Aluminium Magnesium Boride
Transcript of Aluminium Magnesium Boride
-
7/24/2019 Aluminium Magnesium Boride
1/2
Aluminium magnesium boride
Aluminum magnesium boride or BAM is achemical
compound of aluminium, magnesium and boron.
Whereas its nominal formula is AlMgB14, the chemical
composition is closer to Al.Mg.B14. It is aceramic
alloy that is highly resistive to wear and has a low
coefficient of sliding friction, reaching a record value
of 0.02 in lubricated AlMgB14TiB2 composites. First
reported in 1970, BAM has anorthorhombic structure
with four icosahedral B12 units per unit cell.[1] This
ultrahard material has acoefficient of thermal expansion
comparable to that of other widely used materials suchas steel and concrete.
1 Synthesis
BAM powders are produced by heating a nearly
stoichiometric mixture of boron, aluminium and mag-
nesium for a few hours at a temperature in the range
9001500 C. Spurious phases are then dissolved in hot
hydrochloric acid.[1][2] To ease the reaction and make the
product more homogeneous, the starting mixture can be
processed in a high-energy ball mill. All pretreatmentsare carried out in a dry, inert atmosphere to avoid oxida-
tion of the metal powders.[3][4]
BAM films can be coated on silicon or metals bypulsed
laser deposition, using AlMgB14 powder as a target,[5]
whereas bulk samples are obtained by sintering the
powder.[6]
BAM usually contains small amounts of impurity ele-
ments (e.g., oxygen and iron) that enter the material dur-
ing preparation. It is thought that the presence of iron
(most often introduced as wear debris from mill vials
and media) serves as a sintering aid. BAM can be al-
loyed withsilicon,phosphorus,carbon,titanium diboride
(TiB2),aluminium nitride(AlN),titanium carbide(TiC)
orboron nitride(BN).[4][6]
2 Properties
2.1 Structure
Most superhard materials have simple, high-symmetry
crystal structures, e.g., diamond cubic or zinc blende.
However, BAM has a complex, low-symmetry crystalstructure with 64 atoms per unit cell. The unit cell is
orthorhombicand its most salient feature is four boron-
Crystal structure of BAM viewed along the a crystal axis. Blue:
Al, green: Mg, red: B.
containing icosahedra. Each icosahedron contains 12
boron atoms. Eight more boron atoms connect the icosa-
hedra to the other elements in the unit cell. The oc-
cupancy of metal sites in the lattice is lower than one,
and thus while the material is usually identified with theformula AlMgB14, its chemical composition is closer
to Al.Mg.B14.[3][4] Such non-stoichiometry is com-
mon for borides (seecrystal structure of boron-rich metal
boridesand boron carbide). The unit cell parameters of
BAM are a = 1.0313 nm, b = 0.8115 nm, c= 0.5848
nm,Z= 4 (four structure units per unit cell),space group
Imam,Pearson symboloI68, density 2.59 g/cm3.[1] The
melting point is roughly estimated as 2000 C.[7]
2.2 Optoelectronic
BAM has a bandgap of about ~1.5 eV. Significant ab-
sorption is observed at sub-bandgap energies and at-
tributed to metal atoms. Electrical resistivity depends
on the sample purity and is about 104 Ohmcm. The
Seebeck coefficientis relatively high, between 5.4 and
8.0 mV/K. This property originates from electron trans-
fer from metal atoms to the boron icosahedra and is fa-
vorable for thermoelectric applications.[7]
2.3 Hardness
The microhardness of BAM powders is 3235 GPa. Itcan be increased to 4550 GPa upon alloying BAM
with of TiB2[4] or by depositing a quasi-amorphous
1
https://en.wikipedia.org/wiki/Microhardnesshttps://en.wikipedia.org/wiki/Seebeck_coefficienthttps://en.wikipedia.org/wiki/Pearson_symbolhttps://en.wikipedia.org/wiki/Space_grouphttps://en.wikipedia.org/wiki/Boron_carbidehttps://en.wikipedia.org/wiki/Crystal_structure_of_boron-rich_metal_borideshttps://en.wikipedia.org/wiki/Crystal_structure_of_boron-rich_metal_borideshttps://en.wikipedia.org/wiki/Icosahedrahttps://en.wikipedia.org/wiki/Orthorhombichttps://en.wikipedia.org/wiki/Unit_cellhttps://en.wikipedia.org/wiki/Zincblende_(crystal_structure)https://en.wikipedia.org/wiki/Diamond_cubichttps://en.wikipedia.org/wiki/Superhard_materialhttps://en.wikipedia.org/wiki/Boron_nitridehttps://en.wikipedia.org/wiki/Titanium_carbidehttps://en.wikipedia.org/wiki/Aluminium_nitridehttps://en.wikipedia.org/wiki/Titanium_diboridehttps://en.wikipedia.org/wiki/Carbonhttps://en.wikipedia.org/wiki/Phosphorushttps://en.wikipedia.org/wiki/Siliconhttps://en.wikipedia.org/wiki/Sinteringhttps://en.wikipedia.org/wiki/Sinteringhttps://en.wikipedia.org/wiki/Pulsed_laser_depositionhttps://en.wikipedia.org/wiki/Pulsed_laser_depositionhttps://en.wikipedia.org/wiki/Ball_millhttps://en.wikipedia.org/wiki/Hydrochloric_acidhttps://en.wikipedia.org/wiki/Stoichiometrichttps://en.wikipedia.org/wiki/Coefficient_of_thermal_expansionhttps://en.wikipedia.org/wiki/Icosahedronhttps://en.wikipedia.org/wiki/Orthorhombic_crystal_systemhttps://en.wikipedia.org/wiki/Alloyhttps://en.wikipedia.org/wiki/Ceramichttps://en.wikipedia.org/wiki/Boronhttps://en.wikipedia.org/wiki/Magnesiumhttps://en.wikipedia.org/wiki/Aluminiumhttps://en.wikipedia.org/wiki/Chemical_compoundhttps://en.wikipedia.org/wiki/Chemical_compound -
7/24/2019 Aluminium Magnesium Boride
2/2
2 5 EXTERNAL LINKS
BAM film.[5] Addition of AlN or TiC to BAM re-
duces its hardness.[6] By definition, a hardness value ex-
ceeding 40 GPa makes BAM a superhard material. In
the BAMTiB2 composite, the maximum hardness and
toughness are achieved at ~60 vol.% of TiB2.[6] The wear
rate is improved by increasing the TiB2 content to 70
80% at the expense of ~10% hardness loss.[8] The TiB2additive is a wear-resistant material itself with a hardness
of 2835 GPa.[6]
2.4 Thermal expansion
Thethermal expansion coefficient (TEC) for AlMgB14was measured as 9106 K1 by dilatometry and by high
temperatureX-ray diffraction using synchrotron radia-
tion. This value is fairly close to the COTE of widely used
materials such as steel, titanium and concrete. Based on
the hardness values reported for AlMgB14and the mate-
rials themselves being used as wear resistant coatings, the
COTE of AlMgB14 could be used in determining coat-
ing application methods and the performance of the parts
once in service.[3][4]
2.5 Friction
A composite of BAM and TiB2(70 volume percent) has
one of the lowest values of friction coefficients, which
amounts to 0.040.05 in dry scratching by a diamond
tip[5] (cf. 0.04 for Teflon) and decreases to 0.02 in water-
glycol-based lubricants.[9][10]
3 Applications
BAM is commercially available and is being studied for
potential applications. For example, pistons, seals and
blades on pumps could be coated with BAM or BAM
+ TiB2 to reduce friction between parts and to increase
wear resistance. The reduction in friction would reduce
energy use. BAM could also be coated onto cutting tools.
The reduced friction would lessen the force necessary
to cut an object, extend tool life, and possibly allow in-creased cutting speeds. Coatings only 23 micrometers
thick have been found to improve efficiency and reduce
wear in cutting tools.[11]
4 References
[1] V. I. Matkovich and J. Economy (1970). Structure of
MgAlB14 and a brief critique of structural relationships
in higher borides. Acta Cryst. B 26 (5): 616621.
doi:10.1107/S0567740870002868.
[2] Higashi, I; Ito, T (1983). Refinement of the structure ofMgAlB14. Journal of the Less Common Metals92 (2):
239.doi:10.1016/0022-5088(83)90490-3.
[3] Russell, A. M., B. A. Cook, J. L. Harringaand T. L. Lewis
(2002). Coefficient of thermal expansion of AlMgB14.
Scripta Materialia 46 (9): 62933. doi:10.1016/S1359-
6462(02)00034-9.
[4] Cook, B. A., J. L. Harringa, T. L. Lewis and A. M.
Russell (2000). A new class of ultra-hard materials
based on AlMgB14. Scripta Materalia42 (6): 597602.
doi:10.1016/S1359-6462(99)00400-5.
[5] Tian, Y.; Bastawros, A. F.; Lo, C. C. H.; Constant, A.
P.; Russell, A. M.; Cook, B. A. (2003). Superhard
self-lubricating AlMgB14 films for microelectromechan-
ical devices. Applied Physics Letters 83 (14): 2781.
doi:10.1063/1.1615677.
[6] Ahmed, A; Bahadur, S; Cook, B; Peters, J (2006). Me-
chanical properties and scratch test studies of new ultra-
hard AlMgB14 modified by TiB2. Tribology Interna-
tional39 (2): 129.doi:10.1016/j.triboint.2005.04.012.
[7] Werhcit, Helmut; Kuhlmann, Udo; Krach, Gunnar; Hi-gashi, Iwami; Lundstrm, Torsten; Yu, Yang (1993).
Optical and electronic properties of the orthorhombic
MgAIB14-type borides. Journal of Alloys and Com-
pounds202: 269.doi:10.1016/0925-8388(93)90549-3.
[8] Cook, B.A.; Peters, J.S.; Harringa, J.L.; Rus-
sell, A.M. (2011). Enhanced wear resistance in
AlMgB14TiB2 composites. Wear 271 (56): 640.
doi:10.1016/j.wear.2010.11.013.
[9] Kurt Kleiner (2008-11-21).Material slicker than Teflon
discovered by accident. New Scientist. Archived from the
original on 20 December 2008. Retrieved 2008-12-25.
[10] Higdon, C.; Cook, B.; Harringa, J.; Russell, A.; Gold-
smith, J.; Qu, J.; Blau, P. (2011). Friction and wear
mechanisms in AlMgB14-TiB2 nanocoatings. Wear271
(910): 2111.doi:10.1016/j.wear.2010.11.044.
[11] Tough nanocoatins boost industrial energy efficiency.
Ames Laboratory. Press release. Department of Energy.
18 Nov. 2008.
5 External links
Material slicker than Teflon New Scientist Article onBAM.
News on AlMgB14 Press Release with photos.
http://www.ameslab.gov/final/News/2008rel/Nanocoatings.htmlhttp://www.newscientist.com/article/dn16102-material-slicker-than-teflon-discovered-by-accident.htmlhttp://www.ameslab.gov/node/5245https://dx.doi.org/10.1016%252Fj.wear.2010.11.044https://en.wikipedia.org/wiki/Digital_object_identifierhttp://web.archive.org/web/20081220162702/http://www.newscientist.com/article/dn16102-material-slicker-than-teflon-discovered-by-accident.htmlhttp://www.newscientist.com/article/dn16102-material-slicker-than-teflon-discovered-by-accident.htmlhttp://www.newscientist.com/article/dn16102-material-slicker-than-teflon-discovered-by-accident.htmlhttps://dx.doi.org/10.1016%252Fj.wear.2010.11.013https://en.wikipedia.org/wiki/Digital_object_identifierhttps://dx.doi.org/10.1016%252F0925-8388%252893%252990549-3https://en.wikipedia.org/wiki/Digital_object_identifierhttps://dx.doi.org/10.1016%252Fj.triboint.2005.04.012https://en.wikipedia.org/wiki/Digital_object_identifierhttps://dx.doi.org/10.1063%252F1.1615677https://en.wikipedia.org/wiki/Digital_object_identifierhttps://dx.doi.org/10.1016%252FS1359-6462%252899%252900400-5https://en.wikipedia.org/wiki/Digital_object_identifierhttps://dx.doi.org/10.1016%252FS1359-6462%252802%252900034-9https://dx.doi.org/10.1016%252FS1359-6462%252802%252900034-9https://en.wikipedia.org/wiki/Digital_object_identifierhttps://dx.doi.org/10.1016%252F0022-5088%252883%252990490-3https://en.wikipedia.org/wiki/Digital_object_identifierhttps://dx.doi.org/10.1107%252FS0567740870002868https://en.wikipedia.org/wiki/Digital_object_identifierhttps://en.wikipedia.org/wiki/X-ray_diffractionhttps://en.wikipedia.org/wiki/Thermal_expansionhttps://en.wikipedia.org/wiki/Superhard_material