Wear is material loss on surface by means of several different mechanisms.
The two main wearing mechanisms in crusher cavity are:• Abrasive wear• Fatigue wear
The main wearing mechanism in crusher cavity is abrasive wearing. Fatigue wear is also present as wear part are subjected to multiple compression or impact loads.
Abrasive wear (or abrasion) Crushers typically compress the feed materi-al between the fixed and movable wear parts. Besides the breakage of the feed material, this is also wearing material away from the wear part. Wearing micromecha-nisms are:• Microploughing• Microcutting• Microcracking• Microfatigue
During the crushing cycle, gouging or high stress abrasion is present depending on the particle size of feed material. Between the crushing cycles when particles of feed material are sliding against wear parts, low stress abrasion is present.
Gouging abrasion • Large particles• High impact or compression loads• Good work hardening on manganese
High stress or grinding abrasion• Smaller particles• High compression load• Less work hardening on manganese
Low stress or scratching abrasion• No compression load• Scratching abrasion while material is sliding at the surface of wear part• Less work hardening on manganese
Wear parts application guide - Wear and materials
Wear
4
Several different factors affect the wear of wear parts. Type of wear, environmental factors, crusher operating parameters, feed mate-rial and wear part properties are just a few of these.
However, one of the the most notable factor in the wear of crusher wear parts is the abra-siveness of feed material.
The abrasiveness of the feed material can be determined at Metso’s rock laboratory using a test for abrasiveness. The following table indicates the abrasiveness of rock based on this test.
Crushability of the rock can be determined with the same equipment used to identify abrasiveness. Crushability indicates how easi-ly the rock material breaks down. Difficult rock with a low crushability value requires more crushing energy than easier rocks with a higher crushability value.
ABRASIVENESS CLASSIFICATION
French abrasiveness [g/ton] Abrasion index
Non abrasive 0 - 100 -0.1Slightly abrasive 100 - 600 0.1 - 0.4Medium abrasive 600 - 1200 0.4 - 0.6Abrasive 1200 - 1700 0.6 - 0.8Very abrasive 1700 - 0.8 -
CRUSHABILITY CLASSIFICATION
Bond work index[kWh/t]
Crushability [%]
Los Angeles value Ai-8mm product Shatter index
Very easy 0 - 7 50 - 27 - 60 - 40 -Easy 7 - 10 40 - 50 22- 27 45 - 60 35 - 40Medium 10 - 14 30 - 40 17 - 22 30 - 45 30 - 35Difficult 14 - 18 20 - 30 12 - 17 15 - 30 25 - 30Very difficult 18 - - 20 - 12 - 15 - 25
5
CRUSHABILITY CLASSIFICATION
Bond work index[kWh/t]
Crushability [%]
Los Angeles value Ai-8mm product Shatter index
Very easy 0 - 7 50 - 27 - 60 - 40 -Easy 7 - 10 40 - 50 22- 27 45 - 60 35 - 40Medium 10 - 14 30 - 40 17 - 22 30 - 45 30 - 35Difficult 14 - 18 20 - 30 12 - 17 15 - 30 25 - 30Very difficult 18 - - 20 - 12 - 15 - 25
6
Austenitic manganese steelAustenitic manganese steel is a very tough and ductile material having a high impact toughness. Mn-steel is rather soft material having an initial hardness of approx. 220-250 HV. The wear resistance of manganese steel is based on a work hardening phenomenon.
When the surface of Mn-steel is under heavy impact or a compressive load, it hardens from the surface while the base material remains tough. The depth and hard-ness of work hardened surface vary depend-ing on application and Mn-steel grade.
The work hardened layer can be between 10 and 15 mm deep and hardness can be up to 600 HV in primary applications. In fine crushing applications the work hardened layer is thinner and hardness is usually around 350-500 HV.The Mn/C ratio and amount of Cr is not only relevant when it comes to the wear resis-tance of Mn-steel. The entire casting process
needs to be well optimized to produce high quality wear parts. Below are a few critical steps to producing high quality Mn-steel castings.
It all begins with raw material selection where raw materials are carefully selected for melting in order to get the material analysis inside strict specifications and to reduce the amount of certain impurities. During melting and pouring the temperatures are carefully controlled in order to achieve fine grain structure for the castings. At the same time samples are taken to verify the material analysis and adjust if necessary. Melted metal is then poured into sand molds where the metal slowly solidifies. The molds have carefully designed feeding and gating chan-
nels to ensure solid castings. Heat treatment is another critical step to
producing ductile high quality castings. Temperature, time and quenching need to be well controlled in order to avoid grain boundary carbide formation. After the heat treatment has been completed, castings are machined according to strict tolerance to ensure a perfect fit to the crusher.
Besides the casting, the cavity shape has a significant effect on the performance of the crusher and lifetime of wear parts. Cavity shapes are optimized by using sophisticated simulation tools and continuous testing and follow-up.
High
High
Low
Low
Mn/C -ratio
Mn-content %
Work hardening starts with lower impact energy: - weak feed - small gradation - low reduction ratio
Work hardening starts with high impact energy: - high-strength feed - large gradation - high reduction ratio
Steel strength increases
Steel toughness increases
Utilization areas of di�erent Mn-grades
7
Distance from surface
Work Hardening vs. Final Hardness
HBHardness
When Mn-steel liners get good lifetime the work hardening process has succeeded and hardness pro�le is good
Maximum hardness depends onapplication, gradation, feedstrength, etc.
PrimarySecondaryFine
Abrasion resistance
Austenitic manganese steel
Martensitic steels
White cast iron
Ceramics
Toughness
Metso XT seriesThe Metso XT series has a wide range of Mn-steels with different alloying to suit each customer’s application and the relevant rock properties. The XT series covers Mn grades from 11% to 24% and some grades are alloyed with Cr and other alloying elements.
All materials are not available for each crusher.
Mn grade Alloying
XT510 Low grade Hadfield manganese steel
XT520 Low grade manganese steel with molybde-nium alloying
XT610 Low grade manganese steel with chromium alloying
XT710 High grade manganese steel with chromium alloying
XT720 High grade manganese steel with chromium alloying
XT750 High grade special manganese steel
XT770 High grade special manganese steel with molybdenium alloying
XT810 High grade manganese steel with chro-mium alloying and special treatment
8
This material group offers quenched and tempered (QT) in good toughness for various crushing applications of impact and compressing crushing.
These steels has been tailored for various so-lutions having optimum microstructure with sufficent hardness and toughness achieved by heat treatment process called quenching and tempering. Precise control of time and temperature are the key parameters. Some grades are thermomechanically rolled. (AR steels or so called boron steels).
Conserning wear these steel give the sufficent hardness and toughness combina-tion with economical way.
Consult your Metso representative for ap-plications. Typical applications are in HSI and
primary gyratory wear parts.
QT steels (Martensitic and AR steels)
Composites
Abrasion resistance
Austenitic manganese steel
Martensitic steels
White cast iron
Ceramics
Toughness
9
High chromium ironsThis material group is offering classical solutions as well as more specialised solutions.
These materials are of low cost, and good choise for many applications. The wear resistance is based on the hard carbides on the relative hard matrix, still the composition and structure can be tailored considerably. Generally high cromium irons are commonly used in abrasive wear applications.
Consult your Metso representative for applications. Typical examples are VSI and HSI
components and primary gyratory concaves.
Abrasion resistance
Austenitic manganese steel
Martensitic steels
White cast iron
Ceramics
Toughness
10
Metal matrix composites (MMC)MMC material group is the newest in Metso offering. Metal matrix composites are com-bining tough metallic matrix and hard ceramic or hard metallic materials together.
Wear resistance of material is combined with both optimum material strength (hard-ness) and toughness properties. The increas-ing strength (in metallic materials with sufficient toughness) has generally been observed to increase wear resistance in many wear environments. However, increas-ing strength generally results in loss of toughness.
In order to achieve the higher strength and toughness of metallic material, compos-ite structure is the most promising solution.
Consult your Metso representative for applications. Examples of product are for example Xwin® product range in HSI crush-ers.
Xwin® is a registered trademark of Magotteaux.
Hybrid materialsHybrid materials are constantly increasing in Metso offering. Hybrid materials are combin-ing several kinds of materials together and can be called also as multimaterials.
These kind of structures have clear benefit in extreme operations, they can be tailored
for specific operation and form a functional wear control areas. The most wear resistant materials are located where they are needed, and with multimaterial joints even tailored surface (topocraphy) can be formed in wear surfaces.
Hybrid can be combination of several types of irons, steels and ceramics or even rubber with the ceramics or metals.
Consult your Metso representative for applications. Typical example of product: Super jaws.
Weld overlaysWeld overlays combine high wear resistance on the surface and tough basematerial. Some of the overlays are well repairable on the field operations.
The most classical overlay has the properi-ties of the high chromium iron, but there is also more sophisticated overlays available as well. The clear advantage of the overlays is
that they can easily be welded on the places where highest wear resistance is needed and the usage of the expensive material is mini-mized.
Consult your Metso representative for applications and overlay selection. Typical products are shields, quards and liners.
Composites
Abrasion resistance
Austenitic manganese steel
Martensitic steels
White cast iron
Ceramics
Toughness
Composites
11
Legal noticeMetso reserves the right to make changes in specifications and other information con-tained in this publication without prior notice and the reader should in all cases consult Metso to determine whether any such changes have been made. This manual may not be reproduced and is intended for the exclusive use of Metso customer.
The terms and conditions governing the sale of Metso hardware products and the licens-ing and use of Metso software products con-sists solely of those set forth in the written contract between Metso and its customer. No statement contained in this publication, including statements regarding capacity, suitability for use, or performance of prod-ucts, shall be considered a warranty by Metso for any purpose or give rise to any liability of Metso.
In no event will Metso be liable for any incidental, indirect, special, or consequential damages (including lost profits), arising out of or relating to this publication or the information contained in it, even if Metso has been advised, knew, or should have known of the possibility of such damages.
Metso, 2011. All rights reserved.
Expect results
Expect results is our promise to our customers and the essence of our strategy. It is the attitude we share globally. Our business is to deliver results to our customers, to help them reach their goals.
Metso’s Mining and Construction Technology, Lokomonkatu 3, PO Box 306, FI-33101 Tampere, Finland SUBJ
ECT
TO A
LTER
ATIO
N W
ITH
OU
T PR
IOR
NO
TIC
E.
BRO
CH
URE
NO
. 260
4-03
-11-
SBL/
TAM
PERE
- EN
GLI
SH
©20
11 M
ETSO