Biodegradable Polymers:
What is Polymer Degradation?
polymer degradation was viewed negatively as a process where properties and performance deteriorated with time.
Some of the important properties of a biodegradablebiomaterial can be summarized as follows The material should not evoke a sustained inflammatory or
toxic response upon implantation in the body. The material should have acceptable shelf life. The degradation time of the material should match the
healing or regeneration process.The degradation products should be non-toxic, and able to get
metabolized and cleared from the body. The material should have appropriate permeability and
processibility for the intended application.
Hydrolytically degradable polymers are polymers that have hydrolytically labile
chemical bonds in their back bone.
The functional groups susceptible to hydrolysis include
1) esters,
2) orthoesters,
3) anhydrides,
4) carbonates,
5) amides,
6) urethanes,
7) ureas,
Biodegradable Polymers
Carbonyl bond to
ONS
R1 C X
O
R2
OH2
R1 C OH
O
+ HX R2
Where X= O, N, S
R1 C O
O
R2
Ester
R1 C NH
O
R2
Amide
R1 C S
O
R2
A.
Thioester
X C X'
O
R2R1
OH2
+ HX' R2X C OH
O
R1
Where X and X’= O, N, S
B.
O C O
O
R2R1 NH C O
O
R2R1 NH C NH
O
R2R1
Carbonate Urethane Urea
C.R1 C X
O
C
O
R2
OH2
+R1 C OH
O
HX C
O
R2
R1 C NH
O
C
O
R2 R1 C O
O
C
O
R2
Imide Anhydride
Where X and X’= O, N, S
Biodegradable Polymers
Biodegradable PolymersAcetal:
Hemiacetal:
Ether
Nitrile
Phosphonate
Polycyanocrylate
OH2+C
O
H H
R' OHO C O
H
H
R R' R OH +
OC
C
C C
C
OH
OH
OH
OH
OH OHC
C
C C
OH
OH
OH
OH
H2O+
C==O
H
H2O
R C O C R'
H H
H HOH2
R C OH
H
H
R' C OH
H
H
+
R C R
C N
H
R C R
C O
H
NH2
R C R
C O
H
OH
OH2 OH2
RO P OR'
O
OR''
OH P OH
O
OR''
OH2+ +R OH OH R'
R C C C C R'
CN
C
OR''
CNH
H O C
OR'''
O
H
H
OH2R C C C
CN
C
OR''
H
H O
H
H
OH C R'
CN
C
OR'''
O
+
Synthetic or Natural Biodegradable PolymersWhy Do We Prefer Synthetic Ones?
Tailor-able properties Predictable lot-to-lot uniformity Free from concerns of immunogenicity Reliable source of raw materials
Degradation:The process of polymer chain scission by the cleavage of bonds between the monomers in polymer backbone•Biodegradation:The chemical breakdown of materials by the action of living organisms which leads to changes in physical properties. •Erosion:The mass loss of a polymer matrix due to the loss of monomers, oligomersor even pieces of non-degraded polymer. Erosion can be the result of 1. biological, 2. chemical 3. or physical effects. Degradation is the most important part of erosion.
Degradable mechanism
•Degradation is characterized by a loss of molecular weight and initiates polymer erosion. •Four major modes of polymers degradations:
1. Photo-degradation 2. Mechanical-degradation3. Thermal-degradation4. Chemical-degradation•Chemical degradation is the most important for biodegradable polymers
Hydrolysisis the most important mode of chemical
degradation.
•Hydrolysis------breakdown of organic materials
through the use of water
Catalyzed by acids, based, salts, or enzymes.
The result of its chemical structure, its morphology, its
dimensions and the body’s environment.
General stages of hydrolysis
A :Starts with water penetrates deeply into the interior areas
B :The functional groups in polymer chains hydrolyze and absorb
the water. Water reacts with the polymer resulting in cleavage of
covalent chemical bonds
C :Polymer is broken down to oligomersand monomers
(transported from the polymer bulk controlled by diffusion)
D: The release of degradation products leads to the mass loss
which is characteristic for erosion.
Factors affecting the velocity of degradation
1. Chemical bond nature: functional groups
(depend on main chain structure: anhydride > ester > carbonate)
2. Water uptake: degradation rates increase when raising the content of the hydrophilic components
3. PH: change degradation rates of polyesters by orders of magnitude
4. Crystallinity (Amorphous phase is only accessible to permeants and susceptible to enzyme attack.
4. GLASS TRANSITION TEMPERATURE:
1. The glassy / rubbery state of the polymer has a impact on chain mobility and
permeability characteristics of the polymer.
2. The molecular chain mobility determines the vunerability of the polymer to enzyme
attack.
3. The lysed fragments are unable to diffuse through the polymer in the gassy state
leading to intensification of autocatalyticic hydrolysis as in polymer s like PLGA
and PLA.
5. PHYSICAL DIMENSION:
Size and surface to volume ratio are significant in biodegradation
Particularly in important in primary stage of biodegradation when phagocytosis occurs
Factors Influence the Degradation Behavior Chemical Structure and Chemical Composition Distribution of Repeat Units in Multimers Molecular Weight Polydispersity Presence of Low Mw Compounds (monomer, oligomers, solvents, plasticizers, etc) Presence of Ionic Groups Presence of Chain Defects Presence of Unexpected Units Configurational Structure Morphology (crystallinity, presence of microstructure, orientation and residue
stress) Processing methods & Conditions Method of Sterilization Annealing Storage History Site of Implantation Absorbed Compounds Physiochemical Factors (shape, size) Mechanism of Hydrolysis (enzymes vs water)
Enzymatic degradation
•Mainly effective for naturally polymers(polysaccharides and polypeptides)•Serve a classic catalytic function, altering reaction rate (via ion or charge transfer) by modifying activation energy
Degradation Schemes Surface erosion with polymer which are hydrophobic but
contains labile chemical groups that are hydrolysable (poly(ortho)esters and polyanhydrides)
Sample is eroded from the surface SE maintains the bulk integrity Mass loss is faster than the ingress of water into the bulk
Bulk degradation (PLA,PGA,PLGA, PCL) Degradation takes place throughout the whole of the sample Ingress of water is faster than the rate of degradation
Polymer Degradation by Erosion (1)
Erodible Matrices or Micro/Nanospheres
Classification based on Chemical mechanisms includes :
Type-I: This type of erosion is evident with water soluble polymers
that are cross linked to form water insoluble. When placed in water
it swells to extent permitted to cross link density then cleavage of
crsosslinks takes place leading to further swelling of
polymer and finally dissolve.
Type-II: Occurs with polymers that were already water insoluble but converted to water soluble by hydrolysis,Ionisation
Type-III :Polymer having high MW but transformed to small water soluble by hydrolytic cleavage of labile groups
Classification of Biodegradable Polymers
PLGA/PLA
Polyglycolide
is a highly crystalline polymer (45–55% crystallinity)
The glass transition temperature of the polymer ranges from 35 to 40 1C . the melting point is greater than 200 1C.
Due to its excellent fiber forming ability, polyglycolide was initially investigated for
developing resorbable sutures. The first biodegradable synthetic suture called
DEXONs that was approved by the United States (US) Food and Drug Administration
Solubility: Insoluble with most organic solvent except
Halogenated hydrocarbons,tetrahydrofuran,dioxane,ethylacetate.
Polyglycolide is a bulk degrading polymer,
degrades by the non-specific scission of the ester backbone.
The polymer is known to lose its strength in 1–2 months when hydrolyzed and losses
mass within 6–12 months.
Rate of hydration and degree of degradation can be increased by increasing the
glycolide ratio in copolymer.
In the body, polyglycolides are broken down into glycine which can be excreted in the urine or converted into carbon dioxide and water via the citric acid cycle
Polylactides
Unlike glycolide, lactide is a chiral molecule and exist in two optically
active forms; L-lactide and D-lactide.
The polymerization of these monomers leads to the formation of
semi-crystalline polymers.
The polymerization of racemic (D,L)-lactide and mesolactide however,
results in the formation of amorphous polymers.
Among these monomers, L-lactide is the naturally occurring isomer.
poly(L-lactide) (PLLA) is also a crystalline polymer (37% crystallinity)
and the degree of crystallinity depends on the molecular weight and
polymer processing parameters.
It has a glass transition temperature of 60–65 1C and a melting
temperature of approximately 175 1C. Poly(L-lactide) is a slow-degrading polymer compared to polyglycolide. being more hydrophobic than polyglycolide,
the degradation rate of PLLA is very low.
It has been reported that high molecular weight PLLA can take
between 2 and 5.6 years for total resorption in vivo
Poly(DL-lactide) (PDLLA) is an amorphous polymer due to the random distribution of L-
and D-lactide units
has a glass transition temperature of 55–60 1C.
Due to its amorphous nature the polymer shows much lower strength (1.9 GPa)
compared to poly(L-lactide). This polymer loses its strength within 1–2 months when
hydrolyzed and undergoes a loss in mass within 12–16 months .
Being a low strength polymer with faster degradation rate compared to poly(L-lactide),
it is a preferred candidate for developing drug delivery
Polylactides undergo hydrolytic degradation via the bulk erosion mechanism by the
random scission of the ester backbone. It degrades into lactic acid a normal human
metabolic by-product, which is broken down into water and carbon dioxide via the
citric acid cycle
PLGA A co-polymer containing glycolic acid (GA) and L-lactic acid (LA).
Both L- and DL-lactides have been used for co-polymerization. In the composition
range of 25–75%, poly(L-lactide-co-glycolide) forms amorphous polymers. The
intermediate co-polymers were found to be much more unstable compared to the
homopolymers. Thus, 50/50 poly(DL-lactide-co-glycolide) degrades in approximately 1–
2 months, 75/25 in 4–5 months and 85/15 in 5–6 months.
PuraSorbsPLG is a semicrystalline bioresorbable co-polymer of L-lactide and glycolide with a monomer ratio of 80L:20G.
PLGA has been shown to under go bulk erosion through hydrolysis of the ester bonds
and the rate of degradation depends on a variety of parameters including the LA/GA
ratio, molecular weight, and the shape and structure of the matrix. PLGA demonstrates
good cell adhesion and proliferation making it a potential candidate for tissue
engineering applications
Several drug delivery vehicles composed of PLGA, such as microspheres,
microcapsules, nanospheres and nanofibers have been developed for the controlled
release of drugs or proteins.
Depending on the nature of the PLGA used, the drug or protein has been shown to have
varying extents of interactions with the base polymer resulting in rapid or prolonged
release profiles .However, due to the bulk degradation of the polymers, the achievement
of zero-order release kinetics from these polymer matrices has been found to be difficult.
Another concern with using PLGA as a protein delivery vehicle is the possibility of
protein denaturation within the delivery vehicle due to the bulk degradation mechanism
of the polymer and the acidic degradation products produced.
This has led to the search for surface eroding polymers as ideal candidates for
developing drug delivery vehicles. Surface eroding polymers have a greater ability to
achieve zero-order release kinetics for molecules delivered from the matrix and are able
to protect hydrolytically sensitive molecules by encapsulation.
PCL is a biodegradable and nontoxic polyester .
Carpolactone is prepared by oxidation of cyclohexanone with peracetic acid.
which is then polymerized by ring-opening polymerization in presence of tin octate
catlyst.
Polymerization may be by anionic, cationic ,coordination and radical type.
PCL is soluble in a wide range of solvents.
Its glass transition temperature is low,around -60 °C,
and its melting point is 60 – 65 °C.
PCL is a semi-rigid material at room te mperature
PCL is a semicrystalline polymer due to its regular structure
Degradation Nonenzymatic Hydrolysis of PCL yields 6-hydroxycaproic acid which enters the citric acid cycle and is metabolized.
Poly Carpo Lactones
1. PCL has been used clinically as a degradable staple for wound closure
2. 1-year drug delivery system for contraceptives
3. Biodegradibility can be increased by copolymerisation
4. Have good permeability to low MW drugs(<400D)
5. PCL typically has the highest percent crystallinity and the slowest degradation
rate as compared to the most common biodegradable polymers typically used for
drug delivery such as PLA or PLGA.
Chitin and chitosan. Structurally chitosan is a linear polysaccharide consisting of b (1-4) linked D-glucosamine with randomly located N-acetylglucosamine groups depending upon the degree of deacetylation of the polymer. Chitosan is derivedfrom chitin which is a fully acetylated polymer and forms the exoskeleton of arthropod
Enzymes, such as chitosanase, lysozyme and papain are known to degrade chitosan
in vitro .
The in vivo degradation of chitosan is primarily due to lysozyme and takes place
through the hydrolysis of the acetylated residues.
The rate of degradation of chitosan inversely depends on the degree of crosslinking,
acetylation and crystallinity of the polymer ,.
The highly deacetylated form exhibits the lowest degradation rates and may last
several months
Poly(ortho esters)Poly(ortho esters) were developed by the ALZA corporation (Alzamers) as a
hydrophobic, surface eroding polymer designed specifically for drug delivery
applications. Although the ortho ester linkages are hydrolytically labile, the polymer is
hydrophobic enough such that its erosion in aqueous environments is very slow. The
unique feature of poly(ortho esters) is that in addition to its surface erosion
mechanism, the rate of degradation for these polymers, pH sensitivity, and glass
transition temperatures can be controlled by using diols with varying levels of chain
flexibility.
The pH sensitivity of the poly(ortho esters) has lead to the development of several
drug delivery systems using this polymer.
The rate of drug release is predominantly controlled by the rate of polymer hydrolysis
through the use of acidic or basic excipients.
Exist in 4 forms
(POE III polymer : gel-like material at room temperature) this viscous nature helps
in incorporation of therapeutic agents into the polymer matrix without the need for
solvents .
POE IV has been considered to be the biomaterial with greatest potential having
well controlled release profiles for a wide range of pharmaceutical agents, including
proteins.
Upon exposure to aqueous environments, the latent acid will undergo hydrolysis,
and the liberated lactic or glycolic acid will catalyze further polymer hydrolysis
Chitosan is soluble in weekly acidic solutions resulting in the formation of a cationic
polymer with a high charge density and can therefore form polyelectrolyte complexes
with wide range of anionic polymers
The strong positive charges on chitosan makes it a very effective mucoadhesive as it
can strongly interact with the negatively charged mucous membrane.
Chitosan has the ability to act as a permeation enhancer through its interaction with the
cell membrane resulting in a structural reorganization of tight-junction associated
proteins. This, along with its mucoadhesive property, makes it a suitable
candidate for use in both oral and nasal vaccination formulations.
chitin and chitosan have shown to have stimulatory properties on macrophages, and
chemoattractive properties on neutrophils .
These properties, along with its antibacterial, hemostatic properties give chitosan
enourmous potential as a natural polymer for wound healing applications.
Alginic acid. Alginic acid present within the cell walls and intercellular spaces of brown algae
Due to its non-toxicity, alginate has been extensively used as a food additive
and a thickener in salad dressings and ice creamsAlginate is a non-branched, binary copolymer of (1-4) glycosidically linked b-D-mannuronic acid and a-L-guluronic acid monomers. They are high molecular weight polymers having molecular weights up to 500 kDa. Aqueous solutions of alginates show non-Newtonian behavior.
Main disadvantages of using alginate-based materials is their inability to undergo enzymatic degradation by mammals.Poor bioadhesive property.Developing alginate gels by gamma irradiation has been reported to be anotherelegant way for developing degradable alginate gels
Another method to induce biodegradation to alginate-based materials is by
chemical modification, which involves oxidation of the polymer backbone by
periodate resulting in formation of hydrolytically labile bond and the rate of
hydrolysis of the resulting polymer depends on pH and temperature
Fibrin Fibrin is a biopolymer similar to collagen that is involved in the natural blood clotting
process.
Fibrin is derived from fibrinogen
It has excellent biocompatibility, biodegradability, injectability
the presence of several extracellular matrix proteins, such as fibronectin, that
favorably affects cell adhesion and proliferation.
Due to its injectability and biodegradability, fibrin has also been investigated as a
carrier vehicle for bioactive molecules.
Several cross-linking techniques are also currently under investigation to control the
release profile of bioactive molecules from the fibrin matrix.
Fibrin matrices have also been found to be excellent cell carrier vehicles. Bioseeds is
a fibrin-based product obtained by mixing keratinocytes with fibrin and is used to treatchronic wounds.
The fibrin clot, once formed, can undergo degradation called fibrinolysis in the body initiated by a complex cascade of enzymes present in the human body
Albumin
Albumin is the most abundant protein in human blood plasma accounting to almost
50% of total plasma mass.
Albumin is a water soluble-protein with a molecular weight of 66 kDa.
All tissues in human body have the ability to degrade albumin, making it a highly
preferred degradable biopolymer for medical applications.
Due to its solubility and the presence of functional groups along the polymer chain,
albumin can be easily processed into various shapes and forms such as membranes,
microspheres, nanofibers and nanospheres.
Due to its excellent blood compatibility, albumin has been extensively investigated as a
carrier vehicle for intravenous drug/gene delivery .
Albumin has also been investigated as coating materials for cardiovascular devices.
GelatinHeterogenious product obtained by irreversible hydrolyticExtraction of treated animal collagen Physicochemical properties depends on source of collagen, Thermal degradation , pH value,extraction method, Electrolyte contentAdvantagesEasy availabilityLow antigen profile Low temperature preparation technique Poor binding to drug molecules