MALZEME YAPISI VE MALZEME YAPISI VE MUAYENESİ DERSİ MUAYENESİ DERSİ
LABORATUAR UYGULAMASILABORATUAR UYGULAMASI
ÇELİK MİKROYAPILARIÇELİK MİKROYAPILARI
![Page 2: Celik Ve Dokme Demirlerin Mikro Yapilari](https://reader031.fdocuments.net/reader031/viewer/2022013108/551f0aa0497959d9398b4fb1/html5/thumbnails/2.jpg)
![Page 3: Celik Ve Dokme Demirlerin Mikro Yapilari](https://reader031.fdocuments.net/reader031/viewer/2022013108/551f0aa0497959d9398b4fb1/html5/thumbnails/3.jpg)
![Page 4: Celik Ve Dokme Demirlerin Mikro Yapilari](https://reader031.fdocuments.net/reader031/viewer/2022013108/551f0aa0497959d9398b4fb1/html5/thumbnails/4.jpg)
Microstructure of a very-low-carbon interstitial-free steel
![Page 5: Celik Ve Dokme Demirlerin Mikro Yapilari](https://reader031.fdocuments.net/reader031/viewer/2022013108/551f0aa0497959d9398b4fb1/html5/thumbnails/5.jpg)
Cementite (arrows) at ferrite grain boundaries 0.04% C steel. 500×
![Page 6: Celik Ve Dokme Demirlerin Mikro Yapilari](https://reader031.fdocuments.net/reader031/viewer/2022013108/551f0aa0497959d9398b4fb1/html5/thumbnails/6.jpg)
Microstructure of plain carbon UNS G10150 steel showing equiaxed ferrite grains with pearlite islands
![Page 7: Celik Ve Dokme Demirlerin Mikro Yapilari](https://reader031.fdocuments.net/reader031/viewer/2022013108/551f0aa0497959d9398b4fb1/html5/thumbnails/7.jpg)
Microstructure of a slow-cooled UNS G10080 steel showing pearlite islands in a ferritic matrix
![Page 8: Celik Ve Dokme Demirlerin Mikro Yapilari](https://reader031.fdocuments.net/reader031/viewer/2022013108/551f0aa0497959d9398b4fb1/html5/thumbnails/8.jpg)
Microstructure of an as-rolled microalloyed steel plate showing equiaxed ferrite grains withbands.
![Page 9: Celik Ve Dokme Demirlerin Mikro Yapilari](https://reader031.fdocuments.net/reader031/viewer/2022013108/551f0aa0497959d9398b4fb1/html5/thumbnails/9.jpg)
![Page 10: Celik Ve Dokme Demirlerin Mikro Yapilari](https://reader031.fdocuments.net/reader031/viewer/2022013108/551f0aa0497959d9398b4fb1/html5/thumbnails/10.jpg)
Microstructure of plain carbon UNS G10400 steel showing equiaxed proeutectoid ferrite grainsoutlining the prior-austenite grain boundaries. The matrix is pearlite
![Page 11: Celik Ve Dokme Demirlerin Mikro Yapilari](https://reader031.fdocuments.net/reader031/viewer/2022013108/551f0aa0497959d9398b4fb1/html5/thumbnails/11.jpg)
![Page 12: Celik Ve Dokme Demirlerin Mikro Yapilari](https://reader031.fdocuments.net/reader031/viewer/2022013108/551f0aa0497959d9398b4fb1/html5/thumbnails/12.jpg)
Microstructure of plain carbon UNS G10800 steel showing colonies of pearlite. 4% picral etch.Original magnification 200×
![Page 13: Celik Ve Dokme Demirlerin Mikro Yapilari](https://reader031.fdocuments.net/reader031/viewer/2022013108/551f0aa0497959d9398b4fb1/html5/thumbnails/13.jpg)
Microstructure of pearlite colonies in plain carbon UNS G10800 steel taken in the scanning electron microscope. 4% picral etch. Original magnification 2000×
![Page 14: Celik Ve Dokme Demirlerin Mikro Yapilari](https://reader031.fdocuments.net/reader031/viewer/2022013108/551f0aa0497959d9398b4fb1/html5/thumbnails/14.jpg)
Microstructure of pearlite colonies in plain carbon UNS G10800 steel taken in the scanningelectron microscope. The plates of cementite are clearly revealed. 4% picral etch. Original magnification10,000×
![Page 15: Celik Ve Dokme Demirlerin Mikro Yapilari](https://reader031.fdocuments.net/reader031/viewer/2022013108/551f0aa0497959d9398b4fb1/html5/thumbnails/15.jpg)
Microstructure of plain carbon UNS G10200 steel showing acicular ferrite with some pearlite(dark etching constituent). This type of acicular appearance is called Widmanstätten structure. 500×
![Page 16: Celik Ve Dokme Demirlerin Mikro Yapilari](https://reader031.fdocuments.net/reader031/viewer/2022013108/551f0aa0497959d9398b4fb1/html5/thumbnails/16.jpg)
Microstructure of 1.2% C-Fe alloy showing cementite outlining the prior-austenite grainboundaries and cementite needles in the grains of pearlite. The grain-boundary cementite is calledproeutectoid cementite. This microstructure represents a hypereutectoid steel. 4% picral etch. Originalmagnification 200×
![Page 17: Celik Ve Dokme Demirlerin Mikro Yapilari](https://reader031.fdocuments.net/reader031/viewer/2022013108/551f0aa0497959d9398b4fb1/html5/thumbnails/17.jpg)
![Page 18: Celik Ve Dokme Demirlerin Mikro Yapilari](https://reader031.fdocuments.net/reader031/viewer/2022013108/551f0aa0497959d9398b4fb1/html5/thumbnails/18.jpg)
(a) YMK demiri birim hücresinde karbon atomu, küpün kenarındaki geniş arayer boşluğuna yerleşmiştir. (b) HMK demiri birim hücresinde küpün kenar atomları arasında daha küçük arayer boşlukları bulunur. (c) HMT birim hücre HMK birim
hücrenin karbon atomu tarafından bozulmasıyla meydana gelmektedir.
![Page 19: Celik Ve Dokme Demirlerin Mikro Yapilari](https://reader031.fdocuments.net/reader031/viewer/2022013108/551f0aa0497959d9398b4fb1/html5/thumbnails/19.jpg)
![Page 20: Celik Ve Dokme Demirlerin Mikro Yapilari](https://reader031.fdocuments.net/reader031/viewer/2022013108/551f0aa0497959d9398b4fb1/html5/thumbnails/20.jpg)
Microstructure of water-quenched low-alloy steel showing lath martensite. 2% nital etch. Original magnification 500×
![Page 21: Celik Ve Dokme Demirlerin Mikro Yapilari](https://reader031.fdocuments.net/reader031/viewer/2022013108/551f0aa0497959d9398b4fb1/html5/thumbnails/21.jpg)
Microstructure of water-quenched UNS G10800 steel showing plate martensite. The light regions between the martensite plates are retained austenite. 1000×
![Page 22: Celik Ve Dokme Demirlerin Mikro Yapilari](https://reader031.fdocuments.net/reader031/viewer/2022013108/551f0aa0497959d9398b4fb1/html5/thumbnails/22.jpg)
1.7 karbonlu ötektoidüstü çelikte iğnesel martenzit (a) Martenzit açık, artık östenit koyu. (b) martenzit koyu, artık östenit açık
![Page 23: Celik Ve Dokme Demirlerin Mikro Yapilari](https://reader031.fdocuments.net/reader031/viewer/2022013108/551f0aa0497959d9398b4fb1/html5/thumbnails/23.jpg)
Fe-0.2C alloy in the (a) water-quenched condition, followed by tempering at 690 °C
![Page 24: Celik Ve Dokme Demirlerin Mikro Yapilari](https://reader031.fdocuments.net/reader031/viewer/2022013108/551f0aa0497959d9398b4fb1/html5/thumbnails/24.jpg)
Fe-1.2C alloy in the (a) water-quenched condition, followed by tempering at 690° C (1275 °F) for(b) 1.5 × 103 s, (c) 1.03 × 104 s, and (d) 6.05 × 105 s
![Page 25: Celik Ve Dokme Demirlerin Mikro Yapilari](https://reader031.fdocuments.net/reader031/viewer/2022013108/551f0aa0497959d9398b4fb1/html5/thumbnails/25.jpg)
Microstructure of a dual-phase sheet steel with islands of martensite in a matrix of ferrite. 4%picral etch. 500×
![Page 26: Celik Ve Dokme Demirlerin Mikro Yapilari](https://reader031.fdocuments.net/reader031/viewer/2022013108/551f0aa0497959d9398b4fb1/html5/thumbnails/26.jpg)
![Page 27: Celik Ve Dokme Demirlerin Mikro Yapilari](https://reader031.fdocuments.net/reader031/viewer/2022013108/551f0aa0497959d9398b4fb1/html5/thumbnails/27.jpg)
Microstructure of heat treated low-alloy steel showing bainite. 4% picral + 2% nital etch. Original magnification 500×
![Page 28: Celik Ve Dokme Demirlerin Mikro Yapilari](https://reader031.fdocuments.net/reader031/viewer/2022013108/551f0aa0497959d9398b4fb1/html5/thumbnails/28.jpg)
Microstructure of quenched low-alloy steel showing a bainitic structure (granular bainite). 4% picral + 2% nital. Original magnification 1000×
![Page 29: Celik Ve Dokme Demirlerin Mikro Yapilari](https://reader031.fdocuments.net/reader031/viewer/2022013108/551f0aa0497959d9398b4fb1/html5/thumbnails/29.jpg)
Microstructure of quenched and tempered low-alloy UNS G43400 steel showing a mixture of bainite (dark etching constituent) and martensite (lighter gray). 4% picral + 2% nital etch. Original magnification 500×
![Page 30: Celik Ve Dokme Demirlerin Mikro Yapilari](https://reader031.fdocuments.net/reader031/viewer/2022013108/551f0aa0497959d9398b4fb1/html5/thumbnails/30.jpg)
Effect of carburizing time on case in 0.15% C steel (0.17C-0.5Si-0.64Mn, wt%) after slow cooling from pack carburization at 940 °C (1725 °F) for (a) 1 h, (b) 2 h, and (c) 4 h., 500×.
![Page 31: Celik Ve Dokme Demirlerin Mikro Yapilari](https://reader031.fdocuments.net/reader031/viewer/2022013108/551f0aa0497959d9398b4fb1/html5/thumbnails/31.jpg)
Grain structure of austenitic type 316L, solution annealed at 954 °C (1750 °F) and etched with (a)waterless Kalling's and (b) Beraha's tint etch
![Page 32: Celik Ve Dokme Demirlerin Mikro Yapilari](https://reader031.fdocuments.net/reader031/viewer/2022013108/551f0aa0497959d9398b4fb1/html5/thumbnails/32.jpg)
AISI H13, heated to 1025 °C (1875 °F), air quenched, and double tempered at 595 °C (1100 °F). 42 HRC. All martensite plus a small amount of very fine undissolved carbide. 2% nital. 1000×
![Page 33: Celik Ve Dokme Demirlerin Mikro Yapilari](https://reader031.fdocuments.net/reader031/viewer/2022013108/551f0aa0497959d9398b4fb1/html5/thumbnails/33.jpg)
MALZEME YAPISI VE MALZEME YAPISI VE MUAYENESİ DERSİ MUAYENESİ DERSİ
LABORATUAR UYGULAMASI LABORATUAR UYGULAMASI
DÖKME DEMİR DÖKME DEMİR MİKROYAPILARIMİKROYAPILARI
![Page 34: Celik Ve Dokme Demirlerin Mikro Yapilari](https://reader031.fdocuments.net/reader031/viewer/2022013108/551f0aa0497959d9398b4fb1/html5/thumbnails/34.jpg)
![Page 35: Celik Ve Dokme Demirlerin Mikro Yapilari](https://reader031.fdocuments.net/reader031/viewer/2022013108/551f0aa0497959d9398b4fb1/html5/thumbnails/35.jpg)
![Page 36: Celik Ve Dokme Demirlerin Mikro Yapilari](https://reader031.fdocuments.net/reader031/viewer/2022013108/551f0aa0497959d9398b4fb1/html5/thumbnails/36.jpg)
Hypoeutectic as-cast gray iron (Fe-2.8%C-1.85%Si-0.5%Mn-0.04%P-0.025%S). Flake graphitetype A. As-polished. 100×
![Page 37: Celik Ve Dokme Demirlerin Mikro Yapilari](https://reader031.fdocuments.net/reader031/viewer/2022013108/551f0aa0497959d9398b4fb1/html5/thumbnails/37.jpg)
Hypereutectic as-cast gray iron (Fe-3.3%C-2.75%Si-0.88%Mn-0.42%P-0.086%S). Flakegraphite type B. As-polished. 90× (microscopic examination 100×)
![Page 38: Celik Ve Dokme Demirlerin Mikro Yapilari](https://reader031.fdocuments.net/reader031/viewer/2022013108/551f0aa0497959d9398b4fb1/html5/thumbnails/38.jpg)
Hypereutectic as-cast gray iron (Fe-4.3%C-1.5%Si-0.5%Mn-0.12%P-0.08%S). Flake graphitetype C (kish graphite). As-polished. 100×
![Page 39: Celik Ve Dokme Demirlerin Mikro Yapilari](https://reader031.fdocuments.net/reader031/viewer/2022013108/551f0aa0497959d9398b4fb1/html5/thumbnails/39.jpg)
Hypereutectic as-cast gray iron (Fe-3.4%C-3.4%Si-0.07%Mn-0.04%P-0.03%Cr-0.47%Cu).Pointlike flake graphite type D. As-polished. 100×
![Page 40: Celik Ve Dokme Demirlerin Mikro Yapilari](https://reader031.fdocuments.net/reader031/viewer/2022013108/551f0aa0497959d9398b4fb1/html5/thumbnails/40.jpg)
Hypereutectic as-cast gray iron (Fe-2.18%C-2.49%Si-0.7%Mn-0.06%P-0.05%S). Flake graphitetype E. As-polished. 100×.
![Page 41: Celik Ve Dokme Demirlerin Mikro Yapilari](https://reader031.fdocuments.net/reader031/viewer/2022013108/551f0aa0497959d9398b4fb1/html5/thumbnails/41.jpg)
As-cast ductile iron. Nodular graphite size is 100 μm. As-polished. 100×
![Page 42: Celik Ve Dokme Demirlerin Mikro Yapilari](https://reader031.fdocuments.net/reader031/viewer/2022013108/551f0aa0497959d9398b4fb1/html5/thumbnails/42.jpg)
Ductile iron. Ferritic matrix. The casting was annealed at 900 °C (1650 °F), held 2 h, quickfurnace cooled to 730 °C (1345 °F), slow furnace cooled to 600 °C (1110 °F), and air cooled. Etched with4% nital. 100×
![Page 43: Celik Ve Dokme Demirlerin Mikro Yapilari](https://reader031.fdocuments.net/reader031/viewer/2022013108/551f0aa0497959d9398b4fb1/html5/thumbnails/43.jpg)
As-cast ductile iron. Ferritic-pearlitic matrix. Etched with 4% nital. 100×
![Page 44: Celik Ve Dokme Demirlerin Mikro Yapilari](https://reader031.fdocuments.net/reader031/viewer/2022013108/551f0aa0497959d9398b4fb1/html5/thumbnails/44.jpg)
Nodular graphite in as-cast ductile iron examined with SEM. Sample was deeply etched with 50% HCl. 1000×
![Page 45: Celik Ve Dokme Demirlerin Mikro Yapilari](https://reader031.fdocuments.net/reader031/viewer/2022013108/551f0aa0497959d9398b4fb1/html5/thumbnails/45.jpg)
As-cast iron with compacted graphite (Fe-3.7%C-2.3%Si-0.21%Mn-0.03%P-0.01%S-0.82%Ni-0.02%Mg). Graphite size is 80 to 160 μm. As polished. 100×
![Page 46: Celik Ve Dokme Demirlerin Mikro Yapilari](https://reader031.fdocuments.net/reader031/viewer/2022013108/551f0aa0497959d9398b4fb1/html5/thumbnails/46.jpg)
As-cast iron with compacted graphite (Fe-2.8%C-1.9%Si-0.55%Mn-0.04%P-0.2%S-0.018%Mg).Ferritic-pearlitic matrix. Etched with 4% nital. 100×
![Page 47: Celik Ve Dokme Demirlerin Mikro Yapilari](https://reader031.fdocuments.net/reader031/viewer/2022013108/551f0aa0497959d9398b4fb1/html5/thumbnails/47.jpg)
Malleable iron (Fe-2.95%C-1.2%Si-0.53%Mn-0.06%P-0.21%S-0.08%Cr-0.10%Cu-0.07%Ni-<0.01%Al). The casting was annealed: at 950 °C (1740 °F), held 10 h, furnace cooled to 720 °C (1330 °F),held 16 h, and air cooled. Pearlitic-ferritic matrix. Etched with 4% nital. 125× (microscopicmagnification 100×)
![Page 48: Celik Ve Dokme Demirlerin Mikro Yapilari](https://reader031.fdocuments.net/reader031/viewer/2022013108/551f0aa0497959d9398b4fb1/html5/thumbnails/48.jpg)
As-cast white iron (Fe-3.0%C-2.7%Si-0.45%Mn-0.07%P-0.025%S). C, cementite; P, pearlite.Etched with 4% nital. 400×
![Page 49: Celik Ve Dokme Demirlerin Mikro Yapilari](https://reader031.fdocuments.net/reader031/viewer/2022013108/551f0aa0497959d9398b4fb1/html5/thumbnails/49.jpg)
White high-chromium cast iron (see Fig. 43). PC, primary carbides; EC, eutectic carbides inmartensitic matrix with fine, globular secondary carbides. The casting was heat treated at 1000 °C (1830°F), held 1 h, furnace cooled to 550 °C (1020 °F), held 4 h in a 400 °C (750 °F) salt bath, and air cooled.Etched with glyceregia. 1000×
![Page 50: Celik Ve Dokme Demirlerin Mikro Yapilari](https://reader031.fdocuments.net/reader031/viewer/2022013108/551f0aa0497959d9398b4fb1/html5/thumbnails/50.jpg)
As-cast gray iron (Fe-3.33%C-1.64%Si-0.31%Mn-1.37%P-0.107%S). Ternary phosphoruseutectic. Etched with 4% nital. 1300× (microscopic magnification 1000×)