS, LTD, (Head Office & Factory) #972, Toerae-ri, Hallim-myeon, Gimhae-si, Gyeongnam, Korea. Phone : 82-55-340-0777 Fax: 82-55-340-0739 E-mail : [email protected] (Keoje office) #218-4, Jangpyung-ri, Shinhyun-Yub, Gyeongnam, Korea. Phone:82-55-633-6770 Fax: 82-55-633-6771 (Ulsan Office) #1093-15, Bangeo-Dong, Dong-Gu, Ulsan, Korea TEL 82-52-233-9756/9757 FAX 82-52-201-6659 Malaysia CHUGOKU PAINTS (MALAYSIA) SDN. BHD., (Sales Office) 1201 & 1209, Block A, Menara PJ 18, Persiaran Barat, 46050 Petaling Jaya, Selangor, Malaysia Phone:60-(3)79564373/79562528/79586100

Fax:60-(3)79560219 E-mail: [email protected] (Factory) PLO 430, Jalan Emas Dua, Pasir Gudang Industrial Estate 81700 Pasir Gudang, Johor, Malaysia Phone:60-(7)2511502 Fax:60-(7)2511871 (Penang Office For Domestic Sales) 23, Lorong Perusahaan Sungai Lokan 3/3, 13800 Sungai Dua Butterworth, Penang, Malaysia Phone:60-(4)3566700/3566701 Fax:60-(4)3565699 Agent SING HUA FU HARDWARE SDN. BHD. No. 19-21, Chengal Rd., P.O. Box 1676, 96008 Sibu, Sarawak, Malaysia Phone:60-(84)321496, 321502 Fax:60-(84)326767, 324400 Philippines Licensee CHARTER CHEMICAL & COATING CORP. #1 Mercedes Ave., San Miguel 1600, Pasig City, Philippines Phone:63-(2)641-7101 Fax:63-(2)641-2724 Agent/Stock MAINCOAT, INC. (Manila) Warehouse #5, Piscor Compound, Amang Rodriguez Avenue, Manggahan, Pasig City 1600, Philippines Phone:63-(2)6419951~4 Fax:63-(2)6419863 MAINCOAT, INC. (Cebu) HVG Arcade, Subangdaku, Mandaue City, Philippines Phone:63-(32)346-84-26/346-80-58 Fax:63-(32)346-80-57 Agent/Stock MAINCOAT, INC. (Davao) 6/F Che Yong Cua And Asso. Bldg. Torres Obrero, Davao City Philippines Phone:63-(82)221-2008 Fax:63-(82)221-28-06 MAINCOAT, INC. (GENERAL SANTOS) Blk.21 Lot 2, Phase B, Dona Soledad, Subdivision Makar, General Santos, Philippines Phone:63-(83)552-87-53 MAINCOAT, INC. (CAGAYAN) C/O PICMW Shipyard Corp. Jasaan, Misamis Oriental, Philippines Phone:63-(912)710-02-07 MAINCOAT, INC. (ZAMBOANGA) Kawit, Mega Shipyard, Zamboanga City, Philippines Phone:63-9164333336 Singapore CHUGOKU MARINE PAINTS (SINGAPORE) PTE.,LTD. (Sales & Purchasing Department) 22 Tuas Street, Singapore 638459

Phone:65-6861-6500 Fax:65-6861-3002 Telex:RS 21854 CHUGOKU E-mail : [email protected] (Factory) 21, Tuas Street, Singapore 638458 Phone:65-6861-2264 Fax:65-6861-8306 Telex:RS 21854 CHUGOKU (Financial Department ) 19, Tuas Street, Singapore 638456 Phone:65-6861-2264 Fax:65-6863-8540 CMP HOLDINGS PTE.,LTD. 22, Tuas Street Singapore 638459 Phone:65-6861-6500 Fax:65-6861-3002 (Technical Division) 21, Tuas Street, Singapore 638458 Phone:65-6863-8302 Fax:65-6861-8306 Agent INTRACO LIMITED 230, Victoria Street #12-00 Bugis Junction Towers, Singapore 188024 Phone:65-337-0011 Fax:65-337-7200 Telex:RS 21413 Thailand TOA-CHUGOKU PAINTS CO.,LTD. 159 Sermmit Tower, 19th floor, Soi Sukhumvit 21, Sukhumvit Road, North Klongtoey, Wattana, Bangkok 10110, Thailand Phone:66-(2)2602701 Fax:66-(2)2602700 E-mail: [email protected] TOA-CHUGOKU PAINTS CO.,LTD. (Factory) Wellgrow Industrial Estate 110 Moo 5, Bangna-Trad KM. 36 Rd. T. Bangsamak, A. Bangpakong, Chachoengsao Province 24180, Thailand Phone:66-(38)570499/570501 Fax:66-(38)570500 Vietnam Licensee/Agent/Stock (Marine Paints) HAIPHONG PAINT COMPANY (Head Office. Hai Phong) 12, Lach Tray, Hai Phong, Vietnam Phone:84-(31)843287 Fax:84-(31)845180

Licensee/Agent/Stock (Marine Paints) HAIPHONG PAINT COMPANY (Ho Chi Minh City Office) 306/4D, Binh Gia Street, Ward 13 - Tan Binh District, Ho Chi Minh City, Vietnam Phone:84-(8)8426627 Fax:84-(8)8100677

CMP Datasheet (2003APR)1

Documents

Transcript of CMP Datasheet (2003APR)1