Boosting solar-cell efficiencywith quantum-dot-basednanotechnology
Seth Hubbard and Ryne Raffaelle
Inserting indium arsenide quantum dots into crystalline III-V
semiconductor-based photovoltaics results in both enhanced short-
circuit current and improved efficiency.
Every hour, the sun radiates more energy onto the Earths
surface than is consumed globally in one year. However, to best
harness this vast source of power, efficient and cost-effective so-
lar photovoltaic (PV) energy conversion is required. In partic-
ular, improving the efficiency of III-V-type semiconductor PV
devices is a goal for both the space and terrestrial research
communities. Current high-performance space technology relieson crystalline III-V materials to produce conversion efficiencies
greater than 31%.1 High power-conversion efficiencies directly
increase mass-specific power, thus lowering the costs associ-
ated with spacecraft deployment. Additionally, recent advances
have demonstrated that III-V-based concentrator PVs can pro-
duce high efficiencies (> 40%) and, therefore, reduce the cost of
power generation.2
Numerous approaches can increase both solar-cell efficiency
and/or mass-specific power, including lightweight substrates,
substrate removal, or bandgap engineering of multijunction
solar cells (MJSCs) using quantum dots (QDs).3, 4 Luque and
Marti5 also proposed a novel extension of the bandgap engi-
neering approach. It uses multiple QD superlattices to form an
optically isolated intermediate band (IB) within the bandgap of
a standard single-junction solar cell. Photons with energy below
the host bandgap are absorbed from the host valence to the inter-
mediate band, and from the intermediate to the host conduction
band. As these lower-energy photons are normally lost to trans-
mission in standard single-junction solar cells, the IB approach
may result in a high limiting efficiency. Recently, several exper-
iments have demonstrated the key operating principles of the
IB solar cell using both indium arsenide6, 7 (InAs) and gallium
antimonide8
QDs in a gallium arsenide (GaAs) host.
Figure 1. (a) Quantum-dot (QD)-enhanced solar-cell design concept.
(b) Current density-voltage curves for control and 520 layer enhanced
cells under one sun global air mass 1.5 (AM1.5g) light. These cells
did not have antireflective coating. InGaP: Indium gallium phosphide.
GaAs: Gallium arsenide.
The Rochester Institute of Technologys NanoPower Research
Laboratories (NPRL) have made significant advances in this area
by developing new nanomaterials and devices. We have engi-
neered III-V-type solar cells to take advantage of the extended
absorption
spectrum of lower-bandgap heterostructures (such as QDs) in-
serted into the current-limiting junction of an MJSC.4 The larger
absorption spectrum of the nanostructures enhances the over-
all short-circuit current and global efficiency of the cell. Mod-
els of an indium gallium phosphide (InGaP)/indium gallium
arsenide (InGaAs)/germanium (Ge) triple-junction solar cell, in
which QDs extend the middle junctions absorption spectrum,
indicate that we could raise the theoretical limiting efficiency to
47% under one sun illumination. These devices may also have
additional benefits, such as enhanced radiation tolerance and
temperature coefficients.9
Continued on next page
-
8/2/2019 Boosting Solar-cell Efficiency
2/3
10.1117/2.1201002.002553 Page 2/3
Figure 2. 520 layer QD-enhanced solar cells show a net increase in
external quantum efficiency (EQE) at IR wavelengths compared to the
baseline GaAs.
We demonstrated the feasibility of the QD tuning approach us-
ing strain-balanced InAs dots inserted in the intermediate (i)
region of a GaAs p-i-n solar cell.7,10 The solar-cell structure
(grown by organometallic vapor-phase epitaxy) is shown in
Figure 1(a). Figure 1(b) shows the illuminated one sun global
air mass 1.5 (AM1.5g) current density-voltage .JV / curves for
a control GaAs cell without quantum dots and for cells with
520 stacked layers of InAs QDs. We fabricated these cells us-
ing standard III-V processing technology and a concentrator
grid designed with 20% metallization coverage. The control re-
sults were equal or close to the standard values for GaAs solar
cells. Figure 1(a) clearly shows the enhancement in short-circuit
current using QDs. This is a direct result of photo-generated
current contributed by the nanoparticles. We expect the trend
to continue with addition of QDs, because a greater portion
of the sub-GaAs bandgap solar spectrum should be absorbed
with increasing number (i.e., volume). Additionally, the strain-balancing technique employed for QD growth led to higher ma-
terial quality in layers grown on top of the InAs nanoparticles.
This has enabled short-circuit current enhancement and minimal
open-circuit voltage degradation.7
Measuring the cells external quantum efficiency (EQE) pro-
vided a spectroscopic means to study how QDs affect the de-
vice current-voltage characteristics. EQE measures the number
of electrons or holes collected as photocurrent per incident pho-
ton at a particular wavelength. Figure 2 shows the EQE for the
baseline and 520 QD samples. All three QD samples show an
increased response at wavelengths greater than the GaAs band
Figure 3. Direct air mass 1.5 (AM1.5d) efficiency and short-circuit
current (JSC ) versus concentration for the baseline and QD cells. The
enhanced cells show improved efficiency at higher concentration.
edge. This indicates that a portion of the short-circuit current of
these cells is generated by QD-related absorption processes. Ad-
ditionally, increasing the number of layers raises the EQE at all
QD-related transitions. At 909nm (1.36eV) this amounted to in-
creases from 2.5 to 9.2% by increasing the stacking from five to
20 (see Figure 3). This was clear evidence that raising the vol-ume of the quantum-dot absorbers successively increases short-
circuit current.
To assess the spectral enhancement of the QDs at higher con-
centration, we observed the control and 20-layer cells under
high-intensity illumination.11 The trends seen at one sun con-
tinued, with the enhanced cells showing improved short-circuit
currents (see Figure 3). All cells, including the baseline, show a
slight superlinear trend in current, as has been observed in GaAs
materials because of high-level injection effects. The 20-layer
QD cell generated the largest short-circuit current (7.53A/cm2)
at 440suns. This represents an 11% increase compared to the
control-cell current at the same concentration. The open-circuit
voltage for all cells rose logarithmically with concentration.
We calculated the efficiency for each type of cell under di-
rect air mass 1.5 (AM1.5d) conditions (see Figure 3). Efficiency
peaked near 400suns, consistent with our concentrator-grid de-
sign. The QD-enhanced cell showed almost 18% power effi-
ciency at 400suns. This represented a 1% absolute efficiency
improvement compared to the control (a 6% relative improve-
ment). Under high-illumination intensity, the reduced
Continued on next page
-
8/2/2019 Boosting Solar-cell Efficiency
3/3
10.1117/2.1201002.002553 Page 3/3
(longer-wavelength) effective bandgap of the cell, as well as in-
creased optical and thermal extraction of QD-generated carri-
ers, leads to direct improvement in cell efficiency. This boostwas due to higher short-circuit current combined with minimal
open-circuit voltage loss.
Nanomaterial-based energy technologies have great promise
for both terrestrial and extraterrestrial applications. Our exper-
imental demonstration of current and efficiency enhancement
in QD-based solar cells represents a milestone to breaking effi-
ciency limits through using nanomaterials. Our next steps aim
to increase the absorption cross section of the quantum dots by
both increasing the number of QD layers and investigating new
multilayer device designs. In addition, we are continuing our ef-
forts to understand and model radiation and temperature effectsin these solar cells.
We wish to acknowledge the hard work and dedication of the NanoPV
group at NPRL. Specific contributions to this work were submitted
by David Forbes, Cory Cress, John Anderson, and graduate students
Chris Bailey and Stephen Polly. We also acknowledge support for our
work from the US Department of Energy (DE-FG36-08GO18012) and
the US Government.
Author Information
Seth Hubbard
NPRL
Rochester Institute of Technology (RIT)
Rochester, NY
Seth Hubbard is assistant professor of physics at RIT and the
photovoltaics group leader at the NPRL. He currently leads a
team of graduate students and research staff working on the
epitaxial growth, fabrication, and characterization of nanostruc-
tured solar photovoltaic devices.
Ryne RaffaelleNational Center for Photovoltaics
National Renewable Energy Laboratory
Golden, CO
Ryne Raffaelle is currently the director of the National Center for
Photovoltaics. He was formerly the founder and director of the
NPRL. His research interests include energy storage and conver-
sion systems, nanomaterials, and carbon nanotubes.
References
1. M. Stan, D. Aiken, B. Cho, A. Cornfeld, J. Diaz, V. Ley, A. Korostyshevsky,
P. Patel, P. Sharps, and T. Varghese, Very high efficiency triple junction so-lar cells grown by MOVPE, J. Cryst. Growth 310 (23), pp. 52045208, 2008.
doi:10.1016/j.jcrysgro.2008.07.024
2. J. F. Geisz, D. J. Friedman, J. S. Ward, A. Duda, W. J. Olavarria, T. E. Moriarty,
J. T. Kiehl, M. J. Romero, A. G. Norman, and K. M. Jones, 40.8% efficient inverted
triple-junction solar cell with two independently metamorphic junctions, Appl. Phys.
Lett. 93 (12), 2008. doi:10.1063/1.2988497
3. P. Sharps, A. Cornfeld, M. Stan, A. Korostyshevsky, V. Ley, B. Cho, T. Varghese,
J.Diaz,and D. Aiken, The future of high efficiency, multi-junction space solar cells, Proc.
33rd IEEE Photovolt. Spec. Conf. 1, pp. 16, 2008. doi:10.1109/PVSC.2008.4922854
4. S. M. Hubbard, C. Bailey, S. Polly, C. Cress, J. Andersen, D. Forbes, and
R. Raffaelle, Nanostructured photovoltaics for space power, J. Nanophoton. 3 (1),
pp. 031880031816, 2009.
5. A. Luque and A. Marti, Increasing the efficiency of ideal solar cells by photon in-
duced transitions at intermediate levels, Phys. Rev. Lett. 78, pp. 50145017, 1997.
doi:10.1103/PhysRevLett.78.5014
6. A. Marti, E. Antolin, C. R. Stanley, C. D. Farmer, N. Lopez, P. Diaz,
E. Canovas, P. G. Linares, and A. Luque, Production of photocurrent due tointermediate-to-conduction-band transitions: a demonstration of a key operating prin-
ciple of the intermediate-band solar cell, Phys. Rev. Lett. 97, p. 247701, 2006.
doi:10.1103/PhysRevLett.97.247701
7. S. M. Hubbard, C. D. Cress, C. G. Bailey, R. P. Raffaelle, S. G. Bailey, and
D. M. Wilt, Effect of strain compensation on quantum dot enhanced GaAs solar cells,
Appl. Phys. Lett. 92, p. 123512, 2008. doi:10.1063/1.29036998. R. Laghumavarapu, M. El-Emawy, N. Nuntawong, A. Moscho, L. F. Lester,
and D. L. Huffaker, Improved device performance of InAs/GaAs quantum dot solar
cells with GaP strain compensation layers , Appl. Phys. Lett. 91 (24), p. 243115, 2007.
doi:10.1063/1.2816904
9. C. D. Cress, S. M. Hubbard, B. J. Landi, R. P. Raffaelle, and D. M. Wilt, Quantum
dot solar celltolerance to alpha-particle irradiation, Appl. Phys.Lett. 91, p. 183108, 2007.
doi:10.1063/1.2803854
10. C. G. Bailey, S. M. Hubbard, D. V. Forbes, and R. P. Raffaelle, Evaluation of strain
balancing layer thickness for InAs/GaAs quantum dot arrays using high resolution x-
ray diffraction and photoluminescence, Appl. Phys. Lett. 95, pp. 203110203113, 2009.
doi:10.1063/1.3264967
11. S. M. Hubbard, C. Bailey, S. Polly, R. Aguinaldo, D. Forbes, and R. Raffaelle,Characterization of quantum dot enhanced solar cells for concentrator PV, Proc. 34th IEEE
Photovolt. Spec. Conf. 1, pp. 16, 2009.
c
2010 SPIE